KR20100015351A - 폴리아민-폴리아크릴레이트 분산제 - Google Patents
폴리아민-폴리아크릴레이트 분산제 Download PDFInfo
- Publication number
- KR20100015351A KR20100015351A KR1020097020662A KR20097020662A KR20100015351A KR 20100015351 A KR20100015351 A KR 20100015351A KR 1020097020662 A KR1020097020662 A KR 1020097020662A KR 20097020662 A KR20097020662 A KR 20097020662A KR 20100015351 A KR20100015351 A KR 20100015351A
- Authority
- KR
- South Korea
- Prior art keywords
- polyamine
- acrylate
- polyacrylate
- grafted copolymer
- mol
- Prior art date
Abstract
본 발명은, 폴리아민-그래프트-폴리아크릴레이트 블렌드 기재의 액체 분산제, 그의 제조 및 그의 용제형 시스템에서의 용도, 특히 50 000 g/mol 내지 150 000 g/mol의 평균 분자량을 갖고, 다분산도 (Mw/Mn)가 3 초과인, 하기 화학식 1 또는 화학식 1과 Y의 혼합물의 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드에 관한 것이다.
<화학식 1>
T-(A1,A2)-Y
상기 식에서, T는 폴리아민 또는 폴리이민이고, A1은 아미드 또는 이미드로부터 선택된 브릿징 결합이며, A2는 -N-C- 브릿징 결합이고, Y는 하기 화학식 2의 아크릴레이트 잔기이며,
<화학식 2>
상기 식에서,
R1 및 R2는 독립적으로 수소 또는 C1-20알킬, 아릴, 헤테로아릴, 치환된 아릴이고, n은 1 내지 1000의 수이다.
폴리아민-폴리아크릴레이트 블렌드, 액체 분산제
Description
본 발명은, 폴리아민-그래프트(graft)-폴리아크릴레이트 블렌드 기재의 액체 분산제, 그의 제조 및 그의 용제형 시스템에서의 용도에 관한 것이다.
폴리에틸렌이민-폴리메틸메타크릴레이트는 US 6573313으로부터 공지되어 있으며, 상기 문헌에는, 폴리아민의 질소 원자 상에 이후 아크릴레이트의 라디칼 중합을 개시할 수 있는 라디칼을 생성시키는 것을 포함하는 에멀젼 라디칼 중합 방법에 의해 얻어지는 코어 쉘(core shell) 라텍스의 제조가 기재되어 있다. 생성물은 유전자 전달 담체로서 사용될 것으로 고려된다.
분산제로서 사용되는 그래프팅된 공중합체는, 예를 들어 폴리아민-g-폴리에스테르 또는 폴리아민-g-폴리에테르이다. 공개특허 WO 00/024503, WO 04/078333, WO 99/049963, WO 94/021368은, 산성 기와 아민 기 사이의 중화 및 아미드화 반응 둘 다를 통해 PAI 상에 그래프팅된, 히드록시카르복실산의 축중합으로부터 얻어지는, 그래프트 사슬이 1개의 산성 기로 말단-캡핑된 일련의 PAI-기재의 분산제에 관한 것이다. 그래프트 사슬은 비극성이다. 분산제는 주로 비극성 용제형 도료 시스템에 사용된다.
공개특허 WO 01/080987, WO 98/019784, US 9599947, EP 0208041 및 WO 99/055763, US 6583213은, 그래프트 사슬이 락톤 및/또는 그의 유도체의 개환 중합으로부터 얻어지는 일련의 PAI-기재의 분산제를 청구한다. 그래프트 사슬은, 산성 기와 아민 기 사이의 중화 및 아미드화 반응 둘 다를 통해 PAI 상에 그래프팅된, 락톤 또는 알킬 치환된 락톤의 카르복실산 개시된 개환 중합에 의해 얻어지는, 1개의 산성 기로 말단-캡핑된 폴리에스테르이거나; 또는 그래프트 사슬은, 마이클(Michael) 부가반응에 의해 PEI 상에 그래프팅된, 락톤의 2-히드록시 에틸 아크릴레이트 개시된 개환 중합에 의해 얻어지는, 1개의 에틸렌계 불포화 기로 말단-캡핑된 폴리에스테르이다.
WO 05/010109는 일종의 PAI-기재의 폴리에테르 액체 분산제를 청구한다. 그래프팅 사슬은, 숙신산 무수물 및 CH3-(EO)m-(PO)n-NH2의 에스테르화에 의해 얻어지는, 1개의 산성 기로 말단-캡핑된 폴리에테르이다. 이 폴리에테르 사슬은 중화 및 아미드화 반응 둘 다를 통해 PAI 상에 그래프팅된다. 분산제는 극성 유기 또는 수성 도료 시스템에 적용된다.
통상적으로, 청구된 PAI-g-폴리에스테르 및 PAI-g-폴리에테르의 그래프트 사슬은 높은 Tg 및 결정성을 가지며, 이는 이들의 용도를 한정하는데, 예를 들어 저온 적용이 불가능하고, 저장 안정성이 양호하지 못한 것 등이다. 그 외에, 이들 분산제는 모두 "에 그래프팅" 접근법 (즉, 먼저, 그래프트 측쇄를 합성하고, 이어서 이들을 PAI 주쇄 상에 그래프팅함)에 의해 제조되고, 따라서 제조를 위해 적어도 2단계 또는 다단계가 필요하다.
US 2002/143081에는 코어 및 쉘을 포함하는 친양쪽성 나노입자가 개시되어 있다. 입자의 제조 방법은 폴리에틸렌이민에 대한 비닐 단량체의 수성 시스템에서의 그래프트 중합을 포함한다. 그래프트 공중합체 및 폴리메틸메타크릴레이트 단독중합체의 분자량은 500 000 내지 1000 000의 범위이다. 중합된 비닐 단량체의 다분산도 (Mw/Mn)는 1.5 내지 3의 범위이다. 코어 쉘 입자는, 예를 들어 약물 담체로서 사용된다. 중합체는 가죽 마감처리, 도료 종이 및 직물 산업재에 적용될 수 있다고만 언급되었다. 분산제로서의 용도는 구체적으로 개시되어 있지 않다.
본 발명의 일면은, 용제형 시스템에서 저온 용도 및 저점도 용도를 위해 사용될 수 있는 우수한 저장 안정성을 갖는 액체 분산제를 제공하는 것이다.
따라서, 본 발명은, 50 000 g/mol 내지 150 000 g/mol의 평균 분자량을 갖고, 다분산도 (Mw/Mn)가 3 초과인, 하기 화학식 1 또는 화학식 1과 Y의 혼합물의 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드에 관한 것이다.
상기 식에서,
T는 폴리아민 또는 폴리이민이고,
A1은 아미드 (
) 또는 이미드 (
)로부터 선택된 브릿징 결합이며,
A2는 -N-C- 브릿징 결합이고,
Y는 하기 화학식 2의 아크릴레이트 잔기이며,
상기 식에서,
R1 및 R2는 독립적으로 수소 또는 C1-20알킬, 아릴, 헤테로아릴, 치환된 아릴이고,
n은 1 내지 1000의 수이다.
정의
본원에서 사용된 용어 "그래프팅된 공중합체"는, 소위 "으로부터 그래프팅" 방법에 의해 제조된 공중합체를 지칭한다. 아크릴레이트 기는 폴리아민 주쇄를 따라 펜던트(pendent) 기로서 부착된다. 측쇄는 폴리아민 주쇄에 그래프팅된 후 구성된다.
액체는 결정화되지 않는 것을 의미한다.
용어 "폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드"는, 자유 라디칼 중합 (A2 = NC), 마이클 부가반응 (A2 = N-C) 및 에스테르교환반응 (A1 = 아미드 또는 이미드)에 의해 수득가능한 하나 초과의 공중합체가 존재하는 것을 의미한다.
용어 "폴리아민"은 분자 당 2개 이상의 1급 또는 2급 아민 기를 포함하는 화합물을 의미한다. 폴리아민은 MW가 100 내지 100,000 g/mol, 바람직하게는 500 내지 50,000 g/mol인 폴리(C2-6-알킬렌이민), 폴리비닐아민, 폴리알릴아민 또는 폴리(아미드-아민) 덴드리머로부터 선택된다.
폴리(C2-6-알킬렌이민)은, 예를 들어 폴리프로필렌-이민 또는 폴리에틸렌 이민, 바람직하게는 폴리에틸렌이민이다.
n은 바람직하게는 5 내지 100이다. 폴리아크릴레이트 사슬 (n > 1)은 1종의 아크릴레이트 단량체의 단독중합으로부터, 또는 2종 이상의 상이한 아크릴레이트 단량체의 랜덤 공중합으로부터 수득가능하다.
R1은 바람직하게는 수소 또는 메틸이다.
R2는 바람직하게는 수소, 또는 선형 또는 분지형 사슬을 포함한 1개 내지 20개의 탄소 원자를 갖는 알킬 사슬이다. 그 예로는, 메틸, 에틸, 프로필, 이소프로필, n-부틸, sec-부틸, tert-부틸, n-헥실, 2-히드록시 에틸, 2-메톡시 에틸, 2-에톡시 에틸, 보르닐, 이소보르닐, 이소데실, 라우릴, 미리스틸, 스테아릴, 시클로헥실이 있다.
아릴은 바람직하게는 페닐, 나프틸이다.
치환된 아릴은 바람직하게는, 메틸, 에틸, 프로필, 이소프로필, n-부틸, sec-부틸, tert-부틸, n-헥실, 클로로의 치환체를 갖는 치환된 페닐 및 치환된 나프틸이다.
헤테로아릴은 바람직하게는 보르닐, 이소보르닐, 푸르푸릴이다.
T가 폴리에틸렌이민이고, R1이 수소 또는 메틸이며, R2가 C1-20알킬이고, n이 5 내지 100인, 제1항에 따른 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드가 바람직하다.
방법
본 발명의 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드는,
1. 폴리아민 대 아크릴레이트 단량체의 중량비가 1:5 내지 1:100의 범위이고;
2. 자유 라디칼 개시제 대 아크릴레이트 단량체의 중량비가 1:5 내지 1:100의 범위이며;
3. 공정을 불활성 기체 분위기 하에 10℃ 내지 200℃의 온도에서 1-반응기(one pot)에서 수행하고;
4. 공정이 적어도 아크릴레이트와 폴리아민의 에스테르교환반응으로부터 폴리아민 아미드 또는 폴리아민 이미드를 얻는 것, 폴리아민과 아크릴레이트 단량체의 마이클 부가반응으로부터 폴리아민 아크릴레이트를 얻는 것, 및 폴리아민과 아크릴레이트 단량체의 그래프트 중합으로부터 폴리아민-g-폴리아크릴레이트를 얻는 것을 포함하는,
자유 라디칼 개시제의 존재 하에서의 폴리아민 및 아크릴레이트 단량체의 유기 용매 중에서의 공중합에 의해 제조된다.
본 발명은 또한, 상기 방법에 따른 방법에 의해 수득가능한 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드에 관한 것이다.
아크릴레이트 단량체는 CH2=CR1COOR2 (여기서, R1 및 R2는 독립적으로 수소 또는 알킬, 아릴, 헤테로아릴, 치환된 아릴, 예컨대 n-부틸 아크릴레이트, 메틸 아크릴레이트, 메틸 메타크릴레이트, 이소-부틸 메타크릴레이트, tert-부틸 아크릴레이트, n-부틸 메타크릴레이트, 2-히드록실 에틸 아크릴레이트, 2-히드록실 에틸 메타크릴레이트, 이소보르닐 아크릴레이트, 이소보르닐 메타크릴레이트, 글리시딜 메타크릴레이트, 글리시딜 아크릴레이트, 시클로헥실 아크릴레이트, 시클로헥실 메타크릴레이트 등임)로 나타낼 수 있다.
자유 라디칼 개시제는, 2,2'-아조-비스(이소부티로니트릴) (AIBN), 칼륨 퍼술페이트, 2,2'-아조비스(2-아미디노프로판) 디히드로클로라이드, 및 알킬 히드로퍼옥시드, 예컨대 벤조일 퍼옥시드, 디-tert-부틸 퍼옥시드, t-부틸 히드로퍼옥시드, 쿠멘 히드로퍼옥시드, p-이소프로필 쿠멘 히드로퍼옥시드, p-멘탄 히드로퍼옥시드, 또는 피난 히드로퍼옥시드 등으로부터 선택될 수 있다.
2,2'-아조-비스(이소부티로니트릴)이 바람직하다.
폴리아민 대 아크릴레이트 단량체의 중량비는 바람직하게는 1:5 내지 1:50이다.
자유 라디칼 개시제 대 아크릴레이트 단량체의 중량비는 바람직하게는 1:5 내지 1:50이다.
상기 중량비는 폴리아크릴레이트 부분의 분자량을 결정한다.
반응 온도는 바람직하게는 20℃ 내지 120℃이다.
불활성 기체는 바람직하게는 질소이다.
하기 반응식은 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드의 제조에 대한 대표적 반응식이다.
에스테르교환반응은 하기와 같이 나타낼 수 있다.
폴리아민 아미드는 상기에 나타낸 에스테르교환반응 방법에 의해 수득된다. 자유 라디칼 개시제의 존재 하에, 폴리아민 아미드는 화학식 A (여기서, R1 및 R2는 상기에 정의된 바와 같음)의 폴리아민 아미드-폴리아크릴레이트 공중합체로 추가로 반응된다.
마이클 부가반응은 하기와 같이 나타낼 수 있다.
폴리아민에서 아크릴레이트의 불포화 결합으로의 친핵성 부가반응에 의해 화 학식 B (여기서, R1 및 R2는 상기에 정의된 바와 같음)의 폴리아민 아크릴레이트가 형성된다.
그래프팅 공중합은 하기와 같이 나타낼 수 있다.
"으로부터 그래프팅" 방법에서는, 폴리아민이 자유 라디칼 중합을 개시하는 거대개시제로서 사용된다. 아크릴레이트 사슬이 구성되어 화학식 C (여기서, R1 및 R2는 상기에 정의된 바와 같음)의 폴리아민-g-폴리아크릴레이트가 얻어진다.
라디칼 중합에 의해 폴리아크릴레이트 Y가 형성된다.
본 발명은 또한,
(여기서, R1 및 R2 및 n은 상기에 정의된 바와 같음)의 블렌드를 포함하며, 50 000 g/mol 내지 150 000 g/mol의 평균 분자량 및 3 초과의 다분산도 (Mw/Mn)를 갖는 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드에 관한 것이다.
(A + B + C + Y)를 포함하는 블렌드는 낮은 Tg를 갖고 결정화되지 않는 투명한 황갈색 액체이다. 블렌드는 모든 저온 용도에서 분산제로서 사용된다. 분산제는 폭넓은 범위의 비극성 내지 극성의 각종 유기 용매 중에서 가용성이다. 응용시, 분산제는 놀랍게도 우수한 안료 분산 효과 (특히 TPA와 분산제의 우수한 상용성으로 인해 TPA 도료에 대해)를 나타낸다. 그 결과로, 안료 농축물은 저점도를 나타내는데, 이는 높은 안료 부하량을 의미하며, 따라서 높은 생산성이 달성될 수 있다. 분산제는 낮은 응집성, 낮은 시딩(seeding), 높은 광택, 우수한 착색성, 안료 농축물의 저점도, 저온 저장 안정성 등을 나타낸다. 코팅은 높은 광택 및 우수한 착색성을 나타내고, 알키드, CAB 및 TPA 도료 시스템에서 선행 기술에 비해 명 백히 우수한 성능이 달성된다.
분산제 용액은 저온에서 안정하게 유지되고 (50% 용액, -15℃ 미만에서 2주 이상 동안 안정함), 이는 본 발명의 생성물이 사용이 용이하고, 저온 용도에 적용될 수 있다는 것을 의미한다.
또한, 아크릴레이트 단량체의 유형, 아크릴레이트 단량체 대 폴리아민의 비율, 자유 라디칼 개시제 대 아크릴레이트 단량체의 비율, 및 반응 조건을 조정함으로써 분산제의 유리 전이 온도, 결정성, 및 극성을 용이하게 조정할 수 있다.
출발 물질에 대한 접근성
상이한 분자량을 갖는 폴리에틸렌이민은 닛폰 슈쿠바이(Nippon Shukubai)로부터의 시판품이다.
MW 10,000을 갖는 폴리비닐아민은 미쯔비시 가세이(Mitsubishi Kasei)로부터 상업적으로 입수가능하다.
MW 10,000을 갖는 폴리알릴아민은 니또 보세끼(Nitto Boseki)로부터 상업적으로 입수가능하다.
폴리프로필렌이민 덴드리머는 DSM 파인 케미칼즈(DSM Fine Chemicals)로부터 상업적으로 입수가능하고, 폴리(아미드-아민) 덴드리머는 알드리치 케미칼 컴파니(Aldrich Chemical Company)로부터 상업적으로 입수가능하다.
아크릴레이트 단량체, 2,2'-아조-비스(이소부티로니트릴) 및 t-부틸 히드로퍼옥시드는 통상적인 시판품이다.
용도
폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드는, 특히 저온 및 저점도 용도에서, 코팅, 잉크, 전자 재료 등의 폭넓은 응용 분야에서 분산제로서 사용될 수 있다.
본 발명의 폴리아민-그래프트-폴리아크릴레이트는 용제형 시스템, 예컨대 용제형 유기 및 무기 안료 분산액에서, 예를 들어 알키드, CAB (셀룰로스 아세테이트 부티레이트), UV (자외선) 및 TPA (열가소성 아크릴레이트) 도료 시스템에서, 일반적 산업 코팅에서 (특히 자동차 코팅에서) 뿐만 아니라 프린팅 잉크 및 그래픽 기술에서 사용된다.
실시예 1
PEI SP-200 (MW 10,000) 5.0 g, BA 50.0 g, AIBN 6.3 g, 및 톨루엔 85 mL의 혼합물을 질소 하에 35℃에서 24시간 동안, 이어서 60℃에서 70시간 동안 교반하였다. 이어서, 톨루엔을 진공 시스템 하에 제거하였다. 생성물을 황색 액체로서 수득하였다.
실시예 2 내지 64
실시예 2 내지 64는 모두, 하기 표 1에 상세히 나타낸 바와 같이 폴리아민, 아크릴레이트 단량체, 자유 라디칼 개시제의 유형 및 양, 및 반응 조건을 달리한 것을 제외하고는, 실시예 1과 유사한 방식으로 제조하였다.
실시예의 분자량을 하기 표 2에 나타내었다.
성능 스크리닝
수득된 샘플의 분산 효과를 테스트하기 위해, 수지 비함유 안료 농축물을 배합 1에 따라 제조하였다. 밀(mill) 베이스를 스칸덱스 쉐이커(Scandex Shaker) 중에서 1.5시간 동안 유리 비드의 도움 하에 분산시켰다. 그 후, 밀 베이스를 여과시키고, 실온에서 밤새 저장하였다. 테스트를 위한 렛-다운(let-down) (배합 2)은 스토빙 에나멜, CAB 베이스 코트 및 TPA 베이스 코트를 기재로 하였다. 배합 3은 스토빙 에나멜, CAB 도료 및 TPA 도료에 대한 도료 배합을 나타낸다. 도료 제제를 2000 rpm에서 고속 교반 하에 5분 동안 혼합하고, 폴리에스테르 필름 상에 35 내지 75 ㎛의 필름 두께로 도포하였다. 드로-다운(draw-down) 제조 후, 푸어-아웃 (pour out) 테스트를 위해 나머지 도료를 부틸 아세테이트로 1:1 희석하였다.
먼저, 특허, 예를 들어 WO 9421368, USP 6583213, 및 USP 6599947 등에 따라 경쟁 등급물을 합성하였다. 이들 등급물의 성능을 배합 1, 2 및 3에 따라 테스트하였다. 결과는 경쟁 생성물 A가 다른 것들보다 우수한 성능을 갖는 것으로 나타났고, 따라서 이를 본문에서 대표적 분산제로서 선택하였다.
상기 표 1의 실시예 1 내지 64의 성능을 배합 1, 2 및 3에 따라 테스트하였다. 안료 농축물이 양호하게 유동되고, 이들의 점도가 경쟁 생성물 A와 유사하거나 그보다 더 낮은 것으로 나타났다. 안료 농축물의 레올로지 거동을 CR 모드 하에 써모-하케 레오스트레스(Thermo-Haake RheoStress) 600 장비로 측정하였다. 안료 농축물의 초기 점도 (η0) 및 동적 점도 (ηt)를 하기 표 3에 나타내었다. 점도 곡선에 따르면, 피그먼트 화이트 농축물 (PW 21)은 뉴턴(Newtonian) 유동을 나타낸 반면, 피그먼트 블랙 농축물 (스페셜 블랙-100)은 유사소성 유동을 나타내었다. 피그먼트 블루 농축물 (PB 15:2)은 틱소트로픽 특성을 가지며 소성 유동을 나타내었으나, 낮은 전단 응력 (하기 표 3에서, τ)하에서는 용이하게 유동할 수 있었다.
스토브 에나멜 도료, CAB 도료, 특히 TPA 도료에서 테스트시, 분산제의 성능은 일반적으로 만족스런 결과 (예를 들어, 높은 광택 (평균, 60°에서 80 초과), 시딩 없음, 러빙-아웃(rub-out) 없음, 우수한 색 강도 등)를 가지며 매우 우수하였다 (표 4).
용해도 테스트에서는, 샘플을 먼저 50% (w/w)의 농도로 각종 용매 중에 용해시키고, 이어서 25℃ 및 -15℃에서 각각 1개월 동안 유지시켰다. 명백하게, 본 발명의 분산제는 경쟁 생성물에 비해 향상된 용해도를 가졌다 (표 5). 이는, 본 발명의 샘플이 경쟁 생성물 A의 경우에 비해 더 낮은 결정성을 갖고, 각종 용매 시스템에서의 이들의 상용성이 더 우수하다는 것을 나타낸다.
Claims (6)
- 50 000 g/mol 내지 150 000 g/mol의 평균 분자량을 갖고, 다분산도 (Mw/Mn)가 3 초과인, 하기 화학식 1 또는 화학식 1과 Y의 혼합물의 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드.<화학식 1>T-(A1,A2)-Y상기 식에서,T는 폴리아민 또는 폴리이민이고,A1은 아미드 () 또는 이미드 (
)로부터 선택된 브릿징 결합이며,
A2는 -N-C- 브릿징 결합이고,Y는 하기 화학식 2의 아크릴레이트 잔기이며,<화학식 2>
상기 식에서,R1 및 R2는 독립적으로 수소 또는 C1-20알킬, 아릴, 헤테로아릴, 치환된 아릴이고,n은 1 내지 1000의 수이다. - 제1항에 있어서, T가 폴리에틸렌이민이고, R1이 수소 또는 메틸이며, R2가 C1-20알킬이고, n이 5 내지 100인 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드.
- 1. 폴리아민 대 아크릴레이트 단량체의 중량비가 1:5 내지 1:100의 범위이고;2. 자유 라디칼 개시제 대 아크릴레이트 단량체의 중량비가 1:5 내지 1:100의 범위이며;3. 공정을 불활성 기체 분위기 하에 10℃ 내지 200℃의 온도에서 1-반응기(one pot)에서 수행하고;4. 공정이 적어도 아크릴레이트와 폴리아민의 에스테르교환반응으로부터 폴리아민 아미드 또는 폴리아민 이미드를 얻는 것, 폴리아민과 아크릴레이트 단량체의 마이클(Michael) 부가반응으로부터 폴리아민 아크릴레이트를 얻는 것, 및 폴리아민과 아크릴레이트 단량체의 그래프트 중합으로부터 폴리아민-g-폴리아크릴레이트를 얻는 것을 포함하는,자유 라디칼 개시제의 존재 하에서의 폴리아민 및 아크릴레이트 단량체의 유기 용매 중에서의 공중합에 의한, 제1항에 정의된 폴리아민-g-폴리아크릴레이트 그 래프팅된 공중합체 블렌드의 제조 방법.
- 제3항에 따른 방법에 의해 수득가능한 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드.
-
(상기 식에서, R1 및 R2 및 n은 제1항 또는 제2항에서 정의된 바와 같음)의 블렌드를 포함하며, 50 000 g/mol 내지 150 000 g/mol의 평균 분자량 및 3 초과의 다분산도 (Mw/Mn)를 갖는 액체 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드. - 제1항에 따른 폴리아민-g-폴리아크릴레이트 그래프팅된 공중합체 블렌드의 분산제로서의 용도.