KR870004077A - 탄성 실리콘 발포체의 제조 방법 - Google Patents
탄성 실리콘 발포체의 제조 방법 Download PDFInfo
- Publication number
- KR870004077A KR870004077A KR1019860008598A KR860008598A KR870004077A KR 870004077 A KR870004077 A KR 870004077A KR 1019860008598 A KR1019860008598 A KR 1019860008598A KR 860008598 A KR860008598 A KR 860008598A KR 870004077 A KR870004077 A KR 870004077A
- Authority
- KR
- South Korea
- Prior art keywords
- mixture
- component
- units
- weight
- silicon
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (16)
- (A) 필수적으로, (1) 분자당 적어도 평균 약 2개의 비닐 라디칼을 갖는 비닐-함유폴리디오가노실록산(여기서 유기라디칼은 라디칼당 탄소원자 1 내지 6개를 함유하는 알킬라디칼, 페닐 및 비닐로 이루어진 그룹으로부터 선택된다).(2) 분자당 평균 1 내지 2.5개 이상의 실리콘-결합 히드록실라디칼을 가지며, 실리콘 원자당, 라디칼당 탄소원자 1 내지 6개를 함유하는 알킬 라디칼 및 페닐로 이루어진 그룹으로부터 선택된 평균 적어도 1개의 유기 라디칼을 갖는 히드록실화 폴리디오가노실록산.(3) 총혼합물 백만 중량부당 백금 5 내지 200중량부를 제공하기에 충분한 양의 백금 촉매.(4) 분자당 평균 적어도 3개의 실리콘-결합수소원자, 실리콘 원자당 평균 1개 이하의 실리콘-결합수소원자 및 라디칼당 탄소 원자 1 내지 6개를 함유하는 알킬라디칼 및 페닐로 이루어진 그룹으로 부터 선택된 유기라디칼을 갖는 오가노하이드로젠실록산.(5) 필수적으로 SiO4/2단위, 실리콘-결합히드록시 그룹, (CH3)3SiO4/2단위, 및 RaRb′SiO(4-a-b)/2및 R″[Si(R′)bO(3-b)/2]2이의 혼합물로 이루어진 그룹으로부터 선택된 불소-함유단위로 구성되는 수지상 벤젠-가용성 오가노실록산 공중합체로 주로 이루어지는 프로포머(profoamer)[여기에서 R은 적어도 4개의 과불소화 탄소원자를 함유하는 1가 유기라디칼이며 적어도 2개의 연쇄 메틸렌 단위에 의해 또는 적어도 2개의 연쇄 메틸렌 단위에 결합된 산소원자에 의해 상기 불소-함유단위의 실리콘 원자에 결합되고 R′는 탄소수 1 내지 3의 알킬라디칼이며, R″는 적어도 4개의 과불소화 탄소원자를 함유하는 2가 유기 라디칼이고 탄소 또는 산소 원자에 의해 상기 불소-함유 단위의 실리콘 원자에 결합되며, a는 1 또는 2이고 b는 0,1 또는 2이며, a와 b의 합은 3 또는 그 미만이고, 단 R 및 R″가 산소원자에 의해 실리콘에 결합된 불소-함유 단위를 나타내는 경우, 오가노실록산 공중합체는 임의로 일반식 GSiO3/2의 반복단위를 함유하며, 여기서 G는 분자당 평균 적어도 1개의 말단 히드록실 그룹을 함유하는 선형 유기중합체의 히드록실 그룹으로부터 수소원자를 제거하여 수득되는 잔기를 나타내는데, 이는 폴리에테르, 폴리옥시알킬렌 글리콜, 에틸렌성 불포화알코올의 단일 중합체 및 에틸렌성 불포화 알코올과 에틸렌성 불포화 탄화수소와의 공중합체로 이루어진 그룹으로부터 선택되며, SiO4/4단위에 대한 히드록실 및 SiO4/2단위를 제외한 모든 단위의 몰비는 0.7 : 1 내지 1.1 : 1 이고, 상기 불소-함유 단위와 존재하는 GSiO3/2단위의 농도는 (a) 25℃에서 0.08Pa,S 의 점도를 나타내는 히드록실 말단 차단된 폴리디메틸실록산중의 성분(5)의 10중량% 용액에 25℃에서 2.2×10-4N/cm(newtons per cen-timeter)미만의 표면장력을 제공하기에 충분하며, (b) 광학 투명도를 얻기 위해 상기 10중량% 용액에 크실렌 0 내지 100중량%의 첨가를 필요로 하기에 충분한 농도이다], 및 (6) 임의로 액화 발포제를 함유하는 혼합물을 대기압하의 영역에 방출하면 발포체를 형성하기에 충분한 양의 액화 발포제(여기에서 이러한 액화 발포제를 함유하는 혼합물은 초대기압하에서 보존한다), 및 (7) 임의로, 탄소수 1 내지 12의 알코올, 및 (8) 임의로, 필수적으로 비가연성 섬유 및 황을 함유하지 않는 카본블랙으로 구성된 난연성 첨가제로 구성된 성분들을 혼합하고 [여기에서는 비닐라디칼, 실리콘-결합 히드록실 라디칼 및 탄소-결합 히드록실 라디칼의 합에 대한 실리콘-결합수소 원자의 몰비 0.5 : 1 내지 40 : 1 을 제공하기에 충분한 오가노하이드로젠이 존재하며, 혼합물은 25℃에서 100Pa,S미만의 점도를 갖는다]: 그후 (B) 혼합물이 기포를 형성하도록 하고, 주위온도에서 탄성실리콘 발포체를 경화시킴을 특징으로 하여 탄성실리콘 발포체를 제조하는 방법.
- 제 1 항에 있어서, 프로포머(5)가 (A)의 혼합물의 총중량을 기준으로 1 내지 20%의 양으로 존재하는 방법.
- 제 1 항에 있어서, 성분들을 우선 저장할 목적으로 2개의 부분으로 혼합하는데, 성분(3)은 성분(1)및/또는 (2)의 전부 또는 일부와 함께 하나의 부분중에 존재하고, 성분(4)는 성분(1) 및/또는 (2)의 나머지와 함께 다른 한 부분에 존재하며 ; 성분(5)는 2개의 부분 중의 어느 하나 또는 둘다에 존재하고, 저장 후 두개의 부분을 혼합하여 상기 방법에서 (A)의 혼합물을 제공하는 방법.
- 제 1 항에 있어서, 성분(5)의 불소-함유 단위가 일반식 RaRb′SiO(4-a-b)/2의 단위이며, 여기에서 R은 F(CnF2n)(CH2)2Cc이고, R′는 메틸이며 ; a는 1이고 ; b는 0,1 또는 2이며 ; c는 0 또는 1 이고, 상기 불소-함유단위에서 n은 각각 성분(5)의 다른 불소-함유 단위에서의 n의 값에 대하여 동일하거나 상이한 정수를 나타내며, n의 평균값은 4 내지 20인 방법.
- 제 4 항에 있어서, d는 0이고, 성분(5)가 필수적으로 (CH3)3SiO12단위 SiO4/2단위 및 실리콘-결합 히드록실 그룹 0.2 내지 약 4중량%로 구성된 오가노실록산 공중합체와 일반식 F(CF2)nCH2CH2Si(CH3)bCl3-b(여기서 n은 실란들에 따라 변화하며 4 내지 14의정수를 나타낸다)의 동족성 실란의 혼합물과의 반응생성물인 방법.
- 제 4 항에 있어서, d는 1이고, 성분(5)가 필수적으로 (CH3)2SiO1/2단위 SiO4/2단위 및 실리콘-결합 히드록실 그룹 0.2 내지 약 4중량%로 구성된 오가노실록산 공중합체와 일반식 F(CF2)n(CH2)2OH의 동족성 불소-함유 알코올의 혼합물 (여기서 상기 알코올의 각 분자에서 n은 4 내지 14의 짝수정수를 나타낸다)과의 반응생성물인 방법.
- 제 3 항에 있어서, 성분(6)을 각 부분과 혼합하고, 혼합물은 저장을 위해 초대기압하에 보존하며 ; 저장 후 두개의 부분은 혼합하여 방법중의 (A)의 혼합물을 제공하고 단계(B)에서 대기압 하에 방출시키는 방법.
- 제 2 항에 있어서, (A)의 혼합물의 중량을 기준으로 하여 성분(7) 1 내지 10중량%를 (A)의 혼합물에 혼합시키는 방법.
- 제 8 항에 있어서, 알코올(7)이 라우릴 알코올인 방법.
- 제 9 항에 있어서, 필수적으로 성분 (1),(3),(5) 및 (7)로 구성되는 제1조성물을 필수적으로 성분(2) 및 (4)로 구성되는 제2조성물과 혼합하여 바쇼어 탄생(Bashore resiliency)20 미만의 개방 셀(open-cell)발포제를 수득하는 방법.
- 제 2 항에 있어서, (A)의 혼합물의 중량을 기준으로 하여 성분(8) 2 내지 10중량%를 (A)의 혼합물에 혼합물에 혼합시키는 방법.
- 제11항에 있어서, 성분(8)이 필수적으로 세라믹섬유 1 내지 5중량% 및 카본클랙 1 내지 5중량%로 구성되는 방법.
- 제 2 항에 있어서, 탄성 실리콘 발포체의 밀도가 160kg/m3미만인 방법.
- 제13항에 있어서, (A)의 혼합물의 중량을 기준으로 하여 성분(7) 1 내지 10중량%를 (A)의 혼합물에 혼합물에 혼합시키는 방법.
- 제14항에 있어서, (A)의 혼합물의 중량을 기준으로 하여 성분(8) 2 내지 10중량%를 (A)의 혼합물에 혼합물에 혼합시키는 방법.
- 제 1 항의 방법에 의해 제조된 발포체.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.