WO2000052796A1 - Element de laser semiconducteur au nitrure - Google Patents
Element de laser semiconducteur au nitrure Download PDFInfo
- Publication number
- WO2000052796A1 WO2000052796A1 PCT/JP2000/001308 JP0001308W WO0052796A1 WO 2000052796 A1 WO2000052796 A1 WO 2000052796A1 JP 0001308 W JP0001308 W JP 0001308W WO 0052796 A1 WO0052796 A1 WO 0052796A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- nitride semiconductor
- light guide
- laser device
- stripe
- Prior art date
Description
Claims