WO1999005788A1 - Dispositif de traitement d'ondes acoustiques de surface et son procede de fabrication - Google Patents
Dispositif de traitement d'ondes acoustiques de surface et son procede de fabrication Download PDFInfo
- Publication number
- WO1999005788A1 WO1999005788A1 PCT/JP1998/003360 JP9803360W WO9905788A1 WO 1999005788 A1 WO1999005788 A1 WO 1999005788A1 JP 9803360 W JP9803360 W JP 9803360W WO 9905788 A1 WO9905788 A1 WO 9905788A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- electrode
- acoustic wave
- surface acoustic
- metal
- Prior art date
Description
Claims