JPWO2011129167A1 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JPWO2011129167A1 JPWO2011129167A1 JP2011515618A JP2011515618A JPWO2011129167A1 JP WO2011129167 A1 JPWO2011129167 A1 JP WO2011129167A1 JP 2011515618 A JP2011515618 A JP 2011515618A JP 2011515618 A JP2011515618 A JP 2011515618A JP WO2011129167 A1 JPWO2011129167 A1 JP WO2011129167A1
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- ethylene
- adherend
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、前記課題、つまり、粘着力や多種多様な加工特性、ブロッキング性で代表されるハンドリング性(表面特性)をはじめ、特にフィッシュアイ等の凸部欠点やフィルムの各種シワ等が起因で被着体に凹みや変形等の打痕欠点や汚染などが生じることのない表面保護フィルムについて、鋭意検討し、フィッシュアイ等の膨らみによる凸部の応力集中を緩和させる特定な粘着層、中間層、背面層からなる積層形態にすることで、かかる課題を一挙に解決することを究明したものである。
酸化防止剤としては、フェノール系、芳香族アミン系、チオエーテル系、リン系などがあり、少量配合で効果を高めるため、2種以上のものを併用するのが好ましい。例えば、フェノール系とリン系の併用は好ましい方法である。
かかる場合の中間層への添加・混合量としては、後述の背面層構成樹脂30重量%未満までが好ましい。かかるポリプロピレン系樹脂を主体とした背面層樹脂の含有量が多くなると、本発明の骨子である中間層の柔軟性が得られ難くなる。
表面粗さは、(株)小坂研究所製の全自動微細形状測定機(SURFCORDER ET4000A)を用い、JIS B0601−1994に準拠し、フィルム横方向(フィルムのTD方向)に測定長さ2mmで、長手方向(マシン方向)に10μmピッチで20回測定して3次元解析し、算術平均粗さ(Ra)及び、十点平均粗さ(Rz)をそれぞれ求めた(単位はμm)。尚、触針先端半径2.0μm、頂角60°のダイヤモンド針を使用、測定力10μN、カットオフ0.8mmで測定した。
温度23℃、湿度50%RHの条件下で24時間、保管・調整した実施例及び比較例の試料サンプルを被着体に、ロールプレス機((株)安田精機製作所製特殊圧着ローラ)を用い、貼込圧力9,100N/m、貼込速度300cm/分で貼り付けた。しかる後、温度23℃、湿度50%RH条件下で24時間保管した後、各測定と評価に用いた。
引張試験機((株)オリエンテック“テンシロン”万能試験機)を用い、引張速度300mm/分、剥離角度180°にて粘着力を測定した。
被着体と試料サンプルの密着状態を肉眼観察し、次の判定を行った。
B:ごく一部が密着不良で試料フィルムが一部(面積比30%以内)浮いている
C:面積比70%以上の部分でフィルムが被着体から浮いている。
被着体より試料フィルムを剥がした後、暗室内で被着体表面にスポット光を当てて、表面の汚染状態を肉眼観察し、次の判定を行った。
B:軽度の汚染がある
C:汚染している。
予め試料サンプルのフィッシュアイ欠点を国立印刷製造のきょう雑物測定図表と対比し、0.05mm2〜0.1mm2サイズのフィッシュアイ欠点部を選別し、該欠点を有する部分を含む試料サンプルを被着体と貼り合わせた後、両側を平滑なポリカーボネート板(板厚み2mm)で挟み込み、荷重1.3kg/cm2を負荷し、60℃熱風オーブン中で3日間保管した後、室温に戻し、その後、被着体より試料フィルムを剥がした後、被着体がフィッシュアイによりへこみが生じていないか判定した。尚、目視にてフィッシュアイ欠点部が全く見つけられなかったサンプルにおいては、試料サンプルをそのまま使用した。
B:僅かにフィッシュアイによるへこみが認められる
C:フィッシュアイによるへこみが明らかに認められる。
(株)東洋精機製作所製メルトインデックサを用い、JIS K7210−1997に準拠し、ポリプロピレン系樹脂の場合は温度230℃、荷重2.16kg/cm2で、ポリエチレン系樹脂及びエチレン・メチルメタクリレートの場合は温度190℃、荷重2.16kg/cm2で測定した。単位はいずれもg/10分である。
各層の構成樹脂を次のように準備した。
粘着層樹脂として、リン系酸化防止剤1000ppmを含有する密度0.922g/cm3、融点116℃、190℃下MFR5.0g/10分のエチレン・ヘキセン−1共重合体(直鎖状低密度ポリエチレン)を用い、中間層樹脂として、密度0.923g/cm3、190℃下MFR10g/10分の高圧法低密度ポリエチレン91重量%に粘着層樹脂6.6重量%及び後述の背面層構成樹脂組成物2.4重量%からなる樹脂組成物(耳部を回収することを想定した組成物とした)をヘンシェルミキサにて均一に混合したものを用い、背面層樹脂として、230℃下MFR35g/10分、エチレン含有量5重量%のエチレン−プロピレンランダム共重合体80重量%と190℃下MFR2g/10分、密度0.92g/cm3の低密度ポリエチレン20重量%からなる樹脂組成物をヘンシェルミキサにて均一に混合したものを用い、φ90mm(粘着層用)とφ115mm(中間層用)とφ65mm(背面層用)との3台の押出機を有する口金幅2400mmのTダイ型複合製膜機を用い、上記準備した樹脂組成物をそれぞれの押出機に導入し、粘着層厚み比率22%、中間層厚み比率70%、背面層厚み比率8%となるよう各押出機の吐出量を調整し、複合Tダイから押出温度200℃にて押出し、フィルム厚み35μmの3層積層フィルムを製膜し、一旦、ロール状に巻き取った。
粘着層樹脂としては、実施例1と同一のエチレン・ヘキセン−1共重合体(直鎖状低密度ポリエチレン)を用い、中間層樹脂として、密度0.964g/cm3、融点135℃、190℃下MFR7.0g/10分の高密度ポリエチレン91重量%と粘着層構成樹脂であるエチレン・ヘキセン−1共重合体6.6重量%と後述の背面層構成樹脂組成物2.4重量%とをヘンシェルミキサにて均一に混合したものを用い、背面層樹脂として、融点163℃、230℃下MFR7.5g/10分のホモポリプロピレン98重量%と190℃下MFR2g/10分、密度0.92g/cm3の低密度ポリエチレン2重量%からなる樹脂組成物をヘンシェルミキサにて均一に混合したものを用いる以外は、実施例1と同様にTダイ型3層複合製膜機を用いて、フィルム厚み35μmの3層積層フィルムを製膜した。
各層の構成樹脂を次のように準備した。
粘着層樹脂として、リン系酸化防止剤1000ppmを含有する密度0.922g/cm3、融点116℃、190℃下MFR5.0g/10分のエチレン・ヘキセン−1共重合体(直鎖状低密度ポリエチレン)を40重量%、フェノール系酸化防止剤1200ppmを含有する密度0.875、融点71℃、190℃下MFR3.0g/10分の超低密度ポリエチレンを60重量%からなる樹脂組成物をヘンシェルミキサーにて均一混合したものを用い、中間層樹脂として、密度0.923g/cm3、190℃下MFR10g/10分の低密度ポリエチレンを、背面層樹脂として、230℃下MFR7.5g/10分、密度0.90g/cm3のホモポリプロピレン45重量%と230℃下MFR35g/10分、エチレン含有量5重量%のエチレン−プロピレンランダム共重合体45重量%と190℃下MFR2g/10分、密度0.92g/cm3の低密度ポリエチレン10重量%からなる樹脂組成物をヘンシェルミキサにて均一に混合したものを用い、φ90mm(粘着層用)とφ115mm(中間層用)とφ65mm(背面層用)との3台の押出機を有する口金幅2400mmのTダイ型複合製膜機を用い、上記準備した樹脂組成物をそれぞれの押出機に導入し、粘着層厚み比率20%、中間層厚み比率72%、背面層厚み比率8%となるよう各押出機の吐出量を調整し、複合Tダイから押出温度210℃にて押出し、フィルム厚み30μmの3層積層フィルムを製膜し、一旦、ロール状に巻き取った。背面層のポリプロピレン系の混合樹脂のMFRは、前述の計算方法で16.2g/10分である。
次いで、ロール状に巻き取ったフィルムを、スリット機に掛けて幅1300mm、長さ3,000mのサイズに仕上げ、ロール状に巻き上げたフィルムサンプルを得た。尚、スリット機にて所定幅の製品を得る際にも、離型処理等の処理を施す必要もなく、何ら抵抗なく容易にスリット機へ送り出す(巻き出す)ことができ、ブロッキングは全く認められなかった。
粘着層樹脂として、実施例1のエチレン・ヘキセン−1共重合体(直鎖状低密度ポリエチレン)100重量%に代え、密度0.93g/cm3、190℃下MFR7g/10分のMMA10重量%共重合されたエチレン・メチルメタクリレート共重合体60重量%と実施例1のエチレン・ヘキセン−1共重合体40重量%を用い、中間層樹脂として、上記粘着層に用いたものと同一のエチレン・メチルメタクリレート共重合体を用いる以外は実施例1と同様にして、フィルム厚み35μmの3層積層フィルムを製膜し、一旦、ロール状に巻き取った。
また、フィッシュアイは、実施例1と同様に視認されなかったが、フィッシュアイの被着体への転写性(被着体への凹み発生)評価を実施したところ、被着体への凹みはなく、また、背面層の凹凸による被着体への転写も認められなかった。
粘着層樹脂として190℃下MFR7g/10分のMMA10重量%共重合されたエチレン・メチルメタクリレート共重合体100重量%を用いる以外は実施例1と同様にして、
フィルム厚み35μm、幅1600mm、長さ7,000mの3層積層フィルムを仕上げた。尚、所定幅の製品を得る際にも、何ら抵抗なく容易にスリット機へ送り出す(巻き出す)ことができ、ブロッキングは全く認められなかった。
各層の構成樹脂を次ぎのように準備した。
粘着層樹脂としては、比較例1と同一のエチレン・ヘキセン−1共重合体(直鎖状低密度ポリエチレン)を用い、中間層樹脂として、密度0.964g/cm3、融点134℃、190℃下MFR7.5g/10分の高密度ポリエチレンを、背面層樹脂として、190℃下MFR5.5g/10分、密度0.923g/cm3の低密度ポリエチレン94重量%、190℃下MFR2g/10分、密度0.92g/cm3の低密度ポリエチレン1重量%、230℃下MFR40g/10分、エチレン含有量5重量%のエチレン−プロピレンランダム共重合体4重量%に加え、滑剤として平均粒子径2.0μmのソジウムカルシウムアルミノシリケート1.0重量%からなる樹脂組成物をヘンシェルミキサにて均一に混合したものを用い、実施例2と同様にTダイ型3層複合製膜機を用いて、フィルム厚み30μmの3層積層フィルムを製膜した。
中間層樹脂として、実施例2の粘着層に用いたものと同一の密度0.875g/cm3、MFR3g/10分の超低密度ポリエチレンを用いる以外は実施例1と同様にして実施例5のフィルムを得た。
Claims (3)
- 粘着層と中間層と背面層の3層積層形態からなり、該粘着層は、エチレン・α−オレフィン共重合体およびエチレン・メチルメタクリレート共重合体からなる群より選ばれた少なくとも1種からなり、該中間層は密度0.870〜0.935g/cm3のポリエチレン系樹脂およびエチレン・メチルメタクリレート共重合体からなる群より選ばれた少なくとも1種を含有し、該背面層は、ポリプロピレン系樹脂と低密度ポリエチレンから構成されてなり、該背面層の表面粗さが算術平均粗さ(Ra)として0.6μm以上、十点平均粗さ(Rz)で4μm以上であることを特徴とする表面保護フィルム。
- 背面層を構成するポリプロピレン系樹脂の230℃、荷重2.16kg/cm2下でのメルトフローレートが5〜50g/10分の範囲であって、かつ、低密度ポリエチレンの190℃、荷重2.16kg/cm2下でのメルトフローレートが0.5〜5g/10分であることを特徴とする請求項1記載の表面保護フィルム。
- 粘着層と中間層と背面層の3層積層形態からなり、中間層が、密度0.870〜0.935g/cm3のポリエチレン系樹脂およびエチレン・メチルメタクリレート共重合体からなる群より選ばれた少なくとも1種と、粘着層構成樹脂及び背面層構成樹脂との混合樹脂組成からなることを特徴とする請求項1または2に記載の表面保護フィルム。