WO2006008930A1 - リチウム二次電池用負極材料及びその製造方法、並びにそれを用いたリチウム二次電池用負極及びリチウム二次電池 - Google Patents
リチウム二次電池用負極材料及びその製造方法、並びにそれを用いたリチウム二次電池用負極及びリチウム二次電池 Download PDFInfo
- Publication number
- WO2006008930A1 WO2006008930A1 PCT/JP2005/011974 JP2005011974W WO2006008930A1 WO 2006008930 A1 WO2006008930 A1 WO 2006008930A1 JP 2005011974 W JP2005011974 W JP 2005011974W WO 2006008930 A1 WO2006008930 A1 WO 2006008930A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- negative electrode
- lithium secondary
- secondary battery
- particles
- polymer
- Prior art date
Abstract
Description
Claims