WO2011034035A1 - 活性エネルギー線硬化型樹脂組成物、その硬化物及びフィルム - Google Patents
活性エネルギー線硬化型樹脂組成物、その硬化物及びフィルム Download PDFInfo
- Publication number
- WO2011034035A1 WO2011034035A1 PCT/JP2010/065779 JP2010065779W WO2011034035A1 WO 2011034035 A1 WO2011034035 A1 WO 2011034035A1 JP 2010065779 W JP2010065779 W JP 2010065779W WO 2011034035 A1 WO2011034035 A1 WO 2011034035A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- meth
- acrylate
- resin composition
- curable resin
- active energy
- Prior art date
Abstract
Description
本発明で用いるウレタン(メタ)アクリレート(A)は、重量平均分子量(Mw)が5,000~30,000の範囲であるポリアルキレングリコール(C)と、ポリイソシアネート(D)と、分子構造中にヒドロキシル基を有する(メタ)アクリレート(E)とを必須の原料成分として反応させて得られるものである。指紋跡を目立ちにくくするには、指紋跡の表面での光の乱反射を抑えるために指紋跡をなるべく平たくぬれ広がらせることが必要である。一方、拭取りやすくするためにはハードコート層と指紋跡との接触面積をなるべく小さくすることが必要である。このように、指紋跡の目立ちにくさと指紋跡の拭取りやすさは相反する性質であるところ、本発明では、ウレタン(メタ)アクリレート(A)の必須の原料成分として、重量平均分子量(Mw)が5,000~30,000の範囲であるポリアルキレングリコール(C)を用いる事によって、上記相反する性質を共に満足する活性エネルギー線硬化型樹脂組成物を完成するに至った。
測定装置 ;東ソー株式会社製 HLC-8220GPC
カラム ;東ソー株式会社製 TSK-GUARDCOLUMN SuperHZ-L
+東ソー株式会社製 TSK-GEL SuperHZM-M×4
検出器 ;RI(示差屈折計)
データ処理;東ソー株式会社製 マルチステーションGPC-8020modelII
測定条件 ;カラム温度 40℃
溶媒 テトラヒドロフラン
流速 0.35ml/分
標準 ;単分散ポリスチレン
試料 ;樹脂固形分換算で0.2質量%のテトラヒドロフラン溶液をマイクロフィルターでろ過したもの(100μl)
測定装置 ;東ソー株式会社製 HLC-8220GPC
カラム ;東ソー株式会社製 TSK-GUARDCOLUMN SuperHZ-L
+東ソー株式会社製 TSK-GEL SuperHZM-M×4
検出器 ;RI(示差屈折計)
データ処理;東ソー株式会社製 マルチステーションGPC-8020modelII
測定条件 ;カラム温度 40℃
溶媒 テトラヒドロフラン
流速 0.35ml/分
標準 ;単分散ポリスチレン
試料 ;樹脂固形分換算で0.2質量%のテトラヒドロフラン溶液をマイクロフィルターでろ過したもの(100μl)
ポリアルキレングリコール1〔重量平均分子量(Mw):8000〕4000g(0.5モル)、トルエンジイソシアネート174g(1モル)をフラスコに仕込んだ。触媒としてオクタン酸スズ(II)とオクタン酸亜鉛(II)をそれぞれ200ppm、酸化防止剤としてジブチルヒドロキシトルエン3000ppm、重合禁止剤としてメトキノン300ppmとなるようにフラスコに加え、更に、酢酸ノルマルブチルを固形分が80%となるように加え混合し、系内の温度を80℃に調整した。
第1表に示す原料及び配合量で合成を行う以外は合成例1と同様にしてウレタンアクリレート(A2)及びウレタンアクリレート(A3)を得た。ウレタンアクリレート(A2)及び(A3)の重量平均分子量(Mw)と数平均分子量(Mn)の値を第1表に示す。
IPDI(イソホロンジイソシアネート)ヌレート266g(0.4モル)、HPA104g(0.8モル)をフラスコに仕込んだ。触媒としてオクタン酸スズ(II)とオクタン酸亜鉛(II)をそれぞれ200ppm、酸化防止剤としてジブチルヒドロキシトルエン3000ppm、重合禁止剤としてメトキノン300ppmとなるようにフラスコに加え、更に、酢酸ノルマルブチルを固形分が80%となるように加え混合し、系内の温度を80℃に調整した。系内に空気を吹き込みながら80℃で1時間反応させイソシアネート基を含有するウレタンアクリレートを得た。その後、系内にポリアルキレングリコール2〔重量平均分子量(Mw):15000〕3000g(0.2モル)を投入した。系内の温度を80℃に維持し系内のイソシアネート基が完全に消失するまで反応させウレタンアクリレート(A4)を得た。ウレタンアクリレート(A4)の重量平均分子量(Mw)と数平均分子量(Mn)の値を第1表に示す。
第1表に示す原料及び配合量で合成を行う以外は合成例1と同様にして比較対照用ウレタンアクリレート(a1)を得た。ウレタンアクリレート(a1)の重量平均分子量(Mw)と数平均分子量(Mn)の値を第1表に示す。
ポリアルキレングリコール3〔重量平均分子量(Mw):2000〕4000g(2モル)、イソホロンジイソシアネート222g(1モル)をフラスコに仕込んだ。触媒としてオクタン酸スズ(II)とオクタン酸亜鉛(II)をそれぞれ200ppm、酸化防止剤としてジブチルヒドロキシトルエン3000ppm、重合禁止剤としてメトキノン300ppmとなるようにフラスコに加え、更に、酢酸ノルマルブチルを固形分が80%となるように加え混合し、系内の温度を80℃に調整した。
※表中の値はモル数
ポリアルキレングリコール1:重量平均分子量(Mw)が8000のポリプロピレンオキシ鎖を有するグリコール。
ポリアルキレングリコール2:重量平均分子量(Mw)が15000のポリプロピレンオキシ鎖を有するグリコール。
ポリアルキレングリコール3:重量平均分子量(Mw)が2000のポリプロピレンオキシ鎖を有するグリコール。
TDI:トルエンジイソシアネート
H12MDI:4,4ービス(シクロヘキシルイソシアネート)
IPDI:イソホロンジイソシアネート
HEA:ヒドロキシエチルアクリレート
HPA:ヒドロキシプロピルアクリレート
PETA:ペンタエリスリトールトリアクリレート
ペンタエリスリトールトリアクリレートとペンタエリスリトールテトラアクリレートの混合物(質量比60/40)535.5質量部をフラスコに仕込んだ。触媒としてオクタン酸スズ(II)とオクタン酸亜鉛(II)をそれぞれ200ppm、酸化防止剤としてジブチルヒドロキシトルエン3000ppm、重合禁止剤としてメトキノン300ppmとなるようにフラスコに加え、更に酢酸ノルマルブチルを固形分が80%となるように混合し、系内の温度を50℃に調整した。
ウレタンアクリレート(A1)3部、ウレタンアクリレート(B1)48.5部、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物(質量比40/60)48.5部、1-ヒドロキシシクロヘキシルフェニルケトン4質量部、酢酸ノルマルブチル104部を混合し、固形分量が50%の活性エネルギー線硬化型組成物(1)を得た。組成物(1)を用いて下記条件にてフィルム上にハードコート層を形成し、ハードコート層の硬度、付着した指紋跡の目立ちにくさ及び付着した指紋跡の拭き取りやすさを下記基準に従って評価した。付着した指紋跡の目立ちにくさ及び付着した指紋跡の拭き取りやすさは、ハードコート層を形成した初期段階と指紋跡の付着と除去を20回繰り返した後の段階のそれぞれについて評価した。付着した指紋跡の除去は、後述する指紋跡の拭き取りやすさの評価方法で行った。尚、ウレタンアクリレート(B1)48.5部、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物(質量比40/60)48.5部の混合物のアクリロイル当量は104g/molであった。
組成物(1)PETフィルムに乾燥膜厚が5μmになるようにバーコーターを用いて塗工した。70℃で5分間溶剤を乾燥させた後、高圧水銀灯(80W/cm)で照射量が500mJ/cm2となるように紫外線を照射し、ハードコート層を得た。尚、紫外線の照射は窒素雰囲気下で行った。
JIS K5600-5-4にしたがって鉛筆硬度測定を行った。1つの硬度につき5回測定を行い、4回以上傷がつかない硬度を硬化塗膜の有する硬度とした。
指紋跡の目立ちにくさは視認角度で定量評価した。視認角度とは、ハードコート層に付着させた指紋跡に対する目視角度を90度から徐々に下げていき、指紋跡が確認され始める角度をいう。視認角度が小さいほど、指紋跡の目立ちにくさが良好である。
指紋跡の拭き取り易さは、指紋跡をハードコート層から除去する際のふき取り回数で評価した。具体的には、ハードコート層に付着させた指紋跡の上にティッシュペーパーを1Kg(5.7平方センチメートルあたり)で往復させ、付着した指紋跡が完全に見えなくなるまでの往復回数で定量評価した。この往復回数が少ないほど、指紋跡の拭取りやすさが良好である。
第2表に示す配合で行う以外は実施例1と同様にして活性エネルギー線硬化型樹脂組成物2~4及び比較対照用活性エネルギー線硬化型樹脂組成物1’~3’を調製した。実施例1と同様の評価を行った結果を第3表に示す。
多官能アクリレート(B2):ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物(質量比40/60)
多官能アクリレート(B1)と多官能アクリレート(B2)とを質量比1:1で混合した混合物のアクリロイル基当量は104g/mol
光開始剤:1-ヒドロキシシクロヘキシルフェニルケトン
希釈溶剤:酢酸ノルマルブチル
Claims (10)
- 重量平均分子量(Mw)が5,000~30,000の範囲であるポリアルキレングリコール(C)と、ポリイソシアネート(D)と、分子構造中にヒドロキシル基を有する(メタ)アクリレート(E)とを必須の原料成分として反応させて得られるウレタン(メタ)アクリレート(A)と、多官能(メタ)アクリレート(B)とを、(A)と(B)との質量比[(A)/(B)]が0.1/99.9~15/85の範囲となるように含有することを特徴とする活性エネルギー線硬化型樹脂組成物。
- 前記ポリアルキレングリコール(C)としてポリプロピレングリコールを用いることを特徴とする請求項1記載の活性エネルギー線硬化型樹脂組成物。
- 前記ポリイソシアネート(D)として脂環式ジイソシアネートを用いることを特徴とする請求項1記載の活性エネルギー線硬化型樹脂組成物。
- 前記ヒドロキシル基を有する(メタ)アクリレート(E)として(メタ)アクリロイル基を一つ有するヒドロキシ(メタ)アクリレートを用いることを特徴とする請求項1記載の活性エネルギー線硬化型樹脂組成物。
- 前記ウレタン(メタ)アクリレート(A)が、ポリアルキレングリコール(C)とポリイソシアネート(D)とを、ポリアルキレングリコール(C)のヒドロキシル基のモル数FCと、ポリイソシアネート(D)のイソシアネート基のモル数FDとの比[FC/FD]が1/1.05~1/3となる範囲で反応させてイソシアネート基含有ウレタンプレポリマーを得、該イソシアネート基含有ウレタンプレポリマーと分子構造中にヒドロキシル基を有する(メタ)アクリレート(E)とを、イソシアネート基含有プレポリマーのイソシアネート基のモル数FNCOと分子構造中にヒドロキシル基を有する(メタ)アクリレート(E)のヒドロキシル基のモル数FEとの比[FNCO/FE]が1/1~1/1.2となる範囲で反応させて得られるものである請求項1記載の活性エネルギー線硬化型樹脂組成物。
- 前記多官能(メタ)アクリレート(B)として、モノマー型の多官能(メタ)アクリレート(b1)と、分子量が600~3,000の範囲であるオリゴマー型多官能(メタ)アクリレート(b2)とを併用することを特徴とする請求項1記載の活性エネルギー線硬化型樹脂組成物。
- 前記分子量が600~3,000の範囲であるオリゴマー型多官能(メタ)アクリレート(b2)が多官能ウレタン(メタ)アクリレートである請求項6記載の活性エネルギー線硬化型樹脂組成物。
- 前記モノマー型の多官能(メタ)アクリレート(b1)と分子量が600~3,000の範囲であるオリゴマー型多官能(メタ)アクリレート(b2)との質量比[(b1)/(b2)]が1/2~2/1の範囲である請求項6記載の活性エネルギー線硬化型樹脂組成物。
- 請求項1~8のいずれか1つに記載の活性エネルギー線硬化型樹脂組成物を硬化させてなることを特徴とする硬化物。
- 請求項1~8のいずれか1つに記載の活性エネルギー線硬化型樹脂組成物を硬化させてなる硬化層をフィルム状基材上に有することを特徴とするフィルム。