WO2009145320A1 - ヒドロキシアルキルトリエチレンジアミン類の製造方法、及びそれを用いたポリウレタン樹脂製造用の触媒組成物 - Google Patents
ヒドロキシアルキルトリエチレンジアミン類の製造方法、及びそれを用いたポリウレタン樹脂製造用の触媒組成物 Download PDFInfo
- Publication number
- WO2009145320A1 WO2009145320A1 PCT/JP2009/059903 JP2009059903W WO2009145320A1 WO 2009145320 A1 WO2009145320 A1 WO 2009145320A1 JP 2009059903 W JP2009059903 W JP 2009059903W WO 2009145320 A1 WO2009145320 A1 WO 2009145320A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formula
- above formula
- represented
- group
- reaction
- Prior art date
Abstract
Description
で示されるヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法としては、例えば、ピペラジンと2,3-ジブロモプロパン酸エチルとを反応させて1,4-ジアザビシクロ[2.2.2]オクタン-2-カルボン酸エチルを調製し、次いで得られたエステルを還元して1,4-ジアザビシクロ[2.2.2]オクタン-2-メタノール(すなわち、ヒドロキシメチルトリエチレンジアミン)を得る方法が知られている(例えば、特許文献1参照)。
(I)ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法、
(II)ヒドロキシアルキルピペラジン類及び/又はヒドロキシピペラジンの製造方法、(III)ヒドロキシアルキルトリエチレンジアミン類を含むポリウレタン樹脂製造用の触媒組成物、及びそれを用いたポリウレタン樹脂の製造方法、
である。
(I-1)ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法:
[1]モノ置換ジヒドロキシアルキルピペラジン類及び/又はジ置換ヒドロキシアルキルピペラジン類を、酸触媒の存在下で分子内脱水縮合反応させることを特徴とする、ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法。
[上記式(2a)中、R、及びnは上記式(1a)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンを得ることを特徴とする上記[1]又は上記[2]に記載の製造方法。
[上記式(4a)中、R、及びnは上記式(1a)と同じ定義である。]
で示される化合物との付加反応により得られるモノ置換ジヒドロキシアルキルピペラジン類であることを特徴とする上記[3]に記載の製造方法。
[上記式(4b)中、R、及びnは上記式(1a)と同じ定義である。]
で示される化合物を、酸触媒の存在下で脱水縮合反応することにより得られるモノ置換ジヒドロキシアルキルピペラジン類であることを特徴とする上記[3]に記載の製造方法。
[上記式(4c)中、R、及びnは上記式(1a)と同じ定義であり、Xはハロゲン原子である。]
で示される化合物との反応により得られるモノ置換ジヒドロキシアルキルピペラジン類であることを特徴とする上記[3]に記載の製造方法。
[上記式(5a)中、R、及びnは上記式(1a)と同じ定義である。]
で示される化合物との反応により得られるモノ置換ジヒドロキシアルキルピペラジン類であることを特徴とする上記[3]に記載の製造方法。
[上記式(5b)中、R、及びnは上記式(1a)と同じ定義であり、Xはハロゲン原子である。]
で示される化合物との反応により得られたピペラジンのジアルキルエステル体を還元反応することにより得られるモノ置換ジヒドロキシアルキルピペラジン類であることを特徴とする上記[3]に記載の製造方法。
[上記式(6)中、R1、及びR2は各々独立して水素原子又は直鎖状若しくは分枝状の炭素数1~4のアルキル基を表す。m、及びnは各々独立して0~2の整数を表す。ただし、m+n<4である。]
で示されるヒドロキシアルキルピペラジン類又はヒドロキシピペラジン類と、下記式(7)
[上記式(1d)中、R1~R4、m、及びnは上記式(6)、及び式(7)と同じ定義である。]
で示されるジ置換ヒドロキシアルキルピペラジンを、酸触媒の存在下で分子内脱水縮合反応させ、下記式(2b)
[上記式(2c)中、R1~R4、m、及びnは上記(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類を得ることを特徴とする上記[1]又は[2]に記載の製造方法。
[10]上記式(7)で示されるアルキレンオキサイド類が、エチレンオキサイド又はプロピレンオキサイドであることを特徴とする上記[9]に記載の製造方法。
(II)ヒドロキシアルキルピペラジン類及び/又はヒドロキシピペラジンの製造方法: [11]下記式(8a)
[上記式(8b)中、R1、R2、m、及びnは上記式(6)と同じ定義である。]
で示されるジヒドロキシアルキルエチレンジアミン類を、酸触媒又はラネー金属触媒の存在下で分子内脱水縮合反応させることを特徴とする上記[9]に記載の式(6)で示されるヒドロキシアルキルピペラジン類及び/又はヒドロキシピペラジンの製造方法。
[13]ラネー金属触媒が、ラネー銅触媒を含むことを特徴とする上記[11]又は[12]に記載の製造方法。
(I-2)ヒドロキシアルキルトリエチレンジアミン類の製造方法:
[14]下記式(10)
[上記式(10)中、R1、及びR2は各々独立して水素原子又は炭素数1~4のアルキル基を表す。]
で示されるピペラジン類とグリセリンを、酸触媒の存在下で分子内脱水縮合反応させる、下記式(2d)
[16]酸触媒が、金属リン酸塩及び有機リン化合物からなる群より選ばれる一種又は二種以上の化合物を含むことを特徴とする上記[14]又は[15]に記載の製造方法。
(III)ヒドロキシアルキルトリエチレンジアミン類を含むポリウレタン樹脂製造用の触媒組成物、及びそれを用いたポリウレタン樹脂の製造方法:
[17]ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)又は[泡化反応速度定数/樹脂化反応速度定数]の値が0.5以上の第3級アミン化合物(C)とを含有するポリウレタン樹脂製造用の触媒組成物。
[18]ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン(A)が、下記式(2a)
[上記式(2d)中、R1、及びR2は上記式(10)と同じ定義である。]
で示されるヒドロキシメチルトリエチレンジアミン類からなる群より選ばれる一種又は二種であることを特徴とする上記[17]に記載のポリウレタン樹脂製造用の触媒組成物。
[上記式(11)中、R1~R8は各々独立して、水素原子、ヒドロキシ基、炭素数1~16のアルキル基、炭素数6~16のアリール基、炭素数1~10のヒドロキシアルキル基、炭素数1~10のアミノアルキル基、炭素数1~10のモノメチルアミノアルキル基、又は炭素数1~10のジメチルアミノアルキル基を表し、xは0~11の整数、yは0~11の整数、aは0~10の整数、及びbは0~10の整数、を表す。]
で示されるアミン化合物であることを特徴とする上記[17]乃至[19]のいずれかに記載のポリウレタン樹脂製造用の触媒組成物。
[25]ポリオールとポリイソシアネートとを、上記[17]乃至[24]のいずれかに記載の触媒組成物の存在下で反応させることを特徴とするポリウレタン樹脂の製造方法。
[26]上記[17]乃至[24]のいずれかに記載の触媒組成物の使用量が、ポリオール100重量部に対して0.01~30重量部の範囲であることを特徴とする上記[25]に記載のポリウレタン樹脂の製造方法。
なお、本発明のヒドロキシアルキルピペラジン類及び/又はヒドロキシピペラジンの製造方法のうち、酸触媒を使用する製造方法によれば、反応引火の危険性が高い水素及び/又は還元性の化合物を用いないので、従来方法に比べて簡便且つ安全にヒドロキシアルキルピペラジン類を得ることができる。
さらに、本発明のポリウレタン樹脂製造用の触媒組成物、及びそれを用いたポリウレタン樹脂の製造方法によれば、ポリウレタン製品を生産性、成形性良く製造することができる。
まず、本発明のヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法について説明する。
本発明の第一のヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法(以下、「第一の製造方法」ということがある。)は、モノ置換ジヒドロキシアルキルピペラジン類及び/又はジ置換ヒドロキシアルキルピペラジン類を、酸触媒の存在下で分子内脱水縮合反応させることをその特徴とする。
酸触媒としては、例えば、金属リン酸塩や有機リン化合物等のリン含有物質、窒素含有物質、硫黄含有物質、ニオブ含有物質、シリカ、アルミナ、シリカ-アルミナ、シリカ-チタニア、ゼオライト、ヘテロポリ酸、第4B族金属酸化物縮合触媒、第6B族金属含有縮合触媒、ブレンステッド酸、ルイス酸、リンアミド等が挙げられるが、これらのうちリン含有物質が特に好ましい。
上記した第一の製造方法において、酸触媒の使用量は、特に限定するものではないが、原料である、モノ置換ジヒドロキシアルキルピペラジン類とジ置換ヒドロキシアルキルピペラジン類の合計の使用量に対し、通常0.01~20重量%の範囲、好ましくは0.1~10重量%の範囲である。0.01重量%よりも少ない場合、反応が著しく遅くなるおそれがあり、20重量%を超えて使用しても経済的に不利となるおそれがある。
上記した第一の製造方法において、反応は気相で行っても液相で行っても良い。また、反応は懸濁床による回分、半回分、連続式でも、また固定床流通式でも実施できるが、工業的には、固定床流通式が操作、装置、経済性の面から有利である。
上記した第一の製造方法において、反応が気相で行われる場合、通常は、窒素ガス、アルゴンガス等の反応に不活性なガスの共存下で行われる。かかるガスの使用量は、特に限定するものではないが、原料である、モノ置換ジヒドロキシアルキルピペラジン類とジ置換ヒドロキシアルキルピペラジン類の合計の使用量1モルに対して、通常1~20モル、好ましくは2~10モルの範囲である。
上記式(1a)で示されるモノ置換ジヒドロキシアルキルピペラジン類としては、特に限定するものではないが、例えば、ジヒドロキシプロピルピペラジン類、ジヒドロキシブチルピペラジン類、ジヒドロキシペンチルピペラジン類、ジヒドロキシヘキシルピペラジン類等が挙げられる。上記式(1a)で示されるモノ置換ジヒドロキシアルキルピペラジン類としては、具体的には、下記式(3a)
上記した第一の製造方法において、上記式(1a)又は(1b)で示されるモノ置換ジヒドロキシアルキルピペラジン類としては、特に限定するものではなく、例えば、市販品を用いてもよいし、調製品を用いても良い。
また、上記した製造方法においては、例えば、下記式(6)
[上記式(6)中、R1、及びR2は各々独立して水素原子又は直鎖状若しくは分枝状の炭素数1~4のアルキル基を表す。m、及びnは各々独立して0~2の整数を表す。ただし、m+n<4である。]
で示されるヒドロキシアルキルピペラジン類と、下記式(7)
[上記式(1d)中、R1~R4、m、及びnは上記(6)、及び式(7)と同じ定義である。]
で示されるジ置換ヒドロキシアルキルピペラジン類を、酸触媒の存在下で分子内脱水縮合反応させると、下記式(2b)
[上記式(2c)中、R1~R4、m、及びnは上記(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類を得ることができる。
上記式(6)、式(1c)、式(1d)、式(2b)、及び式(2c)中、置換基R1、R2は、各々独立して水素原子又は直鎖状若しくは分枝状の炭素数1~4のアルキル基を表し、具体的にはメチル基、エチル基、プロピル基、イソプロピル基、ブチル基等が例示される。中でも、水素原子、メチル基又はエチル基が好ましい。また、上記式(6)、式(1c)、式(1d)、式(2b)、及び式(2c)中、m、及びnは各々独立して0~2の整数を表す。
上記式(6)で示されるヒドロキシアルキルピペラジン類としては、特に限定するものではないが、例えば、2-ヒドロキシメチルピペラジン、2-ヒドロキシエチルピペラジン、2-(ヒドロキシプロピル)ピペラジン、ヒドロキシブチルピペラジン、ヒドロキシペンチルピペラジン、ヒドロキシヘキシルピペラジン等が挙げられる。
また、上記した第一の製造方法において使用される、上記式(7)で示されるアルキレンオキサイド類としては、特に限定するものではないが、例えば、エチレンオキサイド、プロピレンオキサイド等が好適なものとして挙げられる。
得られるジ置換ヒドロキシアルキルピペラジン類としては、特に限定するものではないが、例えば、1-ヒドロキシエチル-3-ヒドロキシメチルピペラジン、1-(1’-メチル-2’ヒドロキシエチル)-3-ヒドロキシメチルピペラジン等が挙げられる。
得られるヒドロキシアルキルトリエチレンジアミン類としては、特に限定するものではないが、例えば、2-ヒドロキシメチルトリエチレンジアミン、2-ヒドロキシメチル-6-メチルトリエチレンジアミン、2-ヒドロキシエチルトリエチレンジアミン、ヒドロキシプロピルトリエチレンジアミン、ヒドロキシブチルトリエチレンジアミン等が挙げられる。
この方法によれば、上記した第一の製造方法において、原料として使用される上記式(6)で示されるヒドロキシアルキルピペラジン類を製造することができる。
本発明のヒドロキシアルキルピペラジン類及び/又はヒドロキシピペラジンの製造方法は、上記式(8a)で示されるジヒドロキシアルキルエチレンジアミン類、及び/又は上記式(8b)で示されるジヒドロキシアルキルエチレンジアミン類を、酸触媒又はラネー金属触媒の存在下で分子内脱水縮合反応させて、上記式(6)で示されるヒドロキシアルキルピペラジン類を得ることをその特徴とする。
上記した製造方法において、使用されるジヒドロキシアルキルエチレンジアミン類としては、上記式(8a)や、式(8b)で示される化合物であればよく、特に限定するものではない。例えば、ジヒドロキシプロピルエチレンジアミン類、ジヒドロキシブチルエチレンジアミン類、ジヒドロキシペンチルエチレンジアミン類、ジヒドロキシヘキシルエチレンジアミン類等が挙げられる。
上記した製造方法においては、このようなジヒドロキシアルキルエチレンジアミン類として、市販品を用いてもよいし、合成品を用いてもよい。
で示されるジヒドロキシプロピルエチレンジアミンが例示される。このジヒドロキシプロピルエチレンジアミンは、例えば、エチレンジアミンをグリシドール等のエポキシアルコールと付加反応させたり、エチレンジアミンをクロロプロパンジオールと付加反応させることにより得られる。
で示されるジヒドロキシプロピルエチレンジアミンが例示される。このジヒドロキシプロピルエチレンジアミンは、例えば、エチレンジアミンとジヒドロキシアセトンを水素化触媒の存在下で反応することにより得られる。
上記した製造方法において、分子内脱水縮合反応は、上記式(8a)で示されるジヒドロキシアルキルエチレンジアミン類、及び/又は上記式(8b)で示されるジヒドロキシアルキルエチレンジアミン類を、酸触媒又はラネー金属触媒に接触させることで実施される。
上記した製造方法において、酸触媒としては、例えば、金属リン酸塩や有機リン化合物等のリン含有物質、窒素含有物質、硫黄含有物質、ニオブ含有物質、シリカ、アルミナ、シリカ-アルミナ、シリカ-チタニア、ゼオライト、ヘテロポリ酸、第4B族金属酸化物縮合触媒、第6B族金属含有縮合触媒、ブレンステッド酸、ルイス酸、リンアミド等が挙げられるが、これらのうちリン含有物質が特に好ましい。
上記した有機リン化合物としては、特に制限はなく、従来公知のものでよく、上記の第一の製造方法で例示したものと同様である。
上記した製造方法では、酸触媒として、これらの化合物から選ばれる一種又は二種以上を用いることができる。
上記した製造方法において使用されるラネー金属触媒には、本発明の趣旨に反しない程度で、任意の触媒活性金属を含むことができる。
上記したヒドロキシアルキルピペラジン類の製造方法において、ラネー金属触媒の使用量は、特に限定するものではないが、原料である、上記式(8a)で示されるジヒドロキシアルキルエチレンジアミン類と上記式(8b)で示されるジヒドロキシアルキルエチレンジアミン類の合計の使用量に対し、通常0.1~20重量%の範囲であり、0.5~10重量%の範囲が好ましい。0.1重量%よりも少ない場合、反応が著しく遅くなるおそれがあり、20重量%を超えて使用しても経済的に不利となるおそれがある。
上記した製造方法においては、希釈剤として、窒素ガス、水素ガス、アンモニアガス、水蒸気、炭化水素等の不活性ガスや、水、不活性な炭化水素等の不活性溶媒を用いて、原料である、上記式(8a)や、式(8b)で示されるジヒドロキシアルキルエチレンジアミン類を希釈し、反応を進行させることができる。これらの希釈剤は任意の量で使用でき、特に限定するものではないが、[上記式(8a)で示されるジヒドロキシアルキルエチレンジアミン類と上記式(8b)で示されるジヒドロキシアルキルエチレンジアミン類の合計の使用量]/[希釈剤の使用量]のモル比は0.01~1の範囲とすることが好ましい。モル比0.01以上とすると、上記式(6)で示されるヒドロキシアルキルピペラジン類の生産性が向上する。また、モル比1以下とすると、上記式(6)で示されるヒドロキシアルキルピペラジン類の選択性が向上する。
上記した製造方法において、希釈剤は、上記式(8a)や、式(8b)で示されるジヒドロキシアルキルエチレンジアミン類と同時に反応器内に導入してもよいし、予め上記式(8a)や、式(8b)で示されるジヒドロキシアルキルエチレンジアミン類を希釈剤に溶解させた後に、原料溶液として反応器に導入してもよい。
本発明の第二の製造方法は、上記式(10)で示されるピペラジン類とグリセリンを、酸触媒存在下で分子内脱水縮合反応させ、上記式(2d)で示されるヒドロキシメチルトリエチレンジアミン類を得ることをその特徴とする。
ここで、上記式(10)で示されるピペラジン類としては、例えば、ピペラジン、メチルピペラジン、エチルピペラジン、ジメチルピペラジン等が好適なものとして挙げられる。本発明においては、これらのうち一種を単独で又は二種以上を併用して用いることができる。
上記した第二の製造方法においては、上記の有機リン化合物から選ばれる一種又は二種以上を用いることができる。
上記した第二の製造方法において、反応は気相で行っても液相で行っても良い。また、反応は懸濁床による回分、半回分、連続式でも、また固定床流通式でも実施できるが、工業的には、固定床流通式が操作、装置、経済性の面から有利である。
上記した第二の製造方法において、上記した希釈剤は上記式(10)で示されるピペラジン類及び/又はグリセリンと同時に反応器内に導入してもよいし、予め上記式(10)で示されるピペラジン類及び/又はグリセリンを希釈剤に溶解させた後に、原料溶液として反応器に導入してもよい。
上記した第二の製造方法において、[上記式(10)で示されるピペラジン類]/[グリセリン]のモル比は、通常0.02~50、好ましくは0.05~20の範囲である。モル比を0.02以上50以下にすることで、副反応が抑制されるため、上記式(2d)で示されるヒドロキシメチルトリエチレンジアミン類の選択率が向上する
上記した第二の製造方法において、反応温度は、通常150~500℃、好ましくは200~400℃の範囲である。反応温度は500℃以下とすることで、原料及び生成物の分解が抑制されるため、上記式(2d)で示されるヒドロキシメチルトリエチレンジアミン類の選択率が向上し、150℃以上とすることで十分な反応速度が得られる。
本発明のポリウレタン樹脂製造用の触媒組成物は、ヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)又は[泡化反応速度定数/樹脂化反応速度定数]の値が0.5以上の第3級アミン化合物(C)とを含有する。
上記した触媒組成物において、上記したヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)としては、上記式(2a)で示されるヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン、上記式(2b)で示されるヒドロキシアルキルトリエチレンジアミン類、及び/又は上記式(2c)で示されるヒドロキシアルキルトリエチレンジアミン類、並びに上記式(2d)で示されるヒドロキシメチルトリエチレンジアミン類等が例示される。これらのうち、上記式(2d)で示されるヒドロキシメチルトリエチレンジアミン類が好適に用いられる。本発明の触媒組成物においては、これらのうち一種を単独で又は二種以上を併用して用いることができる。
上記した触媒組成物において、上記したヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)としては、特に限定するものではないが、好ましくは、上記式(11)で示されるアミン化合物である。
上記式(11)で示されるアミン化合物の置換基R1~R8としては、各々独立して、水素原子、ヒドロキシ基、メチル基、ヒドロキシエチル基、ヒドロキシプロピル基、アミノエチル基、アミノプロピル基、モノメチルアミノエチル基、モノメチルアミノプロピル基、ジメチルアミノエチル基、又はジメチルアミノプロピル基が好ましい。
N,N-ジメチルエチレンジアミン、N,N-ジメチルプロピレンジアミン、N,N-ジメチルテトラメチレンジアミン、N,N-ジメチルペンタメチレンジアミン、N,N-ジメチルヘキサメチレンジアミン、N,N-ジメチルヘプタメチレンジアミン、N,N-ジメチルオクタメチレンジアミン、N,N-ジメチルノナメチレンジアミン、N,N-ジメチルデカメチレンジアミン、N-メチルエチレンジアミン、N-メチルプロピレンジアミン、N-メチルテトラメチレンジアミン、N-メチルペンタメチレンジアミン、N-メチルヘキサメチレンジアミン、N-メチルヘプタメチレンジアミン、N-メチルオクタメチレンジアミン、N-メチルノナメチレンジアミン、N-メチルデカメチレンジアミン、N-アセチルエチレンジアミン、N-アセチルプロピレンジアミン、N-アセチルテトラメチレンジアミン、N-アセチルペンタメチレンジアミン、N-アセチルヘキサメチレンジアミン、N-アセチルヘプタメチレンジアミン、N-アセチルオクタメチレンジアミン、N-アセチルノナメチレンジアミン、N-アセチルデカメチレンジアミン、N,N,N’-トリメチルジエチレントリアミン、N,N,N’,N”-テトラメチルトリエチレンテトラミン、N,N,N’,N”,N”’-ペンタメチルテトラエチレンペンタミン、N,N,N’,N”,N”’N””-ヘキサメチルペンタエチレンヘキサミン等の1級アミン化合物類、
N,N’-ジメチルエチレンジアミン、N,N’-ジメチルプロピレンジアミン、N,N’-ジメチルヘキサメチレンジアミン、トリメチルエチレンジアミン、トリメチルプロピレンジアミン、トリメチルテトラメチレンジアミン、トリメチルペンタメチレンジアミン、トリメチルヘキサメチレンジアミン、トリメチルヘプタメチレンジアミン、トリメチルオクタメチレンジアミン、トリメチルノナメチレンジアミン、トリメチルデカメチレンジアミン、テトラメチルジエチレントリアミン、ペンタメチルトリエチレンテトラミン、ヘキサメチルテトラエチレンペンタミン、ヘプタメチルペンタエチレンヘキサミン、ビス(N,N-ジメチルアミノプロピル)アミン、N-メチルピペラジン等の2級アミン化合物類、
N,N-ジメチルアミノエタノール、N,N-ジメチルアミノイソプロパノール、N,N-ジメチルアミノエトキシエタノール、N,N-ジメチルアミノエトキシイソプロパノール、N,N,N’-トリメチルアミノエチルエタノールアミン、N,N-ジメチルアミノエチル-N’-メチルアミノエチル-N”-メチルアミノエタノール、N,N-ジメチルアミノエチル-N’-メチルアミノエチル-N”-メチルアミノイソプロパノール、N,N-ジメチルアミノエトキシエトキシエタノール、N,N-ジメチルアミノエトキシエトキシイソプロパノール、N,N-ジメチル-N’-(2-ヒドロキシエチル)エチレンジアミン、N,N-ジメチル-N’-(2-ヒドロキシエチル)プロパンジアミン、N,N-ジメチル-N’,N’-ビス(2-ヒドロキシプロピル)-1,3-プロパンジアミン、N,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテル、N,N,N’-トリメチル-N’-(2-ヒドロキシイソプロピル)ビス(2-アミノエチル)エーテル、N,N-ビス(3-ジメチルアミノプロピル)-N-イソプロパノールアミン、N,N-ジメチルアミノヘキサノール、5-ジメチルアミノ-3-メチル-1-ペンタノール、N,N,N’-トリメチル-N’-(2-ヒドロキシエチル)プロピレンジアミン、N,N,N’-トリメチル-N’-(2-ヒドロキシプロピル)プロピレンジアミン等のアルカノールアミン類等、
が例示される。
上記した触媒組成物において、ヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)との混合比率は、特に限定するものではないが、通常、ヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)の重量比(すなわち、[ヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)]/[ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)])が、通常1/99~99/1の範囲になるように混合比率を調節する。更に好ましくは5/95~95/5の範囲である。重量比がこの範囲を超えると両触媒の相乗効果が得られない場合があり、ポリウレタン樹脂の物性及び触媒活性の点で満足できる性能を発揮しない場合がある。
すなわち、トルエンジイソシアネートとジエチレングリコールを、イソシアネート基/水酸基のモル比が1.0になるように仕込み、触媒として第3級アミン化合物を一定量添加し、ベンゼン溶媒中で一定の温度に保って反応させ、未反応イソシアナート量を測定する。ここで、トルエンジイソシアネートとジエチレングリコールの反応が各々の濃度に一次であると仮定すると、次式が成立する。
dx/dt=k(a-x)2 (1)
上記式(1)において、
x:反応したNCO基の濃度(mol/L)、
a:NCO基の初期濃度(mol/L)、
k:反応速度定数(L/mol・h)、
t:反応時間(h)である。
1/(a-x)=kt+1/a (2)
上記式(2)より反応速度定数kを求め、下記式(3)に代入して触媒定数Kcを求める。
k=ko+KcC (3)
上記式(3)において、
ko:無触媒の反応速度定数(L/mol・h)、
Kc:触媒定数(L2/g・mol・h)、
C:反応系の触媒濃度(mol/L)である。
Kc/mc=k1w (4)
一方、第3級アミン化合物の泡化反応定数(k2w)は、上記した樹脂化反応と同様の条件でトルエンジイソシアネートと水をベンゼン溶媒中で反応させることにより、上記と同様にして求める。
Kc/mc=k2w (5)
上記した触媒組成物において用いられる第3級アミン化合物は、文献既知の方法にて容易に製造できる。例えば、ジオールとジアミンとの反応やアルコールのアミノ化による方法、モノアミノアルコール又はジアミンの還元メチル化による方法、アミン化合物とアルキレンオキサイドとの反応による方法等が挙げられる。
本発明のポリウレタン樹脂の製造方法は、ポリオールとイソシアネートを、上記した本発明の触媒組成物、及び必要に応じて発泡剤、界面活性剤、難燃剤、架橋剤等の存在下に反応させることを特徴とする。
上記したポリウレタン樹脂の製造方法において、本発明の触媒組成物の使用量は、使用されるポリオール100重量部に対し、通常0.01~30重量部の範囲であるが、好ましくは0.1~20重量部の範囲である。0.01重量部より少ないと触媒の効果が得られない場合がある。一方、30重量部を超えると、触媒を増やした効果が得られないばかりでなく、ポリウレタン樹脂の物性が悪化する場合がある。
低沸点炭化水素としては、通常、沸点が通常-30~70℃の炭化水素が使用され、その具体例としては、プロパン、ブタン、ペンタン、シクロペンタン、ヘキサン及びこれらの混合物が挙げられる。
上記したポリウレタン樹脂の製造方法において、上記原料を混合した混合液を急激に混合し、攪拌した後、適当な容器又はモールドに注入して発泡成型することにより行われる。混合、攪拌は一般的な攪拌機や専用のポリウレタン発泡機を使用して実施すれば良い。ポリウレタン発泡機としては高圧、低圧及びスプレー式の機器が使用できる。
本発明のポリウレタン樹脂の製造方法は、自動車内装材として用いられる軟質ポリウレタンフォームのカーシート、半硬質ポリウレタンフォームのインスツルメントパネルやハンドル及び硬質ポリウレタンフォームにて製造される断熱材の製造に特に好適に使用される。
軟質ウレタンフォームの物性としては、特に限定するものではないが、一般的には、密度が10~100kg/m3、圧縮強度(ILD25%)が200~8000kPa、伸び率が80~500%の範囲である。ここで、ILD(Indentation Load Deflection)25%とは、試料であるウレタンフォームに対し、より硬い物体(例えば、半径10cmの金属製円盤)を試料厚みに対し25%押し込んだ際の抵抗をもって測定される。
また、使用するポリオール、イソシアネート原料も軟質ポリウレタンフォームと同様であるため、半硬質ポリウレタンフォームは、一般に軟質ポリウレタンフォームに分類される。
半硬質ウレタンフォームの物性は、特に限定するものではないが、一般的には、密度が40~800kg/m3、圧縮強度(ILD25%)が10~200kPa、伸び率が40~200%の範囲である。
本発明において、軟質ポリウレタンフォームは、使用する原料及びフォーム物性から半硬質ポリウレタンフォームを含む場合がある。
硬質ウレタンフォームの物性は、特に限定するものではないが、一般的には、密度が10~100kg/m3、圧縮強度が50~1000kPaの範囲である。
200mlの三口フラスコに、ピペラジン86.1g(1.0モル)、及び溶媒としてメタノール100mlを仕込み、窒素雰囲気下でグリシドール22.2g(0.3モル)を4時間かけて滴下した。三口フラスコをオイルバス中に保持し、反応液の温度は60℃に保った。グリシドールの滴下終了後、単蒸留により反応液中の溶媒であるメタノール、及び未反応のピペラジンを留去した。生成物を真空乾燥し、白色粘調固体45.2gを得た。この物質は、上記式(3a)で示されるジヒドロキシプロピルピペラジン(以下、DHPP-3aと称する。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
ピペラジン86.1g(1.0モル)、グリセリン92.1g(1.0モル)、触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0g、及び溶媒として水600mlを1000mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPa(ゲージ圧、以下同様である。)であった。反応時間は2時間であった。反応終了後、蒸留により反応液中の溶媒である水、未反応のピペラジン、グリセリン、及び副生物を留去した後、目的物(白色粘調固体16.4g)を得た。この物質は、DHPP-3aであることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
ピペラジン86.1g(1.0モル)、クロロプロパンジオール55.3g(0.5モル)、及び溶媒としてメタノール200mlを500mlの三口フラスコに仕込み、窒素雰囲気下で60℃に加熱した。この時の反応容器圧力は大気圧であった。反応時間は16時間であった。反応終了後、濃度5mol/Lの水酸化ナトリウム水溶液(100ml)を添加することで反応液を分層した後、1-ブタノールで有機層に含まれる生成物を抽出した。蒸留により反応液中の溶媒である水、未反応のピペラジン、及び副生物等を留去した後、目的物(白色粘調固体56.1g)を得た。この物質は、DHPP-3aであることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
ピペラジン86.1g(1.0モル)、ジヒドロキシアセトン90.1g(1.0モル)、触媒としてラネーニッケル10g(乾燥重量5.0g)、及び溶媒としてエタノール100mlを1000mlオートクレーブに充填し、水素雰囲気下で90℃に加熱した。この時の反応容器圧力は11.0MPaであった。反応時間は3時間であった。反応終了後、単蒸留により反応液中の溶媒であるエタノール、未反応のピペラジン等を留去した後、褐色透明液体105.7gを得た。この物質は、上記式(3b)で示されるジヒドロキシプロピルピペラジン(以下、DHPP-3bと称する。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
2000mlの三口ナスフラスコに、ピペラジン86.1g(1.0モル)、ブロモマロン酸ジエチル119.5g(0.5モル)、及び溶媒としてアセトニトリル800mlを仕込み、80℃に加熱して反応させた。反応容器圧力は大気圧、反応時間は24時間であった。反応液をろ過、エバポレータを用いて溶媒を留去した後に、シリカゲルカラムを用いて精製し、淡黄色透明の中間体生成物85.5gを得た。この物質は、ピペラジンのモノアルキルエステル体(すなわち、2-(ピペラジン-1-イル)マロン酸ジエチル)であることが、核磁気共鳴分析によって確認された。この中間体生成物85.5g(0.35モル)を、脱水したテトラヒドロフラン溶媒中で、水素化リチウムアルミニウム(0.70モル)を用いて還元した後、反応液をろ過、エバポレーターを用いて溶媒を留去した後、残渣を真空乾燥し、褐色透明液体39.5gを得た。この物質は、DHPP-3bであることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
調製例1で得られたDHPP-3a 16.0g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3aの転化率は59%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが85%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが13%であった。
調製例1で得られたDHPP-3aに代えて、調製例2で得られたDHPP-3aを用いた以外は実施例1と同様にして、反応を実施した。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3aの転化率は60%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが84%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが14%であった。
調製例1で得られたDHPP-3aに代えて、調製例3で得られたDHPP-3aを用いた以外は実施例1と同様にして、反応を実施した。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3aの転化率は61%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが85%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが14%であった。
調製例1で得られたDHPP-3a 16.0g(0.10モル)、溶媒として水100ml、及び触媒としてフェニルホスホン酸(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3aの転化率は67%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが76%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが24%であった。
調製例1で得られたDHPP-3a 16.0g(0.10モル)、及び溶媒として水100mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素パージ後、280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、DHPP-3aの転化率は0%であった。
調製例1で得られたDHPP-3a 16.0g(0.10モル)、溶媒として水100ml、及びラネーニッケル触媒10.0g(乾燥重量5.0g)を200mlオートクレーブに充填し、窒素パージ後、水素加圧した状態で150℃に加熱した。この時の反応容器圧力は10.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、DHPP-3aの転化率は0%であった。
調製例4で得られたDHPP-3b 16.0g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3bの転化率は84%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが90%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが5%であった。
調製例5で得られたDHPP-3b 16.0g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3bの転化率は85%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが91%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが4%であった。
調製例4で得られたDHPP-3b 16.0g(0.10モル)、溶媒として水100ml、及び触媒としてフェニルホスホン酸(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPP-3bの転化率は75%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが73%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが21%であった。
調製例4で得られたDHPP-3b 16.0g(0.10モル)、及び溶媒として水100mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素パージ後、280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、DHPP-3bの転化率は0%であった。
調製例4で得られたDHPP-3b 16.0g(0.10モル)、溶媒として水100ml、及びラネーニッケル触媒10.0g(乾燥重量5.0g)を200mlオートクレーブに充填し、窒素パージ後、水素加圧した状態で150℃に加熱した。この時の反応容器圧力は10.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、DHPP-3bの転化率は0%であった。
200mlの三口フラスコに、エチレンジアミン120.2g(2.0モル)、及び溶媒としてメタノール100mlを仕込み、窒素雰囲気下でグリシドール44.4g(0.6モル)を4時間かけて滴下した。三口フラスコをオイルバス中に保持し、反応液の温度を60℃に保った。グリシドールの滴下終了後、単蒸留により反応液中の溶媒であるメタノール、及び未反応のエチレンジアミンを留去した。さらに、生成物を真空乾燥し、黄白色固体72.2gを得た。この物質は、上記式(9a)で示される2,3-ジヒドロキシプロピルエチレンジアミン(以下、2,3-DHPEDAと略す。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
調製例7(ジヒドロキシプロピルエチレンジアミンの合成).
エチレンジアミン480.8g(8.0モル)、ジヒドロキシアセトン90.1g(1.0モル)、触媒としてラネーニッケル30g(乾燥重量15.0g)、及び溶媒としてエタノール200mlを1000mlオートクレーブに充填し、水素雰囲気下で90℃に加熱した。この時の反応容器圧力は11.0MPaであった。反応時間は3時間であった。反応終了後、単蒸留により反応液中の溶媒であるエタノール、未反応のエチレンジアミン等を留去した後、黄白色固体80.7gを得た。この物質は、上記式(9b)で示される1,3-ジヒドロキシプロピルエチレンジアミン(以下、1,3-DHPEDAと略す。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
調製例6で得られた2,3-DHPEDA 13.4g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDA転化率は80%であり、生成物の選択率は、ヒドロキシメチルピペラジンが70%、ヒドロキシメチル基が脱離して生成したピペラジンが12%、エチレンジアミンが15%であった。
調製例6で得られた2,3-DHPEDA 13.4g(0.10モル)、溶媒として水100ml、及び触媒としてフェニルホスホン酸(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、DHPEDA転化率は65%であり、生成物の選択率は、ヒドロキシメチルピペラジンが56%、ヒドロキシメチル基が脱離して生成したピペラジンが14%、エチレンジアミンが27%であった。
調製例7で得られた1,3-DHPEDA 13.4g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、1,3-DHPEDA転化率は80%であり、生成物の選択率は、ヒドロキシメチルピペラジンが70%、ヒドロキシメチル基が脱離して生成したピペラジンが12%、エチレンジアミンが15%であった。
内径60mmの石英ガラス管中央部に、実施例8で用いたものと同様のリン酸アルミニウム(和光純薬工業社製、化学用)20ml、その上下部に外径3mmのラッシヒリング(Raschig Ring)充填剤を詰めた。リン酸アルミニウム層及びラッシヒリング層の温度は300℃に保ち、上部より、調製例6で得られた2,3-ジヒドロキシプロピルエチレンジアミン(2,3-DHPEDA)の水溶液[ジヒドロキシプロピルエチレンジアミン:水=13:87重量比]を、GHSV=1500h-1の速度(GHSVとは、Gas Hourly Space Velocityのことである。)で滴下した。得られた反応液をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は85%であり、生成物の選択率は、ヒドロキシメチルピペラジンが76%、ヒドロキシメチル基が脱離して生成したピペラジンが9%、エチレンジアミンが12%であった。
調製例6で得られた2,3-DHPEDA13.4g(0.10モル)、及び溶媒として水100mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素パージ後、280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、2,3-DHPEDAの転化率は0%であった。
調製例7で得られた1,3-DHPEDA13.4g(0.10モル)、及び溶媒として水100mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素パージ後、280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、1,3-DHPEDAの転化率は0%であった。
調製例7で得られた1,3-DHPEDA13.4g(0.10モル)、溶媒としてエタノール100ml、及びラネーニッケル触媒10.0g(乾燥重量5.0g)を200mlオートクレーブに充填し、窒素パージ後、水素加圧した状態で150℃に加熱した。この時の反応容器圧力は15.0MPaであった。反応時間は3時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、1,3-DHPEDA転化率は24%であり、生成物の選択率は、ヒドロキシメチルピペラジンが40%、ヒドロキシメチル基が脱離して生成したピペラジンが23%、エチレンジアミンが37%であった。
10Lオートクレーブに、エチレンジアミン1202g(20モル)、及び溶媒としてメタノール1000mlを仕込み、窒素雰囲気下でクロロプロパンジオール663g(6モル)を2時間かけて滴下した。オートクレーブを加熱し、反応液温度を、100℃に調整した。この時の反応容器圧力は0.5MPaであった。クロロプロパンジオールの滴下終了後、熟成時間は4時間であった。この反応液を48%水酸化ナトリウム水溶液(333ml)で中和した後、濾過操作を行った。この操作により得た濾液の低沸分を、エバポレーターにて留去した後、蒸留精製により、微黄色固体833gを得た。この物質は、上記式(9a)で示される2,3-ジヒドロキシプロピルエチレンジアミン(以下、2,3-DHPEDAと略す。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
10Lオートクレーブに、エチレンジアミン1202g(20モル)、及び溶媒としてメタノール1000mlを仕込み、窒素雰囲気下でグリシドール444g(6モル)を4時間かけて滴下した。オートクレーブを加熱し、反応液の温度を60℃に保った。グリシドールの滴下終了後、単蒸留により反応液中の溶媒であるメタノール、及び未反応のエチレンジアミンを留去した。生成物を真空乾燥し、黄白色固体722gを得た。この物質は、上記式(9a)で示される2,3-DHPEDAであることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
調製例8で得られた2,3-DHPEDA 124g(0.92モル)、溶媒として水500ml、及び触媒としてラネー銅(川研ファインケミカル社製、商品名:CDT-60)6.2gを1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は96.2%であり、生成物の選択率はヒドロキシメチルピペラジンが68%であった。
調製例9で得られた2,3-DHPEDA 124g(0.92モル)、溶媒として水500ml、及び触媒としてラネー銅(川研ファインケミカル社製、商品名:CDT-60)6.2gを1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は95.9%であり、生成物の選択率はヒドロキシメチルピペラジが67%であった。
調製例8で得られた2,3-DHPEDA 60g(0.45モル)、溶媒として水540ml、及び触媒としてラネー銅6.0g、(川研ファインケミカル社製、商品名:CDT-60)を1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は99.7%であり、生成物の選択率はヒドロキシメチルピペラジンが70%であった。
調製例8で得られた2,3-DHPEDA 180g(1.50モル)、溶媒として水420ml、及び触媒としてラネー銅7.2g、(川研ファインケミカル社製、商品名:CDT-60)を1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は84.8%であり、生成物の選択率はヒドロキシメチルピペラジンが52%であった。
溶媒として水200ml、及び触媒としてラネー銅20.0g、(川研ファインケミカル社製、商品名:CDT-60)を1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。
次いで、調製例8で得られた2,3-DHPEDA 200g(1.50モル)を水267mlに溶解させたものを定量ポンプでオートクレーブ内に滴下供給した。滴下時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は100%であり、生成物の選択率はヒドロキシメチルピペラジンが61%であった。
調製例8で得られた2,3-DHPEDA 50g(0.37モル)、溶媒として水50ml、及び触媒としてラネーニッケル2.5g、(エボニックデグサジャパン社製、商品名:B111W)を200mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAの転化率は53.1%であり、生成物の選択率はヒドロキシメチルピペラジンが21%であった。
調製例8で得られた2,3-DHPEDA 201g(1.50モル)、溶媒として水201ml、及び触媒として銅クロム触媒10.1g(日揮触媒化成社製、商品名:N203S)を1000mlオートクレーブに充填し、水素雰囲気下で165℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAは、転化率が低すぎる為、副生物と分離できなかった。ヒドロキシメチルピペラジンの収率は5.6%であった。
調製例8で得られた2,3-DHPEDA 200g(1.49モル)、溶媒として水200ml、及び触媒として銅クロム触媒10.0g(日揮触媒化成社製、商品名:N203S)を1000mlオートクレーブに充填し、水素雰囲気下で200℃に加熱した。この時の反応容器圧力は3.5MPaであった。反応時間は4時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、2,3-DHPEDAは、転化率が低すぎる為、副生物と分離できなかった。ヒドロキシメチルピペラジンの収率は5.3%であった。
(1)1-ヒドロキシエチル-3-ヒドロキシメチルピペラジンの合成.
J.Med.Chem,36,2075(1993)に記載の方法によって合成したヒドロキシメチルピペラジン116.2g(1.0モル)、及び溶媒としてメタノール200mlを1000mlオートクレーブに充填し、窒素雰囲気下でエチレンオキサイド44.1g(1.0モル)を滴下した。なお、オートクレーブを氷水浴することで滴下開始時の反応温度は0℃に調整した。この時の反応容器圧力は0.1MPaであった。反応時間は3時間であった。反応終了後、オートクレーブを加温して、60℃で3時間熟成した。その後、単蒸留により反応液中の溶媒であるエタノール、及び未反応の2-ヒドロキシメチルピペラジン等を留去した。生成物を真空乾燥することで、白色固体154.6gを得た。この物質は、上記式(4)で示されるジヒドロキシアルキルピペラジン誘導体に該当する、1-ヒドロキシエチル-3-ヒドロキシメチルピペラジン(以下、HEHMPと略す。)であることが、ガスクロマトグラフィー質量分析及び核磁気共鳴分析によって確認された。
(2)2-ヒドロキシメチルトリエチレンジアミンの合成.
上述のHEHMP16.0g(0.10モル)、溶媒として水100ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、HEHMPの転化率は98%であり、生成物の選択率は、2-ヒドロキシメチルトリエチレンジアミンが92%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンは1%以下であった。
実施例19の(1)で得られたHEHMP16.0g(0.10モル)、溶媒として水100ml、及び触媒としてフェニルホスホン酸(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した。その結果、HEHMPの転化率は88%であり、生成物の選択率は、ヒドロキシメチルトリエチレンジアミンが85%,ヒドロキシメチル基が脱離して生成したトリエチレンジアミンが5%であった。
実施例19の(1)で得られたHEHMP16.0g(0.10モル)、及び溶媒として水100mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素パージ後、280℃に加熱した。この時の反応容器圧力は8.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、HEHMPの転化率は0%であった。
実施例19の(1)で得られたHEHMP16.0g(0.10モル)、溶媒として水100ml、及びラネーニッケル触媒10.0g(乾燥重量5.0g)を200mlオートクレーブに充填し、窒素パージ後、水素加圧した状態で150℃に加熱した。この時の反応容器圧力は10.0MPaであった。反応時間は2時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、HEHMP転化率は0%であった。
次に、本発明の第二のヒドロキシアルキルトリエチレンジアミン類の製造方法を以下の実施例により更に詳細に説明するが、本発明はこれらに限定して解釈されるものではない。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒としてフェニルホスホン酸(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は41%であり、ヒドロキシメチルトリエチレンジアミンの収率は10%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は53%であり、ヒドロキシメチルトリエチレンジアミンの収率は12%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒としてシリカ-アルミナ(日揮化学社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は38%であり、ヒドロキシメチルトリエチレンジアミンの収率は10%であった。
ピペラジン15.5g(0.18モル)、グリセリン82.9(0.90モル)、溶媒として水135ml、及び触媒としてリン酸アルミニウム(和光純薬工業社製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は89%であり、ヒドロキシメチルトリエチレンジアミンの収率は8%であった。
ピペラジン77.5g(0.90モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒としてリン酸アルミニウム(和光純薬工業製、化学用)5.0gを200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は11%であり、選択率は、ヒドロキシメチルトリエチレンジアミンが2%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、及び溶媒として水135mlを、触媒を添加せずに、200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は0%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒としてラネーニッケル(デグサ社製、B111W)12.5gを、200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は0%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒として酸化チタン(IV)(和光純薬工業社製、化学用)5.0gを、200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は0%であった。
ピペラジン15.5g(0.18モル)、グリセリン16.6(0.18モル)、溶媒として水135ml、及び触媒として酸化銅(II)(和光純薬工業社製、化学用)5.0gを、200mlオートクレーブに充填し、窒素雰囲気下で280℃に加熱した。この時の反応容器圧力は6.0MPaであった。反応時間は12時間であった。
反応生成物をガスクロマトグラフィーで分析した結果、ピペラジンの転化率は0%であった。
上記比較例11~比較例14から明らかなように、本発明の酸触媒を使用しない場合には、ヒドロキシメチルトリエチレンジアミンが得られなかった。
特許文献1に記載の方法に準じて、ヒドロキシメチルトリエチレンジアミンの調製を行った。
2Lのセパラブルフラスコにピペラジン43.1g(0.5mol)、及びトリエチルアミン151.8g(1.5mol)を仕込み、トルエン(1000ml)で希釈した。窒素置換後、これにトルエン(500ml)で希釈した2,3-ジブロモプロピオン酸エチル130.0g(東京化成工業社製)を攪拌しながら添加し、100℃で24時間熟成反応を行った。
反応終了後、析出したトリエチルアミンの塩酸塩をろ過により除去し、得られた反応液を濃縮し、トリエチレンジアミンのエステル体(83.7g)を得た。
このトリエチレンジアミンのエステル体をテトロヒドロフランに溶解させ、氷浴下、水素化アルミニウムリチウム(17.1g)のテトロヒドロフラン溶液に攪拌しながら添加した。
室温で2時間反応後、水(17ml)、及び15質量%水酸化ナトリウム水溶液(17ml)を加えて反応を停止し、不溶物をろ過により除去した。
反応液を濃縮後、生成物である2-ヒドロキシアルキルトリエチレンジアミンを酢酸エチルで抽出洗浄した。酢酸エチルを除去し、2-ヒドロキシメチルトリエチレンジアミンを48g得た(収率68%)。
上記比較例15から明らかなように、特許文献1に記載の方法は多段階の反応が必要なため極めて煩雑であった。
次に本発明のヒドロキシアルキルトリエチレンジアミン類を含むポリウレタン樹脂製造用の触媒組成物、及びそれを用いたポリウレタン樹脂の製造方法を以下の実施例により更に詳細に説明するが、本発明はこれらに限定して解釈されるものではない。
ポリオール、セルオープナー、架橋剤、整泡剤、及び水を表1に示した原料配合比にてプレミックスAを調合した。プレミックスA148.1gを500mlポリエチレンカップに取り、触媒として2-ヒドロキシメチルトリエチレンジアミン及びN,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテルを表2に示した配合比(gで表示)にて添加し、20℃に温度調整した。別容器で20℃に温度調整したイソシアネート液を、イソシアネートインデックス[=イソシアネート基/OH基(モル比)×100]が100となる量を、プレミックスAのカップの中に入れ、素早く攪拌機にて6000rpmで5秒間攪拌した。混合攪拌した混合液を60℃に温度調節した2リットルのポリエチレンカップに移し、発泡中の反応性を測定した。また、得られた成型フォームから、フォーム密度を測定し比較した。結果を表2に示す。
表2中の各測定項目の測定方法は以下のとおりである。
(1)反応性の測定項目.
クリームタイム:発泡開始時間、フォームが上昇開始する時間を目視にて測定した。
ゲルタイム:反応が進行し液状物質より、樹脂状物質に変わる時間を測定した。
ライズタイム:フォームの上昇が停止する時間を目視にて測定した。
(2)フォームコア密度.
モールド成型フォームの中心部を7cm×7cm×5cmの寸法にカットし、寸法、重量を正確に測定してコア密度を算出した。
(3)フォームの臭気.
フォームコア密度を測定したフォームから5cm×5cm×5cmの寸法のフォームをカットし、マヨネーズ瓶の中に入れ蓋をした。この瓶を80℃で1時間加熱後、瓶を室温まで冷却し、10人のモニターにそのフォームの臭いを嗅がせ、臭いの強さを測定した。
◎:殆ど臭い無し、 ○:わずかにあり、 △:臭気あり、 ×:強い臭気有り。
N,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテルの代わりに表2に示したアミン化合物を使用した以外は、実施例26と同じ手法を用いてフォームを形成した。結果をあわせて表2に示す。
2-ヒドロキシメチルトリエチレンジアミン及びN,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテルの代わりに、トリエチレンジアミン(東ソー社製、商品名:TEDA-L33)及びビス(ジメチルアミノエチル)エーテル70%ジプロピレングリコール溶液(東ソー社製、商品名:TOYOCAT-ET)を使用した以外は、実施例26と同じ手法を用いてフォームを形成した。結果をあわせて表2に示す。
2-ヒドロキシメチルトリエチレンジアミン及びN,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテルの代わりに、N,N-ジメチルアミノエタノールを使用した以外は、実施例26と同じ手法を用いてフォームを形成した。結果をあわせて表2に示す。
一方、反応型触媒であるN,N-ジメチルアミノエタノールを単独で用いた場合(比較例17)、触媒活性が低く、フォームからアミン触媒の臭気が確認され、アミン触媒に起因する自動車インストルパネルのPVC変色、窓ガラスの曇り現象を防止することができなかった。
参考例1.
窒素置換した200mlの三角フラスコに、ジエチレングリコール(DEG)の濃度が0.15mol/Lになるように調製したDEG含有ベンゼン溶液50mlを採取し、これにN,N,N’,N”,N”-ペンタメチルジエチレントリアミン(東ソー社製、商品名:TOYOCAT-DT)を60.7mg(0.35mmol)加え、A液とした。
次に、窒素置換した100mlの三角フラスコに、2,6-トルエンジイソシアネート(TDI)の濃度が0.15mol/Lになるように調製したTDI含有ベンゼン溶液50mlを採取し、B液とした。
A液及びB液をそれぞれ30℃にて30分間保温後、B液をA液に加えて、攪拌しながら反応を開始した。反応開始後、10分毎に反応液を約10ml採取し、未反応のイソシアナートを過剰のジ-n-ブチルアミン(DBA)溶液と反応させ、残存したDBAを0.2N塩酸エタノール溶液で逆滴定して未反応イソシアナート量を定量した。
触媒として表3に示した第3級アミン化合物を使用した以外は、参考例1と同様にして樹脂化反応速度定数k1wを算出した。結果を表3にあわせて示す。
参考例9.
窒素置換した200mlの三角フラスコに、水の濃度が0.078mol/Lになるように調製した水含有ベンゼン溶液100mlを採取し、これにN,N,N’,N”,N”-ペンタメチルジエチレントリアミン(東ソー社製、商品名:TOYOCAT-DT)を60.7mg(0.35mmol)加え、A液とした。
次に、窒素置換した100mlの三角フラスコに、2,6-トルエンジイソシアネート(TDI)の濃度が0.78mol/Lになるように調製したTDI含有ベンゼン溶液10mlを採取し、B液とした。
A液及びB液をそれぞれ30℃にて30分間保温後、B液をA液に加えて、攪拌しながら反応を開始した。反応開始後、10分毎に反応液を約10ml採取し、未反応のイソシアナートを過剰のジ-n-ブチルアミン(DBA)溶液と反応させ、残存したDBAを0.2N塩酸エタノール溶液で逆滴定して未反応イソシアナート量を定量した。
上記したとおり、反応速度定数k(L/mol・h)を、イソシアネートと水の反応(泡化反応)が各々の濃度に1次であると仮定して求めた。また、各触媒に対応する速度定数Kc(L2/eq・mol・h)を反応速度定数kを触媒濃度で除することで求めた。さらに、Kcを触媒の分子量で除して重量当りの活性能とみなしうるk2w(L2/g・mol・h)を求めた。結果を表3にあわせて示す。
触媒として表3に示した第3級アミン化合物を使用した以外は、参考例9と同様にして泡化反応速度定数k2wを算出した。結果を表3にあわせて示す。
(泡化/樹脂化活性比の算出)
表3の結果から、第3級アミン化合物の泡化/樹脂化活性比(=[樹脂化反応速度定数k1w/泡化反応速度定数k2w])を求めた。その結果を表4にあわせて示す。
ポリオール、セルオープナー、架橋剤、整泡剤、及び水を表5に示した原料配合比にてプレミックスAを調合した。
プレミックスA148.1gを500mlポリエチレンカップに取り、触媒として比較例15で合成した2-ヒドロキシメチルトリエチレンジアミン、及びビス(ジメチルアミノエチル)エーテル70質量%ジプロピレングリコール溶液(東ソー社製、商品名:TOYOCAT-ET)を表6に示した配合比(gで表示)にて添加し、20℃に温度調整した。
別容器で20℃に温度調整したイソシアネート液を、イソシアネートインデックス[=イソシアネート基/OH基(モル比)×100]が100となる量を、プレミックスAのカップの中に入れ、素早く攪拌機にて6000rpmで5秒間攪拌した。
混合攪拌した混合液を60℃に温度調節した2リットルのポリエチレンカップに移し、発泡中の反応性を測定した。また、得られた成型フォームから、フォーム密度を測定し比較した。結果を表6に示す。
なお、表6の(1)反応性の測定項目、(2)フォームコア密度、及び(3)フォームの臭気等の各測定項目の測定方法は、表2における測定方法と同様である。
ビス(ジメチルアミノエチル)エーテルの代わりに表6に示したアミン化合物を使用した以外は、実施例32と同じ手法を用いてフォームを形成した。結果を表6にあわせて示す。
実施例32~実施例43は、本発明の触媒組成物を使用した例であるが、表6から明らかなとおり、いずれも触媒活性が高く、得られたフォームからアミン触媒の臭気はほとんど確認できなかった。
ビス(ジメチルアミノエチル)エーテルの代わりに表7に示したアミン化合物を使用した以外は、実施例32と同じ手法を用いてフォームを形成した。結果をあわせて表7に示す。
触媒として比較例15で合成した2-ヒドロキシメチルトリエチレンジアミンを単独で使用した以外は、実施例32と同じ手法を用いてフォームを形成した。結果をあわせて表7に示す。
2-ヒドロキシメチルトリエチレンジアミンの代わりにトリエチレンジアミン(東ソー社製、商品名:TEDA-L33)を使用した以外は、実施例32と同じ手法を用いてフォームを形成した。結果をあわせて表7に示す。
表7から明らかなとおり、第3級アミン化合物として、[泡化反応速度定数/樹脂化反応速度定数]の値が0.5より小さいものを使用した場合(比較例18、及び比較例19)、触媒の使用部数が多くなり、フォームからアミン触媒の臭気が確認された。このため、アミン触媒に起因する自動車用インストルメントパネルのPVC変色、窓ガラスの曇り現象を防止することができなかった。
また、2-ヒドロキシメチルトリエチレンジアミンを単独で用いた場合(比較例20)、得られたフォームからのアミン触媒の臭気を低減することは可能であったが、クリームタイムが遅く、生産性良くフォームを得ることができなかった。
一方、2-ヒドロキシメチルトリエチレンジアミンを使用せず、ポリウレタン樹脂製造用の触媒として一般に使用されているトリエチレンジアミン33.3質量%ジプロピレングリコール溶液(東ソー社製、TEDA-L33)及びビス(ジメチルアミノエチル)エーテル70質量%ジプロピレングリコール溶液(東ソー社製、商品名:TOYOCAT-ET)を用いた場合(比較例21~比較例23)、フォームからアミン触媒の臭気が確認され、アミン触媒に起因する自動車用インストルメントパネルのPVC変色、窓ガラスの曇り現象を防止することができなかった。
なお、2008年5月30日に出願された日本特許出願2008-142586号、2008年7月9日に出願された日本特許出願2008-178990号、2008年7月16日に出願された日本特許出願2008-185165号、2008年8月7日に出願された日本特許出願2008-204535号、2008年10月29日に出願された日本特許出願2008-278254号、2008年10月31日に出願された日本特許出願2008-281558号、2008年11月20日に出願された日本特許出願2008-296910号、及び2008年11月21日に出願された日本特許出願2008-297912号の明細書、特許請求の範囲、及び要約書の全内容をここに引用し、本発明の明細書の開示として、取り入れるものである。
Claims (26)
- モノ置換ジヒドロキシアルキルピペラジン類及び/又はジ置換ヒドロキシアルキルピペラジン類を、酸触媒の存在下で分子内脱水縮合反応させることを特徴とする、ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミンの製造方法。
- 酸触媒が、金属リン酸塩及び有機リン化合物からなる群より選ばれる一種又は二種以上の化合物を含むことを特徴とする請求項1に記載の製造方法。
- 下記式(6)
[上記式(6)中、R1、及びR2は各々独立して水素原子又は直鎖状若しくは分枝状の炭素数1~4のアルキル基を表す。m、及びnは各々独立して0~2の整数を表す。ただし、m+n<4である。]
で示されるヒドロキシアルキルピペラジン類又はヒドロキシピペラジン類と、下記式(7)
[上記式(7)中、R3、及びR4は各々独立して水素原子又は直鎖状若しくは分枝状の炭素数1~4のアルキル基を表す。]
で示されるアルキレンオキサイド類とを反応させて得られる、下記式(1c)
[上記式(1c)中、R1~R4、m、及びnは上記式(6)、及び式(7)と同じ定義である。]
で示されるジ置換ヒドロキシアルキルピペラジン及び/又は下記式(1d)
[上記式(1d)中、R1~R4、m、及びnは上記式(6)、及び式(7)と同じ定義である。]
で示されるジ置換ヒドロキシアルキルピペラジンを、酸触媒の存在下で分子内脱水縮合反応させ、下記式(2b)
[上記式(2b)中、R1~R4、m、及びnは上記(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類、及び/又は下記式(2c)
[上記式(2c)中、R1~R4、m、及びnは上記(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類を得ることを特徴とする請求項1又は請求項2に記載の製造方法。 - 上記式(7)で示されるアルキレンオキサイド類が、エチレンオキサイド又はプロピレンオキサイドであることを特徴とする請求項9に記載の製造方法。
- 酸触媒が、金属リン酸塩及び有機リン化合物からなる群より選ばれる一種又は二種以上の化合物を含むことを特徴とする請求項11に記載の製造方法。
- ラネー金属触媒が、ラネー銅触媒を含むことを特徴とする請求項11又は請求項12に記載の製造方法。
- 上記式(10)で示されるピペラジン類が、ピペラジン、メチルピペラジン、エチルピペラジン及びジメチルピペラジンからなる群より選ばれる一種又は二種以上のピペラジン類であることを特徴とする請求項14に記載の製造方法。
- 酸触媒が、金属リン酸塩及び有機リン化合物からなる群より選ばれる一種又は二種以上の化合物を含むことを特徴とする請求項14又は請求項15に記載の製造方法。
- ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)又は[泡化反応速度定数/樹脂化反応速度定数]の値が0.5以上の第3級アミン化合物(C)とを含有するポリウレタン樹脂製造用の触媒組成物。
- ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン(A)が、下記式(2a)
[上記式(2a)中、R、及びnは上記式(1a)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン、下記式(2b)
[上記式(2b)中、R1~R4、m、及びnは上記式(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類、及び/又は下記式(2c)
[上記式(2c)中、R1~R4、m、及びnは上記式(6)、及び式(7)と同じ定義である。]
で示されるヒドロキシアルキルトリエチレンジアミン類、並びに下記式(2d)
[上記式(2d)中、R1、及びR2は上記式(10)と同じ定義である。]
で示されるヒドロキシメチルトリエチレンジアミン類からなる群より選ばれる一種又は二種であることを特徴とする請求項17に記載のポリウレタン樹脂製造用の触媒組成物。 - ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)が、下記式(11)
[上記式(11)中、R1~R8は各々独立して、水素原子、ヒドロキシ基、炭素数1~16のアルキル基、炭素数6~16のアリール基、炭素数1~10のヒドロキシアルキル基、炭素数1~10のアミノアルキル基、炭素数1~10のモノメチルアミノアルキル基、又は炭素数1~10のジメチルアミノアルキル基を表し、xは0~11の整数、yは0~11の整数、aは0~10の整数、及びbは0~10の整数、を表す。]
で示されるアミン化合物であることを特徴とする請求項17乃至請求項19のいずれかに記載のポリウレタン樹脂製造用の触媒組成物。 - 上記式(11)で示されるアミン化合物が、N,N-ジメチルエチレンジアミン、N,N’-ジメチルエチレンジアミン、N,N-ジメチルプロピレンジアミン、N,N’-ジメチルプロピレンジアミン、N,N-ジメチルヘキサメチレンジアミン、N,N’-ジメチルヘキサメチレンジアミン、トリメチルジエチレントリアミン、トリメチルエチレンジアミン、トリメチルプロピレンジアミン、トリメチルヘキサメチレンジアミン、テトラメチルジエチレントリアミン、N,N-ジメチルアミノエタノール、N,N-ジメチルアミノイソプロパノール、ビス(3-ジメチルアミノプロピル)アミン、N-メチルピペラジン、N,N-ジメチルアミノエトキシエタノール、N,N,N’-トリメチルアミノエチルエタノールアミン、N,N-ジメチルアミノエチル-N’-メチルアミノエチル-N”-メチルアミノイソプロパノール、N,N-ジメチルアミノエトキシエトキシエタノール、N,N-ジメチル-N’,N’-ビス(2-ヒドロキシプロピル)-1,3-プロパンジアミン、N,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテル、N,N-ビス(3-ジメチルアミノプロピル)-N-イソプロパノールアミン、N,N-ジメチルアミノヘキサノール、及びN,N,N’-トリメチル-N’-(2-ヒドロキシエチル)プロピレンジアミンからなる群より選ばれる一種又は二種以上のアミン化合物であることを特徴とする請求項20に記載のポリウレタン樹脂製造用の触媒組成物。
- ヒドロキシアルキルトリエチレンジアミン類又はヒドロキシトリエチレンジアミン(A)と、ヒドロキシ基、1級アミノ基、及び2級アミノ基からなる群より選ばれる一種又は二種以上の置換基を分子中に有するアミン化合物(B)との混合比率が、[アミン化合物(A)]/[アミン化合物(B)]=1/99~99/1(重量比)であることを特徴とする請求項17乃至請求項21のいずれかに記載のポリウレタン樹脂製造用の触媒組成物。
- [泡化反応速度定数/樹脂化反応速度定数]の値が0.5以上の第3級アミン化合物(C)が、トリエタノールアミン、ビスジメチルアミノエチルエーテル、N,N,N’,N”,N”-ペンタメチルジエチレントリアミン、ヘキサメチルトリエチレンテトラミン、N,N-ジメチルアミノエトキシエタノール、N,N,N’-トリメチルアミノエチルエタノールアミン、N,N-ジメチルアミノエチル-N’-メチルアミノエチル-N”-メチルアミノイソプロパノール及びN,N,N’-トリメチル-N’-(2-ヒドロキシエチル)ビス(2-アミノエチル)エーテルからなる群より選択される1種又は2種以上の化合物であることを特徴とする請求項17乃至請求項19のいずれかに記載のポリウレタン樹脂製造用の触媒組成物。
- ヒドロキシアルキルトリエチレンジアミン又はヒドロキシトリエチレンジアミン(A)と、[泡化反応速度定数/樹脂化反応速度定数]の値が0.5以上の第3級アミン化合物(C)との混合比率が、[アミン化合物(A)]/[第3級アミン化合物(C)]=1/30~30/1(重量比)であることを特徴とする請求項17乃至請求項19、及び請求項23のいずれかに記載のポリウレタン樹脂製造用の触媒組成物。
- ポリオールとポリイソシアネートとを、請求項17乃至請求項24のいずれかに記載の触媒組成物の存在下で反応させることを特徴とするポリウレタン樹脂の製造方法。
- 請求項17乃至請求項24のいずれかに記載の触媒組成物の使用量が、ポリオール100重量部に対して0.01~30重量部の範囲であることを特徴とする請求項25に記載のポリウレタン樹脂の製造方法。