JP2797015B2 - Resin molding - Google Patents
Resin moldingInfo
- Publication number
- JP2797015B2 JP2797015B2 JP10868090A JP10868090A JP2797015B2 JP 2797015 B2 JP2797015 B2 JP 2797015B2 JP 10868090 A JP10868090 A JP 10868090A JP 10868090 A JP10868090 A JP 10868090A JP 2797015 B2 JP2797015 B2 JP 2797015B2
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- dispersed
- test piece
- axis diameter
- polyphenylene ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、耐層剥離性、ウェルド強度保持率、耐熱
性、耐衝撃性、耐薬品性に優れ、電気・電子分野、自動
車分野、各種工業材料分野で利用できる樹脂成形体に関
するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] The present invention is excellent in delamination resistance, weld strength retention, heat resistance, impact resistance, chemical resistance, electric / electronic field, automobile field, various The present invention relates to a resin molded body that can be used in the field of industrial materials.
ポリフェニレンエーテルは透明性、機械的特性、電気
的特性、耐熱性に優れ、吸水性が低くかつ寸法安定性に
優れるものの、成形加工性や耐衝撃性に劣る欠点を有す
るため、ポリスチレン、ハイインパクトポリスチレンと
ブレンドすることにより成形加工性や耐衝撃性の問題点
を改良し、例えば工業部品、電気・電子部品、事務機器
ハウジング、自動車部品、精密部品などの樹脂成形体と
して広く利用されている。しかしながら、このポリフェ
ニレンエーテルとハイインパクトポリスチレンからなる
古典的なポリフェニレンエーテル樹脂組成物（米国特許
第3383435号に開示されている）は、耐衝撃性が改善さ
れるものの、耐薬品性に劣る欠点を有している。Polyphenylene ether is excellent in transparency, mechanical properties, electrical properties, heat resistance, low water absorption and excellent in dimensional stability, but has drawbacks of poor moldability and impact resistance, so polystyrene, high impact polystyrene By improving the processability and impact resistance by blending with resin, it has been widely used as resin molded products such as industrial parts, electric / electronic parts, office equipment housings, automobile parts, precision parts, and the like. However, the classic polyphenylene ether resin composition comprising polyphenylene ether and high-impact polystyrene (disclosed in U.S. Pat. No. 3,383,435) has the disadvantage that, although the impact resistance is improved, the chemical resistance is poor. doing.
このため、例えば、米国特許第3361851号、特公昭42
−7069号には、ポリフェニレンエーテルをポリオレフィ
ンとブレンドすることにより耐溶剤性、耐衝撃性を改良
する提案がなされているものの層剥離現象が著しく実用
に耐えないのが現状である。また、米国特許第3994856
号には、ポリフェニレンエーテルまたはポリフェニレン
エーテルおよびスチレン系樹脂を水添ブロック共重合体
とブレンドすることによる耐衝撃性、耐溶剤性の改良に
関する記載があり、米国特許第4145377号には、ポリフ
ェニレンエーテルまたはポリフェニレンエーテルおよび
スチレン系樹脂とポリオレフィン／水添ブロック共重合
体＝20〜80重量部/80〜20重量部からなる予備混合物お
よび水添ブロック共重合体とブレンドすることによる耐
衝撃性、耐溶剤性の改良に関する記載があり、さらに米
国特許第4166055号、同第4239673号および同第4242263
号には、ポリフェニレンエーテルをブロック共重合体ま
たは水添ブロック共重合体とポリオレフィンとブレンド
することによる耐衝撃性の改良が記載されている。そし
て米国特許第4383082号、ヨーロッパ特許第115712号お
よびドイツ特許第7410861号ではポリフェニレンエーテ
ルをポリオレフィンおよび水添ブロック共重合体とブレ
ンドすることにより耐衝撃性を改良する内容が記載され
ている。For this reason, for example, U.S. Pat.
No. 7069 proposes to improve the solvent resistance and impact resistance by blending polyphenylene ether with a polyolefin, but at present, the delamination phenomenon is remarkably unpractical. Also, U.S. Pat.
No. 4,145,377 describes improvement in impact resistance and solvent resistance by blending polyphenylene ether or polyphenylene ether and a styrene resin with a hydrogenated block copolymer. Impact resistance and solvent resistance by blending with polyphenylene ether and styrene resin and polyolefin / hydrogenated block copolymer = 20-80 parts by weight / 80-20 parts by weight of premix and hydrogenated block copolymer And U.S. Pat.Nos. 4,416,055, 4,396,733 and 4,242,263.
The publication describes the improvement of impact resistance by blending polyphenylene ether with a block copolymer or hydrogenated block copolymer and a polyolefin. U.S. Pat. No. 4,383,082, EP 115712 and German Patent 7410861 describe improving the impact resistance by blending polyphenylene ether with a polyolefin and a hydrogenated block copolymer.
また、米国特許第4863997号および特開昭63−113058
号、同63−225642号、同64−98647号、同64−204939号
および同64−221444号には、ポリオレフィン樹脂とポリ
フェニレンエーテル樹脂からなる樹脂組成物の改質に特
定の水添ブロック共重合体を配合し、耐薬品性、加工性
に優れた樹脂組成物が提案されている。Also, U.S. Pat.No. 4,863,997 and JP-A-63-113058
No. 63-225642, No. 64-98647, No. 64-204939 and No. 64-221444, a specific hydrogenated block copolymer for modifying a resin composition comprising a polyolefin resin and a polyphenylene ether resin. There has been proposed a resin composition which incorporates a coalescence and has excellent chemical resistance and workability.
一方、本出願人は、特開昭63−218748号、同63−2454
53号、および同64−40556号において特定のブロック共
重合体とポリオレフィンのプレコンパウンドをポリフェ
ニレンエーテルと溶融混練して、耐薬品性、加工性に優
れた樹脂組成物を提案した。On the other hand, the present applicant has disclosed Japanese Patent Application Laid-Open Nos. 63-218748 and 63-2454.
No. 53 and No. 64-40556 propose a resin composition excellent in chemical resistance and processability by melt-kneading a pre-compound of a specific block copolymer and polyolefin with polyphenylene ether.
しかしながら、これらポリフェニレンエーテルのポリ
オレフィンをブレンドした樹脂組成物に関する先行技術
は古典的なポリフェニレンエーテル樹脂組成物（ポリフ
ェニレンエーテルとスチレン系樹脂とから構成される組
成物）と比べ、耐溶剤性、耐衝撃性を改良する効果は認
められるものの、その性能は不十分であり、特に、実質
的にポリフェニレンエーテルが50重量％以上かつポリオ
レフィンが20重量％以下で構成される樹脂組成物をこれ
らの先行技術で作成した成形体は層剥離が著しく起こ
り、さらにはウェルドライン部を持つ成形体ではウェル
ド強度（引張強度）の低下が著しく起こり、各種工業素
材として年々高度化しているプラスチックの要求性能に
対応できていない問題点を残している。However, the prior art relating to resin compositions in which these polyphenylene ether polyolefins are blended has a solvent resistance and impact resistance which are lower than those of classic polyphenylene ether resin compositions (compositions composed of polyphenylene ether and styrene resin). Although the effect of improving the above is recognized, its performance is insufficient. In particular, a resin composition composed of substantially 50% by weight or more of polyphenylene ether and 20% by weight or less of polyolefin is prepared by these prior arts. In the molded product which has undergone delamination, the molded product having a weld line portion has a remarkable decrease in weld strength (tensile strength), and cannot meet the performance requirements of plastics, which are becoming increasingly sophisticated as various industrial materials every year. The problem remains.
本発明の目的は、上記した先行技術では達成できなか
ったポリフェニレンエーテルとポリオレフィンを含んだ
成形体の層剥離およびウェルドラインを持つ成形体のウ
ェルド強度を改良した樹脂成形体を提供することにあ
る。It is an object of the present invention to provide a resin molded product in which the molded product containing a polyphenylene ether and a polyolefin, which cannot be achieved by the above-mentioned prior art, has been improved in layer delamination and weld strength of a molded product having a weld line.
本発明者らは、このような現状に鑑み、ポリフェニレ
ンエーテル、ポリオレフィンおよびコンパティビライザ
ーからなる樹脂成形体に関して鋭意検討を重ねた結果、
分散相を形成するポリオレフィンおよびコンパティビラ
イザーを特定の分散状態に制御することにより、ウェル
ドラインを持つ樹脂成形体のウェルド強度を著しく改良
するほかに層剥離も同時に改良し、さらには耐熱性、耐
衝撃性、応力下における耐薬品性に優れた樹脂成形体を
もたらすことを見いだし本発明に到達した。The present inventors, in view of such current situation, as a result of intensive studies on a resin molded body composed of polyphenylene ether, polyolefin and a compatibilizer,
By controlling the polyolefin and compatibilizer that form the dispersed phase to a specific dispersion state, in addition to significantly improving the weld strength of the resin molded body having the weld line, the delamination is also improved at the same time. The present inventors have found that a resin molded article having excellent impact resistance and chemical resistance under stress can be obtained, and arrived at the present invention.
すなわち、本発明は、 樹脂成形体が、 （ａ） 連続相：ポリフェニレンエーテル、 （ｂ） 分散相：実質的に短軸径0.5μｍ以下で分散し
たポリオレフィン外層に、ビニル芳香族化合物−共役ジ
エン化合物共重合体およびビニル芳香族化合物−共役ジ
エン化合物共重合体の水素添加物から選ばれる少なくと
も１種の共重合体が凝集し、かつ、該共重合体が単独で
実質的に短軸径0.3μｍ以下で分散していることを特徴
とする樹脂成形体を提供するものである。That is, the present invention provides a resin molded article comprising: (a) a continuous phase: polyphenylene ether; (b) a dispersed phase: a vinyl aromatic compound-conjugated diene compound in a polyolefin outer layer substantially dispersed with a minor axis diameter of 0.5 μm or less. At least one copolymer selected from a copolymer and a hydrogenated product of a vinyl aromatic compound-conjugated diene compound copolymer is aggregated, and the copolymer is substantially 0.3 μm in minor axis diameter alone. The present invention provides a resin molded product characterized by being dispersed below.
ここで実質的に短軸径が0.5μｍ以下とは、透過型電
子顕微鏡で撮影した40,000倍写真（18cm×25cm）をもと
に短軸径の最大値を測定して計算し、その90％以上が0.
5μｍ以下の短軸径で分散していることをいう。また同
様に、実質的に短軸径0.3μｍ以下で分散しているとい
う意味も、上記と同様にして定義されるものである。Here, the fact that the minor axis diameter is 0.5 μm or less is calculated by measuring the maximum minor axis diameter based on a 40,000 × photograph (18 cm × 25 cm) taken by a transmission electron microscope, and calculating 90% of the maximum value. The above is 0.
It means that the particles are dispersed with a minor axis diameter of 5 μm or less. Similarly, the meaning that the particles are dispersed with a minor axis diameter of 0.3 μm or less is also defined in the same manner as described above.
本発明の樹脂成形体の連続相を形成するポリフェニレ
ンエーテル（以下、単にPPEと略記）は、結合単位： （ここで、R1,R2,R3,およびR4はそれぞれ、水素、ハロ
ゲン、炭素数１〜７までの第一級または第二級低級アル
キル基、フェニル基、ハロアルキル基、アミノアルキル
基、炭化水素オキシ基または少なくとも２個の炭素原子
がハロゲン原子と酸素原子とを隔てているハロ炭化水素
オキシ基からなる群から選択されるものであり、互に同
一でも異なっていてもよい）からなり、還元粘度（0.5g
/dl,クロロホルム溶液,30℃測定）が、0.15〜0.70の範
囲、より好ましくは0.20〜0.60の範囲にあるホモ重合体
および／または共重合体である。このPPEの具体的な例
としては、例えばポリ（2,6−ジメチル−1,4−フェニレ
ンエーテル）、ポリ（２−メチル−６−エチル−1,4−
フェニレンエーテル）、ポリ（2,6−ジフェニル−1,4−
フェニレンエーテル）、ポリ（２−メチル−６−フェニ
ル−1,4−フェニレンエーテル）、ポリ（2,6−ジクロロ
−1,4−フェニレンエーテル）等が挙げられ、さらに2,6
−ジメチルフェノールと他のフェノール類（例えば、2,
3,6−トリメチルフェノールや２−メチル−６−ブチル
フェノール）との共重合体のごときポリフェニレンエー
テル共重合体も挙げられる。中でもポリ（2,6−ジメチ
ル−1,4−フェニレンエーテル）、2,6−ジメチルフェノ
ールと2,3,6−トリメチルフェノールとの共重合体が好
ましく、さらにポリ（2,6−ジメチル−1,4−フェニレン
エーテル）が好ましい。The polyphenylene ether (hereinafter simply abbreviated as PPE) that forms the continuous phase of the resin molded article of the present invention has a bonding unit: (Where R 1 , R 2 , R 3 , and R 4 are each hydrogen, halogen, a primary or secondary lower alkyl group having 1 to 7 carbon atoms, a phenyl group, a haloalkyl group, an aminoalkyl group A hydrocarbon oxy group or a halohydrocarbon oxy group in which at least two carbon atoms separate a halogen atom and an oxygen atom, which may be the same or different from each other) And reduced viscosity (0.5g
/ dl, chloroform solution, measured at 30 ° C) is a homopolymer and / or copolymer having a range of 0.15 to 0.70, more preferably a range of 0.20 to 0.60. Specific examples of the PPE include, for example, poly (2,6-dimethyl-1,4-phenylene ether) and poly (2-methyl-6-ethyl-1,4-
Phenylene ether), poly (2,6-diphenyl-1,4-)
Phenylene ether), poly (2-methyl-6-phenyl-1,4-phenylene ether), poly (2,6-dichloro-1,4-phenylene ether) and the like.
-Dimethylphenol and other phenols (for example, 2,
Polyphenylene ether copolymers such as copolymers with 3,6-trimethylphenol and 2-methyl-6-butylphenol) are also included. Among them, poly (2,6-dimethyl-1,4-phenylene ether) and a copolymer of 2,6-dimethylphenol and 2,3,6-trimethylphenol are preferable, and poly (2,6-dimethyl-1) is more preferable. , 4-phenylene ether) is preferred.
かかるPPEの製造方法は公知の方法で得られるもので
あれば特に限定されるものではなく、例えば、米国特許
第3306874号記載のHayによる第一銅塩とアミンのコンプ
レックスを触媒として用い、例えば2,6−キシレノール
を酸化重合することにより容易に製造でき、そのほかに
も米国特許第3306875号、同第3257357号および同第3257
35号、特公昭52−17880号および特開昭50−51197号およ
び同63−152628号等に記載された方法で容易に製造でき
る。The method for producing such a PPE is not particularly limited as long as it can be obtained by a known method.For example, a complex of a cuprous salt and an amine according to Hay described in U.S. Pat. , 6-xylenol can be easily produced by oxidative polymerization, and in addition, U.S. Patent Nos. 3,306,875, 3,257,357 and 3,257.
No. 35, JP-B-52-17880, JP-A-50-51197 and JP-A-63-152628 can be easily produced.
また、本発明で用いるPPEは、上記したPPEのほかに、
該PPEとα，β−不飽和カルボン酸またはその誘導体と
をラジカル発生剤の存在下、非存在下で溶融状態、溶解
状態、スラリー状態で80〜350℃の温度下で反応させる
ことによって得られる公知の変性（該α，β−不飽和カ
ルボン酸またはその誘導体が0.01〜10重量％グラフトま
たは付加）PPEであってもよく、さらに上記したPPEと該
変性PPEの任意の割合の混合物であってもかまわない。Further, the PPE used in the present invention, in addition to the PPE described above,
It is obtained by reacting the PPE with an α, β-unsaturated carboxylic acid or a derivative thereof in the presence, absence or presence of a radical generator in a molten state, a dissolved state, or a slurry state at a temperature of 80 to 350 ° C. It may be a known modified (the α, β-unsaturated carboxylic acid or its derivative is grafted or added by 0.01 to 10% by weight) PPE, and further a mixture of the above-mentioned PPE and the modified PPE in any ratio. It doesn't matter.
そしてさらに、9,10−ジヒドロ−９−オキサ−10−フ
ォスファフェナントレンをPPE100重量部に対し0.2〜５
重量部添加し溶融混練処理したリン化合物処理PPEも色
調に優れたPPEとして供することができる。Further, 9,10-dihydro-9-oxa-10-phosphaphenanthrene is used in an amount of 0.2 to 5 parts by weight based on 100 parts by weight of PPE.
A phosphorus compound-treated PPE that has been added by weight and melt-kneaded can also be provided as PPE having excellent color tone.
つぎに本発明の樹脂成形体の分散相を形成するポリオ
レフィンは、通常の成形材料として用いられる数平均分
子量が30,000以上のポリオレフィンであり、例えば、高
密度ポリエチレン、超高分子最高密度ポリエチレン、低
密度ポリエチレン、線状低密度ポリエチレン、密度0.90
未満の超低密度ポリエチレン、アイソタクチックポリプ
ロピレンや、エチレン、プロピレン、他のα−オレフィ
ン、不飽和カルボン酸またはその誘導体の中から選ばれ
る２種以上の化合物の共重合体、例えばエチレン／ブテ
ン−１共重合体、エチレン−（メタ）アクリル酸共重合
体、エチレン−（メタ）アクリル酸エステル共重合体、
プロピレン／エチレン（ランダム、ブロック）共重合
体、プロピレン/1−ヘキセン共重合体、プロピレン/4−
メチル−１−ペンテン共重合体、およびポリ（４−メチ
ル−１−ペンテン）、ポリブテン−１等を挙げることが
でき、これらは１種のみならず２種以上を併用すること
ができる。これらのポリオレフィンのうち、ポリエチレ
ンが好ましく、低密度ポリエチレン、線状低密度ポリエ
チレン、高密度ポリエチレンが好ましい。Next, the polyolefin forming the dispersed phase of the resin molded article of the present invention is a polyolefin having a number average molecular weight of 30,000 or more used as a normal molding material, for example, high-density polyethylene, ultra-high-molecular-weight highest-density polyethylene, low-density polyethylene. Polyethylene, linear low density polyethylene, density 0.90
Less than low-density polyethylene, isotactic polypropylene, a copolymer of two or more compounds selected from ethylene, propylene, other α-olefins, unsaturated carboxylic acids or derivatives thereof, for example, ethylene / butene- 1 copolymer, ethylene- (meth) acrylic acid copolymer, ethylene- (meth) acrylic acid ester copolymer,
Propylene / ethylene (random, block) copolymer, propylene / 1-hexene copolymer, propylene / 4-
Methyl-1-pentene copolymer, poly (4-methyl-1-pentene), polybutene-1, and the like can be mentioned, and not only one kind but also two or more kinds can be used in combination. Of these polyolefins, polyethylene is preferred, and low density polyethylene, linear low density polyethylene, and high density polyethylene are preferred.
つぎに本発明の樹脂成形体の分散相を形成するビニル
芳香族化合物−共役ジエン化合物共重合体、ビニル芳香
族化合物−共役ジエン化合物共重合体の水素添加物（以
下、コンパティビライザーと略記）は、ビニル芳香族化
合物と共役ジエン化合物を共重合して得られる共重合
体、ビニル芳香族化合物と共役ジエン化合物を共重合し
て得られる共重合体の水素添加物（共重合した共役ジエ
ン化合物に基づくオレフィン性二重結合の少なくとも50
％以上、好ましくは80％以上が水素添加されている）で
あり、これらの少なくとも１種が用いられる。Next, a vinyl aromatic compound-conjugated diene compound copolymer and a hydrogenated product of a vinyl aromatic compound-conjugated diene compound copolymer which form a dispersed phase of the resin molded article of the present invention (hereinafter, abbreviated as a compatibilityizer) Is a hydrogenated product of a copolymer obtained by copolymerizing a vinyl aromatic compound and a conjugated diene compound, and a copolymer obtained by copolymerizing a vinyl aromatic compound and a conjugated diene compound (copolymerized conjugated diene compound). At least 50 of olefinic double bonds based on
% Or more, preferably 80% or more is hydrogenated), and at least one of them is used.
このコンパティビライザーの共重合形態としてランダ
ム共重合体、ブロック共重合体、グラフト共重合体およ
びこれらの組み合わせが挙げられ、中でもブロック共重
合体が好ましい。Examples of the copolymerization form of the compatibilizer include a random copolymer, a block copolymer, a graft copolymer, and a combination thereof. Among them, a block copolymer is preferable.
このコンパティビライザーを構成するビニル芳香族化
合物としては、例えば、スチレン、α−メチルスチレ
ン、ビニルトルエン、ｐ−第３ブチルスチレン、ジフェ
ニルエチレン等のうちから１種または２種以上が選択で
き、中でもスチレンが好ましい。また、共役ジエン化合
物としては、例えば、ブタジエン、イソプレン、1,3−
ペンタジエン、2,3−ジメチル−1,3−ブタジエン等のう
ちから１種または２種以上が選ばれ、中でもブタジエ
ン、イソプレンおよびこれらの組合わせが好ましい。As the vinyl aromatic compound constituting the compatibilizer, for example, one or more of styrene, α-methylstyrene, vinyltoluene, p-tert-butylstyrene, diphenylethylene and the like can be selected. Styrene is preferred. As the conjugated diene compound, for example, butadiene, isoprene, 1,3-
One or more kinds are selected from pentadiene, 2,3-dimethyl-1,3-butadiene and the like, and among them, butadiene, isoprene and a combination thereof are preferred.
このようなコンパティビライザーの一例としては、ア
ニオン重合して得られるスチレン−ブタジエン共重合
体、さらにこのスチレン−ブタジエン共重合体の水素添
加物が挙げられ、これらは、例えば、英国特許第1,130,
770号および米国特許第3,281,383号および同第3,639,51
7号に記載された方法や英国特許第1,020,720号および米
国特許第3,333,024号および同第4,501,857号に記載され
た方法で容易に製造できる。Examples of such a compatibilizer include a styrene-butadiene copolymer obtained by anionic polymerization, and a hydrogenated product of the styrene-butadiene copolymer.These include, for example, British Patent No. 1,130,
No. 770 and U.S. Pat.Nos. 3,281,383 and 3,639,51
No. 7,020,720 and U.S. Pat. Nos. 3,333,024 and 4,501,857.
これらのコンパティビライザーのうち、ヤング率が15
00kg/cm2以上のビニル芳香族化合物−共役ジエン化合物
ブロック共重合体、ヤング率が1500kg/cm2以上のビニル
芳香族化合物−共役ジエン化合物ブロック共重合体の水
素添加物が好ましい。このコンパティビライザーとして
例えば、旭化成工業（株）より「タフプレン」、「ソル
プレン」、「タフデン」、「アサプレン」、「タフテッ
ク」という商品名で市販されているものを用いることが
できる。Of these compatibilizers, the Young's modulus is 15
A hydrogenated product of a vinyl aromatic compound-conjugated diene compound block copolymer of at least 00 kg / cm 2 and a vinyl aromatic compound-conjugated diene compound block copolymer of a Young's modulus of at least 1500 kg / cm 2 is preferred. As the compatibilizer, for example, those marketed by Asahi Kasei Kogyo Co., Ltd. under the trade names "Tuffrene", "Solprene", "Tuffden", "Asaprene", and "Toughtec" can be used.
本発明は前述のとうり、以下の特徴をもつ樹脂成形体
である。As described above, the present invention is a resin molded article having the following characteristics.
（ａ） 連続相：ポリフェニレンエーテル形成し、 （ｂ） 分散相：実質的に短軸径0.5μｍ以下で分散
したポリオレフィン外層にビニル芳香族化合物−共役ジ
エン化合物共重合体およびビニル芳香族化合物−共役ジ
エン化合物共重合体の水素添加物から選ばれる少なくと
も１種の共重合体が凝集し、かつ、該共重合体が単独
で実質的に短軸径0.3μｍ以下、より好ましくは0.1μｍ
以下で分散している構造をもつことを特徴とする。(A) continuous phase: formed polyphenylene ether; (b) dispersed phase: a vinyl aromatic compound-conjugated diene compound copolymer and a vinyl aromatic compound-conjugated in a polyolefin outer layer substantially dispersed with a minor axis diameter of 0.5 μm or less. At least one copolymer selected from hydrogenated diene compound copolymers is agglomerated, and the copolymer is substantially a minor axis diameter of 0.3 μm or less, more preferably 0.1 μm or less.
The following is characterized by having a dispersed structure.
このような特殊なモルフォロジーを示すことにより、
その成形体は前述の優れた効果を達成するが、成形体の
各成分の量比は、好ましくは以下のごとく選ばれる（た
だし、これに限られるわけではない。） すなわち、通常、上記のポリオレフィンを20重量％未
満、ビニル芳香族化合物−共役ジエン化合物共重合体お
よびビニル芳香族化合物−共役ジエン化合物共重合体の
水素添加物から選ばれる少なくとも１種の共重合体を40
重量％以下、ポリフェニレンエーテルを50〜95重量％含
んだ樹脂成形体であり、中でもポリオレフィンを５〜15
重量％、ビニル芳香族化合物−共役ジエン化合物共重合
体およびビニル芳香族化合物−共役ジエン化合物共重合
体の水素添加物から選ばれる少なくとも１種の共重合体
を10〜35重量％、ポリフェニレンエーテルを90〜50重量
％のものは、耐薬品性、耐熱性、耐衝撃性、ウェルド強
度に優れた樹脂成形体と成り得る。By showing such a special morphology,
Although the molded article achieves the above-mentioned excellent effects, the quantitative ratio of each component of the molded article is preferably selected as follows (but is not limited to this). Less than 20% by weight of at least one copolymer selected from a vinyl aromatic compound-conjugated diene compound copolymer and a hydrogenated product of a vinyl aromatic compound-conjugated diene compound copolymer.
It is a resin molded product containing 50 to 95% by weight of polyphenylene ether, and in particular, 5 to 15% by weight of polyolefin.
% By weight, 10 to 35% by weight of at least one copolymer selected from a vinyl aromatic compound-conjugated diene compound copolymer and a hydrogenated product of a vinyl aromatic compound-conjugated diene compound copolymer, and polyphenylene ether, When the content is 90 to 50% by weight, a resin molded article having excellent chemical resistance, heat resistance, impact resistance, and weld strength can be obtained.
このように、本発明の樹脂成形体は、２種の分散相
（上記のおよび）を有するものであるが、かかる特
徴の中で、コンパティビライザーであるビニル芳香族化
合物−共役ジエン化合物共重合体およびビニル芳香族化
合物−共役ジエン化合物共重合体の水素添加物から選ば
れる少なくとも１種がマトリックスを形成するPPE中に
単独で実質的に短軸径0.3μｍ以下、好ましくは0.1μｍ
以下で分散することによりウェルドラインを持つ樹脂成
形体のウェルド強度に多大な良い結果をもたらす。As described above, the resin molded article of the present invention has two types of dispersed phases (the above and). Among such features, the vinyl aromatic compound-conjugated diene compound copolymer which is a compatibilizer is included. At least one selected from a hydrogenated product of a copolymer and a vinyl aromatic compound-conjugated diene compound copolymer is used alone in PPE forming a matrix, and substantially has a minor axis diameter of 0.3 μm or less, preferably 0.1 μm or less.
By dispersing in the following, a very good result is obtained for the weld strength of the resin molded body having a weld line.
しかしながら、かかるポリオレフィンの短軸径分散が
実質的に0.5μｍを超えたり、あるいは単独で分散する
コンパティビライザーの短軸径分散が実質的に0.3μｍ
を超える樹脂成形体は、層剥離が顕著に見られ、ウェル
ドラインを持つ樹脂成形体のウェルド強度の低下が顕著
に認められる。However, the short axis diameter dispersion of such polyolefins substantially exceeds 0.5 μm, or the short axis diameter dispersion of a compatibilizer that is dispersed alone is substantially 0.3 μm.
In the resin molded product exceeding the above, delamination is remarkably observed, and a decrease in weld strength of the resin molded product having a weld line is remarkably observed.
なお、ポリフェニレンエーテル中に分散相を形成する
ポリオレフィンおよびコンパティビライザーの分散状態
は、通常、電子顕微鏡写真で容易に確認することがで
き、これらの分散相は（長軸径／短軸径）≧１の分散を
示し、具体的には長軸径＝短軸径の時には円状の分散形
態、そのほかに（長軸径／短軸径）＞１の時に、ラメラ
構造の分散形態、またはフィブリル構造の分散形態をと
る。The dispersion state of the polyolefin and the compatibilizer forming a dispersed phase in polyphenylene ether can usually be easily confirmed by an electron micrograph, and these dispersed phases are (major axis diameter / minor axis diameter) ≧ In particular, when the major axis diameter is equal to the minor axis diameter, the dispersion form is circular, and when (major axis diameter / minor axis diameter)> 1, the dispersion form has a lamella structure or a fibril structure. In a dispersed form.
また、実質的に短軸径0.5μｍ以下で分散したポリオ
レフィン外層に凝集したコンパティビライザーの状態も
同様に電子顕微鏡写真で容易に確認できる。In addition, the state of the compatibilizer which is substantially agglomerated in the polyolefin outer layer dispersed with a minor axis diameter of 0.5 μm or less can also be easily confirmed by an electron microscope photograph.
本発明で凝集とは、具体的には、かかるコンパティビ
ライザーが分散したポリオレフィンを微粒子状で取り囲
んだ分散形態や、コンパティビライザーがポリオレフィ
ン外周層を層状で取り囲んだ分散形態を意味するもので
あり、これらの形態に付加えてコンパティビライザーが
ポリオレフィンに融け込んでいても良い。Aggregation in the present invention specifically means a dispersion form in which the compatibilizer surrounds the dispersed polyolefin in fine particles, and a dispersion form in which the compatibilizer surrounds the polyolefin outer layer in a layered manner. In addition to these forms, the compatibilizer may be melted into the polyolefin.
本発明の樹脂成形体は、電子顕微鏡で確認することが
できる上述のこれらの分散形態の１種または２種以上か
ら成ることを特徴とする。The resin molded article of the present invention is characterized by comprising one or more of the above-mentioned dispersion forms which can be confirmed by an electron microscope.
以下、本発明の樹脂成形体の製造方法について説明す
る。Hereinafter, the method for producing the resin molded article of the present invention will be described.
この本発明の樹脂成形体となり得るためには、当然な
がら、供するポリフェニレンエーテル種、ポリオレフィ
ン種、コンパティビライザー種の選択、供する各素材の
量比関係の選択および溶融混合条件などの選択が重要と
なるが、得られる樹脂成形体の層剥離、ウェルドライン
を持つ樹脂成形体のウェルド強度を格段に改良するに
は、樹脂成形体の分散相であるポリオレフィンおよびコ
ンパティビライザーが上記した特定の微分散構造をもた
なければならない。In order to be able to become the resin molded article of the present invention, it is, of course, important to select the polyphenylene ether species, polyolefin species, and compatibilizer species to be provided, the selection of the quantitative ratio relationship of each material to be provided, and the selection of melt mixing conditions. However, in order to significantly improve the delamination of the resin molded product obtained and the weld strength of the resin molded product having a weld line, the polyolefin and the compatibilizer, which are the disperse phase of the resin molded product, have the specific fine dispersion described above. It must have a structure.
かかる本発明の樹脂成形体の分散状態を得る方法は、
上記した各成分を溶融混練するための溶融混練機が、
ニーディングブロックをスクリューの任意の位置に組み
込むことが可能な二軸以上の多軸押出機であり、用いる
スクリューの全ニーディングブロック部分を実質的に
（L/D≧1.5、さらに好ましくは（L/D≧５）〔ここでＬ
は、ニーディングブロックの長さ、Ｄはニーディングブ
ロックの最大外径をあらわす〕に組込み、かつ、（π・
Ｄ・N/h）≧50〔ここで、π;3.14,D:メタリングゾーン
に相当するスクリュー外径、N;スクリュー回転数（回転
／秒）、h;メタリングゾーンの溝深さ〕を満たし、そし
てさらに上記した各成分を、同時に押出機に供給し、
かつ、で示したニーディングブロック部分を組込んだ
位置に該当する押出機のバレル設定温度をPPEのガラス
転移温度（約210℃）以下にして溶融混練する必要があ
る。The method for obtaining the dispersion state of the resin molded article of the present invention is as follows.
A melt kneader for melt kneading the above components,
It is a multi-screw extruder having two or more screws capable of incorporating a kneading block at an arbitrary position of a screw, wherein all kneading blocks of a screw to be used are substantially (L / D ≧ 1.5, more preferably (L / D ≧ 5) [where L
Represents the length of the kneading block, and D represents the maximum outer diameter of the kneading block].
D · N / h) ≧ 50 [where, π; 3.14, D: screw outer diameter corresponding to the metering zone, N: screw rotation speed (rotations / second), h: groove depth of the metering zone] Filling, and further, each of the above components are simultaneously fed to an extruder,
In addition, it is necessary to set the barrel setting temperature of the extruder corresponding to the position where the kneading block portion is incorporated into the glass transition temperature (about 210 ° C.) of the PPE or less, and perform melt-kneading.
これら，に加えて、コンパティビライザーとし
て、少なくともヤング率1500kg/cm2以上のビニル芳香族
化合物−共役ジエン化合物共重合体、および、少なくと
もヤング率1500kg/cm2以上のビニル芳香族化合物−共役
ジエン化合物共重合体の水素添加物から選ばれる少なく
とも１種の共重合体を選択することにより本発明の樹脂
成形体を望ましく得ることができる。These, in addition, compounding a Tiby riser, at least a Young's modulus 1500 kg / cm 2 or more vinyl aromatic compound - conjugated diene compound copolymer, and at least a Young's modulus 1500 kg / cm 2 or more vinyl aromatic compound - conjugated diene By selecting at least one copolymer selected from hydrogenated compounds of the compound copolymer, the resin molded article of the present invention can be desirably obtained.
このような条件下で製造した本発明の樹脂成形体は、
層剥離やウェルドラインを持つ樹脂成形体のウェルド強
度が大幅に改良される。The resin molded article of the present invention manufactured under such conditions,
The weld strength of a resin molding having delamination and a weld line is greatly improved.
本発明では、上記の成分のほかに、本発明の特徴およ
び効果を損わない範囲で必要に応じて他の付加的成分、
例えば、ポリスチレン系樹脂（ポリスチレン、ハイイン
パクトポリスチレン等）や、酸化防止剤、耐候性改良
剤、ポリオレフィン用造核剤、スリップ剤、無機または
有機の充填剤や補強剤（ガラス繊維、カーボン繊維、ウ
ィスカー、マイカ、タルク、炭酸カルシウム、チタン酸
カリウム、ワラストナイト等）、難燃剤、可塑剤（トリ
フェニルホスフェート等のリン系化合物等）、各種着色
剤、帯電防止剤、離型剤等を添加してもかまわない。In the present invention, in addition to the above-mentioned components, other additional components as necessary within a range that does not impair the features and effects of the present invention,
For example, polystyrene resins (polystyrene, high impact polystyrene, etc.), antioxidants, weather resistance improvers, nucleating agents for polyolefins, slip agents, inorganic or organic fillers and reinforcing agents (glass fiber, carbon fiber, whisker) , Mica, talc, calcium carbonate, potassium titanate, wollastonite, etc.), flame retardants, plasticizers (phosphorus compounds such as triphenyl phosphate, etc.), various colorants, antistatic agents, release agents, etc. It doesn't matter.
本発明の樹脂成形体は、ポリフェニレンエーテル中に
分散したポリオレフィン、コンパティビライザーが、上
記した特定の微分散酸状態を示すものであれば、いかな
る成形方法で得られた樹脂成形体であってもよく、例え
ば、ペレット、さらにはこのペレットを用いて圧縮成
形、射出成形、押出成形、中空成形等により各種部品の
樹脂成形体として得ることができる。The resin molded article of the present invention may be a resin molded article obtained by any molding method, as long as the polyolefin dispersed in polyphenylene ether and the compatibilizer show the specific finely dispersed acid state described above. For example, pellets can be obtained as resin molded articles of various parts by using the pellets, for example, by compression molding, injection molding, extrusion molding, or hollow molding.
これら、各種部品として、例えば、自動車部品が挙げ
られ、具体的には、バンパー、フェンダー、ドアーパネ
ル、各種モール、エンブレム、エンジンフード、ホイー
ルキャップ、ルーフ、スポイラー等の外装部品や、イン
ストゥルメントパネル、コンソールボックス、トリム等
の内装部品等に適しており、さらに、電気機器の内外装
部品として好適に使用でき、具体的には、OA機器、テレ
ビ、ビデオ、テレビゲーム、各種ディスクプレーヤー等
のキャビネット、冷蔵庫等の部品用途に適している。These various parts include, for example, automobile parts, and specifically, exterior parts such as bumpers, fenders, door panels, various moldings, emblems, engine hoods, wheel caps, roofs, spoilers, and instrument panels. It is suitable for interior parts such as console boxes, trims, etc., and can also be suitably used as interior and exterior parts of electric equipment, and specifically, cabinets for OA equipment, televisions, videos, video games, various disc players, etc. Suitable for parts such as refrigerators.
本発明の樹脂成形体は、ポリフェニレンエーテル中に
分散するポリオレフィンと、ビニル芳香族化合物−共役
ジエン化合物共重合体およびビニル芳香族化合物−共役
ジエン化合物共重合体の水素添加物から選ばれる少なく
とも１種の共重合体が特定の微分散構造をとるため、層
剥離、ウェルド強度が大幅に改良される。The resin molded article of the present invention comprises a polyolefin dispersed in polyphenylene ether and at least one selected from a hydrogenated product of a vinyl aromatic compound-conjugated diene compound copolymer and a vinyl aromatic compound-conjugated diene compound copolymer. Has a specific finely dispersed structure, so that delamination and weld strength are greatly improved.
本発明を実施例によって、さらに詳細に説明するが、
これらの実施例により限定されるものではない。The present invention will be described in more detail by way of examples.
It is not limited by these examples.
実施例 １ 還元粘度0.56のポリフェニレンエーテル70重量部、低
密度ポリエチレン（サンテックLD−M1804;旭化成工業
（株）製）10重量部、スチレン−ブタジエン共重合体
（アサフレックス810;ヤング率4600kg/cm2、旭化成工業
（株）製）10重量部、スチレン−ブタジエン共重合体
（ソルプレンT406;ヤング率2100kg/cm2,日本エラストマ
ー（株）製）10重量部、9,10−ジヒドロ−９−オキサ−
10−フォスファフェナントレン1.5重量部、トリフェニ
ルフォスフェート７重量部をヘンシェルミキサーでブレ
ンドし、スクリューのニーディングブロック部分を190
℃に設定し、他の部分を270℃に設定した同方向回転二
軸押出機（PCM−30;池貝鉄工（株）製）を用い、全ニー
ディングブロックのL/D＝9.3、（π・Ｄ・N/h）＝157で
溶融混練し、押し出したストランドをペレットとして得
た。ここで得たペレットを280〜300℃に設定したスクリ
ューインライン型射出成形機に供給し、金型温度80℃の
条件で引張試験用テストピースを射出成形した。このテ
ストピースを用いて引張試験（ASTM D−638）を行い、
その破断面より成形体の層剥離の有無を確認したとこ
ろ、なんら層剥離は認められなかった。Example 1 70 parts by weight of polyphenylene ether having a reduced viscosity of 0.56, 10 parts by weight of low-density polyethylene (Suntech LD-M1804, manufactured by Asahi Kasei Corporation), styrene-butadiene copolymer (Asaflex 810; Young's modulus 4600 kg / cm 2) Asahi Kasei Kogyo Co., Ltd.) 10 parts by weight, styrene-butadiene copolymer (Sorprene T406; Young's modulus 2100 kg / cm 2 , Nippon Elastomer Co., Ltd.) 10 parts by weight, 9,10-dihydro-9-oxa-
1.5 parts by weight of 10-phosphaphenanthrene and 7 parts by weight of triphenyl phosphate were blended with a Henschel mixer, and the kneading block portion of the screw was mixed with 190 parts.
° C and the other part was set to 270 ° C using a co-rotating twin-screw extruder (PCM-30; manufactured by Ikegai Iron Works Co., Ltd.). D.N / h) = 157, and the extruded strands were obtained as pellets. The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. Perform a tensile test (ASTM D-638) using this test piece,
When the presence or absence of delamination of the molded article was confirmed from the fractured surface, no delamination was observed.
更に、ウェルドラインをつくることが可能なモールド
を用いて引張試験用テストピースを射出成形し、引張試
験（ASTM D−638）を行いウェルド強度保持率（ウェル
ドラインがあるテストピースの引張強度÷ウェルドライ
ンがないテストピースの引張強度×100％）を求めたと
ころ97％であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain a weld strength (the tensile strength of a test piece having a weld line divided by a weld strength). The tensile strength of a test piece without a line × 100%) was determined to be 97%.
なお、ウェルドラインがあるテストピースとは、中央
部にウエルドラインを持つASTM Type Iのダンベル片
（厚さ1/8インチ）の引張試験用テストピースのことを
いう。以下も同じ。The test piece having a weld line means a test piece for a tensile test of an ASTM Type I dumbbell piece (thickness: 1/8 inch) having a weld line in the center. The same applies to the following.
一方、別の引張試験用テストピースのオスミウム酸
（OsO4）で染色した切片を透過型電子顕微鏡で写真撮影
したところ、低密度ポリエチレンが実質的に0.5μｍ以
下の短軸径で分散し、スチレン−ブタジエン共重合体が
実質的に0.1μｍ以下の短軸径でポリフェニレンエーテ
ル中に分散し、かつ、スチレン−ブタジエン共重合体が
分散相の低密度ポリエチレンの外層に微粒子状で凝集し
ている構造であった。On the other hand, when a section of another test piece for tensile test stained with osmic acid (OsO 4 ) was photographed with a transmission electron microscope, low-density polyethylene was substantially dispersed with a minor axis diameter of 0.5 μm or less, and styrene was removed. A structure in which the butadiene copolymer is substantially dispersed in polyphenylene ether with a minor axis diameter of 0.1 μm or less, and the styrene-butadiene copolymer is aggregated in the form of fine particles in the outer layer of the low-density polyethylene of the dispersed phase. Met.
比較例 １ 用いる押出機を異方向回転二軸押出機（30mm径；ナカ
タニ機械（株）製）にし、全ニーディングブロックのL/
D＝０（この押出機のスクリューは実質的にニーディン
グブロックを組込めない）、（π・Ｄ・N/h）＝36.2に
し、設定温度を240〜270℃にしたほかは、実施例１と同
じ組成で溶融混練し、さらに実施例１と同じ条件で射出
成形した。得た引張試験テストピースを用いて実施例１
と同じ条件で引張試験を行ったところ、テストピースの
破断面の表層部に顕著な層剥離が認められた。Comparative Example 1 The extruder used was a different-direction rotating twin-screw extruder (30 mm diameter; manufactured by Nakatani Machinery Co., Ltd.)
Example 1 except that D = 0 (the screw of this extruder cannot substantially incorporate a kneading block), (π · D · N / h) = 36.2, and the set temperature was 240 to 270 ° C. The composition was melt-kneaded with the same composition as in Example 1, and injection molding was performed under the same conditions as in Example 1. Example 1 using the obtained tensile test piece
A tensile test was carried out under the same conditions as in Example 1. As a result, remarkable delamination was observed at the surface portion of the fractured surface of the test piece.
ウェルドラインを持つテストピースのウェルド強度保
持率を求めたところ64％であった。The weld strength retention of the test piece having a weld line was determined to be 64%.
さらに、別のテストピースを実施例１と同じ条件で透
過型電子顕微鏡を用いて写真撮影したところ、低密度ポ
リエチレンが0.4〜1.7μｍの短軸径で分散し、実質的に
0.5μｍを超える短軸径であった。また、スチレン−ブ
タジエン共重合体は0.5〜1.8μｍの短軸径でポリフェニ
レンエーテル中に分散し、実質的に0.3μｍを超える短
軸径であり、かつ、スチレン−ブタジエン共重合体が分
散相の該低密度ポリスチレンの外層に凝集している構造
であった。Furthermore, when another test piece was photographed using a transmission electron microscope under the same conditions as in Example 1, the low-density polyethylene was dispersed with a short axis diameter of 0.4 to 1.7 μm, and was substantially dispersed.
The minor axis diameter exceeded 0.5 μm. Further, the styrene-butadiene copolymer is dispersed in the polyphenylene ether with a short axis diameter of 0.5 to 1.8 μm, has a short axis diameter substantially exceeding 0.3 μm, and the styrene-butadiene copolymer is a dispersed phase. The structure was such that the low-density polystyrene was aggregated in the outer layer.
実施例２〜３、比較例２〜３ 還元粘度0.49のポリフェニレンエーテル76重量部、高
密度ポリエチレン（サンテックHD−J240;旭化成工業
（株）製）８重量部、スチレン−ブタジエンブロック共
重合体の水素添加物（ポリブタジエン部の水素添加率9
9.9％、ヤング率3200kg/cm2）８重量部、スチレン−ブ
タジエンブロック共重合体の水素添加物（ポリブタジエ
ン部の水素添加率99.9％、ヤング率5300kg/cm2）８重量
部をヘンシェルミキサーでブレンドし、スクリューのニ
ーディングブロック部分に該当する設定温度を200℃に
設定し、他の部分を270℃に設定した同方向回転二軸押
出機（PCM−30;池貝鉄工（株）製）を用い、全ニーディ
ングブロックのL/D＝4.1、（π・Ｄ・N/h）＝94.2（実
施例２）、全ニーディングブロックのL/D＝14、（π・
Ｄ・N/h）＝62.9（実施例３）、全ニーディングブロッ
クのL/D＝2.0、（π・Ｄ・N/h）＝37.7（比較例２）、
全ニーディングブロックのL/D＝０、（π・Ｄ・N/h）＝
62.9（比較例３）の条件で溶融混練し、押し出したスト
ランドをペレットとして得た。ここで得たペレットを28
0〜300℃に設定したスクリューインライン型射出成形機
に供給し、金型温度80℃の条件で引張試験用テストピー
スを射出成形した。このテストピースを用いて引張試験
（ASTM D−638）を行い、その破断面より成形体の層剥
離の有無を確認したところ、実施例２〜３で得られたテ
ストピースはなんら層剥離は認められなかった。しかし
ながら、同じ配合の組成物である比較例２〜３で得られ
たテストピースは顕著な層剥離現象が認められた。Examples 2-3, Comparative Examples 2-3 76 parts by weight of polyphenylene ether having a reduced viscosity of 0.49, 8 parts by weight of high-density polyethylene (Suntech HD-J240; manufactured by Asahi Kasei Corporation), hydrogen of styrene-butadiene block copolymer Additives (hydrogenation rate of polybutadiene part 9
8 parts by weight of 9.9%, Young's modulus 3200 kg / cm 2 ) and 8 parts by weight of hydrogenated styrene-butadiene block copolymer (hydrogenation rate of polybutadiene 99.9%, Young's modulus 5300 kg / cm 2 ) by Henschel mixer Then, using a co-rotating twin-screw extruder (PCM-30; Ikegai Iron Works Co., Ltd.) with the set temperature corresponding to the kneading block part of the screw set to 200 ° C and the other part set to 270 ° C , L / D of all kneading blocks = 4.1, (π · D · N / h) = 94.2 (Example 2), L / D of all kneading blocks = 14, (π · D
D · N / h) = 62.9 (Example 3), L / D of all kneading blocks = 2.0, (π · D · N / h) = 37.7 (Comparative Example 2),
L / D = 0 for all kneading blocks, (π · D · N / h) =
The extruded strands were obtained as pellets by melt-kneading under the conditions of 62.9 (Comparative Example 3). 28 pellets obtained here
The test piece was supplied to a screw in-line type injection molding machine set at 0 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. A tensile test (ASTM D-638) was performed using this test piece, and the presence or absence of delamination of the molded article was confirmed from the fracture surface. As a result, no delamination was observed in the test pieces obtained in Examples 2 and 3. I couldn't. However, in the test pieces obtained in Comparative Examples 2 and 3, which were compositions having the same composition, a remarkable delamination phenomenon was observed.
さらに、ウェルドラインを持つテストピースのウェル
ド強度保持率を求めたところ実施例２は91％、実施例３
は84％であり、比較例２および３はそれぞれ71％,63％
であった。Further, the weld strength retention of the test piece having a weld line was determined.
Is 84%, and Comparative Examples 2 and 3 are 71% and 63%, respectively.
Met.
実施例２〜３、比較例２〜３の各々のテストピースを
ルテニウム酸（RuO4）を用いて染色し、透過型電子顕微
鏡を用いて写真撮影したところ、実施例２〜３はポリフ
ェニレンエーテル中に分散する高密度ポリエチレンが実
質的に0.5μｍ以下の短軸径で分散し、比較例２は0.5μ
ｍ〜1.0μｍの短軸径で高密度ポリエチレンが分散し、
実質的に0.5μｍを超える短軸径であった。比較例３
は、0.5μｍ〜2.3μｍの短軸径で高密度ポリエチレンが
分散し、実質的に0.5μｍを超える短軸径であった。ま
た、コンパティビライザーのスチレン−ブタジエンブロ
ック共重合体の水素添加物は該高密度ポリエチレン外層
に凝集し、そして単独でPPE中に分散しているコンパテ
ィビライザーは実施例２〜３では実質的に短軸径0.1μ
ｍ以下で分散しているが、比較例２〜３では0.1μｍ〜
0.9μｍの短軸径で分散し、実質的に0.3μｍを超える短
軸径であった。Examples 2-3, a test piece of each of Comparative Examples 2-3 were stained with ruthenium acid (RuO 4), was photographed using a transmission electron microscope, Examples 2-3 are in the polyphenylene ether The high-density polyethylene that is dispersed in the dispersion is substantially dispersed with a minor axis diameter of 0.5 μm or less.
High-density polyethylene is dispersed with a short axis diameter of m to 1.0 μm,
The minor axis diameter substantially exceeded 0.5 μm. Comparative Example 3
The high-density polyethylene was dispersed with a short axis diameter of 0.5 μm to 2.3 μm, and the short axis diameter substantially exceeded 0.5 μm. Also, the hydrogenated product of the styrene-butadiene block copolymer of the compatibilizer aggregated in the outer layer of the high-density polyethylene, and the compatibilizer alone dispersed in PPE was substantially equivalent to that of Examples 2-3. Short shaft diameter 0.1μ
m, but in Comparative Examples 2-3, 0.1 μm
It was dispersed with a short axis diameter of 0.9 μm, and had a short axis diameter substantially exceeding 0.3 μm.
比較例 ４ 米国特許第4145377に準拠した組成物の作成。Comparative Example 4 Preparation of a composition according to US Pat. No. 4,145,377.
表１に示す組成のうち、（c1）成分の低密度ポリエチ
レンと（c2）成分のスチレン−ブタジエンブロック共重
合体の水素添加物を、同方向回転二軸押出機（PCM−30;
池貝鉄工（株）製）を用いて設定温度200〜240℃で溶融
混練し、プレコンパウンド（Ｃ）を作成した。さらにこ
こで得たプレコンパウンドと残りの成分を同方向回転二
軸押出機を用いて、設定温度230〜280℃、スクリュー回
転200rpmの条件で溶融混練し、押し出したストランドを
ペレットとして得た。Of the compositions shown in Table 1, (c 1) and low density polyethylene component (c 2) component of the styrene - a hydrogenated product of butadiene block copolymers, co-rotating twin screw extruder (PCM-30;
Pre-compound (C) was prepared by melting and kneading at a set temperature of 200 to 240 ° C. using Ikegai Iron Works Co., Ltd.). Further, the pre-compound obtained here and the remaining components were melt-kneaded using a co-rotating twin-screw extruder under the conditions of a set temperature of 230 to 280 ° C. and a screw rotation of 200 rpm, and an extruded strand was obtained as a pellet.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
テストピースの破断面の表層部に顕著な層剥離が認めら
れた。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
Remarkable delamination was observed in the surface layer portion of the fracture surface of the test piece.
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ66％であった。一方、別の引張試験用テストピー
スのルテニウム酸（RuO4）で染色した切片を透過型電子
顕微鏡で写真撮影したところ、低密度ポリエチレンが0.
8〜2.9μｍの短軸径で分散し、実質的に0.5μｍを超え
る短軸径であった。また、スチレン−ブタジエン共重合
体は0.9〜2.1μｍの短軸径でポリフェニレンエーテル中
に分散し、実質的に0.3μｍを超える短軸径であり、か
つ、スチレン−ブタジエン共重合体が分散相の該低密度
ポリエチレンの外層に凝集している構造であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). The tensile strength of the test piece without the line x 100%) was 66%. On the other hand, when a section of another test piece for tensile test stained with ruthenic acid (RuO 4 ) was photographed with a transmission electron microscope, it was found that the low-density polyethylene had a content of 0.
It was dispersed with a minor axis diameter of 8 to 2.9 μm, and the minor axis diameter substantially exceeded 0.5 μm. Further, the styrene-butadiene copolymer is dispersed in polyphenylene ether with a short axis diameter of 0.9 to 2.1 μm, has a short axis diameter substantially exceeding 0.3 μm, and the styrene-butadiene copolymer is a dispersed phase. The low-density polyethylene had a structure agglomerated in the outer layer.
比較例５〜７ 米国特許第4166055号、同第4239673号および同第4242
263号に準拠した組成物の作成。Comparative Examples 5 to 7 U.S. Pat.
Preparation of a composition according to No. 263.
表２に示す組成を同方向回転二軸押出機（PCM−30;池
貝鉄工（株）製）を用いて設定温度230〜280℃、スクリ
ュー回転200rpmの条件で溶融混練し、押し出したストラ
ンドをペレットとして得た。The composition shown in Table 2 was melt-kneaded using a co-rotating twin-screw extruder (PCM-30; Ikegai Iron Works Co., Ltd.) at a set temperature of 230 to 280 ° C. and a screw rotation of 200 rpm, and the extruded strand was pelletized. As obtained.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
テストピース（比較例５〜７）の破断面の表層部に顕著
な層剥離が認められた。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
Remarkable delamination was observed in the surface layer portion of the fracture surface of the test piece (Comparative Examples 5 to 7).
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ比較例５は59％、比較例６は68％、比較例７は51
％であった。一方、別の引張試験用テストピースのルテ
ニウム酸（RuO4）、またはオスミウム酸（OsO4）で染色
した切片を透過型電子顕微鏡で写真撮影したところ、比
較例５は低密度ポリエチレンが1.1〜2.2μｍの短軸径で
分散し、実質的に0.5μｍを超える短軸径であった。ス
チレン−ブタジエン共重合体の水素添加物は0.7〜2.3μ
ｍの短軸径でポリフェニレンエーテル中に分散し、実質
的に0.3μｍを超える短軸径であり、かつ、スチレン−
ブタジエン共重合体の水素添加物が分散相の該低密度ポ
リエチレンの外層に凝集している構造であった。比較例
６は低密度ポリエチレンが0.8〜2.5μｍの短軸径で分散
し、実質的に0.5μｍを超える短軸径であった。スチレ
ン−ブタジエン共重合体は0.5〜2.4μｍの短軸径でポリ
フェニレンエーテル中に分散し、実質的に0.3μｍを超
える短軸径であり、かつ、スチレン−ブタジエン共重合
体が分散相の該低密度ポリエチレンの外層に凝集してい
る構造であった。比較例７は低密度ポリエチレンが1.3
〜2.6μｍの短軸径で分散し、実質的に0.5μｍを超える
短軸径であった。スチレン−ブタジエン共重合体および
その水素添加物が1.1〜2.8μｍの短軸径でポリフェニレ
ンエーテル中に分散し、実質的に0.3μｍを超える短軸
径であり、かつ、スチレン−ブタジエン共重合体および
その水素添加物が分散相の該低密度ポリエチレンの外層
に凝集している構造であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). The tensile strength of a test piece without a line × 100%) was determined, and the results were 59% for Comparative Example 5, 68% for Comparative Example 6, and 51% for Comparative Example 7.
%Met. On the other hand, when a section of another test piece for tensile test stained with ruthenic acid (RuO 4 ) or osmate (OsO 4 ) was photographed with a transmission electron microscope, Comparative Example 5 showed that the low-density polyethylene was 1.1 to 2.2. The particles were dispersed with a short axis diameter of μm, and had a short axis diameter substantially exceeding 0.5 μm. Hydrogenated styrene-butadiene copolymer is 0.7-2.3μ
m having a minor axis diameter of greater than 0.3 μm, and having a minor axis diameter of greater than 0.3 μm.
The structure was such that the hydrogenated butadiene copolymer was aggregated in the outer layer of the low-density polyethylene in the dispersed phase. In Comparative Example 6, the low-density polyethylene was dispersed with a minor axis diameter of 0.8 to 2.5 μm, and the minor axis diameter substantially exceeded 0.5 μm. The styrene-butadiene copolymer is dispersed in the polyphenylene ether with a short axis diameter of 0.5 to 2.4 μm, has a short axis diameter substantially exceeding 0.3 μm, and the styrene-butadiene copolymer has a low axis of the dispersed phase. The structure was agglomerated in the outer layer of high density polyethylene. Comparative Example 7 had a low density polyethylene of 1.3
It was dispersed with a minor axis diameter of 〜2.6 μm, and had a minor axis diameter substantially exceeding 0.5 μm. A styrene-butadiene copolymer and a hydrogenated product thereof are dispersed in polyphenylene ether with a short axis diameter of 1.1 to 2.8 μm, have a short axis diameter substantially exceeding 0.3 μm, and a styrene-butadiene copolymer and The structure was such that the hydrogenated product was agglomerated in the outer layer of the low-density polyethylene of the dispersed phase.
比較例 ８ 特開昭63−218748号、同63−245453号および同64−40
556号に準拠した組成物の作成。Comparative Example 8 JP-A-63-218748, JP-A-63-245453 and JP-A-64-40
Preparation of a composition according to No. 556.
表３に示す組成のうち、（c1）成分の低密度ポリエチ
レンと（c2）成分のスチレン−ブタジエンラジアルテレ
ブロック共重合体を、同方向回転二軸押出機（PCM−30;
池貝鉄工（株）製）を用いて設定温度200〜240℃で溶融
混練し、プレコンパウンド（Ｃ）を作成した。さらにこ
こで得たプレコンパウンドと残りの成分を同方向回転二
軸押出機を用いて、設定温度230〜280℃、スクリュー回
転200rpmの条件で溶融混練し、押し出したストランドを
ペレットとして得た。Of the composition shown in Table 3, (c 1) and low density polyethylene component (c 2) component of the styrene - butadiene radial teleblock copolymer, co-rotating twin screw extruder (PCM-30;
Pre-compound (C) was prepared by melting and kneading at a set temperature of 200 to 240 ° C. using Ikegai Iron Works Co., Ltd.). Further, the pre-compound obtained here and the remaining components were melt-kneaded using a co-rotating twin-screw extruder under the conditions of a set temperature of 230 to 280 ° C. and a screw rotation of 200 rpm, and an extruded strand was obtained as a pellet.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
層剥離が認められなかった。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
No delamination was observed.
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ72％であった。一方、別の引張試験用テストピー
スのオスミウム酸（OsO4）で染色した切片を透過型電子
顕微鏡で写真撮影したところ、低密度ポリエチレンが0.
3〜1.1μｍの短軸径で分散し、実質的に0.5μｍを超え
る短軸径であった。スチレン−ブタジエンラジアルテレ
ブロック共重合体が分散相の低密度ポリエチレンの外層
に層状で凝集している構造であり、単独でポリフェニレ
ンエーテル中に実質的に0.3μｍ以下で分散したスチレ
ン−ブタジエンラジアルテレブロック共重合体は認めら
れなかった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). The tensile strength of a test piece without a line × 100%) was determined to be 72%. On the other hand, when a section of another test piece for tensile test stained with osmic acid (OsO 4 ) was photographed with a transmission electron microscope, it was found that the low-density polyethylene had a content of 0.
The particles were dispersed with a minor axis diameter of 3 to 1.1 μm, and the minor axis diameter substantially exceeded 0.5 μm. Styrene-butadiene radial teleblock is a structure in which the styrene-butadiene radial teleblock copolymer is layered and aggregated in the outer layer of the low-density polyethylene of the disperse phase, and is substantially dispersed in polyphenylene ether at substantially 0.3 μm or less. No copolymer was found.
実施例４〜６ 表４に示す各成分を実施例１と同じ同方向回転二軸押
出機（PCM−30;池貝鉄工（株）製）を用い、同じ押出機
条件で溶融混練し、押し出したストランドをペレットと
して得た。Examples 4 to 6 The components shown in Table 4 were melt-kneaded and extruded under the same extruder conditions using the same co-rotating twin-screw extruder (PCM-30; Ikegai Iron Works, Ltd.) as in Example 1. The strand was obtained as a pellet.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
実施例４〜６のすべてのテストピースで層剥離が認めら
れなかった。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
No delamination was observed in any of the test pieces of Examples 4 to 6.
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ、実施例４〜６のすべてが100％であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). When the tensile strength of a test piece without a line × 100%) was determined, all of Examples 4 to 6 were 100%.
一方、別の引張試験用テストピースのルテニウム（Ru
O4）で染色した切片を透過型電子顕微鏡で写真撮影した
ところ、実施例４〜６のテストピースすべてにおいて高
密度ポリエチレンが実質的に0.5μｍ以下の短軸径で分
散し、スチレン−ブタジエンブロック共重合体の水素添
加物が分散相の該高密度ポリエチレンの外層に層状で凝
集している構造であり、単独でポリフェニレンエーテル
中に分散したスチレン−ブタジエンブロック共重合体の
水素添加物が実質的に0.1μｍ以下であった。On the other hand, another tensile test piece ruthenium (Ru
When the sections stained with O 4 ) were photographed with a transmission electron microscope, the high-density polyethylene was dispersed with a minor axis diameter of substantially 0.5 μm or less in all of the test pieces of Examples 4 to 6, and a styrene-butadiene block was obtained. The structure is such that the hydrogenated product of the copolymer is layered and agglomerated in the outer layer of the high-density polyethylene of the dispersed phase, and the hydrogenated product of the styrene-butadiene block copolymer dispersed alone in polyphenylene ether is substantially Was 0.1 μm or less.
実施例７〜９ 表５に示す各成分を実施例１と同じ同方向回転二軸押
出機（PCM−30;池貝鉄工（株）製）を用い、同じ押出機
条件で溶融混練し、押し出したストランドをペレットと
して得た。Examples 7 to 9 The components shown in Table 5 were melt-kneaded and extruded under the same extruder conditions using the same co-rotating twin-screw extruder (PCM-30; Ikegai Iron Works, Ltd.) as in Example 1. The strand was obtained as a pellet.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
実施例７〜９のすべてのテストピースで層剥離が認めら
れなかった。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
No delamination was observed in any of the test pieces of Examples 7 to 9.
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ、実施例７〜９のすべてが100％であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). When the tensile strength of a test piece without a line × 100%) was determined, all of Examples 7 to 9 were 100%.
一方、別の引張試験用テストピースのルテニウム（Ru
O4）で染色した切片を透過型電子顕微鏡で写真撮影した
ところ、実施例７〜９のテストピースすべてにおいてポ
リプロピレンが実質的に0.5μｍ以下の短軸径で分散
し、スチレン−ブタジエンブロック共重合体の水素添加
物が分散相のポリプロピレンの外層に層状で凝集してい
る構造であり、単独でポリフェニレンエーテル中に分散
したスチレン−ブタジエンブロック共重合体の水素添加
物が実質的に0.1μｍ以下であった。On the other hand, another tensile test piece ruthenium (Ru
The sections stained with O 4 ) were photographed with a transmission electron microscope. As a result, in all of the test pieces of Examples 7 to 9, polypropylene was substantially dispersed with a short axis diameter of 0.5 μm or less, and the styrene-butadiene block copolymer was dispersed. The combined hydrogenated product has a structure in which the hydrogenated product of the styrene-butadiene block copolymer dispersed alone in polyphenylene ether is substantially 0.1 μm or less. there were.
実施例10〜12 表６に示す各成分を実施例１と同じ同方向回転二軸押
出機（PCM−30;池貝鉄工（株）製，日本国）を用い、同
じ押出機条件で溶融混練し、押し出したストランドをペ
レットとして得た。Examples 10 to 12 The components shown in Table 6 were melt-kneaded using the same co-rotating twin-screw extruder (PCM-30; Ikegai Iron Works, Japan) as in Example 1 under the same extruder conditions. The extruded strand was obtained as a pellet.
ここで得たペレットを280〜300℃に設定したスクリュ
ーインライン型射出成形機に供給し、金型温度80℃の条
件で引張試験用テストピースを射出成形した。このテス
トピースを用いて引張試験（ASTM D−638）を行い、そ
の破断面より成形体の層剥離の有無を確認したところ、
実施例10〜12のすべてのテストピースで層剥離が認めら
れなかった。 The pellets obtained here were supplied to a screw in-line type injection molding machine set at 280 to 300 ° C, and a test piece for a tensile test was injection-molded at a mold temperature of 80 ° C. When a tensile test (ASTM D-638) was performed using this test piece and the presence or absence of layer delamination of the molded body was confirmed from the fracture surface,
No delamination was observed in any of the test pieces of Examples 10 to 12.
さらに、ウェルドラインをつくることが可能なモール
ドを用いて引張試験用テストピースを射出成形し、引張
試験（ASTM D−638）を行いウェルド強度保持率（ウェ
ルドラインがあるテストピースの引張強度÷ウェルドラ
インがないテストピースの引張強度×100％）を求めた
ところ、実施例10〜12のすべてが100％であった。Furthermore, a test piece for a tensile test is injection-molded using a mold capable of forming a weld line, and a tensile test (ASTM D-638) is performed to maintain the weld strength (the tensile strength of the test piece with a weld line divided by the weld strength). When the tensile strength of a test piece without a line × 100%) was determined, all of Examples 10 to 12 were 100%.
一方、別の引張試験用テストピースのルテニウム（Ru
O4）で染色した切片を透過型電子顕微鏡で写真撮影した
ところ、実施例10〜12のテストピースすべてにおいてポ
リプロピレンおよび低密度ポリエチレンが実質的に0.5
μｍ以下の短軸径で分散し、スチレン−ブタジエンブロ
ック共重合体の水素添加物が分散相のポリプロピレンの
外層に層状で凝集している構造であり、単独でポリフェ
ニレンエーテル中に分散したスチレン−ブタジエンブロ
ック共重合体の水素添加物が実質的に0.1μｍ以下であ
った。On the other hand, another tensile test piece ruthenium (Ru
The sections stained with O 4 ) were photographed by transmission electron microscopy, showing that polypropylene and low-density polyethylene were substantially 0.5% in all of the test pieces of Examples 10 to 12.
Styrene-butadiene dispersed in a polyphenylene ether by itself, in which the hydrogenated styrene-butadiene block copolymer is dispersed in a layered form in the outer layer of polypropylene of the dispersed phase, and is dispersed with a minor axis diameter of not more than μm. The hydrogenated product of the block copolymer was substantially 0.1 μm or less.
実施例13 還元粘度0.54のポリフェニレンエーテル65重量部、線
状低密度ポリエチレン（サンテックLL−LM7625;旭化成
工業（株）製）15重量部、スチレン−ブタジエン共重合
体の水素添加物（ヤング率4800kg/cm2、水素添加率99.9
％）10重量部、スチレン−ブタジエン共重合体（ソルプ
レンT406;ヤング率2100kg/cm2、日本エラストマー
（株）製）10重量部をヘンシェルミキサーでブレンド
し、実施例１と同じ押出機を用い、同じ押し出し条件で
溶融混練した。ここで得たペレットのルテニウム酸（Ru
O4）で染色した切片を透過型電子顕微鏡で写真撮影した
ところ、線状低密度ポリエチレンが実質的に0.5μｍ以
下の短軸径で分散し、コンパティビライザーのブロック
共重合体が分散相の線状低密度ポリエチレンに融け込
み、かつ、線状低密度ポリエチレンの外層に層状で凝集
している構造であった。また、単独でポリフェニレンエ
ーテル中に分散したブロック共重合体は実質的に0.1μ
ｍ以下であった。Example 13 65 parts by weight of a polyphenylene ether having a reduced viscosity of 0.54, 15 parts by weight of a linear low-density polyethylene (Suntech LL-LM7625; manufactured by Asahi Kasei Corporation), and a hydrogenated product of a styrene-butadiene copolymer (Young's modulus 4800 kg / cm 2 , hydrogenation rate 99.9
%), 10 parts by weight of a styrene-butadiene copolymer (Sorprene T406; Young's modulus 2100 kg / cm 2 , manufactured by Nippon Elastomer Co., Ltd.) were blended with a Henschel mixer, and the same extruder as in Example 1 was used. Melt kneading was performed under the same extrusion conditions. Ruthenic acid (Ru
When the section stained with O 4 ) was photographed with a transmission electron microscope, the linear low-density polyethylene was substantially dispersed with a minor axis diameter of 0.5 μm or less, and the block copolymer of the compatibilizer was dispersed in the dispersed phase. The structure was such that it melted into the linear low-density polyethylene and was agglomerated in layers in the outer layer of the linear low-density polyethylene. Further, the block copolymer dispersed alone in polyphenylene ether is substantially 0.1 μm.
m or less.
実施例 14 実施例１で得たペレットを280〜300℃に設定した射出
成形に供給し、金型温度90℃の条件でASTM D−648に準
拠したテストピースを成形し、同方法に準拠して熱変形
温度を測定したところ119℃であった。また、同じ射出
条件で、ASTM D−256に準拠したテストピースを成形
し、同方法に準拠して23℃におけるアイゾット衝撃強度
を測定したところ42kg・cm/cmであった。さらに、この
厚さ1/8インチのアイゾット衝撃試験用のテストピース
を用いてベルゲンの1/4楕円法〔長軸24cm、短軸8cmの1/
4楕円治具に固定して一定歪を与える。（SPEジャーナ
ル,667,1962）〕に準じた測定法で、天ぷら油をテスト
ピースに塗布し80℃の条件でクラック発生の臨界歪を測
定したところ0.5％であった。Example 14 The pellets obtained in Example 1 were supplied to an injection molding set at 280 to 300 ° C, and a test piece compliant with ASTM D-648 was molded under the condition of a mold temperature of 90 ° C. The heat distortion temperature was measured to be 119 ° C. Further, under the same injection conditions, a test piece conforming to ASTM D-256 was molded, and the Izod impact strength at 23 ° C. measured according to the same method was 42 kg · cm / cm. Furthermore, using a 1/8 inch thick Izod impact test test piece, Bergen's 1/4 ellipse method (long axis 24 cm, short axis 8 cm 1 /
4Fix to an elliptical jig to give a constant strain. (SPE Journal, 667,1962)] Tempura oil was applied to a test piece and the critical strain at which cracks were generated was measured at 80 ° C., and the result was 0.5%.
第１図は実施例１で得た樹脂成形体の粒子構造体（モル
フォロジー）を示す電子顕微鏡写真であり、第２図は実
施例５で得た樹脂成形体の粒子構造（モルフォロジー）
を示す電子顕微鏡写真である。FIG. 1 is an electron micrograph showing the particle structure (morphology) of the resin molded product obtained in Example 1, and FIG. 2 is the particle structure (morphology) of the resin molded product obtained in Example 5.
FIG.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｃ０８Ｌ 71:12 (58)調査した分野(Int.Cl.6，ＤＢ名) C08L 71/12 C08L 53/02 C08J 5/00──────────────────────────────────────────────────続 き Continuation of the front page (51) Int.Cl. 6 identification code FI C08L 71:12 (58) Investigated field (Int.Cl. 6 , DB name) C08L 71/12 C08L 53/02 C08J 5/00
Claims (1)
したポリオレフィン外層に、ビニル芳香族化合物−共役
ジエン化合物共重合体およびビニル芳香族化合物−共役
ジエン化合物共重合体の水素添加物から選ばれる少なく
とも１種の共重合体が凝集し、かつ、該共重合体が単
独で実質的に短軸径0.3μｍ以下で分散していることを
特徴とする樹脂成形体。1. A resin molded article comprising: (a) a polyphenylene ether as a continuous phase and (b) a polyaromatic outer layer in which a dispersed phase is substantially dispersed with a minor axis diameter of 0.5 μm or less. At least one copolymer selected from a hydrogenated product of a compound copolymer and a vinyl aromatic compound-conjugated diene compound copolymer is aggregated, and the copolymer alone has a substantially short axis diameter of 0.3. A resin molded product characterized by being dispersed at a particle size of not more than μm.