JP5747952B2 - 触媒コンバータの製造方法 - Google Patents
触媒コンバータの製造方法 Download PDFInfo
- Publication number
- JP5747952B2 JP5747952B2 JP2013130706A JP2013130706A JP5747952B2 JP 5747952 B2 JP5747952 B2 JP 5747952B2 JP 2013130706 A JP2013130706 A JP 2013130706A JP 2013130706 A JP2013130706 A JP 2013130706A JP 5747952 B2 JP5747952 B2 JP 5747952B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- dimensional structure
- catalyst component
- slurry
- catalytic converter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このため、ディーゼルエンジンから排出されるパティキュレート排出規制が強化されているが、これに伴い、パティキュレートを効率良く除去できる排ガス浄化材が待望されている。
また、高温域での燃焼とその反応熱によりフィルターの溶損や割れを生じるという問題点を有していた。
更に、特殊な装置を必要とするため、浄化装置としての大型化、高コスト化が生じるという問題点を有していた。
例えば、フィルター上に触媒層をコートし触媒作用によりパティキュレートを処理するパティキュレート浄化用触媒及びその製造方法が提案されている(特許文献1参照。)。
なお、従来のこのような三次元構造担体に触媒を担持した触媒コンバータでは、三次元構造担体の細孔内部に触媒成分が比較的多量に担持されてしまう。
なお、被覆量(触媒コート層への担時量)の測定は、図5〜7に示すように、三次元構造担体のセルにおけるコーナー部、代表的にはハニカムコーナー部を中心として200×200μmを撮影したSEM写真について、全触媒面積に対する何%がセル壁、即ちハニカム表面に存在するかを測定すればよい。
具体的には、上記金属酸化物として、酸化セリウム(CeO2)、酸化プラセオジム(Pr6O11)、酸化イットリウム(Y2O3)、酸化ビスマス(Bi2O3)、酸化ジルコニウム(ZrO2)又は酸化アルミニウム(Al2O3)、及びこれらの任意の組合わせに係るものを使用できる。
代表的には、上記金属酸化物にPt、Pd、Rh、Ag及びAuなどを担持した触媒成分を好適に使用することができる。
セル壁細孔径や気孔率が上記の範囲を逸脱すると、通常の触媒成分スラリーを用いて触媒成分を多孔質担体の表面に付着させようとしても、触媒成分が担体内部の細孔に比較的多量に浸入してしまい、触媒活性を効果的に発揮させ難くなる。なお、気孔率の上限としては、三次元構造担体自体の強度を維持する観点から70vol%以下とすることが好ましい。
なお、これら三次元構造体の材質については、セラミックスとしてはコージェライトや炭化ケイ素など、発泡金属としてはフェライト系ステンレスなどを挙げることができる。
なお、本明細書において、気孔率とは多孔質体であるセル壁の総体積に対する全ての細孔の体積の割合を示し、アルキメデス法により求めることができる。また、セル壁中の細孔の細孔径は水銀圧入法により求めることができる。
本発明の第1の製造方法は、上述の触媒コンバータを製造するに当たり、触媒成分の粉末と熱により消失する消失材を溶媒で分散させてスラリーとする工程と、得られたスラリーを上記の三次元構造担体にコートする工程と、コート後に消失材を消失させるための焼成工程と、を行うものである。
このように、消失材を用いることにより、触媒成分を局在化できることの詳細は必ずしも明確ではないが、例えば、図3に示すように、担体2のセル壁3における細孔3bが消失材12であるカーボン粒子で塞がれ、その後、セル壁3の表面3bに触媒成分11がコートされ、焼成工程によりカーボン粒子が消失除去されるので、触媒成分11が担体2の細孔3b内部には少量しか浸入しないものと思われる。
これら消失材を用いれば、触媒成分を担体表面に留めやすく、速やかに消失させることができるので有効である。
水2000gに、酸化セリウム粉末450g、活性炭125g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、直径144mm、高さ152mm、セル密度400個/in2、セル壁の中心細孔径10〜20μm、気孔率50〜60vol%のSiC製ハニカム担体を用意し、上記触媒スラリ−に浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。
同図より、白色に見える触媒成分11の大部分は、ハニカムコーナーの形状を模した形状(L字状)をなして担体のセル壁3の表面3aに局在化して触媒コート層10を形成しており、しかも担体の細孔3b内部には白点が殆ど存在せず、触媒成分11が殆ど担体の細孔3b内部に浸入していないことが分かる。
なお、触媒成分11は、全担持量の83%が担体の表面3aに被覆されていた。なお、触媒成分の担持率は、以下の式より求めた。
表面担持率(%)=(触媒コート層における触媒成分の面積/全触媒成分の面積)×100
水2000gに、セリウムプラセオジム複合酸化物粉末450g、活性炭125g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、上記触媒スラリ−に浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の82%が担体表面に被覆されていた。
水2000gに、セリウムイットリウム複合酸化物粉末450g、活性炭125g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、上記触媒スラリ−に浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の82%が担体表面に被覆されていた。
水1000gに、ジニトロジアミン白金水溶液(白金濃度:8.02%)488ml、酸化アルミニウム粉末450gを混合し、酸化アルミナ上へ白金を含浸担持した。白金担持量は8%とした。
次に、水2000gに、白金担持酸化アルミニウム粉末450g、活性炭125g、アルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
その後、実施例1で用いたSiC製ハニカム担体を用意し、上記触媒スラリ−に浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の80%が担体表面に被覆されていた。
水1000gに、活性炭125gを混合し、活性炭懸濁液を調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、上記活性炭懸濁液(消失材スラリー)に浸漬し、余分な懸濁液を除去した後、150℃で2時間乾燥した。活性炭層(消失材コート層)の形成量は、担体の1リットルあたり12.5gであった。
水2000gに、酸化セリウム粉末450g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、活性炭層を形成したハニカム担体を上記触媒スラリーに浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の85%が担体表面に被覆されていた。
実施例5と同様に活性炭層(消失材コート層)を形成したハニカム担体を用意した。
水2000gに、セリウムプラセオジム複合酸化物粉末450g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、活性炭層を形成したハニカム担体を上記触媒スラリーに浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の82%が担体表面に被覆されていた。
実施例5と同様に活性炭層(消失材コート層)を形成したハニカム担体を用意した。
水2000gに、セリウムイットリウム複合酸化物粉末450g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
次に、活性炭層を形成したハニカム担体を上記触媒スラリーに浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の81%が担体表面に被覆されていた。
実施例5と同様に活性炭層(消失材コート層)を形成したハニカム担体を用意した。
水1000gに、ジニトロジアミン白金水溶液(白金濃度:8.02%)488ml、酸化アルミニウム粉末450gを混合し、酸化アルミナ上へ白金を含浸担持した。白金担持量は8%とした。
次に、水2000gに、白金担持酸化アルミニウム粉末450g及びアルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
その後、活性炭層を形成したハニカム担体を上記触媒スラリーに浸漬し、余分な触媒スラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の80%が担体表面に被覆されていた。
実施例1の活性炭をポリスチレンビーズに置き換えた以外は、実施例1と同様の操作を繰り返して、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の61%が担体表面に被覆されていた。
実施例2の活性炭をポリスチレンビーズに置き換えた以外は、実施例2と同様の操作を繰り返して、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の59%が担体表面に被覆されていた。
実施例3の活性炭をポリスチレンビーズに置き換えた以外は、実施例3と同様の操作を繰り返して、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の62%が担体表面に被覆されていた。
実施例4の活性炭をポリスチレンビーズに置き換えた以外は、実施例4と同様の操作を繰り返して、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の62%が担体表面に被覆されていた。
水2000gに、酸化セリウム粉末450g、アルミナゾル50gを混合し、攪拌してスラリーを調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、スラリ−に浸漬し、余分なスラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。
図6に、本例の触媒コンバータのハニカムコーナー近傍のSEM写真を示す。図5と異なり、白色の触媒成分11が担体の細孔3bの内部にかなり浸入しており、セル壁3の表面3aに局在する触媒成分11の量が少ないことが分かる。
なお、触媒成分は、全担持量の35%が担体表面に被覆されていた。
水2000gに、セリウムプラセオジム複合酸化物粉末450g、アルミナゾル50gを混合し、攪拌してスラリーを調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、スラリ−に浸漬し、余分なスラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の8%が担体表面に被覆されていた。
水2000gに、セリウムイットリウム複合酸化物粉末450g、アルミナゾル50gを混合し、攪拌してスラリーを調製した。
次に、実施例1で用いたSiC製ハニカム担体を用意し、スラリ−に浸漬し、余分なスラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。触媒成分は、全担持量の7%が担体表面に被覆されていた。
水1000gに、ジニトロジアミン白金水溶液と酸化アルミニウム粉末450gとを混合し、酸化アルミナ上へ白金を含浸担持した。白金担持量は8%とした。
次に、水2000gに、白金担持酸化アルミニウム粉末450g、アルミナゾル50gを混合し、攪拌して触媒スラリーを調製した。
その後、実施例1で用いたSiC製ハニカム担体を用意し、スラリ−に浸漬し、余分なスラリーを除去した後、150℃で2時間乾燥し、400℃で4時間焼成して触媒層を形成し、本例の触媒コンバータを得た。触媒層の形成量は、触媒コンバータの1リットルあたり50gであった。
図7に、本例の触媒コンバータのハニカムコーナー近傍のSEM写真を示す。図5と異なり、白色の触媒成分11が担体の細孔3bの内部に多量に浸入していることが分かる。
なお、触媒成分は、全担持量の7%が担体表面に被覆されていた。
実施例1〜12、比較例1〜4で作製した触媒層を形成した触媒コンバータを一部くり抜き構造体容量0.076L切り出して評価を行った。
日産自動車製4気筒、排気量2500ccのエンジンにおいて、触媒コンバータにすすを堆積させた。
すすを堆積させた触媒コンバータを固定床流通式反応装置を用いて、触媒性能評価を行った。反応ガスは酸素濃度5%でバランスガスに窒素を用いた。触媒コンバータへ入るガスの温度を500℃、空間速度5万/hrの条件において5分間にすすが酸化して生成したCO、CO2の量で触媒コンバータの性能を比較した。
2 三次元構造担体
3 セル壁
3a 表面
3b 細孔
4 セル
5 セル入り口
6 セル出口
7 目封じ材
10 触媒コート層
10a 表面
10b 細孔
11 触媒成分
12 消失材
Claims (4)
- 触媒成分の粉末と、熱により消失する消失材を溶媒で分散させてスラリーを得る工程と、
セル壁で区画された複数のセルを有し、かつ、このセル壁の細孔径が10〜50μmであり、かつ、気孔率が40vol%以上である三次元構造担体に、得られたスラリーをコートする工程と、
三次元構造担体のセル壁の表面に触媒成分を含む触媒コート層を形成すると共に、三次元構造担体における触媒成分の全担持量の50質量%以上がセル壁の表面に存在するように、消失材を消失させるためにスラリーがコートされた三次元構造担体を焼成する工程と、
を含み、
上記触媒成分が、酸化セリウム(CeO 2 )、酸化プラセオジム(Pr 6 O 11 )及び酸化イットリウム(Y 2 O 3 )から成る群より選ばれた少なくとも1種を含むものであるか、又は酸化セリウム(CeO 2 )、酸化プラセオジム(Pr 6 O 11 )、酸化イットリウム(Y 2 O 3 )、酸化ビスマス(Bi 2 O 3 )、酸化ジルコニウム(ZrO 2 )及び酸化アルミニウム(Al 2 O 3 )から成る群より選ばれた少なくとも1種を含む金属酸化物に白金、パラジウム、ロジウム、銀及び金から成る群より選ばれた少なくとも1種を含むものを担持したものであり、
上記消失材が、活性炭、高分子樹脂ビーズ、セルロース及びもみ殻から成る群より選ばれた少なくとも1種のものである
ことを特徴とする触媒コンバータの製造方法。 - 熱により消失する消失材を溶媒で分散させて消失材スラリーを得る工程と、
セル壁で区画された複数のセルを有し、かつ、このセル壁の細孔径が10〜50μmであり、かつ、気孔率が40vol%以上である三次元構造担体に、得られた消失材スラリーをコートし、乾燥して消失材コート層を形成する工程と、
消失材がコート層が形成された三次元構造担体に、触媒成分の粉末を溶媒で分散させた触媒スラリーをコートする工程と、
三次元構造担体のセル壁の表面に触媒成分を含む触媒コート層を形成すると共に、三次元構造担体における触媒成分の全担持量の50質量%以上がセル壁の表面に存在するように、消失材を消失させるためにスラリーがコートされた三次元構造担体を焼成する工程と、
を含むことを特徴とする触媒コンバータの製造方法。 - 上記消失材として、活性炭、高分子樹脂ビーズ、セルロース及びもみ殻から成る群より選ばれた少なくとも1種のものを使用することを特徴とする請求項2に記載の触媒コンバータの製造方法。
- 上記高分子樹脂ビーズが、ポリスチレンビーズ又はポリプロピレンビーズであることを特徴とする請求項1又は3に記載の触媒コンバータの製造方法。