KR20020056377A - 반도체 소자의 확산 방지막 형성 방법 - Google Patents
반도체 소자의 확산 방지막 형성 방법 Download PDFInfo
- Publication number
- KR20020056377A KR20020056377A KR1020000085726A KR20000085726A KR20020056377A KR 20020056377 A KR20020056377 A KR 20020056377A KR 1020000085726 A KR1020000085726 A KR 1020000085726A KR 20000085726 A KR20000085726 A KR 20000085726A KR 20020056377 A KR20020056377 A KR 20020056377A
- Authority
- KR
- South Korea
- Prior art keywords
- cobalt silicide
- forming
- semiconductor device
- diffusion barrier
- contact hole
- Prior art date
Abstract
본 발명은 플러그 형성 공정시에 일어나는 반응성을 최소화하여 공정 마진을 충분히 확보하고 공정을 단순화 할 수 있도록한 반도체 소자의 확산 방지막 형성 방법에 관한 것으로, 반도체 기판상에 절연층을 형성하고 선택적으로 패터닝하여 콘택홀을 형성하는 단계;상기 콘택홀을 포함하는 전면에 코발트실리사이드 형성하는 단계;상기 코발트실리사이드를 열공정으로 하부의 기판과 반응이 없는 상태로 상변이 코발트실리사이드를 형성함과 동시에 상기 상변이 코발트실리사이드상에 코발트 나이트라이드가 형성되도록 하는 것이다.
Description
본 발명은 반도체 소자에 관한 것으로, 특히 플러그 형성 공정시에 일어나는 반응성을 최소화하여 공정 마진을 충분히 확보하고 공정을 단순화 할 수 있도록한 반도체 소자의 확산 방지막 형성 방법에 관한 것이다.
현재 반도체 소자의 내부 배선층(inter connection layer)은 소자의 고집적화에 따라서 확산방지막 Ti/TiN 증착후 텅스텐 플러그 공정을 많이 이용하고 있다.
그에 따라 텅스텐 증착공정시에 그 하부의 금속 확산 방지막의 불균일한 증착 또는 그 박막이 얇을 경우 이후 텅스텐 증착 공정에서 사용하는 WF6가스와 하부 타이타늄과의 강한 반응성으로 인하여 볼캐이노 발생의 원인이 되기도 한다.
이하, 첨부된 도면을 참고하여 종래 기술의 반도체 메모리 장치에서 채택하는 확산 방지막에 대하여 설명하면 다음과 같다.
도 1은 종래 기술의 텅스텐 볼케이노 발생 영역을 나타낸 사진이다.
종래 기술에서는 절연층을 증착한후에 콘택홀 형성 공정을 진행하고, 콘택홀을 포함하는 표면에 금속 확산 방지막으로 Ti/TiN을 증착한다.
그리고 상기 콘택홀내에 텅스텐을 증착 매립하여 플러그를 형성한다.
이와 같은 증착 공정에서 금속 확산방지막으로 사용하는 티타늄과 타타늄나이트라이드는 각각의 역할이 틀리다.
하부의 티타늄은 실리콘과의 반응을 통하여 콘택 저항을 낮추기 위한 목적으로 사용하며 상부의 티타늄나이트라이드는 후속 텅스텐 증착 공정에서 사용되는 WF6가스와 그 아래쪽 티타늄과의 반응을 억제하기 위하여 사용된다.
티타늄과 WF6가스의 반응으로 인하여 도 1에서와 같이 반도체 소자의 콘택홀 저항에 치명적인 볼캐이노 발생으로 소자의 신뢰성을 떨어뜨리게 된다.
이처럼 현재의 공정에서 티타늄나이트라이드 박막의 균일한 증착과 적정 두께의 증착이 점점 어려워짐에 따라서 소자의 집적도가 높아질수록 증착 장비의 개선내지는 교체가 필요하게 되었다.
이와 같은 종래 기술의 반도체 소자의 금속 확산 방지막은 다음과 같은 문제가 있다.
확산 방지막으로 사용하는 티타늄 나이트라이드의 균일한 두께의 증착이 어렵고, 티타늄과 WF6가스의 반응으로 인한 볼캐이노 현상을 완전하게 억제하지 못하여 소자의 적정한 콘택 저항의 확보가 어렵다.
본 발명은 이와 같은 종래 기술의 확산 방지막의 문제를 해결하기 위한 것으로, 본 발명은 반도체 소자에 관한 것으로, 특히 플러그 형성 공정시에 일어나는 반응성을 최소화하여 공정 마진을 충분히 확보하고 공정을 단순화 할 수 있도록한 반도체 소자의 확산 방지막 형성 방법을 제공하는데 그 목적이 있다.
도 1은 종래 기술의 텅스텐 볼케이노 발생 영역을 나타낸 사진
도 2는 확산 방지막 형성 물질에 따른 물성 비교 그래프
도 3a내지 도 3c는 본 발명에 따른 확산 방지막 형성 공정을 위한 공정 단면도
도면의 주요 부분에 대한 부호의 설명
31. 반도체 기판 32. 절연층
33. 콘택홀 34. 코발트 실리사이드
34a. 상변이 코발트 실리사이드 35. 코발트 나이트라이드
이와 같은 목적을 달성하기 위한 본 발명에 따른 반도체 소자의 확산 방지막 형성 방법은 반도체 기판상에 절연층을 형성하고 선택적으로 패터닝하여 콘택홀을 형성하는 단계;상기 콘택홀을 포함하는 전면에 코발트실리사이드 형성하는 단계;상기 코발트실리사이드를 열공정으로 하부의 기판과 반응이 없는 상태로 상변이 코발트실리사이드를 형성함과 동시에 상기 상변이 코발트실리사이드상에 코발트 나이트라이드가 형성되도록 하는 것을 특징으로 한다.
이하, 첨부된 도면을 참고하여 본 발명에 따른 반도체 소자의 확산 방지막형성 방법에 관하여 상세히 설명하면 다음과 같다.
도 2는 확산 방지막 형성 물질에 따른 물성 비교 그래프이고, 도 3a내지 도 3c는 본 발명에 따른 확산 방지막 형성 공정을 위한 공정 단면도이다.
본 발명은 금속 확산방지막으로 사용되던 물질을 달리하여 텅스텐 증착 공정에서의 볼캐이노의 발생을 원천적으로 막을 수 있고 또한 코발트실리사이드를 직접 증착함에 따라서 하부 실리콘서브의 손실없이 반도체 소자에서 원하는 콘택 저항을 얻을 수 있어서 반도체소자의 수율 및 신뢰를 높일 수 있도록한 것이다.
즉, 타이타늄계열의 확산방지막 대신 그에 준하는 저항을 갖는 코발트실리사이드를 이용하는 확산 방지막을 제안한다.
타이타늄 계열과 코발트 계열의 실리사이드의 물성 비교는 도 2에서와 같다.
먼저, 도 3a에서와 같이, 반도체 기판(31)상에 절연층(32)을 형성하고 선택적으로 패터닝하여 콘택홀(33)을 형성한다.
그리고 도 3b에서와 같이, 자연 산화막을 제거하는 클리닝 공정을 진행한후 금속확산방지막 역할을 수행하는 코발트실리사이드(34)를 물리적 기상 증착 방법으로 300~1000Å 두께로 증착한다.
여기서, 증착 온도는 0~400℃이다.
이어, 도 3c에서와 같이, 코발트실리사이드(34)는 약 600℃ 이상의 열공정을 거쳐서 하부의 실리콘 서브와의 반응이 거의 없는 상태로 다시 재반응을 하여 비저항이 낮은 상변이 코발트실리사이드(CoSi2)(34a)를 형성한다.
여기서, 상변이 코발트실리사이드(CoSi2)(34a)는 오믹 콘택층으로 작용한다.
그리고 상기 상변이 코발트실리사이드(CoSi2)(34a)상에는 상기 열공정에 의해 코발트 나이트라이드(35)가 형성된다.
열공정은 N2분위기의 RTP(Rapid Thermal Process) 또는 어닐링 공정으로 진행하고 RTP 온도는 550~850℃, 어닐링 온도는 450~700℃로 진행한다.
그리고 상변이 코발트실리사이드(34a)와 코발트나이트라이드(35)의 생성비율이 1:1~5 정도가 된다.
이러한 코발트실리사이드는 티타늄실리사이드 형성과 비교하여 도 2에서와 같이, 거의 비슷한 비저항을 갖고 또한 베리어 크기(barrier height)도 거의 비슷하게 된다.
따라서, 이미 적용되고 있는 소자에서의 공정들 특히 이온주입 공정에 대해 특별한 변화를 요구하지 않는다.
이러한 코발트실리사이드를 물리적 기상 증착 방법으로 직접 증착후 열공정으로 재반응을 시키는 경우의 가장 큰 장점은 역시 서브 실리콘의 손실이 거의 없어서 콘택홀 형성시의 식각공정에의 마진을 높일 수 있다는 것이다.
그리고 후속 텅스텐 증착 공정에서의 볼케이노의 사고 가능성을 거의 없앨 수 있다.
이와 같은 본 발명에 따른 반도체 소자의 확산 방지막 형성 방법은 다음과같은 효과가 있다.
타이타늄/타이타늄나이트라이드 증착후 열공정을 거치는 공정을 증착 공정 그리고 열공정의 2단계로 공정수를 줄일 수 있고 또한 공정의 안정성을 확보할 수 있음으로 인하여 현재의 공정보다 훨씬 큰 공정 마진을 갖는다.
또한 텅스텐 볼케이노를 완벽하게 막을 수 있다는 장점을 갖는다.
그리고 새로운 장비의 추가 없이 타켓만을 바꿔서 그 장비를 그대로 활용할 수 있어서 특별한 투자비용이 필요하지 않아 경제적인 측면에서 유리하다.
Claims (4)
- 반도체 기판상에 절연층을 형성하고 선택적으로 패터닝하여 콘택홀을 형성하는 단계;상기 콘택홀을 포함하는 전면에 코발트실리사이드 형성하는 단계;상기 코발트실리사이드를 열공정으로 하부의 기판과 반응이 없는 상태로 상변이 코발트실리사이드를 형성함과 동시에 상기 상변이 코발트실리사이드상에 코발트 나이트라이드가 형성되도록 하는 것을 특징으로 하는 반도체 소자의 확산 방지막 형성 방법.
- 제 1 항에 있어서, 코발트실리사이드를 물리적 기상 증착 방법으로 0 ~ 400℃의 온도로 300~1000Å 두께로 증착하는 것을 특징으로 하는 반도체 소자의 확산 방지막 형성 방법.
- 제 1 항에 있어서, 열공정을 N2분위기의 RTP(Rapid Thermal Process) 또는 어닐링 공정으로 진행하는 것을 특징으로 하는 반도체 소자의 확산 방지막 형성 방법.
- 제 3 항에 있어서, RTP 온도는 550~850℃, 어닐링 온도는 450~700℃로 진행하는 것을 특징으로 하는 반도체 소자의 확산 방지막 형성 방법.