JPWO2014156638A1 - 全固体二次電池 - Google Patents
全固体二次電池 Download PDFInfo
- Publication number
- JPWO2014156638A1 JPWO2014156638A1 JP2015508265A JP2015508265A JPWO2014156638A1 JP WO2014156638 A1 JPWO2014156638 A1 JP WO2014156638A1 JP 2015508265 A JP2015508265 A JP 2015508265A JP 2015508265 A JP2015508265 A JP 2015508265A JP WO2014156638 A1 JPWO2014156638 A1 JP WO2014156638A1
- Authority
- JP
- Japan
- Prior art keywords
- layer
- negative electrode
- current collector
- active material
- electrode active
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)銅または銅合金を含む負極集電体と、前記負極集電体と対向して設けられたアルミニウム、アルミニウム合金またはステンレスからなる正極集電体との間に、前記負極集電体側から、前記負極集電体の表面に形成された負極活物質層と、1価または2価の金属と硫黄を含む硫化物固体電解質を含む固体電解質層と、前記正極集電体の表面に形成された正極活物質層と、が順に積層され、前記負極集電体の前記負極活物質層が形成される面に、耐硫化性層を有することを特徴とする全固体二次電池。
(2)前記耐硫化性層が、硫化銅を含む硫化銅層であることを特徴とする(1)に記載の全固体二次電池。
(3)前記硫化銅層の厚さが0.01〜1μmであることを特徴とする(2)に記載の全固体二次電池。
(4)前記耐硫化性層が、酸化銅を含む酸化銅層であることを特徴とする(1)に記載の全固体二次電池。
(5)前記酸化銅層の厚さが0.01〜1μmであることを特徴とする(4)に記載の全固体二次電池。
(6)前記酸化銅層は、酸化第一銅を主に含む負極集電体側の第1層と、酸化第二銅層を主に含む表層側の第2層とを有することを特徴とする(4)に記載の全固体二次電池。
(7)前記耐硫化性層が、ニッケル、亜鉛、スズから選ばれる少なくとも1種を含む耐硫化性金属層であることを特徴とする(1)に記載の全固体二次電池。
(8)前記耐硫化性金属層の厚さが0.01〜5μmであることを特徴とする(7)に記載の全固体二次電池。
(9)前記耐硫化性金属層の亜鉛またはスズが、前記負極集電体に含まれる銅と拡散合金化していることを特徴とする(7)に記載の全固体二次電池。
(10)前記拡散合金化層の上層に、さらにニッケル層が形成されていることを特徴とする(9)記載の全固体二次電池。
(11)銅または銅合金を含む負極集電体と、前記負極集電体と対向して設けられたアルミニウム、アルミニウム合金またはステンレスからなる正極集電体との間に、前記負極集電体側から、前記負極集電体の表面に形成された負極活物質層と、1価または2価の金属と硫黄を含む硫化物固体電解質を含む固体電解質層と、前記正極集電体の表面に形成された正極活物質層と、が順に積層され、前記負極集電体の前記負極活物質層が形成される表面の圧縮強度が1250〜3000MPaであることを特徴とする全固体二次電池。
(12)前記負極集電体の前記負極活物質層が形成される表面の圧縮弾性率が60〜125GPaであることを特徴とする(11)に記載の全固体二次電池。
(13)前記負極集電体の表面に、モリブデンまたはタングステンを含有する銅電析層を有し、前記銅電析層の厚さが0.1〜2.5μmであることを特徴とする(11)記載の全固体二次電池。
(14)前記正極活物質層に含まれる正極活物質として、硫黄、MxMo6X8−y(M=金属、X=S、Se、Te、0≦x≦4.0、0≦y≦0.2)、Mo6S8−x(0≦x≦0.2)のいずれかを用いることを特徴とする(1)または(11)記載の全固体二次電池。
(15)前記負極活物質層に含まれる負極活物質が、MxPy(0.9≦x,y≦10、M=Si,Sn,In,Al,Zn)であることを特徴とする(1)または(11)記載の全固体二次電池。
(16)前記負極活物質層中に、前記硫化物固体電解質が含まれていることを特徴とする(1)または(11)記載の全固体二次電池。
本発明の第1の実施形態について図面に基づいて詳細に説明する。図1は、第1の実施形態に係る全固体二次電池の断面図である。第1の実施形態に係る全固体二次電池1は、対向して設けられた負極集電体3と正極集電体17の間に、負極集電体3側から、負極活物質層5、固体電解質層9、正極活物質層13が積層されている。負極活物質層5は、負極活物質7、硫化物固体電解質11を含む。固体電解質層9は硫化物固体電解質11を含む。正極活物質層13は、正極活物質15、硫化物固体電解質11、導電助剤8を含む。 以下に、各層の構成について説明する。
負極集電体は、銅または銅合金を含む基材上に、負極活物質層が形成される面に、耐硫化性層を有する。第1の実施形態では、耐硫化性層として硫化銅層23を用いる。図2において、負極集電体3は、基材21の負極活物質層5が形成される面に、硫化銅層23が積層されている。形成する硫化銅層23の厚さは0.01〜1μmであり、化合物形態は硫化第一銅が主に形成されている。
硫化処理または硫化銅層形成には、銅系の基材21を硫化カリウムや硫化ナトリウムの水溶液へ浸漬処理する。塩素イオンやアンモニウムイオンを含有させるとさらに良い。pHは酸性または弱アルカリ性が良い。温度は室温で良い。時間は形成厚さによるが、10秒程度から数10秒程度、長くとも1分程度で、本発明の用途には足りる。本硫化処理の前処理として、浸漬脱脂またはカソード脱脂、次いで酸洗(中和)処理を施すことが好ましい。基材表面の洗浄と共に硫化処理時の基材濡れ性を向上させることができる。
硫化銅層23は耐硫化腐食性を有している。さらに、硫化第一銅や硫化第二銅はともに良導性である。特に、硫化銅層23が硫化第一銅である場合、硫化銅層と基材銅箔との密着性が良好である。
硫化物固体電解質11は、1価または2価の金属と硫黄を含む固体電解質である。硫化物固体電解質11に含まれる金属はLi、NaまたはMgが望ましい。イオン伝導性を有する、実用的な固体電解質として、Li+伝導体か、Na+伝導体、或いはMg2+伝導体が当面可能である。
Sを含む硫化物固体電解質には、Li2S−P2S5系、Li2S−P2S5−SiS2系、Li2S−P2S5−P2O5系、Li2S−SiS2−Li3PO4系、Li2S−SiS2−Li4SiO4系、Li2S−B2S3−LiI系、Li3+5xP1−xS4系(0.06≦x≦0.08)、Li3+5xP1−xS4−zOz系(0.02≦x≦0.11、0.20≦z≦1.55)、Li2S−GeS2−Li3PO4系、またはLi2S−GeS2−P2S5系、Li2S−GeS2−P2O5系等々を用いることができる。具体例として、70Li2S−30P2S5、75Li2S−15P2S5−10P2O5、63Li2S−36SiS2−1Li3PO4、57Li2S−38SiS2−5Li4SiO4、30Li2S−26B2S3−44LiI、Li7P3S11、Li3−25PO−95S4、Li3−35PO−93S4、Li3−35PO−93S3−5O0.5、Li10−GeP2−S12、Li3−25GeO−25PO−25S4、などを挙げることができる。
正極集電体17は、アルミニウム、アルミニウム合金またはステンレスからなる。正極集電体17として、純Al系の1000系や、Al−Mn系の3000系とAl−Fe系の8000系などが主に用いられる。さらに具体的には、1085や1N30、および1100の純Al系、並びに3003や8021の合金系である。ステンレスは合金組成や番手にかかわらず用いることができるが、含有成分と組成により耐食性とコストが大きく相違するので、注意が必要である。
正極活物質15には、リチウムイオン二次電池に一般的に用いられる正極活物質を使用できる。例えば、コバルト酸リチウムであり、LCO表面にニオブ酸リチウム(LiNbO3)などの酸化物をコーティングしたものである。また、LCOのCoをNiやMn、またはAlで一部を置換した三元系正極なども同様に用いることができる。さらには、正極活物質15として、硫黄、MxMo6X8−y(M=Cuなどの金属、X=S、Se、Te、0≦x≦4.0、0≦y≦0.2)の銅シュブレル化合物やMo6S8−x(0≦x≦0.2)のシュブレル化合物を用いることができる。これらのシュブレル化合物は固体電解質との混合体として使用することで、正極活物質15と正極集電体17との界面抵抗が大きくならない複合体とすることができる。具体的には、Cu2Mo6S8やMo6S8を挙げることができる。正極活物質15の粒径はサブミクロンからミクロンオーダーである。さらに、正極活物質層13には、アセチレンブラックなどの導電助剤8を混合して導電パスを形成し易くする。
負極活物質7には、リチウムイオン二次電池に一般的に用いられる負極活物質を使用できる。例えば、黒鉛(人造黒鉛または天然黒鉛)などのカーボン系活物質であり、シリコンやSiO系(Si+SiO2、SiOx)のシリコン酸化物、スズなどの合金系負極材料である。或いは、カーボン系材料と合金系材料の混成も用いることができる。特に本発明においては、銅箔に腐食に強い耐硫化性層を有するため、負極活物質には、MxPy(0.9≦x、y≦10、M=Si,Sn,In,Al,Zn)を用いることができ、これらは充放電に伴う体積変化が小さいという特長があるので、高い容量を実現させることができる。具体的には、Sn4P3,Sn3P4,SnP3,InPなどを挙げることができる。
また、負極活物質層5は、負極活物質7を少なくとも混合したスラリーを負極集電体3に塗布して形成されており、全固体二次電池1の構成要素として高い容量と信頼性を実現する。スラリーには、アセチレンブラックなどの導電助剤8と、水系バインダや増粘剤、或いは有機溶剤系のバインダを含む場合が多い。導電助剤8をスラリーに添加することで、図6に示すような負極活物質7と硫化物固体電解質11と導電助剤8を含む負極活物質層83を得ることができる。このことにより、負極活物質層83の導電性が向上する。
第1の実施形態に係る負極集電体3は、表面に耐硫化腐食性の硫化銅層23を有しているため、硫化物固体電解質11を使用しても腐食の心配が無い。さらに、銅系の基材21は高い導電性を有し、硫化第一銅や硫化第二銅はともに良導性であるため、負極集電体3は電気伝導性に優れる。また、硫化銅層23と基材21の密着性が良好である。
次に本発明の第2の実施形態について説明する。第2の実施形態は、第1の実施形態とは、負極集電体に形成された耐硫化性層が異なり、耐硫化性層が酸化銅層である。硫化物固体電解質、正極活物質、負極活物質は、第1の実施形態と同じである。
図3(a)において、第2の実施形態に係る負極集電体3aは、基材31の前記負極活物質層5が形成される面に、酸化銅層33を有する。図3(b)において、第2の実施形態に係る負極集電体3bは、基材31の負極活物質層5が形成される面に、酸化銅層45が積層されている。酸化銅層45は、酸化第一銅を主に含む負極集電体側の第1層41と、酸化第二銅層を主に含む表層側の第2層43とを有する。
形成する酸化銅層33および酸化銅層45の厚さは0.01〜1μmであり、化合物形態は、酸化第一銅主体の酸化銅層33のみでもよいし、基材31側に酸化第一銅主体の第1層41が、次いで表層側に酸化第二銅主体の第2層43が形成されていてもよい。
基材31としては、純銅系では電解銅箔や圧延のタフピッチ銅箔を用いることができ、合金系では主に圧延のCu−Sn系やCu−Fe系、Cu−Zr系、Cu−Cr系、コルソン合金系などの、第二成分以下が0.01質量%〜5質量%程度の固溶または析出強化された希薄合金を用いることができる。Ag以外の添加成分が高いと、導電率が低くなり集電性を低下させる懸念がある。
本酸化処理の前処理として、浸漬脱脂またはカソード脱脂、次いで酸洗(中和)処理を施す事が好ましい。基材表面の洗浄と共に硫化処理時の基材濡れ性を向上させることができる。アルカリ水溶液による処理液自体の脱脂効力も有する。
酸化銅は、酸化反応である腐食に対して高い耐性を有しており、硫化物固体電解質と接触しても腐食の懸念はない。そのため、第2の実施形態に係る負極集電体3aと3bは、表面に耐硫化腐食性の酸化銅層33または45を有しているため、硫化物固体電解質11を使用しても腐食の心配が無い。負極集電体3aと3bでは、酸化銅層33と基材31または、第1層41と基材31の間は、酸化第一銅と銅が接触しているため、基材31と酸化銅層33または酸化銅層45との密着性が良好である。また、酸化銅が半導電性であるため、負極集電体3aと3bの集電を妨げることはない。
次に本発明の第3の実施形態について説明する。第3の実施形態は、第1、第2の実施形態と負極集電体に形成された耐硫化性層が異なり、耐硫化性層が耐硫化性金属層である。硫化物固体電解質、正極活物質、負極活物質は第1の実施形態、第2の実施形態と同じである。
基材51としては、純銅系では電解銅箔や圧延のタフピッチ銅箔を用いることができ、合金系では主に圧延のCu−Sn系やCu−Zn系、Cu−Fe系、Cu−Zr系、Cu−Cr系、コルソン(Cu−Ni−Si)系などの、固溶または析出強化された希薄合金を用いることができる。これら基材表層に形成した耐硫化性層を、加熱ほかの拡散処理により基材合金化させても良い。
耐硫化性金属層53は、硫化物による腐食に耐えるNiやZn、Snなどを含む。そのため、第3の実施形態に係る負極集電体3cは、表面に耐硫化腐食性の耐硫化性金属層53を有しているため、硫化物固体電解質11を使用しても腐食の心配が無い。多層とした耐硫化性金属層形態では、第一層金属層のZnやSnは、基材Cuと直ぐに相互拡散して拡散合金化層を形成する。拡散合金化層によって基材Cuの耐腐食性と耐熱性を向上させる。特にSnは、Cu3Sn(ε相)とCu6Sn5(η’相)の化合物を形成して基材の保護性が向上する。二次電池の作動環境は80℃に及ぶこともあり、この場合には基材成分が表層に拡散移動することがあり、これにより前記の耐硫化性が低下して、表層で高抵抗の硫化物を生じて電池性能の劣化に繋がる。なお、前述した様に、拡散合金化層上にNi系金属層を形成することもできる。耐硫化金属層、またはさらに前記の多層金属層形態とすることで、このような高温作動環境による電池セルの劣化を防止または抑止することができる。また、銅系の基材51は導電性が高く、耐硫化性金属層53も良導性の金属を主体としているため、負極集電体3cは良好な集電性を有する。また、電析で成膜された耐硫化性金属層53は、基材51との密着性が良好であり、これらの間の界面接触抵抗を低下させることができる。
次に本発明の第4の実施形態について説明する。第4の実施形態は、負極集電体の負極活物質層が形成される表面の圧縮強度が1250〜3000MPaであることを特徴とする。また、負極集電体の負極活物質層が形成される表面の圧縮弾性率が60〜125GPaであることが好ましい。硫化物固体電解質、正極活物質、負極活物質は、第1〜第3の実施形態と同じである。
本電析層形成の前処理として、浸漬脱脂またはカソード電解脱脂、次いで酸洗(中和)処理を施しても良い。基材表面の洗浄と共に硫化処理時の基材濡れ性を向上させることができる。アルカリ水溶液による処理液自体の脱脂効力も有する。
第4の実施形態に係る負極集電体は、負極活物質層が形成される表面の機械強度が高いため、高い耐プレス性を有している。そのため、硫化物固体電解質を用いて、一体プレス成型にて全固体二次電池を作製しても、負極集電体の破断などの不良や集電劣化を生じることがない。また、従来プレス成型ができなかったセルに対してもプレス成型が可能となるという点で生産性が向上する。特に、電析で成膜された銅電析層63は、基材61との密着性が良好である。また、銅系の基材61は導電性が高く、MoやWを含有する銅電析層63は高導電性を有するので、集電性、密着性共に良好であり、一体成型セル構成に好適である。集電体そのものを高強度または高弾性材料とすることも可能であるが、高コスト材料を用いることになり、実用は難しい。耐プレス性を要する強度または弾性率は、集電体表層に付帯していれば良いので、例えば前記の耐硫化性金属層を形成する表面処理工程において、連続して当該高強度または高弾性率を有する銅電析層を形成すれば、コストを低く抑えることができ経済的に、本特性を付帯させることが可能になる。
全固体二次電池1の製造方法は特に限定されないが、以下の方法により製造することができる。まず、正極活物質15、硫化物固体電解質11をそれぞれプレスによりペレット成型する。その後、正極集電体17、正極活物質15のペレット、硫化物固体電解質11のペレット、負極活物質7、負極集電体3を重ねて、正極集電体/正極活物質層/固体電解質層/負極活物質層/負極集電体の構成にて、プレス押圧一体化成型し全固体二次電池を作製することができる。
(固体電解質作成方法)
固体電解質の原料として、Li2SとP2S5をAr雰囲気グローブボックス内にて乳鉢で混合した後、Zrポット内にZrボールと共に封入し、プラネタリタイプボールミルにて、室温のまま500rpmにて15時間メカニカルミリング(以下MM)処理を施し、70Li2S−30P2S5のアモルファス微粒子を得た。示差熱分析により200℃に発熱ピークを有し、結晶化することが判った。2時間加熱処理により結晶化させた試料をペレット化させて、カーボン(ペースト)電極を形成した後、交流インピーダンス法により伝導度を測定した。その結果、10−3S/cmと高い値を示し、本材料が高いLiイオン伝導性を有することが判った。
(負極集電体:硫化銅層形成)
20μm厚さの電解銅箔(純銅系)を、5g/dm3K2S水溶液、pH1.5、室温に30秒間浸漬処理した後に、水洗乾燥した。本硫化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、多くはCu2S酸化還元電位にプラトー領域を有し、その還元電気量から約0.1μm厚さのCu2S層が表面に形成されていることが判った。
(正極活物質層)
正極活物質層として、ニオブ酸リチウム(LiNbO3)を最表層に被覆したコバルト酸リチウム(LiCoO2)と本固体電解質、およびアセチレンブラックを45:50:5の割合で混合した複合層を用いた。表面被覆には転動流動層コーティング装置を用いて、リチウムのアルコキシドとニオブのアルコキシドを溶解したエチルアルコール溶液を噴霧して被覆した後、酸素雰囲気中にて加熱してアルコールを分解させた。
(負極活物質層)
人造黒鉛と本固体電解質を60:40の割合で混合した複合層を用いた。
(全固体二次電池作製方法)
正極活物質層、固体電解質層はそれぞれプレスによりペレット成型した後に、正極集電体、正極活物質層ペレット、固体電解質層ペレット、負極活物質、負極集電体を重ねて、正極集電体/正極活物質層/固体電解質層/負極活物質層/負極集電体の構成にて、プレス押圧一体化成型し全固体二次電池を作製した。なお、正極集電体には1000系Al箔を用いた。
(固体電解質作成方法)
固体電解質の原料としてLi2SとP2S5とP2O5を用いて、70Li2S−20P2S5−10P2O5組成を得る投入割合であること以外は、実施例1−1と同じ条件でアモルファス微粒子を得た。示差熱分析結果から300℃×2時間熱処理した結晶化試料をペレット化させてイオン伝導度を測定したところ、約10−3S/cmであった。
(負極集電体:硫化銅層形成)
実施例1−1と同様に形成した。
(正極活物質層)
正極活物質層は、Mo6S8と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを40:55:5の割合で混合した複合層とした。Mo6S8は、Cu2Mo6S8を酸性水溶液による還元処理を行って得たものを用いた。
(負極活物質層)
実施例1−1と同様とした。
(全固体二次電池作成方法)
実施例1−1と同様に行った。
(固体電解質作成方法)
実施例1−2と同様に作成した。
(負極集電体:硫化銅層形成)
実施例1−2と同様に形成した。
(正極活物質層)
実施例1−2と同様とした。
(負極活物質層)
Sn4P3と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5を1:1の割合で混合した複合層を用いた。Sn4P3はSnとリンを組成比になる様にボールミルで300rpm3時間MM処理して合成したものを用いた。
(全固体二次電池作成方法)
実施例1−2と同様に行った。
(固体電解質作成方法)
実施例1−3と同様に作成した。
(負極集電体:硫化銅層形成)
実施例1−3と同様に形成した。
(正極活物質層)
正極活物質層に、硫黄粉末と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを30:60:10の割合で混合した複合層を用いた。
(負極活物質層)
実施例1−3と同様とした。
(全固体二次電池作成方法)
実施例1−3と同様に行った。
(固体電解質作成方法)
実施例1−1と同様に作成した。
(負極集電体:硫化銅層形成)
20μm厚さの電解銅箔(純銅系)を、5g/dm3K2S水溶液、pH1.5、室温に6秒間浸漬処理した後に、水洗乾燥した。本硫化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、多くはCu2S酸化還元電位にプラトー領域を有し、その還元電気量から約0.01μm厚さのCu2S層が表面に形成されていることが判った。
(正極活物質層)
実施例1−1と同様に形成した。
(負極活物質層)
実施例1−1と同様に形成した。
(全固体二次電池作成方法)
実施例1−1と同様に形成した。
(固体電解質作成方法)
実施例1−1と同様に作成した。
(負極集電体:硫化銅層形成)
20μm厚さの電解銅箔(純銅系)を、5g/dm3K2S水溶液、pH1.5、室温に200秒間浸漬処理した後に、水洗乾燥した。本硫化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、多くはCu2S酸化還元電位にプラトー領域を有し、その還元電気量から約1μm厚さのCu2S層が表面に形成されていることが判った。
(正極活物質層)
実施例1−1と同様に形成した。
(負極活物質層)
実施例1−1と同様に形成した。
(全固体二次電池作成方法)
実施例1−1と同様に形成した。
(固体電解質作成方法)
実施例1−1と同様に行った。
(負極集電体:酸化銅層形成)
20μm厚さの電解銅箔(純銅系)を、1g/dm3NaOH水溶液、pH10、室温にて30秒間浸漬中、電流密度1A/dm2にてアノード電解処理をした後に、水洗乾燥した。本酸化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、CuOとCu2Oの還元電位と思われるプラトー領域が現れ、その還元電気量から銅箔上に順に0.1μm厚さのCu2O層と0.2μm厚さのCuO層が表面に形成されていることが判った。
(正極活物質層)
実施例1−1と同様とした。
(負極活物質層)
実施例1−1と同様とした。
(全固体二次電池作成方法)
実施例1−1と同様に行った。
(固体電解質作成方法)
固体電解質の原料としてLi2SとP2S5とP2O5を用いて、70Li2S−20P2S5−10P2O5組成を得る投入割合であること以外は、実施例2−1と同じ条件でアモルファス微粒子を得た。示差熱分析結果から300℃2時間熱処理した結晶化試料をペレット化させてイオン伝導度を測定したところ、約10−3S/cmであった。
(負極集電体:酸化銅層形成)
実施例2−1と同様に行った。
(正極活物質層)
正極活物質層は、Mo6S8と固体電解質、並びにアセチレンブラックを40:55:5の割合で混合した複合層とした。Mo6S8は、Cu2Mo6S8を酸性水溶液による還元処理を行って得たものを用いた。
(負極活物質層)
実施例2−1と同様とした。
(全固体二次電池作成方法)
実施例2−1と同様に行った。
(固体電解質作成方法)
実施例2−2と同様に作成した。
(負極集電体:酸化銅層形成)
実施例2−2と同様に行った。
(正極活物質層)
実施例2−2と同様とした。
(負極活物質層)
Sn4P3と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5を1:1の割合で混合した複合層を用いた。Sn4P3はSnとリンを組成比になる様にボールミルで300rpm3時間MM処理して合成したものを用いた。
(全固体二次電池作成方法)
実施例2−2と同様に行った。
(固体電解質作成方法)
実施例2−3と同様に作成した。
(負極集電体:酸化銅層形成)
実施例2−3と同様に行った。
(正極活物質層)
正極活物質層に、硫黄粉末と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを30:60:10の割合で混合した複合層を用いた。
(負極活物質層)
実施例2−3と同様とした。
(全固体二次電池作成方法)
実施例2−3と同様に行った。
(固体電解質作成方法)
実施例2−1と同様に行った。
(負極集電体:酸化銅層形成)
20μm厚さの電解銅箔(純銅系)を、1g/dm3NaOH水溶液、pH10、室温にて5秒間浸漬中、電流密度0.2A/dm2にてアノード電解処理をした後に、水洗乾燥した。本酸化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、CuOとCu2Oの還元電位と思われるプラトー領域が現れ、その還元電気量から銅箔上に順に0.001μm厚さのCu2O層と0.01μm厚さのCuO層が表面に形成されていることが判った。
(正極活物質層)
実施例2−1と同様とした。
(負極活物質層)
実施例2−1と同様とした。
(全固体二次電池作成方法)
実施例2−1と同様に行った。
(固体電解質作成方法)
実施例2−1と同様に行った。
(負極集電体:酸化銅層形成)
20μm厚さの電解銅箔(純銅系)を、1g/dm3NaOH水溶液、pH10、室温にて30秒間浸漬中、電流密度3A/dm2にてアノード電解処理をした後に、水洗乾燥した。本酸化処理銅箔を、充分N2脱気した0.5N-KCl水溶液中でカソード還元処理をしたところ、CuOとCu2Oの還元電位と思われるプラトー領域が現れ、その還元電気量から銅箔上に順に0.1μm厚さのCu2O層と0.9μm厚さのCuO層が表面に形成されていることが判った。
(正極活物質層)
実施例2−1と同様とした。
(負極活物質層)
実施例2−1と同様とした。
(全固体二次電池作成方法)
実施例2−1と同様に行った。
(固体電解質作成方法)
固体電解質の原料として、Li2SとP2S5をAr雰囲気グローブボックス内にて乳鉢で混合した後、Zrポット内にZrボールと共に封入し、プラネタリタイプボールミルにて、室温のまま500rpmにて20時間のMM処理を施し、70Li2S−30P2S5のアモルファス微粒子を得た。示差熱分析により200℃に発熱ピークを有し、結晶化することが判った。2時間加熱処理により結晶化させた試料をペレット化させて、カーボン(ペースト)電極を形成した後、交流インピーダンス法により伝導度を測定した。その結果、10−3S/cmと高い値を示し、本材料が高いLiイオン伝導性を有することが判った。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、25g/dm3硫酸ニッケル水溶液、pH1.5、室温に15秒間浸漬、電析処理した後に、水洗乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約0.2μm厚さのNi層が形成されていることが判った。
(正極活物質層)
実施例1−1と同様とした。
(負極活物質層)
実施例1−1と同様とした。
(全固体二次電池作成方法)
実施例1−1と同様に行った。
(固体電解質作成方法)
固体電解質の原料としてLi2SとP2S5とP2O5を用いて、70Li2S−20P2S5−10P2O5組成を得る投入割合であること以外は、実施例3−1と同じ条件でアモルファス微粒子を得た。示差熱分析結果から300℃2時間熱処理した結晶化試料をペレット化させてイオン伝導度を測定したところ、約10−3S/cmであった。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、5g/dm3硫酸スズ水溶液、pH1.5、室温に15秒間浸漬、電析処理した後に、水洗後、125℃加熱乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約0.2μm厚さのSn層が形成されていることが判った。さらに、断面のSEM観察とEPMA分析によりSnが基材銅へ拡散し合金化していることが判った。
(正極活物質層)
正極活物質層は、Mo6S8と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを40:55:5の割合で混合した複合層とした。Mo6S8は、Cu2Mo6S8を酸性水溶液による還元処理を行って得たものを用いた。
(負極活物質層)
実施例3−1と同様とした。
(全固体二次電池作成方法)
実施例3−1と同様に行った。
(固体電解質作成方法)
実施例3−2と同様に作成した。
(負極集電体:耐硫化性金属層形成)
実施例3−2と同様に形成した。
(正極活物質層)
実施例3−2と同様とした。
(負極活物質層)
Sn4P3と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、およびアセチレンブラックを50:45:5の割合で混合した複合層を用いた。Sn4P3はSnとリンを組成比になる様にボールミルで300rpm3時間MM処理して合成したものを用いた。
(全固体二次電池作成方法)
実施例3−2と同様に行った。
(固体電解質作成方法)
実施例3−3と同様に作成した。
(負極集電体:耐硫化性金属層形成)
実施例3−3と同様に形成した。
(全固体二次電池作成方法)
(正極活物質層)
正極活物質層に、硫黄粉末と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを30:60:10の割合で混合した複合層を用いた。
(負極活物質層)
実施例3−3と同様とした。
(全固体二次電池作成方法)
実施例3−3と同様に行った。
(固体電解質作成方法)
実施例3−2と同様とした。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、250g/dm3硫酸亜鉛水溶液に、室温で120秒間浸漬、5A/dm2電析処理した後に、水洗後乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約2μm厚さのZn層が形成されていることが判った。さらに、断面のSEM観察とEPMA分析によりZnが基材銅へ拡散し合金化していることが判った。
(正極活物質層)
実施例3−2と同様とした。
(負極活物質層)
実施例3−2と同様とした。
(全固体二次電池作成方法)
実施例3−2と同様とした。
(固体電解質作成方法)
実施例3−1と同様とした。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、500g/dm3スルファミン酸ニッケル水溶液(ホウ酸30g/dm3、塩化ニッケル30g/dm3含有)、40℃に10秒間浸漬、2A/dm2電析処理した後に、水洗乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約0.01μm厚さのNi層が形成されていることが判った。
(正極活物質層)
実施例3−1と同様とした。
(負極活物質層)
実施例3−1と同様とした。
(全固体二次電池作成方法)
実施例3−1と同様に行った。
(固体電解質作成方法)
実施例3−1と同様とした。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、500g/dm3スルファミン酸ニッケル水溶液(ホウ酸30g/dm3、塩化ニッケル30g/dm3含有)、室温40℃に400秒間浸漬、10A/dm2電析処理した後に、水洗乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約5μm厚さのNi層が形成されていることが判った。
(正極活物質層)
実施例3−1と同様とした。
(負極活物質層)
実施例3−1と同様とした。
(全固体二次電池作成方法)
実施例3−1と同様に行った。
(固体電解質作成方法)
実施例3−1と同様とした。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、250g/dm3硫酸スズ水溶液、室温に15秒間浸漬、3A/dm2電析処理した後に、水洗後、100℃加熱乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約0.2μm厚さのSn層が形成されていることが判った。さらに、断面のSEM観察とEPMA分析によりSnが基材銅へ拡散し合金化していることが判った。さらに、本電析処理銅箔を500g/dm3スルファミン酸ニッケル水溶液(ホウ酸30g/dm3、塩化ニッケル30g/dm3含有)、40℃に150秒間浸漬、10A/dm2電析処理した後に、水洗乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約2μm厚さのNi層が形成されていることが判った。すなわち、第1層としてSn拡散合金化層が形成され、その上層に第2層としてNi層が形成された。
(正極活物質層)
実施例3−1と同様とした。
(負極活物質層)
実施例3−1と同様とした。
(全固体二次電池作成方法)
実施例3−1と同様に行った。
(固体電解質作成方法)
固体電解質の原料として、Li2SとP2S5をAr雰囲気グローブボックス内にて乳鉢で混合した後、Zrポット内にZrボールと共に封入し、プラネタリタイプボールミルにて、室温のまま500rpmにて20時間のMM処理を施し、70Li2S−30P2S5のアモルファス微粒子を得た。示差熱分析により200℃に発熱ピークを有し、結晶化することが判った。2時間加熱処理により結晶化させた試料をペレット化させて、カーボン(ペースト)電極を形成した後、交流インピーダンス法により伝導度を測定した。その結果、10−3S/cmと高い値を示し、本材料が高いLiイオン伝導性を有することが判った。
(負極集電体:耐硫化性金属層形成)
20μm厚さの電解銅箔(純銅系)を、500g/dm3スルファミン酸ニッケル水溶液(ホウ酸30g/dm3、塩化ニッケル30g/dm3含有)40℃に150秒間浸漬、10A/dm2電析処理した後に、水洗乾燥した。本電析処理銅箔を表面のコクール溶解試験から、約2μm厚さのNi層が形成されていることが判った。
(正極活物質層)
実施例1−1と同様とした。
(負極活物質層)
実施例1−1と同様とした。
(全固体二次電池作成方法)
実施例1−1と同様に行った。
(固体電解質作成方法)
実施例3−1と同様に行った。
(負極集電体:銅電析層形成)
20μm厚さの電解銅箔(純銅系)を、銅と硫酸が50g/dm3の水溶液にモリブデン酸ナトリウムを1g/dm3、40℃にて15秒間浸漬中、電流密度2A/dm2にて電析した後に、水洗乾燥した。このMo含有銅電析層形成銅箔を、AESによりデプスプロファイル分析を実施したところ、Moが確かに表層0.5μmに亘って、マトリクスのCuと共に検出されていることが判った。
(正極活物質層)
実施例1−1と同様とした。
(負極活物質層)
実施例1−1と同様とした。
(全固体二次電池作成方法)
正極複合層、固体電解質層はそれぞれ2t/cm3、1t/cm3の荷重にてプレスしてペレット成形した。負極活物質として、別途、常法により人造黒鉛とバインダを含む負極活物質層を先の電析層形成銅箔に塗工形成した。その後正極集電体/正極活物質層/固体電解質層/負極活物質層/負極集電体の構成にて、再び1t/cm3にてプレス押圧一体化成型した。
(固体電解質作成方法)
固体電解質の原料としてLi2SとP2S5とP2O5を用いて、70Li2S−20P2S5−10P2O5組成を得る投入割合であること以外は、実施例4−1と同じ条件でアモルファス微粒子を得た。示差熱分析結果から300℃2時間熱処理した結晶化試料をペレット化させてイオン伝導度を測定したところ、約10−3S/cmであった。
(負極集電体:銅電析層形成)
20μm厚さの電解銅箔(純銅系)を、銅が50g/dm3、硫酸75g/dm3の水溶液にタングステン酸ナトリウムを1g/dm3、40℃にて30秒間浸漬中、電流密度5A/dm2にて電析して、水洗乾燥した。このW含有銅電析層形成銅箔を、AESによりデプスプロファイル分析を実施したところ、Wが確かに表層0.5μmに亘って、マトリクスのCuと共に検出されていることが判った。
(正極活物質層)
正極活物質層は、Mo6S8と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを40:55:5の割合で混合した複合層とした。Mo6S8は、Cu2Mo6S8を酸性水溶液による還元処理を行って得たものを用いた。
(負極活物質層)
実施例4−1と同様とした。
(全固体二次電池作成方法)
実施例4−1と同様に行った。
(固体電解質作成方法)
実施例4−2と同様に作成した。
(負極集電体:銅電析層形成)
実施例4−2と同様に行った。
(正極活物質層)
実施例4−2と同様とした。
(負極活物質層)
Sn4P3と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、およびアセチレンブラックを50:45:5の割合で混合した複合層を用いた。Sn4P3はSnとリンを組成比になる様にボールミルで300rpm3時間MM処理して合成したものを用いた。
(全固体二次電池作成方法)
実施例4−2と同様に行った。
(固体電解質作成方法)
実施例4−3と同様に作成した。
(負極集電体:銅電析層形成)
実施例4−3と同様に行った。
(正極活物質層)
正極活物質層に、硫黄粉末と合成結晶化させた固体電解質である70Li2S−20P2S5−10P2O5、並びにアセチレンブラックを30:60:10の割合で混合した複合層を用いた。
(負極活物質層)
実施例4−3と同様とした。
(全固体二次電池作成方法)
実施例4−3と同様に行った。
(固体電解質作成方法)
実施例4−1と同様に行った。
(負極集電体:銅電析層形成)
20μm厚さの電解銅箔(純銅系)を、銅と硫酸が50g/dm3の水溶液にモリブデン酸ナトリウムを1g/dm3、40℃にて5秒間浸漬中、電流密度2A/dm2にて電析した後に、水洗乾燥した。このMo含有銅電析層形成銅箔を、AESによりデプスプロファイル分析を実施したところ、Moが確かに表層0.1μmに亘って、マトリクスのCuと共に検出されていることが判った。
(正極活物質層)
実施例4−1と同様とした。
(負極活物質層)
実施例4−1と同様とした。
(全固体二次電池作成方法)
実施例4−1と同様とした。
(固体電解質作成方法)
実施例4−1と同様に行った。
(負極集電体:銅電析層形成)
20μm厚さの電解銅箔(純銅系)を、銅と硫酸が50g/dm3の水溶液にモリブデン酸ナトリウムを1g/dm3、40℃にて70秒間浸漬中、電流密度2A/dm2にて電析した後に、水洗乾燥した。このMo含有銅電析層形成銅箔を、AESによりデプスプロファイル分析を実施したところ、Moが確かに表層2.5μmに亘って、マトリクスのCuと共に検出されていることが判った。
(正極活物質層)
実施例4−1と同様とした。
(負極活物質層)
実施例4−1と同様とした。
(全固体二次電池作成方法)
実施例4−1と同様とした。
負極集電体に硫化処理や酸化処理、電析処理のいずれもしていない標準電解銅箔を用いた以外は実施例1−1と同様に行った。
負極集電体に電析層形成処理をしていない電池用標準電解銅箔を用いた以外は実施例4−1と同様に行った。
負極集電体に電析層形成処理をしていないプリント回路用標準電解銅箔を用いた以外は実施例4−1と同様に行った。
全固体二次電池より、充放電試験を0.5Cレートにて100サイクル実施した。
実施例4−1〜4−6、比較例2〜3については、負極集電体用銅箔の表面の圧縮強度と圧縮弾性率として、電析層表面からナノ・インデンテーション・テスター((株)エリオニクス製 ENT−1100a)により、負荷条件50mNにより10点測定した平均値を求めた。
3………負極集電体
5………負極活物質層
7………負極活物質
8………導電助剤
9………固体電解質層
11………硫化物固体電解質
13………正極活物質層
15………正極活物質
17………正極集電体
21………基材
23………硫化銅層
31………基材
33………酸化銅層
41………第1層
43………第2層
45………酸化銅層
51………基材
53………耐硫化性金属層
61………基材
63………銅電析層
81………全固体二次電池
83………負極活物質層
(固体電解質作成方法)
実施例4−1と同様に行った。
(負極集電体:銅電析層形成)
20μm厚さの電解銅箔(純銅系)を、銅と硫酸が50g/dm3の水溶液にモリブデン酸ナトリウムを1g/dm3、40℃にて5秒間浸漬中、電流密度2A/dm2にて電析した後に、水洗乾燥した。このMo含有銅電析層形成銅箔を、AESによりデプスプロファイル分析を実施したところ、Moが確かに表層0.1μmに亘って、マトリクスのCuと共に検出されていることが判った。
(正極活物質層)
実施例4−1と同様とした。
(負極活物質層)
実施例4−1と同様とした。
(全固体二次電池作成方法)
実施例4−1と同様とした。
Claims (16)
- 銅または銅合金を含む負極集電体と、前記負極集電体と対向して設けられたアルミニウム、アルミニウム合金またはステンレスからなる正極集電体との間に、前記負極集電体側から、前記負極集電体の表面に形成された負極活物質層と、1価または2価の金属と硫黄を含む硫化物固体電解質を含む固体電解質層と、前記正極集電体の表面に形成された正極活物質層と、が順に積層され、前記負極集電体の前記負極活物質層が形成される面に、耐硫化性層を有することを特徴とする全固体二次電池。
- 前記耐硫化性層が、硫化銅を含む硫化銅層であることを特徴とする請求項1に記載の全固体二次電池。
- 前記硫化銅層の厚さが0.01〜1μmであることを特徴とする請求項2に記載の全固体二次電池。
- 前記耐硫化性層が、酸化銅を含む酸化銅層であることを特徴とする請求項1に記載の全固体二次電池。
- 前記酸化銅層の厚さが0.01〜1μmであることを特徴とする請求項4に記載の全固体二次電池。
- 前記酸化銅層は、酸化第一銅を主に含む負極集電体側の第1層と、酸化第二銅層を主に含む表層側の第2層とを有することを特徴とする請求項4記載の全固体二次電池。
- 前記耐硫化性層が、ニッケル、亜鉛、スズから選ばれる少なくとも1種を含む耐硫化性金属層であることを特徴とする請求項1に記載の全固体二次電池。
- 前記耐硫化性金属層の厚さが0.01〜5μmであることを特徴とする請求項7に記載の全固体二次電池。
- 前記耐硫化性金属層の亜鉛またはスズが、前記負極集電体に含まれる銅と拡散合金化した、拡散合金化層を形成することを特徴とする請求項7記載の全固体二次電池。
- 前記拡散合金化層の上層に、さらにニッケル層が形成されていることを特徴とする請求項9記載の全固体二次電池。
- 銅または銅合金を含む負極集電体と、前記負極集電体と対向して設けられたアルミニウム、アルミニウム合金またはステンレスからなる正極集電体との間に、前記負極集電体側から、前記負極集電体の表面に形成された負極活物質層と、1価または2価の金属と硫黄を含む硫化物固体電解質を含む固体電解質層と、前記正極集電体の表面に形成された正極活物質層と、が順に積層され、前記負極集電体の前記負極活物質層が形成される表面の圧縮強度が1250〜3000MPaであることを特徴とする全固体二次電池。
- 前記負極集電体の前記負極活物質層が形成される表面の圧縮弾性率が60〜125GPaであることを特徴とする請求項11に記載の全固体二次電池。
- 前記負極集電体の表面に、モリブデンまたはタングステンを含有する銅電析層を有し、前記銅電析層の厚さが0.1〜2.5μmであることを特徴とする請求項11に記載の全固体二次電池。
- 前記正極活物質層に含まれる正極活物質として、硫黄、MxMo6X8−y(M=金属、X=S、Se、Te、0≦x≦4.0、0≦y≦0.2)、Mo6S8−x(0≦x≦0.2)のいずれかを用いることを特徴とする請求項1または請求項11に記載の全固体二次電池。
- 前記負極活物質層に含まれる負極活物質が、MxPy(0.9≦x,y≦10、M=Si,Sn,In,Al,Zn)であることを特徴とする請求項1または請求項11に記載の全固体二次電池。
- 前記負極活物質層中に、前記硫化物固体電解質が含まれていることを特徴とする請求項1または請求項11に記載の全固体二次電池。