WO2005054322A2 - Verfahren zur umsetzung von (i) thermoplastischen polyurethanen mit (ii) isocyanatgruppen aufweisenden verbindungen - Google Patents
Verfahren zur umsetzung von (i) thermoplastischen polyurethanen mit (ii) isocyanatgruppen aufweisenden verbindungen Download PDFInfo
- Publication number
- WO2005054322A2 WO2005054322A2 PCT/EP2004/013474 EP2004013474W WO2005054322A2 WO 2005054322 A2 WO2005054322 A2 WO 2005054322A2 EP 2004013474 W EP2004013474 W EP 2004013474W WO 2005054322 A2 WO2005054322 A2 WO 2005054322A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- isocyanate groups
- extruder
- compounds
- iia
- compounds containing
- Prior art date
Abstract
Description
Claims