JP4263403B2 - シリコン結晶化方法 - Google Patents
シリコン結晶化方法 Download PDFInfo
- Publication number
- JP4263403B2 JP4263403B2 JP2001399924A JP2001399924A JP4263403B2 JP 4263403 B2 JP4263403 B2 JP 4263403B2 JP 2001399924 A JP2001399924 A JP 2001399924A JP 2001399924 A JP2001399924 A JP 2001399924A JP 4263403 B2 JP4263403 B2 JP 4263403B2
- Authority
- JP
- Japan
- Prior art keywords
- mask
- laser beam
- silicon
- stage
- moving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の属する技術分野】
本発明は低温ポリシリコンを形成する装置と、その装置を利用したシリコン結晶化方法に関する。
【0002】
【従来の技術】
一般に、シリコンは状態によって非晶質シリコン(amorphous silicon)と結晶質シリコン(crystalline silicon)に分けることができる。
【0003】
前記非晶質シリコンは、低い温度で蒸着して薄膜(thin film)を形成することが可能であって、主に低い溶融点を有するガラスを基板に用いる液晶パネル(liquid crystal panel)のスイッチング素子(switching device)に多く用いる。
しかし、前記非晶質シリコン薄膜は、液晶パネル駆動素子の電気的特性と信頼性低下及び表示素子大面積化に難しさがある。
【0004】
大面積の液晶パネル映像駆動回路、一体型ラップトップコンピュータ(laptop computer)、壁掛けTV用液晶表示素子の商用化は優秀な電気的特性(例えば高い電界効果移動度(30cm2/VS)と高周波動作特性及び低い漏れ電流(leakage current)の画素駆動素子応用を要求しこれは高品位多結晶シリコン(poly crystalline silicon)の応用を要求している。
【0005】
特に、多結晶シリコン薄膜の電気的特性は結晶粒(grain)の大きさに大きく影響を受ける。すなわち、結晶粒の大きさが増加するによって電界効果移動度も一緒に増加する。
【0006】
したがって、このような点を考慮してシリコンを単結晶化する方法が大きな問題点として浮び上がっており、最近になってエネルギー源をレーザーとしてシリコン結晶の側面成長を誘導して巨大な単結晶シリコンを製造するSLS(sequential lateral solidification:連続的な側面固状化)技術が提案された。
【0007】
前記SLS技術は、シリコングレーンが液状シリコンと固状シリコンの境界面でその境界面に対して垂直方向に成長するという事実を利用したものであって、レーザーエネルギーの大きさとレーザービーム(laser beam)の照射範囲の移動を適切に調節してシリコングレーンを所定の長さだけ側面成長させることによって、非晶質シリコン薄膜を結晶化させるものである。
【0008】
このようなSLS技術を実現するためのSLS装置は図1に図示したとおりである。
【0009】
前記SLS装置32は、レーザービーム34を発生するレーザー発生装置36と、前記レーザー発生装置36を通して放出されたレーザービームを集束させる集束レンズ40と、サンプル44にレーザービームを分けて照射させるマスク38と、前記マスク38の下部に位置して前記マスクを通過したレーザービーム34を所定の比率で縮少する対物レンズ42とで構成される。
【0010】
前記レーザービーム発生装置36は、光源で加工されていないレーザービームを放出させて、減衰器(図示せず)を通過させてレーザービームのエネルギー大きさを調節して、前記集束レンズ40を通してレーザービーム34を照射する。
【0011】
前記マスク38に対応する位置には、非晶質シリコン薄膜が形成された基板44が固定されたX−Yステージ46が配置してある。
【0012】
この場合、従来においては前記レーザービーム発生装置36と前記マスク38は一定の位置に固定されている構造であるので、前記サンプル44の全領域を結晶化するためには前記X−Yステージ46をX方向及びY方向に微少に移動することによってサンプルの結晶領域を拡大していくことができる。
【0013】
前述した構成で、前記マスク38は前記レーザービームを通過させる透過領域である多数のスリットAと、レーザービームを吸収する前記スリットA間の領域である吸収領域Bに区分される。
【0014】
この時、前記マスクに構成されたスリットAの幅は、1次レーザービーム照射によって結晶化されるシリコン結晶のグレーンの大きさを決定し、前記スリットとスリットの間隔は側面成長したグレーンの大きさを決定する。
【0015】
前述したような従来のSLS結晶化装置を利用してシリコンを結晶化する方法を説明する。
【0016】
一般に、結晶質シリコンは、非晶質シリコン膜を蒸着した後にこれを利用して形成する。前記非晶質シリコン膜は一般に化学気相蒸着法(CVD)等を用いて基板に蒸着され、薄膜内に水素を多く含有している。
【0017】
前記水素は熱によって薄膜を離脱する特徴があるために、前記非晶質シリコン膜を1次で熱処理して脱水素化過程を経ることが必要である。
【0018】
なぜなら、水素を予め除去しない場合には結晶質シリコン薄膜の表面が非常に荒くなり電気的に特性がよくないためである。
【0019】
図2は脱水素化過程を経て一部分が結晶化された非晶質シリコン膜52が形成された基板44を示す。
【0020】
図示したような、レーザービームを利用した結晶化は基板44の全面積を同時に結晶化できない。
【0021】
なぜなら、レーザービームのビーム幅とマスク(図1の38)の大きさが制限されているために基板が大面積になるほど基板の上に前記一つのマスク(図1の38)を何度も配列して、その度ごとに結晶化過程を繰り返すことによって結晶化がなされる。
【0022】
この時、前記単一マスクに対応する面積Cだけ結晶化された領域を1ブロック(Block)と定義すれば、前記1ブロック内の結晶化は多次のレーザービーム照射を通してなされる。
【0023】
以下、図3Aないし図3Cを参照して非晶質シリコン膜の結晶化工程を説明する。
【0024】
図3Aないし図3Cは、従来のSLS装置を利用した非晶質シリコン薄膜の結晶化過程を順序どおり図示した平面図である。(ここでは、図2について説明した1ブロック単位の結晶化の例を挙げて説明する。また、前記マスクには3個のスリットが形成されていると仮定する。)
【0025】
図3Aはレーザービームを1次照射した場合、非晶質シリコンが結晶質シリコンに結晶化された段階を図示した図面である。
【0026】
まず、非晶質シリコン薄膜52の上部に位置した前記マスク(図1の38)を通してレーザービームを1次照射する。この時、照射されたレーザービームは前記マスクに構成された多数のスリット(図1のA)によって分けられて部分的(D、E、F)に非晶質シリコン薄膜52を溶かし液状化する。この場合、前記レーザーエネルギーの程度は前記非晶質シリコン薄膜が完全に溶ける程度の高エネルギー領域帯を用いる。
【0027】
前記のようにして完全にメルティングされて液状化されたシリコンは、レーザービームの照射が終わると非晶質シリコン領域と液状化されたシリコン領域の界面56でシリコングレーン58aの側面成長が進められる。グレーンの側面成長は前記界面56に対して垂直に起きる。
【0028】
結果的に、前記マスク(図1の38)に構成したスリット(図1のA)の数だけ1ブロック内に部分的に結晶化された領域D、E、Fが発生する。
【0029】
次に、図3Bはレーザービームを2次照射して、グレーンが成長した様子を図示した図面である。
【0030】
前記1次レーザービーム照射後に、前記X−Yステージ(図1の46)をグレーンの側面成長の長さと同じか小さく数μm移動した後、再び2次レーザービーム照射を実施する。前記2次照射されたレーザービームに触れたシリコン部分は液状化された後再び結晶化される。
【0031】
この時、1次照の射結果により形成された多結晶シリコン領域のシリコングレーン58aがシード(Seed)として働いて、シリコン熔融領域にグレーンの側面成長がなされる。
【0032】
2次照射が終わった後のシリコン結晶58bは、1次照射によって成長したグレーン58aに連続してさらに側面成長する。
【0033】
したがって、前述したような工程を多数繰り返して図3Cに示したように1ブロックに該当する非晶質薄膜を結晶質シリコン薄膜58cに形成することができる。
【0034】
また、前記ブロック単位の結晶化工程を繰り返して、大きな面積の非晶質薄膜を結晶質薄膜に形成することができる。
【0035】
【発明が解決しようとする課題】
しかし、前述したようなSLS装置の大きな短所は、第一に、前記マスクのスリットを通してレーザビームを照射する方法でなされる結晶化は、数μmから最大限数mm水準の微少な領域を動きながら結晶の成長を誘導するために、前記X−Yステージが比較的に大きな装備では移動距離の円滑な制御がむずかしい。
【0036】
第二に、前記X−Yステージが移動して完全に停止する時までの時間が通常0.1秒から1秒程度かかる。したがってステージが大きくなるほど、また、液晶パネルが大面積であるほどこのようなステージ移動に必要とされる総時間は益々長くなる。したがって、生産収率が著しく低下する。
【0037】
このような問題を解決するための本発明は、前記X−Yステージに比べてその動きがはるかに速くて、微少距離を移動することに有利な小規模のマスク移動ステージを設けて、1ブロック内の結晶化を進める場合には基板を動かさないでマスクを動かす方法を用いる。
【0038】
このようにすると、結晶質シリコン薄膜を製作することにかかる時間を短縮できて、移動距離の制御が円滑になる。
【0039】
したがって、本発明は前記従来のSLS装置を改善する方法で素子を製作する時間を節減して生産性を改善することを目的にする。
【0040】
【課題を解決するための手段】
前述したような目的を達成するためのSLS結晶化装置は、レーザービームを生成するレーザー発生装置と;前記レーザー発生装置に対応する位置に配置されており、固定された基板をX方向またはY方向に動かすX−Yステージと;前記X−Yステージと前記レーザー発生装置間に位置して、レーザービームを通過させる多数のスリットを含むマスクと;前記マスクを通過したレーザービームを所定の比率で縮少する対物レンズと;前記マスクと連結されて、マスクを微少に動かすマスク移動ステージとを含む。
【0041】
本発明の特徴によるポリシリコン結晶化方法は、非晶質シリコン薄膜が蒸着された基板を準備する段階と;前記基板をSLS装置に装着する際に、レーザー発生装置と前記レーザー発生装置に対応する位置に配置されており、X方向またはY方向に動くX−Yステージと、前記X−Yステージと前記レーザー発生装置間に位置して光を通過させる多数のスリット状の透過領域を有するマスクと、前記マスクと連結されてマスクを微少に動かすマスク移動ステージで構成されたSLS結晶化装置の構成において前記X−Yステージに前記基板を固定する段階と;前記マスクに構成された多数のスリットを通して、前記基板にレーザビームを照射する段階と;前記非晶質シリコン薄膜中前記スリットの位置に該当する多数の微少領域が完全に溶けてから固状化されて第1次シリコン結晶に結晶化される段階と;前記マスク移動ステージを利用してマスクを微少な距離だけ移動した後レーザビームを照射して、前記第1シリコン結晶に近接した非晶質シリコンを液状化する段階と;前記液状シリコンが固状化されながら前記第1シリコン結晶のグレーンが連続して側面成長する段階と;前記多数の微少領域で各々側面成長したグレーンとグレーンが衝突して成長が止まった後に、前記X−Yステージで前記基板を移動して、前記基板中結晶化されていない非晶質薄膜領域を前記マスクの下部に整列させる段階を含む。
【0042】
この時、前記グレーンの側面成長は、レーザビームを照射して結晶化する工程を何度も繰り返すことにより達成される。
【0043】
また、前記マスク移動ステージは、前記1次レーザービーム照射で結晶化されたグレーンの大きさと同じか小さな距離で前記マスクを移動することを特徴とする。
さらに、前記マスクの移動距離は数μmであることを特徴とする。
【0044】
【発明の実施の形態】
以下、添付した図面を参照して本発明によるSLS結晶化装置と、これを利用したポリシリコン結晶化方法を以下の実施例を通して詳細に説明する。
【0045】
−−実施例−
図4は、本発明によるSLS装置を図示した概略的な断面図である。
図示したように、本発明による結晶化装置はレーザービーム134を生成するレーザー発生装置136と、前記レーザー装置を通して放出されたレーザービームを集束させる集束レンズ140と、レーザービームをスリットAを通して分けるマスク138と、前記マスク138の下部に位置して前記マスクを通過したレーザービーム134を所定の比率で縮少する対物レンズ142とを含む。
【0046】
また、前記マスク138に対応される位置には非晶質シリコン薄膜が形成された基板144が固定されたX−Yステージ146が配置されている。
【0047】
この場合、本発明によるSLS装置は、マスク移動ステージ160をさらに含む。前記マスク138は所定の方法でマスク移動ステージ160に固定され、前記マスク移動ステージ160の制御によって数μmの微少な距離を移動できる。前記移動ステージ160はその移動範囲が小さいために移動して止まる時間が前記X−Yステージに比べて著しく小さな特徴がある。
【0048】
したがって、非晶質シリコン薄膜をブロック単位で結晶化する過程で、1ブロック内でのレーザービームの微少距離移動は前記マスクステージ(図4の160)を利用したマスクの動きによって制御する。すなわち、1ブロック内でレーザービームが照射される領域をサンプルの動きでないマスク138の動きで定義する。
【0049】
この時、前記マスクステージ160の動きの範囲は限定されているために、基板の結晶領域をブロック単位で動かす場合にのみ前記X−Yステージ146を用いる。
【0050】
このようにすると、前記X−Yステージのみを用いた時より薄膜を結晶化するのに要する時間を著しく短縮できる。
【0051】
以下、図5Aないし図5Fを参照して本発明によるSLS装置を利用したシリコン結晶化工程を説明する。(図5Aないし図5Fは1ブロック単位の結晶化の例を挙げて説明する。)
【0052】
図5A及び図5Fに図示したように、非晶質シリコン膜143が蒸着された基板144をX−Yステージ160に固定した後、前記マスク138の上部からレーザービーム134を照射する。
【0053】
前記レーザービーム134は、前記マスクに構成された多数のスリットAを通して分けられて、図5Bのように1ブロック内の非晶質シリコン薄膜を部分的(G、H、I)に溶かして液状シリコン状態にする。
【0054】
レーザービーム照射を止めると、液状シリコンは急速に冷却されながら非晶質シリコンと液状シリコンの境界150でグレーン148aが成長するようになる。この時グレーン148aの大きさは前記スリットAの幅によって制御できる。
【0055】
次に、マスクステージ160を利用して、前記マスク138を前記グレーンの幅と同じか小さな距離に該当する数μmだけ移動する。
【0056】
このようにすれば図5C及び図5Dに図示したように、前記マスクのスリットAは前記非晶質シリコン薄膜中の結晶化された領域G、H、Iに近接する領域に位置するようになって、まるで基板144を動かした場合と同じ結果を得ることができる。
【0057】
前記のように微少な距離だけ動かしたマスク138にレーザビームを照射すれば、前記レーザービームはマスクの移動に伴って動いたスリットを通過して1次照射時の結晶領域の一部とこれに近接した領域の非晶質シリコン膜を溶かすようになる。
【0058】
また再びレーザービーム照射を止めると、前記第1照射時に形成したグレーン(図5Bの148a)がシードとして働いて図5Dのように側面成長した結晶148bを得ることができる。
【0059】
前述したような工程を繰り返して図5E及び図5Fに図示したように1ブロックのシリコン結晶成長を完了する。
【0060】
この場合、前記各領域G、H、Iで側面成長したグレーンが相互衝突してグレーンの成長は止まるようになる。したがってグレーンの大きさは前記マスクに構成されたスリット間の間隔で制御できる。
【0061】
次に、任意の1ブロックの結晶化がすべて終われば、シリコンの結晶成長がなされていない次のブロックの結晶成長工程を始める。
【0062】
この際、前記ブロック間の移動については、前記マスクステージ(図4の160)より移動距離が大きなX−Yステージ146をX軸またはY軸に移動して結晶化工程を進ればよい。
【0063】
【発明の効果】
本発明によるSLSシリコン結晶化装置は、大きさが小さくて微少距離制御が円滑なマスク移動ステージをさらに追加することによって、規模が大きなX−Yステージを用いる場合より移動して停止させる時間が短くて工程時間を短縮できる効果がある。
また、工程時間が短縮されるので大面積を結晶化することが可能である。
【図面の簡単な説明】
【図1】従来のSLS結晶化装置を概略的に図示した図である。
【図2】従来のSLS装置によって部分的に結晶化が進められた非晶質シリコン薄膜が蒸着された基板を図示した図である。
【図3A】従来のSLS装置を利用して、非晶質シリコン薄膜を結晶質シリコン薄膜に結晶化する過程を図示した図である。
【図3B】従来のSLS装置を利用して、非晶質シリコン薄膜を結晶質シリコン薄膜に結晶化する過程を図示した図である。
【図3C】従来のSLS装置を利用して、非晶質シリコン薄膜を結晶質シリコン薄膜に結晶化する過程を図示した図である。
【図4】本発明によるSLS結晶化装置を概略的に図示した図である。
【図5】(A)〜(F)は、本発明によるSLS結晶化装置を利用して、非晶質シリコン薄膜を結晶質シリコン薄膜に結晶化する過程を図示した図である。
【符号の説明】
132:SLS装置
136:レーザー装置
138:マスク
140:集束レンズ
142:対物レンズ
144:サンプル
146:X−Yステージ
160:マスク移動ステージ
Claims (6)
- レーザビームを生成するレーザ発生装置と、前記レーザ発生装置に対応する位置に配置されたX方向またはY方向に動くX−Yステージと、前記X−Yステージと前記レーザ発生装置間に位置してレーザビームを通過させる多数のスリットを含むマスクと、前記マスクを通過したレーザビームを所定の比率で縮少する対物レンズと、前記マスクと連結されてマスクを微少に動かすマスク移動ステージを含むSLS結晶化装置によるシリコン結晶化方法であって、
非晶質シリコン薄膜が蒸着された基板を準備する段階と;
前記X−Yステージに前記基板を固定する段階と;
前記マスクに構成された多数のスリットを通して、前記基板にレーザビームを照射する段階と;
前記非晶質シリコン薄膜中の前記スリットの位置に対応する多数の微少領域が完全溶けてから固状化されて第1次シリコン結晶に結晶化される段階と;
前記マスク移動ステージを利用してマスクを微少な距離だけ移動した後にレーザビームを照射して、前記第1シリコン結晶に近接した非晶質シリコンを液状化する段階と;
前記液状シリコンが、固状化されながら前記第1シリコン結晶のグレーンに連続して側面成長する段階と;
前記多数の微少領域で各々側面成長したグレーンとグレーンが衝突して成長が止まった時点で、前記X−Yステージの前記基板を移動して、前記基板中の結晶化されていない非晶質薄膜領域を前記マスクの下部に整列する段階とを含むことを特徴とするシリコン結晶化方法。 - 前記グレーンの側面成長は、レーザビームを照射して結晶化する工程を何度も繰り返すことにより生じさせることを特徴とする請求項1に記載のシリコン結晶化方法。
- 前記マスク移動ステージは、前記1次レーザビーム照射で結晶化されたグレーンの大きさと同じか小さな距離で前記マスクを移動することを特徴とする請求項1に記載のシリコン結晶化方法。
- 該SLS結晶化装置は、該マスクと該レーザ発生装置との間に配置された集束レンズをさらに含み、前記集束レンズは、レーザ装置を通して放出されたレーザビームを集束させることを特徴とする請求項1に記載のシリコン結晶化方法。
- 前記X−Yステージの移動距離は、前記マスクの移動距離より大きいことを特徴とする請求項1に記載のシリコン結晶化方法。
- 前記マスクの移動距離は、前記グレーンの側面成長の幅と同じか小さな距離であることを特徴とする請求項5に記載のシリコン結晶化方法。