JP2009516022A - 向上した熱伝導率を有する硬質ポリウレタン発泡体の成形方法 - Google Patents
向上した熱伝導率を有する硬質ポリウレタン発泡体の成形方法 Download PDFInfo
- Publication number
- JP2009516022A JP2009516022A JP2008540091A JP2008540091A JP2009516022A JP 2009516022 A JP2009516022 A JP 2009516022A JP 2008540091 A JP2008540091 A JP 2008540091A JP 2008540091 A JP2008540091 A JP 2008540091A JP 2009516022 A JP2009516022 A JP 2009516022A
- Authority
- JP
- Japan
- Prior art keywords
- foam
- polyol
- aromatic
- blowing agent
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
A)有機ポリイソシアネート、
B)物理的発泡剤、
C)3以上の官能性および300〜800のヒドロキシル数を持つ少なくとも1つのポリオールを含むポリオール組成物、
D)全ポリオール配合物の0〜2.5重量%で存在する水、
E)触媒、および
F)補助物質および/または添加剤、
を含み、発泡体が、33〜38kg/m3の成形密度を有する、発泡体を提供する。
ゲルまたはゲル化時間:ゲル時間は、混合開始から、スティックが、延伸された時に発泡体延伸繊維中へ導入される瞬間までを範囲とする。
膨張時間:膨張時間は、混合開始から、発泡体の膨張が完了する瞬間までを範囲とする。
不粘着時間:不粘着時間は、混合開始から、発泡体表面が作業者の指に粘着しなくなる瞬間までを範囲とする。
脱型時間:発泡体の射出および金型を開くまでの間の時間。
ポリオール組成物:イソシアネート分子と反応することのできる、存在するポリオール、架橋剤および鎖伸長剤の合計セット。
ポリオール配合物:ポリオール組成物+添加剤、例えば、物理的発泡剤を除く、触媒、界面活性剤、水等。
プレミックス:ポリオール配合物+全ての物理的発泡剤。
系または発泡体配合物:プレミックスおよびイソシアネート成分の組合せ。
自由膨張密度(FRD):300g以上の全体の系配合物重量から製造された自由膨張発泡体(周囲空気圧で)の中心から得られる、100x100x100mmブロックから測定される密度。FRDはkg/m3で報告される。
最小充填密度(MFD):金型を完全に充填するのに必要な最少重量およびこの金型の容量から決定される密度。MFDはkg/m3で報告される。
最少充填重量(MFW):金型を完全に充填するのに必要な最少重量。MFWはkgで報告される。
成形密度(MD):金型中に射出された重量およびこの金型の容量から決定される密度。MDはkg/m3で報告される。測定される成形密度は、サンプルの重量を計り、この重量を、サンプルの測定容量で割ることにより、mmにおける100x100x「厚さ」(スキンを含む)の最低5個のサンプルの平均から決定される。
過充填:過充填は、[射出された重量*100/MFW]として定義される。過充填はパーセントで報告される。
充填率:充填率は、[成形密度/FRD]として定義される。充填率は無次元数として報告される。
圧力:圧力は、金型における空気圧または金型壁上での発泡体の質量圧のいずれかである。全ての圧力は、mbar(またはhPa)単位の絶対圧で報告される。参照圧力は、海抜=0barゲージで、1000mbar=1000hPa=凡そ1気圧である。
DSD 287.02 Dow Chemical Companyから入手できる、365のヒドロキシル数、25℃で2000mPa.sの粘度および2.3%の水含有量で配合されたポリオール。
Voratec SD 308 Dow Chemical Companyから市販されている、385のヒドロキシル数、25℃で3500mPa.sの粘度および2.4%の水含有量で配合されたポリオール。
ポリオール配合物A 1.0%の水だけを含む以外はVoractec SD 308と同じに配合されたポリオール。
Voranol RN 482 Dow Chemical Companyから入手できる、490のヒドロキシル数を持つプロポキシル化ソルビトール。
Voranol CP 1055 Dow Chemical Companyから入手できる、156のヒドロキシル数を持つプロポキシル化グリセロール。
Voranol RA 640 Dow Chemical Companyから入手できる、640のヒドロキシル数を持つプロポキシル化エチレンジアミン。
Stepanpol PS 3152 Stepanから入手ができ、315のヒドロキシル数を有する芳香族ポリエステルポリオール。
Tercarol 5903 Dow Chemical Companyから入手できる、440のヒドロキシル数を持つプロポキシル化トルエンジアミン。
ポリオールA 500のヒドロキシル数を持つプロポキシル化アンモニア。
Voratec SD 100 Dow Chemical Companyから入手できるポリマーMDI。
Polycat 5 Air Products & Chemicals Inc.から入手できるアミン触媒。
Polycat 8 Air Products & Chemicals Inc.から入手できるアミン触媒。
Dabco TMR−30 Air Products & Chemicals Inc.から入手できる触媒。
Silicon A 商標TEGOSTAB(商標)Aのシリコン界面活性剤としてGoldschmidt−Degussaから入手できる硬質発泡体界面活性剤。
Silicon B 商標NIAX(商標)の界面活性剤として入手できる、GE Plasticsから入手できる硬質発泡体界面活性剤。
(比較例C1*およびC2*)
(実施例1)
(実施例2および3)
(実施例4)
(比較例C4、C5および実施例5)
Claims (21)
- 1.03〜1.9の充填率で反応混合物を密閉金型キャビティ中へ射出する方法により得られ、発泡体製造後24時間で測定して、ラムダ(10℃)(mW/m.K)に対する成形発泡体密度(kg/m3)の比が1.65〜2.15を有する成形硬質ポリウレタン発泡体であって、前記金型キャビティが減圧下にあり、前記反応混合物が、
A)有機ポリイソシアネート、
B)物理的発泡剤、
C)3以上の官能性および300〜800のヒドロキシル数を持つ少なくとも1つのポリオールを含むポリオール組成物、
D)全ポリオール配合物の0〜2.5重量%で存在する水、
E)触媒、および
F)補助物質および/または添加剤、
を含み、前記発泡体が33〜38kg/m3の成形密度を有する発泡体。 - 前記金型キャビティの圧力が300〜950mbarである、請求項1に記載の発泡体。
- 前記金型キャビティが500〜850mbarの初期圧力を有する、請求項2に記載の発泡体。
- 前記充填率が1.1〜1.6である、前記請求項のいずれかに記載の発泡体。
- イソシアネート指数が105〜125である、前記請求項のいずれかに記載の発泡体。
- 有機ポリイソシアネートが、4,4’−、2,4’−および2,2’−ジフェニルメタンジイソシアネート、ポリフェニル−ポリメチレンポリイソシアネート、2,4−および2,6−トリレンジイソシアネート、またはこれらの混合物から選択される芳香族ポリイソシアネートである、前記請求項のいずれかに記載の発泡体。
- 有機ポリイソシアネートが、ジフェニルメタンジイソシアネートおよびポリフェニル−ポリメチレンポリイソシアネートの混合物であり、前記ジフェニルメタンジイソシアネート異性体含有量が、前記ポリイソシアネートの30〜60重量%である、請求項6に記載の発泡体。
- 10℃の平均温度で、発泡体製造後24時間で測定して、18〜21〜21mW/m.Kの熱伝導率を有する、請求項1に記載の発泡体。
- 19〜20mW/m.Kのラムダを有する、請求項1に記載の発泡体。
- 物理的発泡剤が10℃を超える沸点を有する、請求項1に記載の発泡体。
- 前記発泡剤が、炭化水素、ハイドロフルオロカーボン、ハイドロクロロフルオロカーボン、ギ酸メチルまたはトランス−ジクロロエテンである、請求項10に記載の発泡体。
- 前記発泡剤が、245fa、365mfc、227またはこれらの混合物である、請求項10に記載の発泡体。
- 前記発泡剤が、n−ペンタン、イソ−ペンタン、シクロペンタン、n−ブタン、シクロヘキサンまたはこれらの混合物から選択される炭化水素である、請求項10に記載の発泡体。
- 前記物理的発泡剤が、ポリオール組成物の10〜30重量%の量で存在する、請求項10に記載の発泡体。
- 脱型時間が6分未満である、請求項1に記載の発泡体。
- 脱型時間が5分未満である、請求項1に記載の発泡体。
- ポリオール組成物が、25℃で1000mPa.sの粘度を有する、請求項1に記載の発泡体。
- ポリオール組成物が、アミンを含む少なくとも1つの芳香族開始剤分子上への、少なくとも1つのアルキレンオキシドのアニオン重合付加により調製される少なくとも1つのポリオールを含む、請求項1に記載の発泡体。
- 前記開始剤が、芳香族ポリカルボン酸、芳香族ヒドロカルボン酸および芳香族アミノカルボン酸、芳香族モノアミンおよびポリアミン、フェノールの縮合体、ホルムアルデヒドおよび場合によりジアルカノールアミン、またはこれらの混合物から選択される、請求項18に記載の発泡体。
- 前記開始剤分子が、1,2−、1,3−および1,4−フェニレンジアミン、1,3−、2,4−、3,4−および2,6−トリレンジアミン、4,4’−、2,4’−および2,2−ジアミノジフェニルメタン、ポリフェニル−ポリメチレン−ポリアミン、およびこれらの混合物から選択される芳香族ポリアミンである、請求項18に記載の発泡体。
- 前記芳香族アミン開始ポリオールが、ポリオール組成物の10〜60重量%を占める、請求項20に記載の発泡体。