JP5690947B2 - タッチパネル用粘着剤組成物、粘着フィルム及びタッチパネル - Google Patents
タッチパネル用粘着剤組成物、粘着フィルム及びタッチパネル Download PDFInfo
- Publication number
- JP5690947B2 JP5690947B2 JP2013538662A JP2013538662A JP5690947B2 JP 5690947 B2 JP5690947 B2 JP 5690947B2 JP 2013538662 A JP2013538662 A JP 2013538662A JP 2013538662 A JP2013538662 A JP 2013538662A JP 5690947 B2 JP5690947 B2 JP 5690947B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- sensitive adhesive
- pressure
- touch panel
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
以下、本発明に係る実施例及び本発明に係らない比較例により本発明をより詳しく説明するが、本発明の範囲は下記に提示した実施例によって制限されるものではない。
窒素ガスが還流され、温度調節が容易になるように冷却装置を設けた1L反応器に、エチルヘキシルアクリレート(EHA)55重量部;イソボルニルアクリレート(IBOA)20重量部;及び2−ヒドロキシエチルアクリレート(HEA)25重量部を投入して部分重合させることにより、粘度が3500cpsのシロップを得た。前記の部分重合されたアクリル系樹脂(A)の重量平均分子量は120万だった。
製造例1で製造された部分重合されたアクリル系樹脂(A)100重量部に対して、多官能性架橋剤であるヘキサンジオールジアクリレート0.2重量部、エポキシ系シランカップリング剤(KBM403、Shin-Etsu社(製))0.3重量部、ウレタンアクリレート1.5重量部及び光開始剤(Irgacure651、Ciba Specialty Chemicals社(製))0.3重量部を配合して粘着剤組成物を製造し、これにより粘度が1,500〜2,500cpsのコーティング液を製造した。次いで、製造されたコーティング液を離型処理されたポリエチレンテレフタレートフィルム(厚さ:75μm)に、UV硬化後の厚さが100μmになるようにバーコーターを用いてコーティングした。その後、UVランプを用いて紫外線を5分間照射して硬化させることにより粘着フィルムを製造した。
実施例及び比較例で製造された粘着フィルムから離型フィルムを除去し、前記粘着剤の一方の面にはハードコーティングされたポリカーボネート(PC)フィルムのハードコーティング面を付着し、粘着剤のもう一方の面には一方の面にITO層が形成されたポリエチレンテレフタレート(PET)フィルムのITO面が付着するように圧着して試片(PETフィルムのITO面/粘着剤/PCフィルムのハードコーティング面)を製造した。その後、前記試片を90℃及び90%RHの恒温恒湿条件で5日間放置し、気泡、浮き及び/又は剥離発生有無を観察して耐久性を下記基準で評価した。
○:浮き、剥離又は気泡の発生無し
△:浮き、剥離又は気泡の発生相当有り
×:浮き、剥離又は気泡の発生多く有り
Claims (17)
- 重量平均分子量が100万以上である、部分重合されたアクリル系樹脂;
ヘキサンジオールジ(メタ)アクリレート、トリメチロールプロパントリオキシエチルジ(メタ)アクリレート、アルキレングリコールジ(メタ)アクリレート、ジアルキレングリコールジ(メタ)アクリレート、トリアルキレングリコールジ(メタ)アクリレート、ジシクロペンテニルジ(メタ)アクリレート、ジシクロペンテニルオキシエチルジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、ジペンタエリトリトールヘキサジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート及びペンタエリトリトールトリ(メタ)アクリレートからなる群から選ばれる一つ以上である、多官能(メタ)アクリレートからなる多官能性架橋剤;
ハイドロカーボン系樹脂又はその水素添加物、ロジン樹脂又はその水素添加物、ロジンエステル樹脂又はその水素添加物、テルペン樹脂又はその水素添加物、テルペンフェノール樹脂又はその水素添加物、重合ロジン樹脂又は重合ロジンエステル樹脂からなる群から選ばれる一つ以上であり、上記のアクリル系樹脂100重量部に対して、1重量部〜100重量部である粘着性付与樹脂;
及びエポキシ系シランカップリング剤を含む、一方の面に導電層が形成されている電導性プラスチックフィルムの導電層に付着される粘着剤層に用いられるタッチパネル用粘着剤組成物。 - 部分重合されたアクリル系樹脂が、重合度が5%〜60%である、請求項1に記載のタッチパネル用粘着剤組成物。
- 部分重合されたアクリル系樹脂が、(メタ)アクリル酸エステル系単量体及び架橋性単量体を含む単量体混合物の重合体である、請求項1に記載のタッチパネル用粘着剤組成物。
- (メタ)アクリル酸エステル系単量体が、アルキル(メタ)アクリレートである、請求項3に記載のタッチパネル用粘着剤組成物。
- 架橋性単量体が、ヒドロキシル基含有単量体、カルボキシル基含有単量体又は窒素含有単量体である、請求項3に記載のタッチパネル用粘着剤組成物。
- 多官能性架橋剤が、部分重合されたアクリル系樹脂100重量部に対して、0.01重量部〜10重量部で含まれる、請求項1に記載のタッチパネル用粘着剤組成物。
- エポキシ系シランカップリング剤が、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルメチルジエトキシシラン、γ−グリシドキシプロピルトリエトキシシラン及び2−(3,4−エポキシシクロヘキシル)−エチルトリメトキシシランからなる群から選ばれた一つ以上である、請求項1に記載のタッチパネル用粘着剤組成物。
- エポキシ系シランカップリング剤が、部分重合されたアクリル系樹脂100重量部に対して、0.1重量部〜1.0重量部で含まれる、請求項1に記載のタッチパネル用粘着剤組成物。
- 光開始剤をさらに含む、請求項1に記載のタッチパネル用粘着剤組成物。
- 光開始剤が、ベンゾイン系開始剤、ヒドロキシケトン系開始剤又はアミノケトン系開始剤である、請求項9に記載のタッチパネル用粘着剤組成物。
- 基材フィルム;及び前記基材フィルムの一方の面又は両面に形成され、請求項1〜10のいずれか一項に記載の粘着剤組成物の硬化物を含む粘着剤層を含む、タッチパネル用粘着フィルム。
- 粘着剤層が、厚さが50μm〜300μmである、請求項11に記載のタッチパネル用粘着フィルム。
- 基材フィルムが、ポリエチレンテレフタレートフィルム、ポリテトラフルオロエチレンフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、ポリブテンフィルム、ポリブタジエンフィルム、塩化ビニル共重合体フィルム、ポリウレタンフィルム、エチレン−ビニルアセテートフィルム、エチレン−プロピレン共重合体フィルム、エチレン−アクリル酸エチル共重合体フィルム、エチレン−アクリル酸メチル共重合体フィルム及びポリイミドフィルムからなる群から選ばれた一つ以上である、請求項11に記載のタッチパネル用粘着フィルム。
- 基材フィルムが、厚さが25μm〜300μmである、請求項11に記載のタッチパネル用粘着フィルム。
- 粘着剤層上に離型フィルムをさらに含む、請求項11に記載のタッチパネル用粘着フィルム。
- 一方の面に導電層が形成されている電導性プラスチックフィルム;及び前記電導性プラスチックフィルムの導電層に付着されており、請求項1〜10のいずれか一項に記載の粘着剤組成物の硬化物を含む粘着剤層を含む、タッチパネル。
- 電導性プラスチックフィルムが、一方の面にITO層が形成されているポリエチレンテレフタレートフィルムである、請求項16に記載のタッチパネル。