JP2003003212A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2003003212A5 JP2003003212A5 JP2001187862A JP2001187862A JP2003003212A5 JP 2003003212 A5 JP2003003212 A5 JP 2003003212A5 JP 2001187862 A JP2001187862 A JP 2001187862A JP 2001187862 A JP2001187862 A JP 2001187862A JP 2003003212 A5 JP2003003212 A5 JP 2003003212A5
- Authority
- JP
- Japan
- Prior art keywords
- soaking
- content
- slab
- pipe
- following formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
【請求項２】
質量％で、Ｃｒ含有量を１０〜２０％、不純物であるＳおよびＰの含有量をそれぞれ０．０５０％以下とし、さらに下記（ａ）式に含まれる成分を適宜含有し、１１００℃以上で均熱する時間（Ｈｒ）の総和がΣｔ１である鋳片、または鋼片を製管用素材として、この素材を１１００℃以上で均熱する時間（Ｈｒ）の総和をΣｔ２とした後、加熱温度Ｔを１１００〜１３００℃（ただし、１２００℃を除く）とし、下記（ｃ）式を満足するように製管することを特徴とする高Ｃｒ系継目無鋼管の製造方法。
【数１】
質量％で、Ｃｒ含有量を１０〜２０％、不純物であるＳおよびＰの含有量をそれぞれ０．０５０％以下とし、さらに下記（ａ）式に含まれる成分を適宜含有し、１１００℃以上で均熱する時間（Ｈｒ）の総和がΣｔ１である鋳片、または鋼片を製管用素材として、この素材を１１００℃以上で均熱する時間（Ｈｒ）の総和をΣｔ２とした後、加熱温度Ｔを１１００〜１３００℃（ただし、１２００℃を除く）とし、下記（ｃ）式を満足するように製管することを特徴とする高Ｃｒ系継目無鋼管の製造方法。
【数１】
本発明は、上記の知見に基づいて完成されたものであり、下記（１）、（２）の高Ｃｒ系継目無鋼管の製造方法を要旨としている。
（１）質量％で、Ｃｒ含有量を１０〜２０％、不純物であるＳおよびＰの含有量をそれぞれ０．０５０％以下とし、さらに下記（ａ）式に含まれる成分を適宜含有し、１１００℃以上で均熱する時間（Ｈｒ）の総和がΣｔ１である鋳片、または鋼片を製管用素材として、この素材を１１００℃以上で均熱する時間（Ｈｒ）の総和をΣｔ２とした後、加熱温度Ｔを１２００℃とし、下記（ｂ）式を満足するように製管することを特徴とする高Ｃｒ系継目無鋼管の製造方法である。
（２）上記（１）と同様に、Ｃｒ含有量を１０〜２０％、不純物であるＳおよびＰの含有量を０．０５０％以下とし、さらに上記（ａ）式に含まれる成分を適宜含有し、１１００℃以上で均熱する時間（Ｈｒ）の総和がΣｔ１である鋳片、または鋼片を製管用素材として、この素材を１１００℃以上で均熱する時間（Ｈｒ）の総和をΣｔ２とした後、加熱温度Ｔを１１００〜１３００℃（ただし、１２００℃を除く）とし、下記（ｃ）式を満足するように製管することを特徴とする高Ｃｒ系継目無鋼管の製造方法である。
（１）質量％で、Ｃｒ含有量を１０〜２０％、不純物であるＳおよびＰの含有量をそれぞれ０．０５０％以下とし、さらに下記（ａ）式に含まれる成分を適宜含有し、１１００℃以上で均熱する時間（Ｈｒ）の総和がΣｔ１である鋳片、または鋼片を製管用素材として、この素材を１１００℃以上で均熱する時間（Ｈｒ）の総和をΣｔ２とした後、加熱温度Ｔを１２００℃とし、下記（ｂ）式を満足するように製管することを特徴とする高Ｃｒ系継目無鋼管の製造方法である。