CN101307217A - 双组分聚氨酯粘合剂 - Google Patents
双组分聚氨酯粘合剂 Download PDFInfo
- Publication number
- CN101307217A CN101307217A CNA2007101038612A CN200710103861A CN101307217A CN 101307217 A CN101307217 A CN 101307217A CN A2007101038612 A CNA2007101038612 A CN A2007101038612A CN 200710103861 A CN200710103861 A CN 200710103861A CN 101307217 A CN101307217 A CN 101307217A
- Authority
- CN
- China
- Prior art keywords
- tackiness agent
- described tackiness
- component
- catalyzer
- glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
成分(都以wt%计) | 1 | 2 | 3 |
0.05 | 0.05 | 0.05 | |
DABCO 33-LV | 0.4 | 0.4 | 0.4 |
8-羟基喹啉 | 0 | 0.05 | 0.15 |
乙二醇 | 9.5 | 9.5 | 9.5 |
Desmophen S1011-35 | 44.25 | 44.25 | 44.25 |
Desmophen F-207 | 44.25 | 44.25 | 44.25 |
配方 | 1 | 2 | 3 |
外观 | 模糊,乳白色 | 模糊,浅绿色 | 模糊,浅绿色 |
粘度(cps) | 6313 | 6350 | 6188 |
固化的粘合剂的诱明度 | 非常轻微的模糊 | 诱明,无色 | 诱明,无色 |
拉伸搭接剪切 | |||
在10min时 | 49.7 | 7.1 | 0 |
在15min时 | 126 | 56.1 | 26.4 |
在20min时 | 163 | 149.6 | 86.1 |
在25min时 | 208* | 184.2* | 156.5 |
固化5天后 | |||
拉伸搭接剪切(室温.) | 541 | 439 | 468 |
拉伸搭接剪切(80℃) | 143 | 206 | 141 |
抗裂剥离(室温) | 17.9 | 20.6 | 20.7 |
成分(都以wt%计) | 4 | 5 | 6 |
DBTDL | 0.08 | 0 | 0 |
DABCO 33-LV | 0 | 0.12 | 0.5 |
Coscat 83 | 0 | 0 | 0.08 |
8-羟基喹啉 | 0 | 0 | 0 |
乙二醇 | 9 | 10 | 8 |
Desmophen S1011-35 | 87 | 90 | 45 |
Desmophen F-207 | 0 | 0 | 43 |
Atlas G-1672 | 4 | 0 | 4 |
配方 | 4 | 5 | 6 |
外观 | 模糊 | 模糊 | 透明 |
粘度(cps) | 7900 | 7875 | 6500 |
固化的粘合剂的透明度 | 轻微混浊 | 模糊 | 透明 |
拉伸搭接剪切 | |||
在10min时 | 3.6 | 3 | 80 |
在15min时 | 5.1 | 8 | 128 |
在20min时 | 8 | 14 | 156 |
在30min时 | 12.8 | 49 | 227 |
在40min时 | 25.1 | 121 | N/A |
在60min时 | 60 | 174 | N/A |
固化5天后 | |||
拉伸搭接剪切(室温) | 549 | 487 | 616 |
拉伸搭接剪切(80℃) | 128 | 150 | 131 |
抗裂剥离(室温) | 6.9 | 13 | 20 |
Claims (20)