JP6190827B2 - 高cteのホウケイ酸カリウムコアガラスおよびそれを含むガラス物品 - Google Patents
高cteのホウケイ酸カリウムコアガラスおよびそれを含むガラス物品 Download PDFInfo
- Publication number
- JP6190827B2 JP6190827B2 JP2014560011A JP2014560011A JP6190827B2 JP 6190827 B2 JP6190827 B2 JP 6190827B2 JP 2014560011 A JP2014560011 A JP 2014560011A JP 2014560011 A JP2014560011 A JP 2014560011A JP 6190827 B2 JP6190827 B2 JP 6190827B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- mol
- glass composition
- concentration
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
他の実施態様
1.ガラス組成物において、
約70モル%〜約80モル%のSiO 2 と;
約0モル%〜約8モル%のAl 2 O 3 と;
約3モル%〜約10モル%のB 2 O 3 と;
約0モル%〜約2モル%のNa 2 Oと;
約10モル%〜約15モル%のK 2 Oと;
約5モル%〜約6モル%のアルカリ土類酸化物と;
を含み、
前記アルカリ土類酸化物がCaO、SrOおよびBaOのうちの少なくとも1つであり;
前記ガラス組成物が、20℃〜300℃の温度範囲にわたり平均して75×10 −7 /℃以上である熱膨張係数を含み;
前記ガラス組成物が250キロポアズ以上の液相粘度を含み:
前記ガラス組成物がMgOを実質的に含まない、ガラス組成物。
2.第1のガラスクラッド層と第2のガラスクラッド層との間に配置されたガラスコア層を含むガラス物品において、前記ガラスコア層が、
約70モル%〜約80モル%のSiO 2 と;
約0モル%〜約8モル%のAl 2 O 3 と;
約3モル%〜約10モル%のB 2 O 3 と;
約0モル%〜約2モル%のNa 2 Oと;
約10モル%〜約15モル%のK 2 Oと;
を含み、20℃〜300℃の温度範囲にわたり平均して75×10 −7 /℃以上である熱膨張係数を含むガラス組成物から成形されている、ガラス物品。
3.前記ガラス組成物が約5モル%〜約6モル%のアルカリ土類酸化物を含み、
前記アルカリ土類酸化物がCaO、SrOおよびBaOのうちの少なくとも1つであり;
前記ガラス組成物がMgOを実質的に含まず;
前記アルカリ土類酸化物が、
・ 約1.5モル%以上のSrOと;
・ 約0モル%〜約2モル%のBaOと;
を含む、実施態様1に記載のガラス組成物または実施態様2に記載のガラス物品。
4.前記ガラス組成物が、
約73モル%〜約77モル%のSiO 2 と;
約0モル%〜約3モル%のAl 2 O 3 と;
約4モル%〜約5モル%のB 2 O 3 と;
約0モル%〜約2モル%のNa 2 Oと;
約11.5モル%〜約12.5モル%のK 2 Oと、
を含む、実施態様1または3に記載のガラス組成物、もしくは実施態様2または3に記載のガラス物品。
5.前記ガラス組成物中のNa 2 Oの濃度が約0.1モル%以上であるか、
前記ガラス組成物がBaOを実質的に含まないか、または
前記ガラス組成物が重金属を実質的に含まないか、
の少なくとも1つである、実施態様1、3および4のいずれかに記載のガラス組成物または実施態様2〜4のいずれかに記載のガラス物品。
6.前記ガラス組成物中のK 2 O濃度(モル%)が、前記ガラス組成物中のB 2 O 3 濃度(モル%)と前記ガラス組成物中のAl 2 O 3 濃度(モル%)の和より大きい、実施態様1および3〜5のいずれかに記載のガラス組成物または実施態様2〜5のいずれかに記載のガラス物品。
7.前記ガラスコア層が平均コア熱膨張係数CTE コア を有し;
前記第1のガラスクラッド層および前記第2のガラスクラッド層が、前記平均コア熱膨張係数CTE コア よりも低い平均クラッド熱膨張係数CTE クラッド を有する、実施態様2〜6のいずれかに記載のガラス物品。
8.前記ガラスコア層の第1の表面が前記第1のガラスクラッド層に直接隣接し、前記ガラスコア層の第2の表面が前記第2のガラスクラッド層に直接隣接する、実施態様2〜7のいずれかに記載のガラス物品。
9.拡散層が、前記第1のガラスクラッド層または前記第2のガラスクラッド層の少なくとも1つと前記ガラスコア層との間に配置されており、前記拡散層の前記平均熱膨張係数が、前記ガラスコア層の平均コア熱膨張係数の値と前記第1のガラスクラッド層または第2のガラスクラッド層のうちの前記少なくとも1つの平均クラッド熱膨張係数の値との間の値を有する、実施態様2〜8のいずれかに記載のガラス物品。
10.LCDおよびLEDディスプレー、コンピュータモニター、現金自動預入支払機(ATM)を含む消費者用または業務用電子デバイスにおけるカバーガラスまたはガラスバックプレーンの利用分野;携帯電話、パーソナルメディアプレーヤーおよびタブレットコンピュータを含むポータブル式電子デバイス用のタッチスクリーンまたはタッチセンサーの利用分野;太陽電池の利用分野;建築用ガラスの利用分野;自動車または車両用ガラスの利用分野;または業務用または家庭用電化製品の利用分野を目的とする、実施態様1および3〜6のいずれかに記載のガラス組成物または実施態様2〜9のいずれかに記載のガラス物品の使用。
Claims (11)
- ガラス組成物において、
70モル%〜80モル%のSiO2と;
0モル%〜8モル%のAl2O3と;
3モル%〜10モル%のB2O3と;
0モル%〜2モル%のNa2Oと;
10モル%〜15モル%のK2Oと;
5モル%〜6モル%のアルカリ土類酸化物であって、主としてSrOまたはBaOを含むアルカリ土類酸化物と;
を含み、
20℃〜300℃の温度範囲にわたり平均して75×10−7/℃以上である熱膨張係数を含み;
250キロポアズ以上の液相粘度を含み;
前記ガラス組成物中のMgOの濃度が1モル%未満であり;および
前記ガラス組成物中のCaOの濃度が0モル%である;
ことを特徴とするガラス組成物。 - 第1のガラスクラッド層と第2のガラスクラッド層との間に配置されたガラスコア層を含むガラス物品において、前記ガラスコア層が、
70モル%〜80モル%のSiO2と;
0モル%〜8モル%のAl2O3と;
3モル%〜10モル%のB2O3と;
0モル%〜2モル%のNa2Oと;
10モル%〜15モル%のK2Oと;
5モル%〜6モル%のアルカリ土類酸化物であって、主としてSrOまたはBaOを含むアルカリ土類酸化物と;
を含み、20℃〜300℃の温度範囲にわたり平均して75×10−7/℃以上である熱膨張係数を含み、MgOの濃度が1モル%未満であり、およびCaOの濃度が0モル%であるガラス組成物から形成されている、ガラス物品。 - 前記アルカリ土類酸化物が、
1.5モル%以上のSrOと;
0モル%〜2モル%のBaOと;
を含む、請求項1記載のガラス組成物。 - 73モル%〜77モル%のSiO2と;
0モル%〜3モル%のAl2O3と;
4モル%〜5モル%のB2O3と;
0モル%〜2モル%のNa2Oと;
11.5モル%〜12.5モル%のK2Oと、
を含む、請求項1または3記載のガラス組成物。 - 前記ガラス組成物中のNa2Oの濃度が0.1モル%以上であるか、
前記ガラス組成物中のBaOの濃度が1モル%未満であるか、または
前記ガラス組成物中の重金属の濃度が1モル%未満であるか、
の少なくとも1つである、請求項1、3および4いずれか1項記載のガラス組成物。 - 前記ガラス組成物中のK2O濃度(モル%)が、該ガラス組成物中のB2O3濃度(モル%)と前記ガラス組成物中のAl2O3濃度(モル%)の和より大きい、請求項1および3〜5いずれか1項記載のガラス組成物。
- 第1のガラスクラッド層と第2のガラスクラッド層との間に配置されたガラスコア層を含むガラス物品において、前記ガラスコア層が、請求項1および3〜6いずれか1項記載のガラス組成物から形成されている、ガラス物品。
- 前記ガラスコア層が平均コア熱膨張係数CTEコアを有し;
前記第1のガラスクラッド層および前記第2のガラスクラッド層が、前記平均コア熱膨張係数CTEコアよりも低い平均クラッド熱膨張係数CTEクラッドを有する、請求項2または7記載のガラス物品。 - 前記ガラスコア層の第1の表面が前記第1のガラスクラッド層に直接隣接し、前記ガラスコア層の第2の表面が前記第2のガラスクラッド層に直接隣接する、請求項2、7および8いずれか1項記載のガラス物品。
- 拡散層が、前記第1のガラスクラッド層または前記第2のガラスクラッド層の少なくとも1つと前記ガラスコア層との間に配置されており、前記拡散層の平均熱膨張係数が、前記ガラスコア層の平均コア熱膨張係数の値と前記第1のガラスクラッド層または第2のガラスクラッド層のうちの前記少なくとも1つの平均クラッド熱膨張係数の値との間の値を有する、請求項2、7および8いずれか1項記載のガラス物品。
- LCDおよびLEDディスプレー、コンピュータモニター、現金自動預入支払機(ATM)を含む消費者用または業務用電子デバイスにおけるカバーガラスまたはガラスバックプレーンの利用分野;携帯電話、パーソナルメディアプレーヤーおよびタブレットコンピュータを含むポータブル式電子デバイス用のタッチスクリーンまたはタッチセンサーの利用分野;太陽電池の利用分野;建築用ガラスの利用分野;自動車または車両用ガラスの利用分野;または業務用または家庭用電化製品の利用分野のための、請求項1および3〜7いずれか1項記載のガラス組成物または請求項2および7〜10いずれか1項記載のガラス物品の使用。