RU2004102045A - Статистический сополимер пропилена и способ его получения - Google Patents
Статистический сополимер пропилена и способ его получения Download PDFInfo
- Publication number
- RU2004102045A RU2004102045A RU2004102045/04A RU2004102045A RU2004102045A RU 2004102045 A RU2004102045 A RU 2004102045A RU 2004102045/04 A RU2004102045/04 A RU 2004102045/04A RU 2004102045 A RU2004102045 A RU 2004102045A RU 2004102045 A RU2004102045 A RU 2004102045A
- Authority
- RU
- Russia
- Prior art keywords
- comonomer
- copolymer
- reactor
- product
- propylene
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
- C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
- C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
- C08F297/083—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins the monomers being ethylene or propylene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F210/04—Monomers containing three or four carbon atoms
- C08F210/06—Propene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F210/16—Copolymers of ethene with alpha-alkenes, e.g. EP rubbers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
- C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
- C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Graft Or Block Polymers (AREA)
- Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
- Polymerisation Methods In General (AREA)
Claims (30)
1. Способ получения статистического сополимера пропилена, включающий полимеризацию пропилена с сомономером, при этом упомянутым сомономером являются этилен или α-олефин, содержащий, по меньшей мере, четыре атома углерода, в присутствии катализатора в многостадийном процессе, включающем полимеризацию пропилена с сомономером в первой зоне реакции, включающей, по меньшей мере, один суспензионный реактор, с получением первого продукта полимеризации, перевод упомянутого первого продукта во вторую зону реакции, включающую, по меньшей мере, один газофазный реактор, и полимеризацию пропилена с сомономером в упомянутом газофазном реакторе в присутствии упомянутого первого продукта полимеризации, где температура в газофазном реакторе, по меньшей мере, на 10°С превышает температуру в суспензионном реакторе.
2. Способ по п.1, где температура в упомянутом газофазном реакторе, по меньшей мере, на 15°С превышает температуру в упомянутом суспензионном реакторе.
3. Способ по п.1 или 2, где содержание сомономера в продукте, полученном в газофазном реакторе, превышает содержание сомономера в продукте, полученном в суспензионном реакторе.
4. Способ по п.3, где содержание сомономера в продукте, полученном в газофазном реакторе, по меньшей мере, на 0,5 мас.%, предпочтительно, по меньшей мере, на 1 мас.% превышает содержание сомономера в продукте, полученном в суспензионном реакторе.
5. Способ по п.1, где упомянутым сомономером является этилен.
6. Способ по п.5, где содержание этилена в продукте, полученном в суспензионном реакторе, находится в диапазоне от 2 до 6 мас.%, предпочтительно от 2 до 4 мас.%.
7. Способ по п.5 или 6, где содержание этилена в продукте, полученном в газофазном реакторе, находится в диапазоне от 3 до 12% (мас.), предпочтительно от 4 до 10 мас.%.
8. Способ по п.1, где суспензионным реактором является реактор для проведения реакции в массе, предпочтительно петлевой реактор для проведения реакции в массе.
9. Способ по п.1, где температура в суспензионном реакторе равна 70°С или более.
10. Способ по п.1, где температура в газофазном реакторе равна 80°С или более, предпочтительно 85°С или более.
11. Способ по п.1, где распределение продуктов между суспензионным реактором и газофазным реактором находится в диапазоне от 30:70 до 70:30, предпочтительно от 40:60 до 60:40, а в особенности от 45:55 до 55:45.
12. Способ по п.1, где катализатором является каталитическая система, относящаяся по типу к катализаторам Циглера-Натта, содержащая компонент катализатора, компонент сокатализатора и внешний донор электронов.
13. Статистический сополимер пропилена, получаемый по способу по пп.1-12.
14. Статистический сополимер пропилена, полученный в результате сополимеризации пропилена с сомономером, при этом сомономером являются этилен или α-олефин, содержащий, по меньшей мере, четыре атома углерода, где распределение сомономера, определенное в соответствии со способом TREF, является мультимодальным, предпочтительно бимодальным; и где количество компонентов упомянутого сополимера, элюированных при температурах вплоть до 90°С, при определении в соответствии со способом TREF, меньше 50 мас.% от полного количества сополимера.
15. Статистический сополимер пропилена по п.14, отличающийся интервалом элюирования, определенным в соответствии со способом TREF, равным 50°С или более.
16. Статистический сополимер пропилена, полученный в результате сополимеризации пропилена с сомономером, при этом сомономером являются этилен или α-олефин, содержащий, по меньшей мере, четыре атома углерода, где сополимер отличается интервалом элюирования, определенным в соответствии со способом TREF, равным 50°С или более, и где количество компонентов упомянутого сополимера, элюированных при температурах вплоть до 90°С, при определении в соответствии со способом TREF, меньше 50 мас.% от полного количества сополимера.
17. Статистический сополимер пропилена по пп.14-16, отличающийся температурой плавления Tm, равной 135°С или более.
18. Статистический сополимер пропилена по пп.14-16, отличающийся уровнем содержания этилена, равным 6 мас.% или менее.
19. Статистический сополимер пропилена, получаемый в результате сополимеризации пропилена с сомономером, при этом сомономером являются этилен или α-олефин, содержащий, по меньшей мере, четыре атома углерода, где статистическим сополимером является унимодальный полимер, а интервал элюирования, определенный по способу TREF, получают в соответствии с уравнением
Y ≤ 4,5·m + 16,
где Y представляет собой интервал элюирования, °C;
m представляет собой процентное содержание этилена в сополимере, мас.%.
20. Статистический сополимер пропилена по пп.14-16, где сомономером является этилен.
21. Статистический сополимер пропилена по п.1, где полное содержание этилена равно 3 мас.% или более, предпочтительно 5 мас.% или более.
22. Статистический сополимер пропилена по п.20, где полное содержание этилена равно 12 мас.% или менее, предпочтительно 8 мас.% или менее.
23. Статистический сополимер пропилена по пп.13-16, где уровень содержания фракций, растворимых в ксилоле, находится в диапазоне от 4 до 24 мас.%, более предпочтительно от 5 до 15 мас.%, а еще более предпочтительно от 6 до 10 мас.%.
24. Изделие, выполненное из сополимера по любому из пп.13-23.
25. Изделие по п.24, имеющее форму пленки.
26. Изделие по п.24, которое получают по способу формования с раздувом.
27. Изделие по п.24, которое получают по способу литья под давлением.
28. Изделие по п.24, имеющее форму волокна.
29. Изделие по п.24, имеющее форму трубы.
30. Применение сополимера по любому из пп.13-23 для получения пленки, изделия, полученного по способам формования с раздувом или литья под давлением, волокна или трубы.