WO1997019206A1 - Verfahren zur elektrolytischen abscheidung von metallschichten - Google Patents
Verfahren zur elektrolytischen abscheidung von metallschichten Download PDFInfo
- Publication number
- WO1997019206A1 WO1997019206A1 PCT/EP1996/005140 EP9605140W WO9719206A1 WO 1997019206 A1 WO1997019206 A1 WO 1997019206A1 EP 9605140 W EP9605140 W EP 9605140W WO 9719206 A1 WO9719206 A1 WO 9719206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- current
- workpieces
- container
- deposition
- Prior art date
Abstract
Description
Claims