WO2013069542A1 - 塩素化塩化ビニル系樹脂の製造方法 - Google Patents
塩素化塩化ビニル系樹脂の製造方法 Download PDFInfo
- Publication number
- WO2013069542A1 WO2013069542A1 PCT/JP2012/078368 JP2012078368W WO2013069542A1 WO 2013069542 A1 WO2013069542 A1 WO 2013069542A1 JP 2012078368 W JP2012078368 W JP 2012078368W WO 2013069542 A1 WO2013069542 A1 WO 2013069542A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- vinyl chloride
- chloride resin
- ultraviolet
- chlorinated vinyl
- ultraviolet led
- Prior art date
Abstract
Description
総消費電力量(W・h)=I×V×t×(光源の個数) (1)
<塩素化塩化ビニル系樹脂の作製>
図1に示すように、紫外線LED光源装置100として、UV-LED光源ユニット(株式会社センテック製、型番「OX223」)を準備した。紫外線LED光源装置100は、ピーク波長が365nmである紫外線LED素子110(日亜化学工業株式会社製、品番「NC4U133」、順電流500mA、順電圧14.9V)を3個有する。
支持体200で支持された1台の紫外線LED光源装置100に代えて、100Wの高圧水銀灯(東芝ライテック株式会社製、電流値1.3A、電圧値100V)を1灯用いた以外は、実施例1と同様にして、塩素化塩化ビニル系樹脂を得た。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B31」)を10重量部、液状の錫系安定剤(日東化成株式会社製、品番「TVS#8831」)を1重量部、粉末状の錫系安定剤(日東化成株式会社製、品番「TVS#8813」)を1重量部、滑剤であるステアリン酸(花王株式会社製、品番「ルナック(登録商標)S-90V」)を1重量部、およびポリエチレンワックス(三井化学株式会社製、品番「Hiwax220MP」)を0.3重量部配合して、8インチロールにて、195℃で5分間混練し、厚み0.6mmのシートを作製した。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B31」)を10重量部、液状の錫系安定剤(日東化成株式会社製、品番「TVS#8831」)を1重量部、粉末状の錫系安定剤(日東化成株式会社製、品番「TVS#8813」)を1重量部、滑剤であるステアリン酸(花王株式会社製、品番「ルナック(登録商標)S-90V」)を1重量部、およびポリエチレンワックス(三井化学株式会社製、品番「Hiwax220MP」)を0.3重量部配合して、8インチロールにて、195℃で5分間混練し、厚み0.6mmのシートを作製した。得られたシートを縦3cm、横5cmに切り取り、200℃のオーブンにて加熱し、シートが黒化するまでの時間を測定した。黒化とは、シートのL値が20以下であることをいう。L値は色差計(日本電色工業株式会社製、品番「ZE-2000」)を使用して測定した。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B31」)を10重量部、液状の錫系安定剤(日東化成株式会社製、品番「TVS#8831」)を1重量部、粉末状の錫系安定剤(日東化成株式会社製、品番「TVS#8813」)を1重量部、滑剤であるステアリン酸(花王株式会社製、品番「ルナック(登録商標)S-90V」)を1重量部、およびポリエチレンワックス(三井化学株式会社製、品番「Hiwax220MP」)を0.3重量部配合して、8インチロールにて、195℃で5分間混練し、厚み0.6mmのシートを作製した。得られたシートを15枚重ね合わせたものを、鋼板にクロームメッキを施して鏡面仕上げされたフェロ板間に挟んだ後、200℃の条件で、圧力を3MPa~5MPaの範囲で調整して10分間プレスし、厚み5mmの板を作製した。得られた板を用い、JIS-K7206に従って、塩素化塩化ビニル系樹脂のビカット軟化点(Vicat軟化点)の測定を行った。但し、荷重を5kgとし、昇温速度は50℃/h(B50法)とした。
<塩素化塩化ビニル系樹脂の作製>
図3に示すように、紫外線LED光源装置100aとして、UV-LED光源ユニット(株式会社センテック製、型番「OX224」)を準備した。紫外線LED光源装置100aは、ピーク波長が365nmである紫外線を照射する紫外線LED素子110a(日亜化学工業株式会社製、品番「NC4U133」、順電流500mA、順電圧14.9V)を12個有する。なお、実施例2で用いた紫外線LED素子の発光スペクトルは、図2に示すとおりであった。
支持体200aに支持された1台の紫外線LED光源装置100aに代えて、100Wの高圧水銀灯(サンエナジー株式会社製、品番「SEH1002J01」、順電流1.1±0.1A、順電圧110±10V)を1灯用いた以外は、実施例2と同様にして、塩素化塩化ビニル系樹脂を得た。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B11A」)を5重量部、液状の錫系安定剤(日東化成株式会社製、品番「N2000C」)を3重量部、PMMA樹脂(株式会社カネカ製、品番「カネエース(登録商標)PA-20」)を1重量部、複合滑剤(川研ファインケミカル株式会社製、品番「VLTN―4」)を1重量部配合して、8インチロールにて、180℃で3分間混練し、厚み0.6mmのシートを作製した。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B11A」)を5重量部、液状の錫系安定剤(日東化成株式会社製、品番「N2000C」)を3重量部、PMMA樹脂(株式会社カネカ製、品番「カネエース(登録商標)PA-20」)を1重量部、複合滑剤(川研ファインケミカル株式会社製、品番「VLTN―4」)を1重量部配合して、8インチロールにて、180℃で3分間混練し、厚み0.6mmのシートを作製した。得られたシートを縦3cm、横3.5cmに切り取り、200℃のオーブンにて加熱し、シートが黒化するまでの時間を測定した。黒化とは、シートのL値が20以下であることをいう。L値は色差計(日本電色工業株式会社製、品番「ZE-2000」)を使用して測定した。
塩素化塩化ビニル系樹脂100重量部に対して、メチルメタクリレート・ブタジエン・スチレン(MBS)樹脂(株式会社カネカ製、品番「カネエース(登録商標)B11A」)を5重量部、液状の錫系安定剤(日東化成株式会社製、品番「N2000C」)を3重量部、PMMA樹脂(株式会社カネカ製、品番「カネエース(登録商標)PA-20」)を1重量部、複合滑剤(川研ファインケミカル株式会社製、品番「VLTN―4」)を1重量部配合して、8インチロールにて、180℃で3分間混練し、厚み0.6mmのシートを作製した。得られたシートを15枚重ね合わせたものを、鋼板にクロームメッキを施して鏡面仕上げされたフェロ板間に挟んだ後、200℃の条件で、圧力を3MPa~5MPaの範囲で調整して10分間プレスし、厚み5mmの板を作製した。得られた板を用い、JIS-K7206に従って、塩素化塩化ビニル系樹脂のビカット軟化点の測定を行った。但し、荷重を5kgとし、昇温速度は50℃/h(B50法)とした。
<塩素化塩化ビニル系樹脂の作製>
図6に示すように、紫外線LED光源装置100bとして、UV-LED光源ユニット(株式会社センテック製、型番「OX558」)を準備した。紫外線LED光源装置100bは、ピーク波長が365nmである紫外線LED素子110b(日亜化学工業株式会社製、品番「NC4U133A」、順電流500mA、順電圧14.9V)を3個有する。
紫外線LED光源装置100bに代えて、紫外線LED光源装置としてUV-LED光源ユニット(株式会社センテック製、型番「OX559」)を1灯用いた以外は、実施例3と同様にして、塩素化塩化ビニル系樹脂を得た。紫外線LED光源装置は、ピーク波長が385nmである紫外線LED素子(日亜化学工業株式会社製、品番「NC4U134A」、順電流500mA、順電圧14.8V)を3個有する。
紫外線LED光源装置100bに代えて、100Wの高圧水銀灯(東芝ライテック株式会社製、順電流1.3A、順電圧100V)を1灯用いた以外は、実施例3と同様にして、塩素化塩化ビニル系樹脂を得た。
<塩素化塩化ビニル系樹脂の作製>
実施例3と同様に、紫外線LED光源装置100bを用いた。
紫外線LED光源装置として、実施例4と同様の紫外線LED光源装置を1灯用いた以外は、実施例5と同様にして、塩素化塩化ビニル系樹脂を得た。
110、110a、110b 紫外線LED素子
200、200a 支持体
300、300a、300b 円筒状容器
400、400a 温水
500、500a ウォーターバス
600、600a、600b 反応器
610、610a タービン翼
620、620a、620b 蓋
700、700a、700b 塩化ビニル系樹脂の水性懸濁液
Claims (5)
- 塩化ビニル系樹脂と塩素が導入された反応器内に紫外線を照射することで、塩化ビニル系樹脂を塩素化させ、塩素化塩化ビニル系樹脂を得ており、
前記紫外線照射は、紫外線LED、有機EL、無機EL及び紫外線レーザーからなる群から選ばれる少なくとも1種の光源を用いて行うことを特徴とする塩素化塩化ビニル系樹脂の製造方法。 - 前記光源が照射する紫外線は、ピーク波長の範囲が290nm以上400nm以下である請求項1に記載の塩素化塩化ビニル系樹脂の製造方法。
- 前記光源が照射する紫外線は、ピーク波長の範囲が350nm以上400nm以下である請求項1又は2に記載の塩素化塩化ビニル系樹脂の製造方法。
- 前記光源は、紫外線LEDである請求項1~3のいずれか1項に記載の塩素化塩化ビニル系樹脂の製造方法。
- 前記塩化ビニル系樹脂への塩素の供給は、塩化ビニル系樹脂の水性懸濁液に塩素を供給することで行われる請求項1~4のいずれか1項に記載の塩素化塩化ビニル系樹脂の製造方法。