KR870004101A - 수-함유 실리콘 발포체 - Google Patents

수-함유 실리콘 발포체 Download PDF

Info

Publication number
KR870004101A
KR870004101A KR1019860008687A KR860008687A KR870004101A KR 870004101 A KR870004101 A KR 870004101A KR 1019860008687 A KR1019860008687 A KR 1019860008687A KR 860008687 A KR860008687 A KR 860008687A KR 870004101 A KR870004101 A KR 870004101A
Authority
KR
South Korea
Prior art keywords
weight
parts
units
component
sio
Prior art date
Application number
KR1019860008687A
Other languages
English (en)
Other versions
KR950000986B1 (ko
Inventor
얼 디틀레인 죤
마리 보맨 데어스
Original Assignee
알빈 어네스트 베이
다우 코닝 코포레이션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 알빈 어네스트 베이, 다우 코닝 코포레이션 filed Critical 알빈 어네스트 베이
Publication of KR870004101A publication Critical patent/KR870004101A/ko
Application granted granted Critical
Publication of KR950000986B1 publication Critical patent/KR950000986B1/ko

Abstract

내용 없음

Description

수-함유 실리콘 발포체
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (16)

  1. (A) 기본적으로, (1) 메틸, 에틸, 프로필, 비닐, 페닐 및 3,3,3-트리플루오로프로필 중에서 선택된 유기그룹을 갖고, 히드록실 또는 비닐 그룹으로 앤드블록되며, 25℃에서 0.4 내지 100Pa·s의 점도를 갖는 폴리디오르가노실록산 100중량부,
    (2) 일반식
    (여기서 R은 탄소수 1 내지 4의 알킬라디칼 또는 페닐이고, R1은 R 또는 수소이고, x는 y의 0 내지 40%이고, y는 3 이상이며, x+y는 실리콘 하이드라이드의 점도가 25℃에서 0.05Pa·s 이하로 되도록 하는 값이다)의 실리콘 하이드라이드 15 내지 50중량부, (3) 물 0.5 내지 15중량부, (4) 백금 촉매형태의, (A) 백만부당 백금 10 내지 100중량부, (5) 임의의 성분인, SiO4/2단위 : 규소-결합 히드록실 그룹 : (CH3)3SiO1/2단위 : 및 RaRb′SiO(4-a-b)/2및 R″[SiO(R′)bO(3-6)/2]2및 이들의 혼합물 [여기서 R은 4개 이상의 과불소화된 탄소원자를 함유하는 1가의 유기 라디칼이며 연쇄의 메틸렌 단위 둘이상에 의해 또는 연쇄의 메틸렌 단위 둘이상에 결합되는 산소원자에 의해 불소-함유 단위의 규소원자에 결합되고, R′는 탄소수 1 내지 3의 알킬 라디칼이고, R″는 4개 이상의 과불소화된 탄소원자를 함유하는 2가의 유기 라디칼이며 탄소 또는 산소원자에 의해 불소-함유단위의 규소원자에 결합되고, a는 1 또는 2이고, b는 0.1 또는 2이며 a와 b의 합은 3이하인데, 단, R 및 R″가 산소원자를 통해 규소에 결합된 불소-함유 단위를 나타내는 경우, 오르가노실록산 공중합체는 임의로 일반식 GSiO3/2(여기서, G는 분자당 평균 하나이상의 말단 히드록실 그룹을 함유하는 선형 유기중합체의 히드록실 그룹으로부터 수소를 제거함으로써 수득된 잔기이며 폴리에테르, 폴리옥시알킬렌글리콜 에틸렌계불포화알코올의 호모폴리머 및 에틸렌계 불포화 알코올과 에틸렌계 불포화 탄화수소와의 공중합체 중에서 선택된다)의 반복 단위를 함유한다]중에서 선택된 불소-함유 단위로 기본적으로 이루어진 수지상 벤젠-가용성 오르가노실록산 공중합체로 기본적으로 이루어진 프로포머(profoamer)(여기에서, SiO4/2단위 및 히드록실이 아닌 모든 단위 : SiO4/2단위의 몰비율은 0.7:1 내지 1.1:1 이며, 언급된 불소-함유단위와 모든 GSiO3/2단위의 농도는 (a) 25℃에서, 0.08Pa·s의 점도를 나타내는 히드록실-앤들블록된 폴리디메틸실록산중의 성분 (5) 의 10중량% 용액에 25℃에서 2.2×10-4N/cm 미만의 표면 장력을 부여하고, (b) 광학적 투명성을 이루기 위해 언급된 10중량% 용액에 크실렌 0 내지 100중량%의 첨가를 필요로 하기에 충분하다.), 및 (6) 임의의 성분인, 탄소수 1 내지 12의 알코올로 이루어진 성분들을 혼합하고, (B) 혼합물을, 주위온도에서 기포를 형성시키고 경화시켜 탄성 실리콘 발포체를 생성시킴을 특징으로 하여, 실온에서 연속-셀(open-cell)실리콘 발포체를 제조하는 방법.
  2. 제 1 항에 있어서, 성분(1)이 하이드록실 앤드블록 그룹을 갖는 폴리디오르실록산 및 비닐 앤드블록 그룹을 갖는 폴리디오르가노실록산으로 이루어지는 방법.
  3. 제 1 항에 있어서, 성분(2)가 15 내지 30중량부의 양으로 존재하는 방법.
  4. 제 3 항에 있어서, 실리콘 하이드라이드가, x가 y의 5% 미만인 실리콘 하이드라이드인 방법.
  5. 제 1 항에 있어서, 성분(3)이 1 내지 5중량부의 양으로 존재하는 방법.
  6. 제 2 항에 있어서, 성분2가 15 내지 30중량부의 양으로 존재하는 방법.
  7. 제 2 항에 있어서, 성분(3)이 1 내지 5중량부의 양으로 존재하는 방법.
  8. 제 1 항에 있어서, 프로포머 (5)가 1 내지 10중량부의 양으로 존재하는 방법.
  9. 제 1 항에 있어서, 성분 (5)의 불소-함유 단위가 일반식 RaRb′SiO(4-a-b)/2(여기서 R은 F(CnF2n)(CH2)2OC이고, R′는 메틸이고, a는 1이고, b는 0,1, 또는 2이고, c는 0 또는 1이며, 언급된 불소-함유 단위 각각의 n은 성분 (5)의 다른 불소-함유 단위 중의 n의 값과 동일하거나 상이한 정수를 나타내고 n의 평균 값은 4 내지 20이다)의 불소-함유 단위인 방법.
  10. 제 1 항에 있어서, 알코올 (6)이 1 내지 5중량부의 양으로 존재하는 방법.
  11. 제10항에 있어서, 알코올이 라우릴 알코올인 방법.
  12. 제10항에 있어서, 알코올이 n-프로판올인 방법.
  13. 제 1 항에 있어서, 저장 목적을 위해, 성분들을 두 파트(성분(4)가 (1)의 모두 또는 일부분과 한파트이고 성분(2)가 다른 파트이다)로 먼저 혼합하는 방법.
  14. 제 1 항의 방법에 의해 제조된 발포체.
  15. 제 8 항의 방법에 의해 제조된 발포체.
  16. 제13항의 방법에 의해 제조된 조성물.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019860008687A 1985-10-16 1986-10-16 수-함유 실리콘 발포체 KR950000986B1 (ko)