JP2008534734A - ポリ塩化ビニル樹脂用のトリエチレングリコールエステル可塑剤組成物及びその製造方法 - Google Patents
ポリ塩化ビニル樹脂用のトリエチレングリコールエステル可塑剤組成物及びその製造方法 Download PDFInfo
- Publication number
- JP2008534734A JP2008534734A JP2008503970A JP2008503970A JP2008534734A JP 2008534734 A JP2008534734 A JP 2008534734A JP 2008503970 A JP2008503970 A JP 2008503970A JP 2008503970 A JP2008503970 A JP 2008503970A JP 2008534734 A JP2008534734 A JP 2008534734A
- Authority
- JP
- Japan
- Prior art keywords
- plasticizer composition
- weight
- composition according
- carbon atoms
- triethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
ASTM,D412UTMに基づいて引張強度と伸張率を測定した。クロスヘッドスピードを200mm/minで引っ張った後、試片が切断される地点を測定し、引張強度及び伸張率を下記数式1及び数式2により計算した。
可塑化効率を表す指標として硬度を測定し、ASTM D2240方法に基づいて、硬度試験器(Aタイプ)の針を試片の一ヶ所に完全に下げて5分後の硬度値を読み取り、それぞれの試片に対して五ヶ所を試験した後、その平均値を取った。前記硬度は、試片を製造した直後に1回測定し、試片を製造した後に1日が経過した後に再び1回さらに測定した。
二つの方法で評価した。最初に、ヘイズメーターを利用してヘイズ値を試片の製造直後に測定し、二番目に、ラップフィルム試片を製造して7日が経過した後に試片を肉眼で観察して、標準可塑剤であるDEHAで製造したラップフィルムに比べて透明度が優れた場合、同等な場合、劣った場合の三つに分けて評価した。
手で直接接触して、DEHAで製造したラップフィルムと比較して5点尺度で、粘着の程度が良好な場合には5点、類似した場合には3点、不十分な場合には1点を付与して評価した。
トリエチレングリコールエステル可塑剤組成物の製造
攪拌器と冷却器とが付着された4口2L丸フラスコにトリエチレングリコール2.5モル、2−エチルへキサン酸5.25モル、安息香酸2.25モル、共留剤であるキシレン60g、触媒としてテトライソプロピルチタネート1.5gを投入した後、220℃まで昇温させて6時間の間反応を行った。
前記で得たトリエチレングリコールエステル混合物の可塑剤としての性能を評価するために、ASTM D638に基づいて試片を製造した。すなわち、ポリ塩化ビニル樹脂((株)LG化学製、製品名LS100S)100重量部に可塑剤として前記で得たトリエチレングリコールエステル混合物36重量部、エポキシ大豆油((株)新東邦製)14重量部、グリコール系防曇剤として日本の理研ビタミン社製のKA−901 2重量部、及びCa−Zn有機複合安定剤として韓国大協社製のLTX−630P 1.2重量部を配合し、ロールミルを利用して175℃で3分間作業して5mmのシートを製作した。次いで、プレス器を利用して185℃で予熱3分、加熱3分及び冷却3分間作業して1mmのシートを生成し、Cタイプに複数個の亜鈴形試片を製造した。前記のように使用した防曇剤は、水蒸気などがラップフィルムの表面に凝縮されてぼやけるのを防止するための添加剤を意味する。
使用する原料の量を下記表1に示したように変化させた点を除いては、前記実施例1の方法と同じ方法でトリエチレングリコールエステル可塑剤組成物を製造した。製造されたトリエチレングリコールエステル混合物を分析した結果、2−(2−(2−(2−エチルヘキサノイルオキシ)エトキシ)エトキシ)エチル2−エチルヘキサノエート30重量%、2−(2−(2−フェニルカルボニルオキシエトキシ)エトキシ)エチル2−エチルヘキサノエート52重量%、及び2−(2−(2−フェニルカルボニルオキシエトキシ)エトキシ)エチルベンゾエート18重量%であった。
使用する原料の量を下記表1に示したように変化させた点を除いては、前記実施例1の方法と同じ方法でトリエチレングリコールエステル可塑剤組成物を製造した。製造されたトリエチレングリコールエステル混合物を分析した結果、2−(2−(2−(2−エチルヘキサノイルオキシ)エトキシ)エトキシ)エチル2−エチルヘキサノエート82重量%、2−(2−(2−フェニルカルボニルオキシエトキシ)エトキシ)エチル2−エチルヘキサノエート15重量%、及び2−(2−(2−フェニルカルボニルオキシエトキシ)エトキシ)エチルベンゾエート1重量%であった。
ラップフィルムの製造に最も広範囲に使われるジ−2−エチルへキシルアジペート((株)LG化学製、商品名:DOA)を可塑剤として使用して、実施例1の方法と同じ方法で試片を製造した。製造された試片で前記実施例1で実施したテストと同じテストを実施して、その結果を下記表2に整理した。
ラップフィルムの製造に広く使われるジイソノニルアジペート((株)LG化学製、商品名:DINA)を可塑剤として使用して、実施例1の方法と同じ方法で試片を製造した。製造された試片で前記実施例1で実施したテストと同じテストを実施して、その結果を下記表2に整理した。
食品包装用として使われる親環境可塑剤であるLGflex EBNW((株)LG化学製)を可塑剤として使用して、実施例1の方法と同じ方法で試片を製造した。製造された試片で前記実施例1で実施したテストと同じテストを実施して、その結果を下記表2に整理した。
ラップフィルムの製造に使われるアセチルモノグリセライド((株)日新乳化製、商品名:SOLFA−AM−GT90)を可塑剤として使用して、実施例1の方法と同じ方法で試片を製造した。製造された試片で前記実施例1で実施したテストと同じテストを実施して、その結果を下記表2に整理した。
Claims (16)
- 下記化学式1:
R1OCO−(CH2)2−O−(CH2)2−O−(CH2)2−OCOR2 ・・・(1)
[ここで、R1は、炭素数3ないし12のアルキル基であり、R2は、炭素数6ないし10のアリール基である]
のように表現されるトリエチレングリコール系化合物。 - R1は、1−エチルペンチル基であり、R2は、フェニル基であることを特徴とする請求項1に記載のトリエチレングリコール系化合物。
- 下記化学式1:
R1OCO−(CH2)2−O−(CH2)2−O−(CH2)2−OCOR2・・・(1)
[ここで、R1は、炭素数3ないし12のアルキル基であり、R2は、炭素数6ないし10のアリール基である]
の化合物を含む可塑剤組成物。 - R1は、1−エチルペンチル基であり、R2は、フェニル基であることを特徴とする請求項3に記載の可塑剤組成物。
- 前記化学式1の化合物の含量は、0.1ないし99.5重量%であることを特徴とする請求項3に記載の可塑剤組成物。
- 下記化学式2:
R3OCO−(CH2)2−O−(CH2)2−O−(CH2)2−OCOR4・・・(2)
[ここで、R3及びR4は、それぞれ独立的に炭素数3ないし12のアルキル基である]
の化合物及び
下記化学式3:
R5OCO−(CH2)2−O−(CH2)2−O−(CH2)2−OCOR6・・・(3)
[ここで、R5及びR6は、それぞれ独立的に炭素数6ないし10のアリール基である]
の化合物をさらに含むことを特徴とする請求項3に記載の可塑剤組成物。 - R1,R3またはR4のアルキル基の炭素数が4ないし10であることを特徴とする請求項6に記載の可塑剤組成物。
- (a)化学式1の化合物10ないし80重量%と、
(b)化学式2の化合物10ないし80重量%と、
(c)化学式3の化合物0ないし60重量%と、を含むことを特徴とする請求項6に記載の可塑剤組成物。 - (i)トリエチレングリコール10ないし40重量%と、
(ii)炭素数3ないし12の脂肪族酸1ないし80重量%と、
(iii)炭素数6ないし10の芳香族酸1ないし60重量%と、
(iv)触媒0.001ないし3重量%と、を混合して反応させるステップを含むことを特徴とする可塑剤組成物の製造方法。 - 前記脂肪酸は、2−エチルへキサン酸であり、前記芳香族酸は、安息香酸であることを特徴とする請求項9に記載の可塑剤組成物の製造方法。
- 前記反応を100ないし300℃で4ないし10時間の間反応させることを特徴とする請求項9に記載の可塑剤組成物の製造方法。
- 共留剤を1ないし10重量%さらに含めて反応させることを特徴とする請求項9に記載の可塑剤組成物の製造方法。
- 前記共留剤は、トルエン、キシレンまたは不活性気体であることを特徴とする請求項12に記載の可塑剤組成物の製造方法。
- 前記触媒は、パラトルエンスルホン酸またはテトライソプロピルチタネートであることを特徴とする請求項9に記載の可塑剤組成物の製造方法。
- 請求項3ないし8のうちいずれか一項に記載の可塑剤組成物を含むポリ塩化ビニル樹脂。
- 請求項3ないし8のうちいずれか一項に記載の可塑剤組成物を含む食品包装用ラップフィルム。