JP3701706B2 - 防汚性樹脂組成物及びその製造方法 - Google Patents
防汚性樹脂組成物及びその製造方法 Download PDFInfo
- Publication number
- JP3701706B2 JP3701706B2 JP05490395A JP5490395A JP3701706B2 JP 3701706 B2 JP3701706 B2 JP 3701706B2 JP 05490395 A JP05490395 A JP 05490395A JP 5490395 A JP5490395 A JP 5490395A JP 3701706 B2 JP3701706 B2 JP 3701706B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- molecule
- resin composition
- carboxyl group
- antifouling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【産業上の利用分野】
本発明は、分子内に金属カルボキシレートを有する樹脂を有効成分とする防汚性組成物及びその製造方法に関する。
【0002】
【従来の技術とその課題】
従来、分子内に金属塩構造を有する樹脂は防汚塗料のバインダーとして研究され、実用化されてきた。最も有名なのが錫のカルボキシレートであるが、このものは毒性が問題となったために、最近は銅や亜鉛のカルボキシレートが用いられている。これらの樹脂の共通点は樹脂中にフリーの水酸基が残存していないことであって、下記一般式(B)又は(C)で表わされる。
Rp−COO−M−(R)n (B)
Rp−COO−M−(OCOR)n (C)
(式中、Rpは基体樹脂を、Mは2価の金属原子を、Rは炭化水素基を、nは1〜3の整数をそれぞれ示す。)
水酸基が存在すると合成時にゲル化してしまうので防汚性樹脂組成物として欠陥を生ずるからである。
化合物(B)の合成はコスト高になり、また、(C)の合成は2個以上の水酸基の反応性差が小さいので種々の化合物の混合物になりやすく、精製は非常にコスト高になる。
【0003】
【課題を解決するための手段】
本発明は、
「1. 一般式
Rp −COO−M−OH (A)
(式中、Rp は基体樹脂を、Mは2価の金属原子をそれぞれ示し、−COO−M−OHは、Rpの側鎖または末端に存在する。)
で表わされる分子内に金属カルボキシレートを有する樹脂を有効成分とし、基体樹脂が分子内にカルボキシル基を有し酸価が30〜300である樹脂に由来する防汚性樹脂組成物。
2. 2価の金属原子が銅、亜鉛、カルシウム、マグネシウム、鉄から選んだ1または2以上である、1項に記載された樹脂組成物。
3. 分子内にカルボキシル基を有し酸価が30〜300である樹脂がビニル重合体である、1項または2項に記載された樹脂組成物。
4. 分子内にカルボキシル基を有し酸価が30〜300である樹脂に2価の金属の酸化物あるいは水酸化物を、該樹脂に対して0.5〜5重量%の水の存在下で反応させることを特徴とする一般式
Rp −COO−M−OH (A)
(式中、Rp は基体樹脂を、Mは2価の金属原子をそれぞれ示し、基体樹脂が分子内にカルボキシル基を有する樹脂に由来し、−COO−M−OH は、Rpの側鎖または末端に存在する。)
で表わされる分子内に金属カルボキシレートを有する樹脂を有効成分とする防汚性樹脂組成物の製造方法。
5. 2価の金属原子が銅、亜鉛、カルシウム、マグネシウム、鉄から選んだ1または2以上である、4項に記載された防汚性樹脂組成物の製造方法。
6. 分子内にカルボキシル基を有し酸価が30〜300である樹脂がビニル重合体である、4項または5項に記載された防汚性樹脂組成物の製造方法。」
に関する。
【0004】
【作用】
本発明者等は上記の点に鑑み、金属カルボキシレートを有する安価な防汚性樹脂組成物及びその合成方法について鋭意研究した結果、分子内にカルボキシル基を有する樹脂に2価の金属の酸化物あるいは水酸化物を少量の水の存在下で反応させることによって上記一般式(A)の構造を有する樹脂をゲル化させずに合成できることを見いだし、本発明を完成するに至った。更に、使用する金属原子が2価であるためにイオン結合による3次元化がおきても不思議ではないが、驚くべきことにカルボキシル基1モルに対し、0.1〜1モルの範囲で2価の金属の酸化物あるいは水酸化物と反応させてもゲル化するようなことはなかった。本発明者は少量の水の存在がイオン結合による3次元化を防止していると考えている。
【0005】
水はカルボキシル基1モルに対し0.1モル以下では構造粘性が発現して樹脂が増粘し、1モル以上では過剰の水が分離するため、いずれも良好な結果が得られない。また、カルボキシレートが生成していることは、IRスペクトルによって確認した。
【0006】
かくして、本発明によれば、一般式
Rp−COO−M−OH (A)
(式中、Rpは基体樹脂を、Mは2価の金属原子をそれぞれ示す。)
で表わされる防汚性樹脂組成物及びその合成方法が提供される。
本発明に用いる2価の金属の酸化物あるいは水酸化物としてはどのようなものでも使用可能であるが、コスト、毒性、反応性等の点から銅、亜鉛、カルシウム、マグネシウム、鉄のいずれかの酸化物あるいは水酸化物が好ましい。
【0007】
本発明に用いる分子内にカルボキシル基を有する樹脂としては、ポリエステル、ポリウレタン、天然樹脂、ビニル重合体等どのようなものでも使用可能であるが、組成変動の自由度からビニル重合体が好ましい。また、該樹脂の分子量が低分子量であれば、1分子あたり1個のカルボキシル基を含有していても構わないが、高分子量になると酸価が30〜300範囲内のものが好ましく、カルボキシル基は1分子あたり2個以上必要となる。
【0008】
本発明の樹脂組成物の合成方法としては、分子内にカルボキシル基を有する樹脂に分子内にカルボキシル基を有する樹脂に対して0.5〜5重量%の水と付加させたい2価の金属の酸化物あるいは水酸化物を添加し、50〜200℃の温度で1〜20時間反応させる。系が水の存在によって濁るようである場合、最小限度の極性溶剤を添加する必要がある。極性溶剤としては、例えば、n−ブタノール、イソプロピルアルコール等のアルコール系溶剤;メチルエチルケトン、メチルイソブチルケトン等のケトン系溶剤;酢酸エチル、酢酸ブチル、酢酸イソブチル等のエステル系溶剤;セロソルブ、ブチルセロソルブ、ジエチレングリコール、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル等のエーテル系溶剤などが挙げられる。最初は粉末状の金属化合物が溶解しないが、反応が進むにしたがって系は透明になる。
【0009】
【実施例】
以下、本発明を実施例によりさらに具体的に説明する。
【0010】
実施例1
アクリル酸7.2重量部、メチルメタクリレート50重量部及びエチルアクリレート42.8重量部からなる数平均分子量10,000の共重合体の50重量%酢酸ブチル溶液200gに、酸化亜鉛8g 、ブタノール5g および水1g を添加し、120℃で10時間反応させて固形分49.2重量%の透明な樹脂溶液を得た。IRによると、1630cm−1に亜鉛カルボキシレートの吸収が大きく現れていた。
【0011】
実施例2
アジピン酸/ネオペンチルグリコール/トリメチロールプロパンからなる末端に水酸基を有するポリエステル樹脂100g に無水コハク酸を付加して数平均分子量3,500、酸価56のポリエステル樹脂を得た。この樹脂111gにセロソルブ100g 、水酸化カルシウム2g および水2g を添加し、100℃で10時間反応させて固形分50.0重量%の透明な樹脂溶液を得た。IRによると、1560cm−1にカルシウムカルボキシレートの吸収が大きく現れていた。
【0012】
応用例
実施例1および2によって得られた樹脂溶液をアルミ板に乾燥膜厚が100μになるように夫々塗布して乾燥後、駿河湾の海水中の深さ1mに設置した。1夏経過後に引き上げてみると、フジツボ等の付着は全く観察されなかった。
比較として、実施例1および2の金属化合物と反応する前の樹脂を塗布した板は、樹脂が溶解して消失し、そのあとに直径0.5〜3mmのフジツボが多数付着していた。
また、何も塗布していないアルミ板には直径0.5〜3mmのフジツボが多数付着していた。
【0013】
【発明の効果】
本発明により得られる樹脂は優れた防汚作用があり、防汚塗料に好適に使用できる。
Claims (6)
- 一般式
Rp −COO−M−OH (A)
(式中、Rp は基体樹脂を、Mは2価の金属原子をそれぞれ示し、−COO−M−OHは、Rpの側鎖または末端に存在する。)
で表わされる分子内に金属カルボキシレートを有する樹脂を有効成分とし、基体樹脂が分子内にカルボキシル基を有し酸価が30〜300である樹脂に由来する防汚性樹脂組成物。 - 2価の金属原子が銅、亜鉛、カルシウム、マグネシウム、鉄から選んだ1または2以上である、請求項1に記載された樹脂組成物。
- 分子内にカルボキシル基を有し酸価が30〜300である樹脂がビニル重合体である、請求項1または2に記載された樹脂組成物。
- 分子内にカルボキシル基を有し酸価が30〜300である樹脂に2価の金属の酸化物あるいは水酸化物を、該樹脂に対して0.5〜5重量%の水の存在下で反応させることを特徴とする一般式
Rp −COO−M−OH (A)
(式中、Rp は基体樹脂を、Mは2価の金属原子をそれぞれ示し、基体樹脂が分子内にカルボキシル基を有する樹脂に由来し、−COO−M−OH は、Rpの側鎖または末端に存在する。)
で表わされる分子内に金属カルボキシレートを有する樹脂を有効成分とする防汚性樹脂組成物の製造方法。 - 2価の金属原子が銅、亜鉛、カルシウム、マグネシウム、鉄から選んだ1または2以上である、請求項4に記載された防汚性樹脂組成物の製造方法。
- 分子内にカルボキシル基を有し酸価が30〜300である樹脂がビニル重合体である、請求項4または5に記載された防汚性樹脂組成物の製造方法。