WO2001081489A1 - Materiau protecteur antisalissure, film protecteur antisalissure, structure submergee et procede d'inhibition des salissures - Google Patents
Materiau protecteur antisalissure, film protecteur antisalissure, structure submergee et procede d'inhibition des salissures Download PDFInfo
- Publication number
- WO2001081489A1 WO2001081489A1 PCT/JP2001/003516 JP0103516W WO0181489A1 WO 2001081489 A1 WO2001081489 A1 WO 2001081489A1 JP 0103516 W JP0103516 W JP 0103516W WO 0181489 A1 WO0181489 A1 WO 0181489A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- antifouling
- acrylate
- meth
- polymer
- Prior art date
Description
Claims