JPH104024A - Method for manufacturing ceramic electronic component - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a method for efficiently manufacturing ceramic electronic components, preventing yield deterioration due to chipping, crack or break of chips which have orientation. SOLUTION: A mother block 1 for forming multiple ceramic electronic components is burned and scribed for forming primary breaking grooves 2 in a predetermined direction. Then the mother block 1 is broken along the primary grooves 2 to form multiple stick-like aggregates 4. Outer electrodes are formed on the aggregates 4. In the breaking grooves forming process, secondary breaking grooves 3 crossing the primary breaking grooves 2 are formed by a scribing method. After forming the outer electrodes 5, the aggregates 4 of are divided into multiple pieces along the secondary breaking grooves 3 with keeping the direction of the outer electrodes 5.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本願発明は、セラミック電子
部品の製造方法に関し、詳しくは、素子の少なくとも一
つの面に配設された外部電極を備えており、表裏や前後
に方向性を有する、表面実装型積層コイル部品などのセ
ラミック電子部品の製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a ceramic electronic component, and more particularly, to a method for manufacturing a ceramic electronic component, comprising an external electrode disposed on at least one surface of an element, and having a front-back and front-back direction. The present invention relates to a method for manufacturing a ceramic electronic component such as a mounting type laminated coil component.

【０００２】[0002]

【従来の技術及び発明が解決しようとする課題】セラミ
ック電子部品の一つに、素子中に配設された積層型コイ
ルと、素子の表面に配設された外部電極とを備えた表面
実装型積層コイル部品がある。この表面実装型積層コイ
ル部品の製造方法の一例を図６のフローチャートを参照
しつつ説明する。まず、セラミック原料からグリーンシ
ートを形成する。そして、このグリーンシートの表面に
導電ペーストを印刷してコイルパターンを形成する。2. Description of the Related Art One of ceramic electronic parts is a surface mount type having a laminated coil disposed in an element and external electrodes disposed on the surface of the element. There are multilayer coil components. An example of a method of manufacturing the surface mount type laminated coil component will be described with reference to a flowchart of FIG. First, a green sheet is formed from a ceramic raw material. Then, a conductive paste is printed on the surface of the green sheet to form a coil pattern.

【０００３】それから、表面にコイルパターンが配設さ
れたグリーンシートを、各コイルパターンが導通するよ
うに積み重ねて未焼成の積層ブロック（マザーブロッ
ク）を形成する。次に、未焼成のマザーブロックをカッ
トして各素子を切り出した後、所定の条件で焼成する。
それから、焼成後の各素子に導電ペーストを塗布、焼付
けした後、メッキを施して外部電極を形成する。最後
に、測定を行い表面実装型積層コイル部品が完成する。[0003] Then, green sheets having a coil pattern disposed on the surface thereof are stacked so that each coil pattern is conducted to form an unfired laminated block (mother block). Next, after cutting the unfired mother block to cut out each element, firing is performed under predetermined conditions.
Then, after applying and baking a conductive paste to each element after firing, plating is performed to form external electrodes. Finally, measurement is performed to complete the surface mount type laminated coil component.

【０００４】すなわち、従来から実施されている表面実
装型積層コイル部品の製造方法では、印刷工程及び積み
重ね工程終了後の未焼成のマザーブロックをカットし、
これを焼成工程で焼成した後、ばらばらになった状態の
各素子に外部電極を形成していた。[0004] That is, in the conventional method of manufacturing a surface-mounted laminated coil component, the unfired mother block after the printing step and the stacking step is cut,
After this was fired in a firing step, external electrodes were formed on each element in a separated state.

【０００５】しかし、上記従来の方法により、表裏や前
後に方向性を有する表面実装型積層コイル部品を製造し
た場合、未焼成のマザーブロックをカットした後の段階
では各素子の方向がばらばらになり、外観上では方向性
が分からなくなってしまうという問題点がある。これ
は、表面実装型積層コイル部品以外のセラミック電子部
品の場合にも当てはまるものである。However, when a surface-mounted laminated coil component having directionality in front and back, front and back, and back and forth is manufactured by the above-described conventional method, the direction of each element becomes different at a stage after cutting the unfired mother block. However, there is a problem in that the direction cannot be understood from the appearance. This also applies to ceramic electronic components other than the surface mount type laminated coil components.

【０００６】そこで、従来は、焼成前にマザーブロック
をカットして個々の素子を切り出すことをせず、マザー
ブロックを焼成した後、ダイシングブレードを用いるダ
イシング法により、図７に示すように、マザーブロック
２１を所定の方向に沿ってカットしてスティック状素子
集合体２２に分割した後、その状態で外部電極２３（図
８(ａ)）を形成し、その後、同じくダイシング法によ
り、スティック状素子集合体２２をカットすることによ
り個々のセラミック電子部品２４（図８(ｂ)）を得るよ
うにしている。しかし、上記従来の方法では、ダイヤモ
ンド粒子を埋め込んだダイシングブレードを用いてマザ
ーブロック２１やスティック状素子集合体２２をカッ
ト、分割するようにしているので、その際に、切削面の
エッジ部分などにチッピング、ワレ、カケなどが発生し
やすく歩留りが低下するという問題点があり、特に素子
が小型化するほどその影響が大きくなる。Therefore, conventionally, the mother block is not cut out before firing and individual elements are not cut out, but after the mother block is fired, a dicing method using a dicing blade is used, as shown in FIG. After the block 21 is cut along a predetermined direction and divided into a stick-shaped element assembly 22, an external electrode 23 (FIG. 8A) is formed in that state, and then the stick-shaped element By cutting the assembly 22, individual ceramic electronic components 24 (FIG. 8B) are obtained. However, in the above-described conventional method, the mother block 21 and the stick-shaped element assembly 22 are cut and divided by using a dicing blade in which diamond particles are embedded. There is a problem that chipping, cracking, chipping, and the like are apt to occur, and the yield is reduced. In particular, as the size of the element is reduced, the influence is increased.

【０００７】また、焼成前に方向性を判断するための認
識マークを個々のチップに付与しておき、チップに分割
して焼成した後、最終の測定・テーピング工程で再整列
させて方向性を合わせる方法もあるが、この方法におい
ては、認識マークを付与する工程、方向性を認識して再
整列させる工程などが必要になるため、コストアップを
招くという問題点がある。[0007] Further, before firing, a recognition mark for judging the direction is given to each chip, divided into chips and fired, and then realigned in the final measurement and taping step to check the direction. Although there is a matching method, this method requires a process of providing a recognition mark and a process of recognizing the direction and realigning, and thus has a problem of increasing costs.

【０００８】本願発明は、上記問題点を解決するもので
あり、方向性のあるセラミック電子部品を、チッピン
グ、ワレ、カケなどによる歩留りの低下を引き起こすこ
となく効率よく製造することが可能なセラミック電子部
品の製造方法を提供することを目的とする。The present invention solves the above-mentioned problems, and a ceramic electronic component capable of efficiently producing a directional ceramic electronic component without lowering the yield due to chipping, cracking, chipping, and the like. An object of the present invention is to provide a method for manufacturing a component.

【０００９】[0009]

【課題を解決するための手段】上記目的を達成するため
に、本願の発明者等は種々の実験、検討を行ない、通
常、固い材料をブレークするには適さないと考えられて
いたスクライブ工法を用いてブレークした場合に、意外
にも、マザーブロックやスティック状素子集合体のよう
な固いセラミック焼結体を、チッピング、ワレ、カケな
どを生じることなくブレークすることが可能であること
を知り、さらに実験を行なって本願発明を完成した。す
なわち、本願第１の発明のセラミック電子部品の製造方
法は、素子の少なくとも一つの面に配設された外部電極
を備えており、表裏や前後に方向性を有するセラミック
電子部品を製造するための方法であって、複数のセラミ
ック電子部品が取り出されることになる未焼成のマザー
ブロックを焼成するマザーブロック焼成工程と、前記マ
ザーブロック焼成工程において焼成されたマザーブロッ
クをスクライブ工法を用いてスクライブすることによ
り、マザーブロックの表面に所定方向に一次ブレーク溝
を形成するブレーク溝形成工程と、前記ブレーク溝形成
工程において形成された一次ブレーク溝に沿ってマザー
ブロックをブレークして複数のスティック状素子集合体
を形成するスティック状素子集合体形成工程と、前記ス
ティック状素子集合体形成工程において形成された各ス
ティック状素子集合体に外部電極を形成する外部電極形
成工程とを含むことを特徴としている。In order to achieve the above object, the inventors of the present application have conducted various experiments and examinations, and have found that a scribe method which is generally considered to be unsuitable for breaking a hard material is used. When using a break, surprisingly, it was possible to break a hard ceramic sintered body such as a mother block or a stick-like element assembly without chipping, cracking, chipping, etc., Further experiments were performed to complete the present invention. That is, the method for manufacturing a ceramic electronic component according to the first invention of the present application includes an external electrode provided on at least one surface of the element, and is used for manufacturing a ceramic electronic component having directionality in front, back, front and rear. A method, wherein a mother block firing step of firing an unfired mother block from which a plurality of ceramic electronic components are to be taken out, and scribing the mother block fired in the mother block firing step using a scribe method. Forming a primary break groove in a predetermined direction on the surface of the mother block, and breaking the mother block along the primary break groove formed in the break groove forming step to form a plurality of stick-shaped element assemblies. Forming a stick-like element assembly, and forming the stick-like element It is characterized in that it comprises an external electrode forming step of forming an external electrode on each stick-shaped element assemblies formed in the body formation step.

【００１０】上記製造方法においては、マザーブロック
を焼成した後、スクライブ工法を用いてスクライブする
ことにより、マザーブロックの表面に所定方向に一次ブ
レーク溝を形成し、この一次ブレーク溝に沿ってマザー
ブロックをブレークすることにより複数のスティック状
素子集合体を形成するようにしているので、ダイシング
法によりカットする場合に生じるようなエッジ部分での
チッピング、ワレ、カケ、シェルクラックなどを発生さ
せることなくマザーブロックをブレークしてスティック
状素子集合体を形成することが可能になる。したがっ
て、方向性のあるセラミック電子部品を、チッピング、
ワレ、カケなどによる歩留りの低下を招いたりすること
なく効率よく製造することが可能になる。なお、本願発
明の方法によれば、上述のように、スティック状素子集
合体の状態で外部電極を形成するようにしているので、
カット工程で各素子をばらばらの状態に切り離してその
後の焼成工程や外部電極形成工程などを進める方法に比
べて容易に所定の方向性を維持した状態で各工程を進め
ることができるようになる。また、各スティック状素子
集合体に外部電極を形成するようにしているので、外部
電極形成工程における素子（スティック状素子集合体）
の取り扱い（ハンドリング）が容易になる。さらに、素
子集合体をスティック状としているので、素子集合体の
保持が容易となり、また各素子（チップ）の整列も必要
がなくなる。その結果、製造工程及び製造設備を簡略化
して、コストダウンを図ることが可能になる。In the above manufacturing method, after the mother block is fired, a primary break groove is formed in a predetermined direction on the surface of the mother block by scribing using a scribing method, and the mother block is formed along the primary break groove. To form a plurality of stick-shaped element aggregates by breaking, so that the chip does not generate chipping, cracks, chips, shell cracks, etc. It becomes possible to form a stick-shaped element aggregate by breaking a block. Therefore, directional ceramic electronic components, chipping,
Efficient production can be achieved without lowering the yield due to cracks or chips. According to the method of the present invention, as described above, since the external electrodes are formed in the state of the stick-shaped element assembly,
In comparison with a method in which each element is separated into discrete states in a cutting step and a subsequent baking step, an external electrode forming step, or the like is performed, each step can be easily performed while maintaining a predetermined directionality. Also, since an external electrode is formed on each stick-shaped element assembly, an element (stick-shaped element assembly) in the external electrode forming step is formed.
Handling becomes easier. Further, since the element assembly is formed in a stick shape, it is easy to hold the element assembly, and it is not necessary to align each element (chip). As a result, the manufacturing process and the manufacturing equipment can be simplified, and the cost can be reduced.

【００１１】また、本願第２の発明のセラミック電子部
品の製造方法は、素子中に配設されたコイルと、素子の
少なくとも一つの面に配設された外部電極とを備えてお
り、表裏や前後に方向性を有する表面実装型のセラミッ
ク電子部品（積層コイル部品）を製造するための方法で
あって、複数のコイルパターンが配設されたグリーンシ
ートを積層して内部に積層型コイルが形成された未焼成
のマザーブロック（積層マザーブロック）を形成するマ
ザーブロック形成工程と、前記マザーブロック形成工程
において形成された積層マザーブロックを焼成するマザ
ーブロック焼成工程と、前記マザーブロック焼成工程に
おいて焼成されたマザーブロックをスクライブ工法を用
いてスクライブすることにより、マザーブロックの表面
に所定方向に一次ブレーク溝を形成するブレーク溝形成
工程と、前記ブレーク溝形成工程において形成された一
次ブレーク溝に沿ってマザーブロックをブレークして複
数のスティック状素子集合体を形成するスティック状素
子集合体形成工程と、前記スティック状素子集合体形成
工程において形成された各スティック状素子集合体に外
部電極を形成する外部電極工程とを含むことを特徴とし
ている。A method of manufacturing a ceramic electronic component according to a second aspect of the present invention includes a coil provided in an element and an external electrode provided on at least one surface of the element. A method for manufacturing a surface-mounted ceramic electronic component (laminated coil component) having directionality in the front and rear direction, wherein a laminated sheet is formed by laminating green sheets provided with a plurality of coil patterns. Mother block forming step of forming the obtained unfired mother block (laminated mother block), mother block firing step of firing the laminated mother block formed in the mother block forming step, and firing in the mother block firing step Scribing the mother block using the scribing method, the primary A break groove forming step of forming a rake groove, and a stick-shaped element aggregate forming step of forming a plurality of stick-shaped element aggregates by breaking a mother block along the primary break groove formed in the break groove forming step. And forming an external electrode on each stick-shaped element assembly formed in the stick-shaped element assembly forming step.

【００１２】この製造方法においては、複数のコイルパ
ターンが配設されたグリーンシートを積層して積層マザ
ーブロックを形成し、これを焼成した後、スクライブ工
法を用いてスクライブすることにより、積層マザーブロ
ックの表面に所定方向に一次ブレーク溝を形成し、この
一次ブレーク溝に沿って積層マザーブロックをブレーク
することにより複数のスティック状素子集合体を形成す
るようにしているので、上記本願第１の発明の場合と同
様に、チッピング、ワレ、カケなどを発生させることな
く、積層マザーブロックをブレークしてスティック状素
子集合体を形成することが可能になる。したがって、上
記本願第１の発明の場合と同様に効率よく表面実装型の
積層コイル部品を製造することが可能になる。In this manufacturing method, a laminated mother block is formed by laminating green sheets on which a plurality of coil patterns are arranged, firing the laminated mother block, and scribed using a scribing method. A primary break groove is formed in a predetermined direction on the surface of the device, and a plurality of stick-like element assemblies are formed by breaking the laminated mother block along the primary break groove. As in the case of (1), it is possible to form a stick-shaped element aggregate by breaking the laminated mother block without causing chipping, cracking, chipping, and the like. Therefore, similarly to the case of the first invention of the present application, it becomes possible to efficiently manufacture a surface-mounted laminated coil component.

【００１３】また、本願発明のセラミック電子部品の製
造方法は、前記ブレーク溝形成工程において、スクライ
ブ工法を用いてスクライブすることにより、一次ブレー
ク溝及び一次ブレーク溝と交差する二次ブレーク溝を形
成しておき、前記外部電極形成工程において外部電極を
形成した後、各スティック状素子集合体を外部電極の方
向性を保ちつつ、前記ブレーク溝形成工程において形成
された前記二次ブレーク溝に沿って複数に分割するステ
ィック状素子集合体分割工程をさらに含むことを特徴と
している。In the method for manufacturing a ceramic electronic component according to the present invention, in the break groove forming step, a primary break groove and a secondary break groove intersecting with the primary break groove are formed by scribing using a scribing method. After the external electrodes are formed in the external electrode forming step, a plurality of stick-shaped element assemblies are formed along the secondary break grooves formed in the break groove forming step while maintaining the directionality of the external electrodes. The method further comprises a step of dividing the stick-shaped element assembly into a plurality of pieces.

【００１４】ブレーク溝を形成する際に、スクライブ工
法を用いてスクライブすることにより、一次ブレーク溝
と交差する方向に二次ブレーク溝を形成しておき、一次
ブレークした後のスティック状素子集合体に外部電極を
形成した後、各スティック状素子集合体を外部電極の方
向性を保ちつつ二次ブレーク溝に沿って複数に分割する
ことにより、一次ブレーク及び二次ブレークのいずれの
工程でも、チッピング、ワレ、カケなどを引き起こすこ
となく効率よくセラミック電子部品を製造することが可
能になる。また、各スティック状素子集合体を外部電極
の方向性を保ちつつ、ブレーク溝形成工程において形成
された二次ブレーク溝に沿って複数に分割してその後の
工程を進めることにより、最終工程まで方向性を合わせ
ることが不要になり、さらに効率よくセラミック電子部
品を製造することができるようになる。なお、本願発明
のセラミック電子部品の製造方法において、スクライブ
工法に用いられるスクライバーのタイプや種類に特別の
制約はないが、好ましいスクライバーとしては、例え
ば、ダイヤモンドや超鋼からなる算盤玉状のスクライブ
チップを、一定の加圧力で基板に押し当てながら転がし
て、基板にブレークのための垂直クラックと歪みを発生
させる方式のスクライバー、あるいは、先端の尖がった
固定のスクライブチップを基板に押し当てながら移動さ
せて基板表面に引っ掻き傷をつける方式のスクライバー
などを挙げることができる。When forming a break groove, a scribing method is used to form a secondary break groove in a direction intersecting with the primary break groove, and the stick-like element assembly after the primary break is formed. After forming the external electrodes, each stick-shaped element assembly is divided into a plurality of pieces along the secondary break grooves while maintaining the directionality of the external electrodes, so that any of the steps of the primary break and the secondary break, chipping, It is possible to efficiently produce a ceramic electronic component without causing cracks or chips. In addition, while maintaining the directionality of the external electrodes, each stick-shaped element assembly is divided into a plurality of pieces along the secondary break grooves formed in the break groove forming step, and the subsequent steps are performed, so that the direction to the final step is achieved. It is no longer necessary to match the properties, and ceramic electronic components can be manufactured more efficiently. In the method of manufacturing a ceramic electronic component of the present invention, there is no particular restriction on the type and type of scriber used in the scribe method, but preferred scribers include, for example, an abacus ball-shaped scribe chip made of diamond or super steel. While pressing against the substrate with a constant pressing force, roll the scriber to generate vertical cracks and distortion for the break on the substrate, or press the fixed scribe chip with a sharp tip against the substrate A scriber of a type in which the substrate surface is moved to scratch the surface of the substrate may be used.

【００１５】[0015]

【発明の実施の形態】以下、本願発明の実施形態を図面
を参照しつつ説明し、本願発明の特徴とするところをさ
らに詳しく説明する。図１は本願発明の一実施形態にか
かるセラミック電子部品（表面実装型積層コイル部品）
の製造方法を示すフローチャート、図２はマザーブロッ
クにブレーク溝を形成した状態を示す斜視図、図３はス
ティック状素子集合体を形成した状態を示す斜視図、図
４はスティック状素子集合体に外部電極を形成した状態
を示す斜視図、図５はスティック状素子集合体をカット
して個々の素子に分割する工程を示す斜視図である。な
お、図２〜図５においては、コイルパターンを省略して
いる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described with reference to the drawings, and features of the present invention will be described in more detail. FIG. 1 is a ceramic electronic component (surface-mounted multilayer coil component) according to an embodiment of the present invention.
FIG. 2 is a perspective view showing a state in which a break groove is formed in the mother block, FIG. 3 is a perspective view showing a state in which a stick-shaped element assembly is formed, and FIG. FIG. 5 is a perspective view showing a state in which the external electrodes are formed, and FIG. 5 is a perspective view showing a step of cutting the stick-shaped element assembly and dividing it into individual elements. 2 to 5, the coil pattern is omitted.

【００１６】本実施形態にかかる表面実装型積層コイル
部品の製造方法においては、まず、セラミック原料から
グリーンシートを形成する。そして、このグリーンシー
トの表面に導電ペーストを印刷してコイルパターンを形
成する。それから、表面にコイルパターンが配設された
グリーンシートを積み重ねて、未焼成のマザーブロック
１を形成した後、これを所定の条件で焼成する。In the method for manufacturing a surface-mounted laminated coil component according to this embodiment, first, a green sheet is formed from a ceramic raw material. Then, a conductive paste is printed on the surface of the green sheet to form a coil pattern. Then, after stacking green sheets having a coil pattern disposed on the surface to form an unfired mother block 1, the green block is fired under predetermined conditions.

【００１７】次いで、焼成後のマザーブロック１にスク
ライブ工法を用いてマトリクス状にブレーク溝２，３を
形成する。具体的には、スクライバーにより、図２に一
点鎖線で示すように、マザーブロック１の列方向Ｘに沿
って複数の一次ブレーク溝２を、マザーブロック１の列
方向Ｘと直交する行方向Ｙに沿って二次ブレーク溝３を
それぞれ形成する。Next, break grooves 2 and 3 are formed in a matrix in the baked mother block 1 by using a scribe method. Specifically, as shown by a dashed line in FIG. 2, a plurality of primary break grooves 2 are formed by a scriber along a column direction X of the mother block 1 in a row direction Y orthogonal to the column direction X of the mother block 1. The secondary break grooves 3 are respectively formed along.

【００１８】そして、ブレーク溝２，３を形成したマザ
ーブロック１を、一次ブレーク溝２に沿ってブレーク
し、図３に示すようなスティック状（短冊状）の素子集
合体４を複数形成する。この場合、例えば、ローラブレ
ーク工法を用いることにより、ブレーク後のスティック
状素子集合体の、表裏、前後の配列をマザーブロックと
同様の状態にして仕上げることが可能であるため、得ら
れたスティック状素子集合体４の表裏や前後の方向性に
誤りが生じることを防止することが可能になり有利であ
る。The mother block 1 having the break grooves 2 and 3 is broken along the primary break grooves 2 to form a plurality of stick-like (strip-like) element assemblies 4 as shown in FIG. In this case, for example, by using the roller break method, it is possible to finish the stick-like element assembly after the break in the same state as the mother block with the front, back, front and rear arrangements. Advantageously, it is possible to prevent an error in the direction of the front and back and the front and rear of the element assembly 4.

【００１９】次いで、図４に示すように、各スティック
状素子集合体４の表面及び裏面側の長手方向に沿う端部
（縁部）及び両端面に導電ペーストを塗布して焼成した
後、その表面にメッキを施して外部電極５を形成する。
なお、外部電極５は、素子の構造に応じて、スティック
状素子集合体４の表面、裏面あるいは両端面のいずれか
一つ又は２つの面に形成するようにしてもよく、その具
体的な形成位置には特に制約はない。Then, as shown in FIG. 4, a conductive paste is applied to the ends (edges) and both end faces along the longitudinal direction of the front and back sides of each stick-shaped element assembly 4 and baked. The external electrodes 5 are formed by plating the surface.
The external electrode 5 may be formed on any one or two of the front surface, the back surface, and both end surfaces of the stick-shaped element assembly 4 depending on the structure of the element. There is no particular restriction on the position.

【００２０】それから、図５に示すように、各スティッ
ク状素子集合体４を外部電極５の方向性を保ちつつ二次
ブレーク溝３に沿って複数に分割してチップ化した後、
測定を行う。これにより、表面実装型積層コイル部品が
完成する。なお、二次ブレークと測定、さらに、この後
に続く出荷のためのテーピング工程を同時並行的に行な
うことにより、最終工程まで方向性を乱すことなく効率
よく製造作業を行なうことが可能になる。Then, as shown in FIG. 5, each stick-shaped element assembly 4 is divided into a plurality of chips along the secondary break grooves 3 while maintaining the directionality of the external electrodes 5, and then formed into chips.
Perform the measurement. Thereby, the surface mount type laminated coil component is completed. By performing the secondary break, the measurement, and the subsequent taping step for shipping at the same time, the manufacturing operation can be performed efficiently without disturbing the direction to the final step.

【００２１】したがって、上記実施形態の製造方法によ
れば、マザーブロック１を焼成した後、スクライブ工法
により列方向Ｘに沿って複数の一次ブレーク溝２を形成
し、行方向Ｙに沿って複数の二次ブレーク溝３を形成
し、スティック状素子集合体形成工程において一次ブレ
ーク溝２に沿ってマザーブロック１を分割し、スティッ
ク状素子集合体分割工程において二次ブレーク溝３に沿
ってスティック状素子集合体４を分割するようにしてい
るので、一次ブレーク及び二次ブレークのいずれの工程
でも、チッピング、ワレ、カケなどを引き起こすことな
くマザーブロック１及びスティック状素子集合体４を分
割することが可能になり、効率よくセラミック電子部品
を製造することができるという特有の効果を得ることが
できる。Therefore, according to the manufacturing method of the above embodiment, after firing the mother block 1, a plurality of primary break grooves 2 are formed along the column direction X by the scribe method, and a plurality of primary break grooves 2 are formed along the row direction Y. A secondary break groove 3 is formed, the mother block 1 is divided along the primary break groove 2 in a stick-like element assembly forming step, and a stick-like element is formed along the secondary break groove 3 in a stick-like element assembly division step. Since the assembly 4 is divided, the mother block 1 and the stick-shaped element assembly 4 can be divided without causing chipping, cracking, chipping, etc. in any of the primary break and the secondary break. And a unique effect that a ceramic electronic component can be manufactured efficiently can be obtained.

【００２２】また、上記実施形態の製造方法では、各一
次ブレーク溝２に沿ってマザーブロック１をブレークし
て複数のスティック状素子集合体４を形成した後、各ス
ティック状素子集合体４に外部電極５を形成するように
しているので、カット工程で各素子をばらばらにした状
態でその後の工程を進める方法に比べて、容易に方向性
を一致させたままで最終工程までの作業を進めることが
可能になる。また、製造設備の構造も簡単となるためコ
ストダウンを図ることが可能になる。さらに、各スティ
ック状素子集合体４に外部電極５を形成するようにして
いるので、外部電極形成工程でのスティック状素子集合
体４の取り扱い（ハンドリング）が容易になる。また、
素子集合体４をスティック状としているので、素子集合
体４の保持が容易となり、またチップの整列も必要がな
くなる結果、コストダウンを実現することができる。ま
た、スクライブ工法によりブレーク溝を形成する際に、
各一次ブレーク溝２と直交する行方向Ｙに沿って複数の
二次ブレーク溝３を形成しておき、二次ブレークと測定
やテーピングをドッキングすべく、各スティック状素子
集合体４を外部電極５の方向性を保ちつつ二次ブレーク
溝３に沿って複数に分割してチップ化し、測定やテーピ
ングを行うことにより、最終工程で素子の方向性を合わ
せるための手間が不要になり、本願発明をさらに実効あ
らしめることができる。Further, in the manufacturing method of the above embodiment, after the mother block 1 is broken along each primary break groove 2 to form a plurality of stick-shaped element assemblies 4, Since the electrodes 5 are formed, compared to a method in which each element is separated in the cutting step and the subsequent steps are performed, it is possible to easily proceed with the operation up to the final step while maintaining the same directionality. Will be possible. Further, since the structure of the manufacturing equipment is simplified, the cost can be reduced. Further, since the external electrodes 5 are formed on each of the stick-shaped element assemblies 4, handling (handling) of the stick-shaped element assemblies 4 in the external electrode forming step is facilitated. Also,
Since the element assembly 4 is formed in a stick shape, it is easy to hold the element assembly 4, and it is not necessary to arrange the chips. As a result, cost reduction can be realized. Also, when forming a break groove by the scribe method,
A plurality of secondary break grooves 3 are formed along a row direction Y orthogonal to each primary break groove 2, and each stick-shaped element assembly 4 is connected to an external electrode 5 in order to dock the secondary break and measurement or taping. By dividing into a plurality of chips along the secondary break groove 3 while maintaining the direction, and performing measurement and taping, it is not necessary to adjust the direction of the element in the final step. In addition, it can be effective.

【００２３】また、上記実施形態においては、表面実装
型積層コイル部品を製造する場合を例にとって説明した
が、本願発明のセラミック電子部品の製造方法は表面実
装型積層コイル部品に限らず、素子の表面に外部電極を
備え、表裏や前後に方向性を有する種々のセラミック電
子部品（積層セラミックコンデンサ、セラミック圧電部
品など）を製造する際にも適用することが可能である。
その場合、具体的には上記実施形態の場合と同様に、複
数のセラミック電子部品が取り出されることになる未焼
成のマザーブロックを焼成した後、マザーブロックの表
面に、スクライブ工法により所定方向にブレーク溝を形
成し、各ブレーク溝に沿ってマザーブロックをブレーク
して複数のスティック状素子集合体を形成すればよく、
その場合にも上記実施形態の場合と同様の効果が得られ
る。Further, in the above-described embodiment, the case of manufacturing a surface mount type laminated coil component has been described as an example. The present invention can also be applied to the production of various ceramic electronic components (multilayer ceramic capacitors, ceramic piezoelectric components, etc.) having external electrodes on the surface and having directionality on the front and back and front and back.
In this case, specifically, similarly to the above embodiment, after firing the unfired mother block from which a plurality of ceramic electronic components are to be taken out, the surface of the mother block is broken in a predetermined direction by a scribe method. A groove may be formed, and a mother block may be broken along each break groove to form a plurality of stick-shaped element aggregates.
In this case, the same effect as in the above embodiment can be obtained.

【００２４】本願発明は、さらにその他の点においても
上記実施形態に限定されるものではなく、マザーブロッ
クの具体的な形状、外部電極のパターン、一次ブレーク
溝及び二次ブレーク溝の形成位置、スクライブ工法によ
るブレーク溝の形成条件、用いるべきスクライバーの種
類などに関し、発明の要旨の範囲内において種々の応
用、変形を加えることが可能である。The present invention is not limited to the above-described embodiment in other respects. The specific shape of the mother block, the pattern of the external electrodes, the positions where the primary break grooves and the secondary break grooves are formed, the scribe With respect to the conditions for forming the break groove by the construction method, the type of scriber to be used, and the like, various applications and modifications can be made within the scope of the invention.

【００２５】[0025]

【発明の効果】上述のように、本願第１の発明は、マザ
ーブロックを焼成した後、スクライブ工法を用いてスク
ライブすることにより、マザーブロックの表面に所定方
向に一次ブレーク溝を形成し、この一次ブレーク溝に沿
ってマザーブロックをブレークすることにより複数のス
ティック状素子集合体を形成するようにしているので、
チッピング、ワレ、カケなどを発生させることなく、マ
ザーブロックをブレークしてスティック状素子集合体を
形成することが可能になる。したがって、方向性のある
セラミック電子部品を、チッピング、ワレ、カケなどに
よる歩留りの低下を招くことなく効率よく製造すること
ができる。As described above, the first invention of the present application forms a primary break groove in a predetermined direction on the surface of the mother block by firing the mother block and then scribing using a scribing method. Since a plurality of stick-like element assemblies are formed by breaking the mother block along the primary break groove,
It is possible to form a stick-shaped element assembly by breaking the mother block without causing chipping, cracking, chipping, and the like. Therefore, it is possible to efficiently manufacture a directional ceramic electronic component without lowering the yield due to chipping, cracking, chipping, and the like.

【００２６】また、本願第２の発明によれば、複数のコ
イルパターンが配設されたグリーンシートを積層して積
層マザーブロックを形成し、これを焼成した後、スクラ
イブ工法を用いてスクライブすることにより、積層マザ
ーブロックの表面に所定方向に一次ブレーク溝を形成
し、一次ブレーク溝に沿って積層マザーブロックをブレ
ークして複数のスティック状素子集合体を形成し、各ス
ティック状素子集合体に外部電極を形成するようにして
いるので、上記の本願第１の発明の場合と同様の効果が
得られ、方向性のある表面実装型積層コイル部品を、チ
ッピング、ワレ、カケなどによる歩留りの低下を招くこ
となく効率よく製造することが可能になる。According to the second aspect of the present invention, a green sheet on which a plurality of coil patterns are provided is laminated to form a laminated mother block, which is fired and then scribed using a scribe method. Thereby, a primary break groove is formed in a predetermined direction on the surface of the laminated mother block, and the laminated mother block is broken along the primary break groove to form a plurality of stick-shaped element aggregates. Since the electrodes are formed, the same effect as in the case of the first invention of the present application can be obtained, and the yield of the directional surface-mounted laminated coil component can be reduced by chipping, cracking, chipping, and the like. It becomes possible to manufacture efficiently without inviting.

【００２７】また、ブレーク溝を形成する際に、スクラ
イブ工法を用いてスクライブすることにより、一次ブレ
ーク溝と交差する方向に二次ブレーク溝を形成してお
き、一次ブレークした後のスティック状素子集合体に外
部電極を形成した後、各スティック状素子集合体を外部
電極の方向性を保ちつつ二次ブレーク溝に沿って複数に
分割することにより、一次ブレーク及び二次ブレークの
いずれの工程でも、チッピング、ワレ、カケなどを引き
起こすことなく効率よくセラミック電子部品を製造する
ことが可能になる。また、各スティック状素子集合体を
外部電極の方向性を保ちつつ、ブレーク溝形成工程にお
いて形成された二次ブレーク溝に沿って複数に分割して
その後の工程を進めることにより、最終工程まで方向性
を合わせることが不要になり、さらに効率よくセラミッ
ク電子部品を製造することができるようになり、本願発
明をより実効あらしめることができる。なお、本願発明
は、マザーブロックやスティック状素子集合体の分割工
程でのチッピング、ワレ、カケなどによる歩留りの低下
を招きやすい小型のセラミック電子部品の製造方法に適
用した場合に特に有意義である。When forming a break groove, scribing is performed by using a scribing method, so that a secondary break groove is formed in a direction intersecting with the primary break groove. After forming the external electrodes on the body, by dividing each stick-shaped element assembly into a plurality of pieces along the secondary break grooves while maintaining the directionality of the external electrodes, in any of the primary break and the secondary break, A ceramic electronic component can be efficiently manufactured without causing chipping, cracking, chipping, and the like. In addition, while maintaining the directionality of the external electrodes, each stick-shaped element assembly is divided into a plurality of pieces along the secondary break grooves formed in the break groove forming step, and the subsequent steps are performed, so that the direction to the final step is achieved. It is no longer necessary to match the properties, and ceramic electronic components can be manufactured more efficiently, and the present invention can be made more effective. The invention of the present application is particularly significant when applied to a method for manufacturing a small-sized ceramic electronic component which is likely to cause a reduction in yield due to chipping, cracking, chipping, and the like in a step of dividing a mother block or a stick-shaped element assembly.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本願発明の一実施形態にかかるセラミック電子
部品（表面実装型積層コイル部品）の製造方法を示すフ
ローチャートである。FIG. 1 is a flowchart illustrating a method for manufacturing a ceramic electronic component (surface-mounted multilayer coil component) according to an embodiment of the present invention.

【図２】本願発明の一実施形態にかかるセラミック電子
部品の製造方法において、マザーブロックにブレーク溝
を形成した状態を示す斜視図である。FIG. 2 is a perspective view showing a state in which a break groove is formed in a mother block in the method of manufacturing a ceramic electronic component according to one embodiment of the present invention.

【図３】本願発明の一実施形態にかかるセラミック電子
部品の製造方法において、スティック状素子集合体を形
成した状態を示す斜視図である。FIG. 3 is a perspective view showing a state in which a stick-shaped element assembly is formed in the method for manufacturing a ceramic electronic component according to one embodiment of the present invention.

【図４】本願発明の一実施形態にかかるセラミック電子
部品の製造方法において、スティック状素子集合体に外
部電極を形成した状態を示す斜視図である。FIG. 4 is a perspective view showing a state in which external electrodes are formed on a stick-shaped element assembly in the method for manufacturing a ceramic electronic component according to one embodiment of the present invention.

【図５】本願発明の一実施形態にかかるセラミック電子
部品の製造方法において、スティック状素子集合体をカ
ットして個々の素子に分割する工程を示す斜視図であ
る。FIG. 5 is a perspective view showing a step of cutting a stick-shaped element assembly and dividing the same into individual elements in the method for manufacturing a ceramic electronic component according to one embodiment of the present invention.

【図６】従来の表面実装型積層コイル部品の製造方法を
示すフローチャートである。FIG. 6 is a flowchart showing a conventional method for manufacturing a surface-mounted laminated coil component.

【図７】従来の表面実装型積層コイル部品の製造工程を
示す図である。FIG. 7 is a view showing a manufacturing process of a conventional surface mount type laminated coil component.

【図８】従来の表面実装型積層コイル部品の製造工程を
示す図である。FIG. 8 is a view showing a manufacturing process of a conventional surface-mounted laminated coil component.

【符号の説明】[Explanation of symbols]

１ マザーブロック ２ 一次ブレーク溝 ３ 二次ブレーク溝 ４ スティック状素子集合体 ５ 外部電極 DESCRIPTION OF SYMBOLS 1 Mother block 2 Primary break groove 3 Secondary break groove 4 Stick-shaped element assembly 5 External electrode

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】素子の少なくとも一つの面に配設された外
部電極を備えており、表裏や前後に方向性を有するセラ
ミック電子部品を製造するための方法であって、 複数のセラミック電子部品が取り出されることになる未
焼成のマザーブロックを焼成するマザーブロック焼成工
程と、 前記マザーブロック焼成工程において焼成されたマザー
ブロックをスクライブ工法を用いてスクライブすること
により、マザーブロックの表面に所定方向に一次ブレー
ク溝を形成するブレーク溝形成工程と、 前記ブレーク溝形成工程において形成された一次ブレー
ク溝に沿ってマザーブロックをブレークして複数のステ
ィック状素子集合体を形成するスティック状素子集合体
形成工程と、 前記スティック状素子集合体形成工程において形成され
た各スティック状素子集合体に外部電極を形成する外部
電極形成工程とを含むことを特徴とするセラミック電子
部品の製造方法。1. A method for manufacturing a ceramic electronic component having an external electrode disposed on at least one surface of an element and having a front-back, front-back, and front-back direction, comprising: A mother block firing step of firing an unfired mother block to be taken out, and scribing the mother block fired in the mother block firing step using a scribing method, thereby forming a primary surface in a predetermined direction on the surface of the mother block. A break groove forming step of forming a break groove; and a stick-like element aggregate forming step of forming a plurality of stick-like element aggregates by breaking a mother block along the primary break groove formed in the break groove forming step. Each of the sticks formed in the stick-shaped element assembly forming step Forming an external electrode on the element assembly. 【請求項２】素子中に配設されたコイルと、素子の少な
くとも一つの面に配設された外部電極とを備えており、
表裏や前後に方向性を有する表面実装型のセラミック電
子部品（積層コイル部品）を製造するための方法であっ
て、 複数のコイルパターンが配設されたグリーンシートを積
層して内部に積層型コイルが形成された未焼成のマザー
ブロック（積層マザーブロック）を形成するマザーブロ
ック形成工程と、 前記マザーブロック形成工程において形成された積層マ
ザーブロックを焼成するマザーブロック焼成工程と、 前記マザーブロック焼成工程において焼成されたマザー
ブロックをスクライブ工法を用いてスクライブすること
により、マザーブロックの表面に所定方向に一次ブレー
ク溝を形成するブレーク溝形成工程と、 前記ブレーク溝形成工程において形成された一次ブレー
ク溝に沿ってマザーブロックをブレークして複数のステ
ィック状素子集合体を形成するスティック状素子集合体
形成工程と、 前記スティック状素子集合体形成工程において形成され
た各スティック状素子集合体に外部電極を形成する外部
電極工程とを含むことを特徴とするセラミック電子部品
の製造方法。2. A device comprising: a coil disposed in an element; and an external electrode disposed on at least one surface of the element.
A method for manufacturing a surface-mounted ceramic electronic component (laminated coil component) having directionality in front and back and front and back, comprising: laminating green sheets on which a plurality of coil patterns are arranged; A mother block forming step of forming an unfired mother block (laminated mother block) on which is formed; a mother block firing step of firing the laminated mother block formed in the mother block forming step; and a mother block firing step. By scribing the fired mother block using a scribing method, a break groove forming step of forming a primary break groove in a predetermined direction on the surface of the mother block, along the primary break groove formed in the break groove forming step Break the mother block and make multiple sticks A stick-shaped element assembly forming step of forming a child assembly; and an external electrode step of forming an external electrode on each stick-shaped element assembly formed in the stick-shaped element assembly forming step. Manufacturing method of ceramic electronic components. 【請求項３】前記ブレーク溝形成工程において、スクラ
イブ工法を用いてスクライブすることにより、一次ブレ
ーク溝及び一次ブレーク溝と交差する二次ブレーク溝を
形成しておき、前記外部電極形成工程において外部電極
を形成した後、各スティック状素子集合体を外部電極の
方向性を保ちつつ、前記ブレーク溝形成工程において形
成された前記二次ブレーク溝に沿って複数に分割するス
ティック状素子集合体分割工程をさらに含むことを特徴
とする請求項１又は２記載のセラミック電子部品の製造
方法。3. In the step of forming a break groove, a primary break groove and a secondary break groove intersecting with the primary break groove are formed by scribing using a scribing method, and an external electrode is formed in the external electrode forming step. After forming, a stick-shaped element assembly dividing step of dividing each stick-shaped element assembly into a plurality of pieces along the secondary break groove formed in the break groove forming step while maintaining the directionality of the external electrode. The method for manufacturing a ceramic electronic component according to claim 1, further comprising: