JP2007224433A - Method for producing carbon nano structure, catalyst metal substrate and catalyst reaction container - Google Patents
Method for producing carbon nano structure, catalyst metal substrate and catalyst reaction container Download PDFInfo
- Publication number
- JP2007224433A JP2007224433A JP2006043736A JP2006043736A JP2007224433A JP 2007224433 A JP2007224433 A JP 2007224433A JP 2006043736 A JP2006043736 A JP 2006043736A JP 2006043736 A JP2006043736 A JP 2006043736A JP 2007224433 A JP2007224433 A JP 2007224433A
- Authority
- JP
- Japan
- Prior art keywords
- carbon
- metal substrate
- space
- catalyst
- catalyst particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、カーボンナノ構造体の製造方法と、カーボンナノ構造体の製造に使用する触媒金属基材および触媒反応容器に関する。 The present invention relates to a method for producing a carbon nanostructure, and a catalytic metal substrate and a catalyst reaction vessel used for producing the carbon nanostructure.
カーボンナノチューブに代表されるカーボンナノ構造体はその特性から、広い用途の応用が考えられている有望な材料である。しかしながらその製造の困難さから高純度かつ高効率で生産する方法の開発が望まれている。 Carbon nanostructures typified by carbon nanotubes are promising materials that are considered to be used in a wide range of applications due to their characteristics. However, the development of a method for producing with high purity and high efficiency is desired because of the difficulty of the production.
カーボンナノチューブを生成させる方法としては、ナノメートルレベルの直径を有する触媒粒子を用いて、アルコール系、炭化水素系等の原料ガスを加熱炉内で熱分解し、触媒粒子上にカーボン結晶を成長させてカーボンナノチューブとする熱分解法が考案されている。熱分解法には、塗布等によって基材上に触媒を担持させる方法や、気相中に触媒を浮遊させる方法等がある。 As a method of generating carbon nanotubes, using catalyst particles having a diameter of nanometer level, a raw material gas such as alcohol or hydrocarbon is pyrolyzed in a heating furnace to grow carbon crystals on the catalyst particles. A thermal decomposition method for carbon nanotubes has been devised. Examples of the pyrolysis method include a method of supporting a catalyst on a substrate by coating or the like, a method of floating a catalyst in a gas phase, and the like.
たとえば特許文献1には、有機遷移金属化合物のガスとキャリアガスと有機化合物のガスとの混合ガスを800〜1300℃に加熱することにより浮遊状態で気相成長炭素繊維を生成する方法が提案されている。 For example, Patent Document 1 proposes a method of generating vapor-grown carbon fibers in a floating state by heating a mixed gas of an organic transition metal compound gas, a carrier gas, and an organic compound gas to 800 to 1300 ° C. ing.
特許文献2には、基板上に触媒金属膜を形成する段階と、該触媒金属膜を蝕刻して分離されたナノサイズの触媒金属粒子を形成する段階と、熱化学気相蒸着装置内へカーボンソースガスを供給して熱化学気相蒸着法で分離されたナノサイズの触媒金属粒子毎にカーボンナノチューブを成長させて基板上に垂直に整列した複数個のカーボンナノチューブを形成する段階を含み、分離されたナノサイズの触媒金属粒子を形成する段階は、アンモニアガス、水素ガスおよび水素化物ガスからなる群から選択されたいずれか1つの蝕刻ガスを熱分解させて使用するガス蝕刻法によって行われるカーボンナノチューブの合成方法が提案されている。
In
特許文献3には、耐熱性の多孔質担体に触媒微粒子を分散担持させた基板上に炭化水素ガスをキャリアガスとともに送り、該炭化水素ガスの熱分解を利用して、単層カーボンナノチューブを気相合成する方法が提案されている。 In Patent Document 3, hydrocarbon gas is sent together with a carrier gas onto a substrate in which catalyst fine particles are dispersedly supported on a heat-resistant porous carrier, and single-walled carbon nanotubes are gasified by utilizing thermal decomposition of the hydrocarbon gas. A method of phase synthesis has been proposed.
特許文献4には、加熱した金属に対し炭素源となるガスを流して、化学気相成長法により該金属表面にカーボンナノチューブを製造する方法であって、該金属の表面にあらかじめ酸化物の微結晶を生成することにより金属表面に微細な凹凸を形成する処理がほどこされていることを特徴とする方法が提案されている。
しかし、特許文献1から4に記載されたような従来の方法では、カーボンナノチューブを製造するときに、カーボンナノチューブだけでなくアモルファスカーボンやグラファイト等が副生成物として生成されるという問題があった。また、触媒がアモルファスカーボン等で覆われてしまうことにより、カーボンナノチューブの成長が止まり、長さはせいぜい数mmであり、数cm以上に長尺化できないという問題があった。 However, the conventional methods described in Patent Documents 1 to 4 have a problem in that when carbon nanotubes are produced, not only carbon nanotubes but also amorphous carbon, graphite, and the like are generated as by-products. Further, since the catalyst is covered with amorphous carbon or the like, the growth of the carbon nanotubes stops, and the length is at most several millimeters, and there is a problem that the length cannot be increased to several centimeters or more.
本発明の目的は、上記課題を解決し、高純度で長尺のカーボンナノ構造体を安定して製造することが可能な、カーボンナノ構造体の新規な製造方法を提供することにある。さらに、本発明の他の目的は、カーボンナノ構造体の製造に使用する触媒金属基材および触媒反応容器を提供することにある。 An object of the present invention is to solve the above-mentioned problems and to provide a novel method for producing a carbon nanostructure capable of stably producing a high-purity and long carbon nanostructure. Furthermore, another object of the present invention is to provide a catalytic metal substrate and a catalytic reaction vessel used for producing a carbon nanostructure.
本発明では、密閉容器と、密閉容器の内部空間を第一の空間と第二の空間に仕切る触媒金属基材と、触媒金属基材を固定する固定部材と、を備えた触媒反応容器を用いてカーボンナノ構造体を製造する。触媒金属基材は、第一の空間に接する第一の表面と第二の空間に接する第二の表面を有するように配置されており、かつ第二の表面の少なくとも一部に触媒粒子を備えている。密閉容器の第一の空間に少なくとも炭素を含む原料ガスを供給し、第一の表面から触媒金属基材の内部を通って第二の表面に達した炭素を、触媒粒子を基点としてカーボンナノ構造体に成長させることによりカーボンナノ構造体を製造する(請求項1)。また、本発明は当該製造に用いる触媒金属基材(請求項5)と、触媒反応容器(請求項6)を提供する。 In the present invention, a catalytic reaction vessel including a sealed container, a catalytic metal base material that partitions the internal space of the sealed container into a first space and a second space, and a fixing member that fixes the catalytic metal base material is used. To produce carbon nanostructures. The catalytic metal substrate is arranged to have a first surface in contact with the first space and a second surface in contact with the second space, and is provided with catalyst particles on at least a part of the second surface. ing. Supply a source gas containing at least carbon to the first space of the sealed container, and the carbon that has reached the second surface from the first surface through the inside of the catalytic metal base is formed from the catalyst particles as a carbon nanostructure. A carbon nanostructure is produced by growing the body (claim 1). The present invention also provides a catalytic metal substrate (Claim 5) and a catalytic reaction vessel (Claim 6) used for the production.
従来は触媒への炭素の供給部分とカーボンナノ構造体の成長部分が分離されていなかったが、本発明では触媒金属基材において炭素を含む原料ガスの供給面(第一の表面)とカーボンナノ構造体の成長面(第二の表面)を別々にし、触媒粒子を基点としてカーボンナノ構造体を成長させている。このため、成長面がアモルファスカーボン等で覆われることが抑制され、高純度のカーボンナノ構造体を安定して成長させることができる。 Conventionally, the carbon supply portion to the catalyst and the growth portion of the carbon nanostructure have not been separated, but in the present invention, the supply surface (first surface) of the raw material gas containing carbon and the carbon nanostructure in the catalyst metal substrate The growth surface (second surface) of the structure is separated, and the carbon nanostructure is grown with the catalyst particle as a base point. For this reason, it is suppressed that the growth surface is covered with amorphous carbon or the like, and a high-purity carbon nanostructure can be stably grown.
なお、本発明における「カーボンナノ構造体」とは、主として炭素からなるチューブ状、渦巻状、ホーン状、球状などのナノメートルレベルの微小構造体をさす。「カーボンナノ構造体」の例としては、カーボンナノチューブ、カーボンナノコイル、カーボンナノホーン等があげられる。 The “carbon nanostructure” in the present invention refers to a nanometer-level microstructure such as a tube, spiral, horn, or sphere mainly composed of carbon. Examples of “carbon nanostructures” include carbon nanotubes, carbon nanocoils, and carbon nanohorns.
さらに、本発明において「触媒金属基材の表面に触媒粒子が備わっている」とは、触媒金属基材から触媒粒子へ炭素が拡散可能なように、触媒粒子が触媒金属基材表面に固定されている状態をいう。例えば、触媒粒子が触媒金属基材から析出して付着している状態、触媒粒子が触媒金属基材に圧着されて密着した状態、触媒金属基材と触媒粒子の界面で化合物が形成されて固定された状態、などである。あるいは触媒金属基材と触媒粒子が接していなくても、炭素の拡散が十分に速い中間層を介して触媒粒子が固定されていても良い。 Further, in the present invention, “the catalyst metal substrate has catalyst particles on the surface” means that the catalyst particles are fixed on the catalyst metal substrate surface so that carbon can diffuse from the catalyst metal substrate to the catalyst particles. The state that is. For example, the catalyst particles are deposited and adhered from the catalyst metal substrate, the catalyst particles are pressed and adhered to the catalyst metal substrate, and a compound is formed and fixed at the interface between the catalyst metal substrate and the catalyst particles. State, etc. Alternatively, even if the catalyst metal substrate and the catalyst particles are not in contact with each other, the catalyst particles may be fixed through an intermediate layer in which carbon diffusion is sufficiently fast.
また、本発明における触媒粒子の形状は特に限定されず、円柱状、角柱状、多面体状、球状、円錐状、角錐状など、いずれでもよい。また、大きさも特に限定されないが、10μm以下が好ましい。さらには大きさが1μm以下のナノ粒子であることが好ましく、カーボンナノ構造体と同程度の大きさの数nmであるとさらに好ましい。小さい方が、ナノサイズであるカーボンナノ構造体の成長の基点となりやすい。また、成長させるカーボンナノ構造体の大きさをそろえるためには、触媒粒子の大きさをそろえておくことが好ましい。 In addition, the shape of the catalyst particles in the present invention is not particularly limited, and may be any of a cylindrical shape, a prismatic shape, a polyhedral shape, a spherical shape, a conical shape, a pyramid shape, and the like. Moreover, although a magnitude | size is not specifically limited, 10 micrometers or less are preferable. Furthermore, it is preferable that it is a nanoparticle with a magnitude | size of 1 micrometer or less, and it is still more preferable in it being several nanometers comparable as a carbon nanostructure. The smaller one tends to be the starting point for the growth of nano-sized carbon nanostructures. In order to align the size of the carbon nanostructures to be grown, it is preferable to align the sizes of the catalyst particles.
本発明における触媒金属基材は板状であることが好ましい。板状とすることで、触媒金属基材の表裏の面を、第一の表面(原料ガスの供給面)と第二の表面(カーボンナノ構造体の成長面)とすることができ、密閉容器内部を仕切ることが容易となる。 The catalytic metal substrate in the present invention is preferably plate-shaped. By adopting a plate shape, the front and back surfaces of the catalytic metal substrate can be used as a first surface (source gas supply surface) and a second surface (carbon nanostructure growth surface). It becomes easy to partition the inside.
また、触媒金属基材を板状とする場合、厚さは50μm以下とすることが好ましい(請求項2)。厚さを50μm以下とすることにより、触媒金属基材の第一の表面から触媒金属基材の内部を通して第二の表面へ炭素を供給する際に、炭素が成長部に達するまでの時間が短縮され、製造コストを節約できる。 Moreover, when making a catalyst metal base material into plate shape, it is preferable that thickness is 50 micrometers or less (Claim 2). By setting the thickness to 50 μm or less, when supplying carbon from the first surface of the catalytic metal substrate to the second surface through the inside of the catalytic metal substrate, the time until the carbon reaches the growth portion is shortened. Saving manufacturing costs.
また、触媒金属基材を板状とする場合、厚さは5μm以上とすることが好ましい。5μm以上とすることにより、触媒金属基材の強度が上がり、カーボンナノ構造体の製造工程において穴が開くなどの破損が生じる可能性が小さくなる。 Moreover, when making a catalyst metal base material into plate shape, it is preferable that thickness shall be 5 micrometers or more. By setting it as 5 micrometers or more, the intensity | strength of a catalyst metal base material goes up, and possibility that breakage, such as a hole opening will arise in the manufacturing process of a carbon nanostructure will become small.
さらに、触媒金属基材は、鉄、コバルト、ニッケルのいずれか、又はこれらのうちの2種以上の合金からなることが好ましい。これらは炭素を含むガスを分解して炭素を析出し、カーボンナノ構造体を生成する触媒として適している材料である。このほか基材としては、炭素ガスを分解して炭素を析出する触媒である他の材料を使用することも可能である。なお、触媒粒子は、炭素であってもかまわない。成長させるカーボンナノ構造体は炭素であるので、当然炭素も成長の基点となりえるからである。 Furthermore, the catalytic metal substrate is preferably made of iron, cobalt, nickel, or an alloy of two or more of these. These are materials suitable as a catalyst for decomposing a gas containing carbon to deposit carbon and generating a carbon nanostructure. In addition, as the base material, it is also possible to use other materials which are catalysts for decomposing carbon gas and depositing carbon. The catalyst particles may be carbon. This is because carbon nanostructures to be grown are carbon, and carbon can naturally be a starting point for growth.
本発明における触媒粒子は、触媒金属基材と異なる物質であることが好ましい(請求項4)。異なる物質であるほうが、特異点として触媒粒子のない基材表面部と組成や構造の差が大きくなり、カーボンナノ構造体が特異点を基点としてさらに成長しやすくなるためである。 The catalyst particles in the present invention are preferably a substance different from the catalyst metal substrate. This is because a different material has a larger difference in composition and structure from the surface portion of the base material having no catalyst particles as a singular point, and the carbon nanostructure is more easily grown from the singular point.
さらに、触媒粒子は、炭素と反応性が高くてカーボンナノ構造体が成長しやすいように、炭素が溶解する物質もしくは炭素と化合物を生成する物質であることが好ましい。具体的な物質としては、例えば、アルミニウム、シリコン、チタン、クロム、マンガン、鉄、コバルト、ニッケル、ジルコニウム、ニオブ、モリブデン、タンタル、タングステン、あるいはこれらの2種以上の合金、などが挙げられる。特に、カーボンナノ構造体を生成する触媒として作用する物質であることが好ましいので、鉄、コバルト、ニッケルのいずれか、又はこれらのうちの2種以上の合金であることが好ましい。なお、触媒粒子を触媒金属基材と異なる物質とする場合には、例えば触媒金属基材の材質を鉄としているときは、触媒粒子として鉄は選択しないことになる。 Furthermore, the catalyst particles are preferably a substance that dissolves carbon or a substance that forms a compound with carbon so that the carbon nanostructure can easily grow because of its high reactivity with carbon. Specific examples of the material include aluminum, silicon, titanium, chromium, manganese, iron, cobalt, nickel, zirconium, niobium, molybdenum, tantalum, tungsten, and alloys of two or more thereof. In particular, since it is preferably a substance that acts as a catalyst for generating a carbon nanostructure, it is preferably iron, cobalt, nickel, or an alloy of two or more of these. When the catalyst particles are different from the catalyst metal substrate, for example, when the material of the catalyst metal substrate is iron, iron is not selected as the catalyst particles.
また、触媒粒子は、触媒金属基材の表面上に複数点在することにより、複数のカーボンナノ構造体を同時に製造することができる(請求項3)。 Further, a plurality of catalyst particles are scattered on the surface of the catalyst metal substrate, whereby a plurality of carbon nanostructures can be produced simultaneously (claim 3).
本発明によれば、触媒粒子を基点としてカーボンナノ構造体を成長させる新規の製造方法が提供される。また、原料ガスの熱分解によって生じた炭素の触媒金属基材への溶解と触媒金属基材からの炭素の析出によるカーボンナノ構造体の成長が、触媒金属基材の異なる部位で生じるため、高純度で長尺のカーボンナノ構造体を安定して製造することができる。 ADVANTAGE OF THE INVENTION According to this invention, the novel manufacturing method which grows a carbon nanostructure from a catalyst particle as a starting point is provided. In addition, the growth of carbon nanostructures due to the dissolution of carbon in the catalytic metal substrate and the deposition of carbon from the catalytic metal substrate caused by the thermal decomposition of the raw material gas occurs at different parts of the catalytic metal substrate. A long carbon nanostructure having a high purity can be stably produced.
(1)触媒金属基材の作製
金属基材表面に触媒粒子を備えさせる方法としては、塗布法、イオン打ち込み法、スパッタリング法、蒸着法、めっき法、などが考えられるが、ここでは塗布による方法を示す。
(1) Preparation of catalytic metal substrate As a method for providing catalyst particles on the surface of a metal substrate, a coating method, an ion implantation method, a sputtering method, a vapor deposition method, a plating method, and the like can be considered. Indicates.
まず、直径20mmφ、厚さ50μmで、純度が99.99%以上の鉄からなる円板状の金属基材1の片面に、粒径5μmのコバルト粉末を分散させたエチルアルコールを塗布した後、乾燥炉を用いて約100℃で乾燥させる。 First, after applying ethyl alcohol in which cobalt powder having a particle diameter of 5 μm is dispersed on one surface of a disk-shaped metal base 1 made of iron having a diameter of 20 mmφ and a thickness of 50 μm and a purity of 99.99% or more, Dry at about 100 ° C. using a drying oven.
次に、真空中または不活性ガス中で、1400℃に加熱する。この加熱により、コバルト粒子が金属基材1の表面に付着する。 Next, it is heated to 1400 ° C. in vacuum or in an inert gas. By this heating, cobalt particles adhere to the surface of the metal substrate 1.
図1は、このようにして作製した触媒金属基材の断面模式図である。板状の鉄製の金属基材1の一方の表面に、複数の触媒粒子2が備わっている様子が示されている。なお、図1では触媒粒子2が金属基材1の表面から突出しているが、表面付近に埋まった状態で表面は平坦であり、触媒粒子の一部が露出している状態でもかまわない。例えば、触媒粒子2を金属基材1より硬い材質とし、図1のように配置された触媒粒子2を、さらに硬質の板材で押すことにより触媒粒子2を金属基材1に埋め込み、その後金属基材1の表面を研磨して平坦にするなどの方法で製造することができる。
FIG. 1 is a schematic cross-sectional view of the catalytic metal substrate produced in this manner. A state in which a plurality of
(2)カーボンナノ構造体の作製
図2はカーボンナノ構造体の製造装置の断面模式図である。図2には、密閉容器23と加熱炉28の断面模式図が示されている。上記で作製した触媒金属基材24を、固定部材25で固定して、円筒状の密閉容器23内に設置する。
(2) Production of carbon nanostructure FIG. 2 is a schematic sectional view of a carbon nanostructure production apparatus. FIG. 2 shows a schematic cross-sectional view of the sealed
密閉容器23の内部は、触媒金属基材24により第一の空間21と第二の空間22に分離されており、炭素を含む原料ガスは第一の空間21に供給される。第一の空間21に接している第一の表面26には炭素が供給され、触媒金属基材24の内部を炭素が通って、第二の空間22に接している触媒金属基材24の第二の表面27に達し、触媒粒子29よりカーボンナノ構造体210が成長する。
The inside of the sealed
炭素を含むガスとしては、メタンガスやアセチレンガスなどの炭化水素ガスや、COガスなどが使用できる。また、原料ガスに、希釈のための不活性ガスや、酸化防止のための還元性ガスを混合することもできる。圧力、流量や、2種以上の混合ガスを供給するときの流量比は、カーボンナノ構造体の成長を制御するために適宜調整することができる。 As gas containing carbon, hydrocarbon gas, such as methane gas and acetylene gas, CO gas, etc. can be used. In addition, an inert gas for dilution and a reducing gas for preventing oxidation can be mixed with the raw material gas. The pressure, the flow rate, and the flow rate ratio when supplying two or more mixed gases can be adjusted as appropriate in order to control the growth of the carbon nanostructure.
空間22に供給するガスは、不活性ガスだけでも良いが、カーボンナノ構造体の成長を促進するように2種以上の混合ガスを使用することもできる。特に、酸化を防止するため、水素ガスなどの還元性ガスを混合しても良いし、還元性ガスのみとしてもよい。また、結晶化促進のために、炭素を含むガスを微量混合してもよい。圧力、流量や、2種以上の混合ガスを供給するときの流量比は、適宜調整することができる。さらには、空間22にはガスを供給せずに、ロータリーポンプなどの真空ポンプで排気しつづけ、真空状態とすることもできる。
The gas supplied to the
カーボンナノ構造体を成長させるときの触媒反応容器の内部の温度は、炭素の鉄に対する溶解度が大きくなるように730℃以上とすることが好ましい。処理時間を長くして、連続的あるいは断続的に成長させることにより、長尺のカーボンナノ構造体を成長させることができる。加熱時間や温度などの成長条件は適宜調整することができる。 The temperature inside the catalytic reaction vessel when the carbon nanostructure is grown is preferably 730 ° C. or higher so that the solubility of carbon in iron is increased. A long carbon nanostructure can be grown by extending the treatment time and growing continuously or intermittently. Growth conditions such as heating time and temperature can be appropriately adjusted.
カーボンナノ構造体の成長方法の一例を以下に示す。空間21に供給する原料ガスはCOガスとし、Arガスおよび水素ガスを混合する。空間21の圧力は1気圧とし、COガスの流量は300ml/分、Arガスの流量は300ml/分、水素ガスの流量は300ml/分とする。
An example of the growth method of the carbon nanostructure is shown below. The source gas supplied to the
空間22に供給するガスはArガスと水素ガスの混合ガスで、圧力は1気圧とする。Arガスの流量は855ml/分、水素ガスの流量は45ml/分とする。
The gas supplied to the
上記のようにガスを供給した状態で、加熱炉28により触媒反応容器の内部の温度を880℃になるように加熱し、3時間保持することにより、触媒粒子29の先端よりカーボンナノ構造体210を成長させることができる。
With the gas supplied as described above, the temperature inside the catalytic reaction vessel is heated to 880 ° C. by the
カーボンナノ構造体であることは、電子顕微鏡などで観察したり、ラマン分光をおこなう等で、確認することができる。 The carbon nanostructure can be confirmed by observing with an electron microscope or performing Raman spectroscopy.
上記に述べた方法は、触媒粒子を基点としてカーボンナノ構造体を成長させるという新規のカーボンナノ構造体の製造方法である。さらに、触媒がアモルファスカーボン等で覆われて成長が止まることがないため、長尺のカーボンナノ構造体を作製することができる。 The method described above is a novel method for producing a carbon nanostructure in which a carbon nanostructure is grown using catalyst particles as a starting point. Furthermore, since the catalyst is covered with amorphous carbon or the like and the growth does not stop, a long carbon nanostructure can be produced.
今回開示された実施の形態はすべての点で例示であって、制限的なものではないと考えられるべきである。本発明の範囲は上記した説明ではなくて特許請求の範囲によって示され、特許請求の範囲と均等の意味および範囲内での全ての変更が含まれることが意図される。 The embodiment disclosed this time is to be considered as illustrative in all points and not restrictive. The scope of the present invention is defined by the terms of the claims, rather than the description above, and is intended to include any modifications within the scope and meaning equivalent to the terms of the claims.
1 金属基材、 2 触媒粒子
21 第一の空間、 22 第二の空間、 23 密閉容器
24 触媒金属基材、 25 固定部材
26 触媒金属基材の第一の表面、 27 触媒金属基材の第二の表面
28 加熱炉、 29 触媒粒子、 210 カーボンナノ構造体
DESCRIPTION OF SYMBOLS 1 Metal base material, 2
Claims (6)
前記触媒金属基材は、前記第一の空間に接する第一の表面と前記第二の空間に接する第二の表面を有するように配置されており、かつ前記第二の表面の少なくとも一部に触媒粒子を備え、
前記第一の空間に少なくとも炭素を含む原料ガスを供給し、
前記第一の表面から前記触媒金属基材の内部を通って前記第二の表面に達した炭素を、前記触媒粒子を基点としてカーボンナノ構造体に成長させることを特徴とする、カーボンナノ構造体の製造方法。 Using a catalytic reaction vessel comprising an airtight container, a catalytic metal base material that partitions the internal space of the airtight container into a first space and a second space, and a fixing member that fixes the catalytic metal base material,
The catalytic metal substrate is disposed to have a first surface in contact with the first space and a second surface in contact with the second space, and at least a part of the second surface. With catalyst particles,
Supplying a source gas containing at least carbon to the first space;
Carbon that has reached the second surface from the first surface through the inside of the catalytic metal substrate is grown into a carbon nanostructure based on the catalyst particles. Manufacturing method.
前記触媒金属基材は、前記第一の空間に接する第一の表面と前記第二の空間に接する第二の表面を有するように配置されており、かつ前記第二の表面の少なくとも一部に触媒粒子を備えている、カーボンナノ構造体製造用の触媒反応容器。 A catalytic reaction vessel comprising a sealed container, a catalytic metal base material that partitions the internal space of the sealed container into a first space and a second space, and a fixing member that fixes the catalytic metal base material,
The catalytic metal substrate is disposed to have a first surface in contact with the first space and a second surface in contact with the second space, and at least a part of the second surface. A catalytic reaction vessel for producing carbon nanostructures, comprising catalyst particles.