JP5966821B2 - ガスバリア積層フィルム - Google Patents
ガスバリア積層フィルム Download PDFInfo
- Publication number
- JP5966821B2 JP5966821B2 JP2012216275A JP2012216275A JP5966821B2 JP 5966821 B2 JP5966821 B2 JP 5966821B2 JP 2012216275 A JP2012216275 A JP 2012216275A JP 2012216275 A JP2012216275 A JP 2012216275A JP 5966821 B2 JP5966821 B2 JP 5966821B2
- Authority
- JP
- Japan
- Prior art keywords
- gas barrier
- vapor deposition
- carboxyl group
- layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ヒドロキシエチルメタクリレート(HEMA)、メチルメタクリレート(MMA)、メタクリル酸(MAA)をモノマーとして共重合させて得られたアクリルポリオール(重量平均分子量10×103)を主剤とし、HDIヌレート型のイソシアネート系硬化剤を主剤のヒドロキシル基量に対して1当量配合したメチルエチルケトン5%溶液、及びヒドロキシエチルメタクリレート(HEMA)、メチルメタクリレート(MMA)、をモノマーとして共重合させて得られたアクリルポリオール(重量平均分子量10×103)を主剤とし、HDIヌレート型のイソシアネート系硬化剤を主剤のヒドロキシル基量に対して1当量配合したメチルエチルケトン5%溶液を調製した。
樹脂基材に、片面がコロナ処理された厚さ12μmの二軸延伸PETフィルム(東レフィルム加工、P60)を使用し、コロナ処理面にグラビアコート機を用い上記アンカーコート層溶液を塗工、乾燥後の厚みが0.17μmのアンカーコート層を積層した。
元素比O/Siが1.5になるように金属珪素粉末及び酸化珪素粉末を混合した材料に、金属スズ粉末を20重量%混合した蒸着材料、及び元素比O/Siが1.5になるように金属珪素粉末及び酸化珪素粉末を混合した材料を作製し、真空蒸着機を使用して、アンカーコート層の上に厚さ0.05μmの蒸着層を積層し、目的のガスバリア積層フィルムを作製した。
ヒドロキシエチルメタクリレート(HEMA)、メチルメタクリレート(MMA)、メタクリル酸(MAA)をモノマーとして共重合させて得られたアクリルポリオール(重量平均分子量10×103)を主剤とし、HDIヌレート型のイソシアネート系硬化剤を主剤のヒドロキシル基量に対して1当量配合したメチルエチルケトン5%溶液、及びポリアクリル酸(PAA)溶液、及びポリビニルアルコール(PVA)溶液を調製した。
グラビアコート機を使用して、蒸着層の上に上記オーバーコート層溶液を塗工、乾燥後の厚みが0.17μmのオーバーコート層を積層した。
実施例1〜4及び比較例1〜3のガスバリア積層フィルムについて、モダンコントロール社製の水蒸気透過度計(MOCON PERMATRAN−W 3/31)により、40℃−90%RH雰囲気下での水蒸気透過度(g/m2・day)を測定した。
蒸着層13が形成されたフィルムを10mm×10mm角に切り取り、X線光電子分光装置(ESCA)により、膜の組成分析を行った。Arイオンで蒸着膜の深さ方向に組成分析を3回以上繰り返し、その平均を求め、金属元素の含有率を算出した。
実施例1では、表1に示すように水蒸気透過度が1.0(g/m2・day)以下であった。それに対し、アンカーコート層にメタクリル酸(MAA)を添加しなかった比較例1では、水蒸気透過度が1.0(g/m2・day)を上回る結果となった。
12…アンカーコート層
13…蒸着層
21…オーバーコート層
31…接着剤層
32…ラミネート樹脂層
10、20、30…ガスバリア積層フィルム
Claims (6)
- 樹脂基材の少なくとも片面にアンカーコート層、蒸着層が順に積層されたガスバリア積層フィルムであって、
前記アンカーコート層が、ヒドロキシル基とカルボキシル基を含有するアクリルポリオールと分子内にイソシアネート基を少なくとも2個以上有するイソシアネート系化合物との複合物によって形成され、且つ、前記蒸着層が、金属珪素と酸化珪素とを含有した蒸着材料に、さらにアルミニウム、亜鉛、スズ、鉄から選ばれるいずれかの金属あるいは金属酸化物を含有した蒸着材料を蒸着させたものであることを特徴とするガスバリア積層フィルム。 - 前記アンカーコート層の、ヒドロキシル基とカルボキシル基を含有するアクリルポリオールについて、水酸基価が50mgKOH/g以上250mgKOH/g以下、酸価が5mgKOH/g以上50mgKOH/g以下であることを特徴とする請求項1に記載のガスバリア積層フィルム。
- 前記蒸着層に、アルミニウム、亜鉛、スズ、鉄から選ばれるいずれかの金属あるいは金属酸化物が含有されており、蒸着膜中にいずれかの金属元素が2 atm.%以上50 atm.%以下含有されてなることを特徴とする請求項1又は2に記載のガスバリア積層フィルム。
- さらに、オーバーコート層を積層し、該オーバーコート層が、ヒドロキシル基を有する水溶性高分子、あるいはカルボキシル基を有する水溶性高分子、あるいはヒドロキシル基とカルボキシル基を含有するアクリルポリオールのいずれかひとつによって形成されることを特徴とする請求項1乃至3のいずれか記載のガスバリア積層フィルム。
- 前記オーバーコート層に、カルボキシル基を含有する化合物が必須成分として含まれおり、カルボキシル基含有化合物に、ポリアクリル酸もしくはヒドロキシル基とカルボキシル基を含有するアクリルポリオールのいずれかひとつが含まれることを特徴とする請求項4に記載のガスバリア積層フィルム。
- 前記オーバーコート層が、分子内にイソシアネート基を少なくとも2個以上有するイソシアネート系化合物を含有することを特徴とする請求項4又は請求項5に記載のガスバリア積層フィルム。