CN1701106A - 电磁屏蔽膜用压敏粘合剂组合物及使用该组合物的电磁屏蔽滤波器 - Google Patents
电磁屏蔽膜用压敏粘合剂组合物及使用该组合物的电磁屏蔽滤波器 Download PDFInfo
- Publication number
- CN1701106A CN1701106A CNA2004800008243A CN200480000824A CN1701106A CN 1701106 A CN1701106 A CN 1701106A CN A2004800008243 A CNA2004800008243 A CN A2004800008243A CN 200480000824 A CN200480000824 A CN 200480000824A CN 1701106 A CN1701106 A CN 1701106A
- Authority
- CN
- China
- Prior art keywords
- methyl
- adhesive composition
- shielding film
- electromagnetic shielding
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及电磁屏蔽膜用粘合剂组合物和使用这种粘合剂组合物的电磁屏蔽滤波器,更具体地,本发明涉及电磁屏蔽膜用粘合剂组合物,其包括:a)i)具有C1-C12烷基的(甲基)丙烯酸酯单体和ii)具有羟基的乙烯单体的丙烯酸系共聚物;和b)多官能基异氰酸酯交联剂。由于使用没有酸性基团的丙烯酸系粘合剂组合物进行透明化从而防止了铜的氧化,本发明的电磁屏蔽滤波器提供了良好的耐久性。
Description
技术领域
本发明涉及电磁屏蔽膜用粘合剂组合物和使用该粘合剂组合物的电磁屏蔽滤波器,特别是涉及电磁屏蔽膜用粘合剂组合物和使用该粘合剂组合物的电磁屏蔽滤波器,其中粘合剂不含酸性基团以防止铜的氧化,从而使其具有优异的耐久性。
背景技术
近来,随着对数字电视和高质量宽屏电视的兴趣增加,正在积极进行阴极射线管(CRT)、液晶显示器(LCD)、和等离子显示器(PDP)的开发。
广泛用作TV显示器的CRT在分辨率和图像质量方面有优势。然而,由于尺寸和重量,它们不适合于40英寸或更大的宽屏幕。
LCD在能耗和驱动电压方面有优势,但是难以将它们制成宽屏幕,并受视角的限制。
PDP可制成约60英寸的宽屏幕。当制造PDP器件时,在底板上形成分隔屏障(partitioned barrier)并在屏障上形成红色、绿色、和蓝色的磷光体层。然后用顶板覆盖底板,使得底板的电极与顶板的电极彼此平行相对。然后,向其中注入放电气体并密封器件。当气体放电时,自等离子体辐射光,用于传送图像,屏障将各个单元室分隔开。
PDP器件分为直流型(DC)和交流型(AC)。在DC器件者,电极暴露于放电区域,而在AC器件中,在电极上形成介质玻璃层。
参考图1,一般的PDP包括外壳11,覆盖所述外壳11的罩15、位于所述外壳11中的驱动电路板12、面板组件13、和电磁屏蔽滤波器14。所述电磁屏蔽滤波器14被由导电材料制成的导电膜覆盖,其位于玻璃板上,提供通过罩15到达外壳11的接地路径(grounding path)。也就是说,从面板组件13产生的电磁波通过电磁屏蔽滤波器14的导电膜在到达用户之前到达罩15和外壳11。为此,电磁屏蔽滤波器14的导电膜与罩15和外壳11是电连接的。
除了屏蔽电磁波之外,所述电磁屏蔽滤波器屏蔽近红外线、保护面板免受外部冲击、改善彩色分辨率、防止反射和增强对比度。
以前,广泛使用满足工业A类标准(表面电阻<2.5Ω/□)的透明导电膜如Ag多层淀积膜制造用于等离子显示器的电磁屏蔽滤波器膜。但是近来,随着对家用等离子显示器的需要的增加,正在广泛使用满足B类标准(表面电阻<1.5Ω/□)的铜蚀刻网格(mesh)或导电纤维网格,其中通过无电镀法将铜或镍涂覆在聚酯纤维上。
通常,通过使用透明的粘合剂对聚对苯二甲酸乙二醇酯衬底施用厚度为约10μm的铜箔并将其蚀刻为节距(pitch)≈300μm和行距(linewidth)≈10μm,制造网格型电磁屏蔽膜。
当将这种电磁屏蔽膜与功能膜如抗反射膜层压时,由于铜箔网格在两个膜之间形成缝隙。然后,由于空气和聚合物层的折射率不同,等离子显示器发出的光被散射,从而降低可见度。因此,应该通过称为透明化(transparentization)的工艺除去缝隙。
对于透明化,已经发展了使用热熔性树脂的方法(日本专利公开Hei 9-258378)、使用粘合剂的方法、填充流体树脂的方法(美国专利6,197,408)等等。这其中,最简单和广泛使用的方法为使用粘合剂的方法,通过这种方法可通过施加压力而无需额外工艺实现透明化。在使用粘合剂的透明化中,电磁屏蔽滤波器的耐久性主要取决于粘合剂的组分。
通常,广泛使用橡胶、丙烯酰基粘合剂(acryl)、和有机硅(silicone)作为粘合剂。这其中,由于不同的熔化性质,丙烯酸系粘合剂最普遍用于制备功能性粘合剂组合物。当在常温下轻微地加压时,一般的丙烯酸系粘合剂都具有优异的粘合性。这是因为构成粘合剂的聚合物分子为液体并对压力敏感。
由于各个功能性膜的作用,电磁屏蔽滤波器提供具有良好分辨率的颜色和图像质量。如果在使用过程中滤波器变色,则其不能提供良好的分辨率和图像质量。因此,在耐久性试验前后的透射率和颜色应该没有变化。特别是,由于铜网格在高温和高湿度条件下的氧化引起的变色是严重的问题。
粘合剂在其与铜网格接触的区域的耐久性是一个问题。在中性状态时,铜为红色,但当其被氧化时由于Cu2+而变为蓝色。因此,使透明化的粘合剂变色的原因是铜的氧化。
在广泛使用的丙烯酸系粘合剂组合物中,使用几种官能团来交联粘合剂。具体地,当使用具有酸性基团(-COOH)的单体时,酸性基团(-COOH)在高温和高湿度条件下使铜氧化,从而使电磁屏蔽滤波器变色和颜色分辨率降低。
附图说明
图1表示等离子显示器的结构。
图2a和图2b表示在透明化前后的电磁屏蔽膜的剖视图。
图3表示等离子显示器的电磁屏蔽滤波器的剖视图。
图4a到图4d表示实施例1到实施例3和比较例1在耐久性试验前后的透射率测量结果。
*附图中主要部件的符号说明*
11---外壳 12---驱动电路板 13---面板组件 14---电磁屏蔽滤波器15---罩 21,31---透明衬底 22,32---粘合剂层 23,33---铜箔层 24,34---黑色屏幕 25,35---粘合剂 26,36---透明衬底 27,37---强化玻璃 38---颜色校正层 39---近红外线屏蔽层 40---近红外线屏蔽层
[技术问题]
本发明的目的是提供通过防止铜的氧化而具有优异耐久性的电磁屏蔽膜用粘合剂组合物,和使用这种粘合剂组合物的电磁屏蔽滤波器。
[技术方案]
为实现所述目的,本发明提供了电磁屏蔽膜用丙烯酸系粘合剂组合物,其包括:
a)i)具有C1-C12烷基的(甲基)丙烯酸酯单体和ii)具有羟基的乙烯单体(vinylic monomer)的丙烯酸系共聚物;和
b)多功能异氰酸酯交联剂。
本发明还提供用于等离子显示器的电磁屏蔽滤波器,其使用了所述电磁屏蔽膜用丙烯酸系粘合剂组合物。
[有益效果]
因为本发明的电磁屏蔽滤波器使用没有酸性基团的丙烯酸系粘合剂组合物被透明化,防止了铜的氧化,这改善了耐久性并防止电磁屏蔽滤波器的变色。
[最佳方式]
以下参考附图更详细地描述本发明。
如图2a所示,在透明化之前电磁屏蔽膜从上到下包括铜箔层23、黑色屏幕层24、粘合剂层25和透明衬底层26。当在将透明衬底21如抗反射膜粘到铜箔23上时,形成空气层。空气层与用聚合物膜制成的透明衬底21之间折射率的不同使由等离子显示器发出的光发生散射,从而降低可见度。
因此,如图2所示,使用交联剂、UV或EB对粘合剂组合物进行交联,从而除去空气层。这种除去空气层的工艺称为透明化工艺。
如果本发明的电磁屏蔽膜用粘合剂组合物中使用的粘合剂由于交联密度或分子量太低而弹性太低,则在高温下可形成引起散射的气泡。另外,如果长时间使用弹性太大的粘合剂,则过度的交联可引起层的剥离。由于粘合剂的粘弹性主要取决于聚合物链的分子量、分子量分布、或分子结构,特别是分子量,优选使用分子量为300,000到2,000,000的丙烯酸系聚合物。可通过常规的游离基共聚合法制备所述粘合剂。
更具体地,电磁屏蔽膜用丙烯酸系粘合剂组合物优选包括:
a)100重量份的丙烯酸系共聚物,其为以下i)和ii)的丙烯酸系共聚物:
i)90到99.9重量份的具有C1-C12烷基的(甲基)丙烯酸酯单体;和
ii)0.1到10重量份的具有羟基的乙烯单体;和
b)0.01到10重量份的多官能基异氰酸酯交联剂。
更优选地,相对于100重量份的所述丙烯酸系共聚物包括94重量份到99.9重量份的所述具有C1-C12烷基的(甲基)丙烯酸酯单体。如果含量低于90重量份,则最初的粘合性变差并且成本增加。
优选地,对于所述具C1-C12烷基的(甲基)丙烯酸酯单体,使用在烷基中具有1-12个碳原子、优选具有2-8个碳原子的丙烯酸(或甲基丙烯酸)烷基酯。优选所述(甲基)丙烯酸烷基酯在烷基中具有2-8个碳原子是因为,如果烷基太长,则粘合剂的粘结性(cohesiveness)降低。具体地说,可使用(甲基)丙烯酸丁酯、(甲基)丙烯酸-2-乙基己酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸甲酯、(甲基)丙烯酸正丙酯、(甲基)丙烯酸异丙酯、(甲基)丙烯酸叔丁酯、(甲基)丙烯酸戊酯、(甲基)丙烯酸正辛酯或(甲基)丙烯酸异壬酯。
并且,可以使用单体如丙烯腈、苯乙烯、(甲基)丙烯酸缩水甘油酯、和乙酸乙烯酯用于控制粘合剂的玻璃化转化温度或提供其它性质。
所述具有羟基的乙烯单体用于提供粘结性,使得粘合剂不被在高温下与所述多官能基异氰酸酯交联剂的反应破坏。优选地,相对于100重量份的所述丙烯酸系共聚物,所述乙烯单体的含量为0.1到10重量份。如果含量低于0.1重量份,则粘合剂容易在高温下被破坏。另外,如果含量超过10重量份,可降低粘合剂在高温下的流动性。
对于所述具有羟基的乙烯单体,可使用(甲基)丙烯酸-2-羟乙酯、(甲基)丙烯酸-2-羟丙酯、2-羟基乙二醇(甲基)丙烯酸酯(2-hydroxyethyleneglycol(meth)acrylate)或2-羟基丙二醇(甲基)丙烯酸酯(2-hydroxypropyleneglycol(meth)acrylate)。
优选地,相对于100重量份的所述丙烯酸系共聚物包括0.01到10重量份的所述多官能基异氰酸酯交联剂。如果含量低于0.01重量份,则交联不充分。另外,如果含量超过10重量份,则可能由于过度交联发生层的剥离。
所述多官能基异氰酸酯交联剂通过交联保持粘合剂在高温下的粘结性,从而改善粘合可靠性。对于所述多官能基异氰酸酯交联剂,可使用甲苯二异氰酸酯、二苯甲烷二异氰酸酯、六亚甲基二异氰酸酯、或甲苯二异氰酸酯的三羟甲基丙烷加合物。在形成粘合剂层过程中,所述多官能基异氰酸酯交联剂不引起异氰酸酯基团的交联,这使得能够均匀地涂覆。在涂覆工艺完成之后,在进行干燥和老化工艺时形成交联。因此可以得到粘结性改善的粘合剂层。改善的粘结性改善了粘合剂的物理性能和可切割性(cuttability)。
同样,可以加入硅烷偶联剂以改善粘合耐久性。所述硅烷偶联剂随时间和加热改善粘合性,并从而防止鼓气泡和防止在高温和高湿度条件下的剥离,增强耐久性和可靠性。优选地,相对于100重量份的所述丙烯酸系共聚物包括的所述硅烷偶联剂为0.01到10重量份。如果含量低于0.01重量份,则粘合性随时间和加热的改善只是轻微的。另外,如果其超过10重量份,则可能发生鼓气泡或剥离,降低耐久性和可靠性。
对于所述硅烷偶联剂,可使用β-(3,4-环氧环己基)乙基三甲氧基硅烷、γ-环氧丙氧基丙基三甲氧基硅烷、γ-环氧丙氧基丙基甲基二乙氧基硅烷或γ-环氧丙氧基丙基三乙氧基硅烷。
另外,可使用1到100重量份的粘合剂树脂用于改善粘合性(adhesivity)。然而,如果过量使用所述粘合剂树脂,可能降低粘合剂的粘结性。对于所述粘合剂树脂,可使用(水合)烃类树脂、(水合)松香树脂、(水合)松香酯树脂、(水合)萜烯树脂、(水合)萜烯酚醛树脂、聚合松香树脂、或聚合松香酯树脂。
在本发明中,可通过溶液聚合、光聚合、本体聚合、悬浮聚合、或乳液聚合,优选溶液聚合使所述丙烯酸系共聚物聚合。优选地,聚合温度为50℃到140℃,并在单体均匀混和时加入引发剂。
优选地,本发明的电磁屏蔽膜用丙烯酸系粘合剂树脂的交联密度为1-95%。
可通过公知的适当地选择光引发剂的光聚合固化制备本发明的电磁屏蔽膜组合物用丙烯酸系粘合剂树脂。本发明的丙烯酸系粘合剂树脂组合物可用于起偏振器、光学功能膜、光控制膜等。此外,其可用于工业片,包括反射片、建筑用粘合剂片、摄影粘合剂片、用于绘制行车道的粘合剂片、光学粘合剂、和电子器件用粘合剂。
在本发明的电磁屏蔽膜用丙烯系粘合剂组合物的透明化过程中,优选在涂覆之前用有机溶剂稀释丙烯酸系粘合剂组合物以改善其涂覆特征。
优选地,加入多功能交联剂作为交联剂。更优选地,可加入异氰酸酯交联剂、环氧交联剂、氮丙啶交联剂、或金属螯合型交联剂。对于所述异氰酸酯交联剂,可使用甲苯二异氰酸酯、二苯甲烷二异氰酸酯、或六亚甲基二异氰酸酯。
在形成粘合剂层的过程中,所述多官能基异氰酸酯交联剂不引起异氰酸酯基团的交联,使其能够均匀地涂覆。在涂覆工艺完成之后,在进行干燥和老化工艺时形成交联,因此,得到粘结性改善的粘合剂层。改善的粘结性改善粘合剂的物理性能如耐久性、可靠性、粘合性、和可切割性。
可使用UV或EB,而不使用交联剂实现交联。
如果需要,本发明的电磁屏蔽膜用丙烯酸系粘合剂组合物可进一步包括近红外线吸收剂、环氧树脂、固化剂、硅烷偶联剂、增塑剂、紫外线稳定剂、抗氧化剂、染料、增强剂、或填料。
通过在80℃的高温下曝光500小时、或在60℃和90%RH(相对湿度)条件下曝光500小时并测量曝光前后透射率的变化测试透明化之后的电磁屏蔽膜的耐久性。透射率变化越大,则耐久性越差。
如果使用由具有酸性基团的丙烯酸系共聚物制备的粘合剂进行透明化,则残留的酸性基团使铜氧化,变为蓝色。因此,电磁屏蔽膜的透射率显著降低并且电磁屏蔽膜的耐久性也降低。
然而,在本发明中,通过使用电磁屏蔽膜用粘合剂组合物交联除去空气层。因此,透明化工艺很简单。此外,由于使用了没有酸性基团的丙烯酰基单体,防止了交联之后铜的氧化。因此,即使在高温或高湿度条件下电磁屏蔽膜的透射率也几乎没有改变,从而改善耐久性。
本发明还提供了等离子显示器电磁屏蔽滤波器,其通过层压在电磁屏蔽膜的透明衬底36下面的强化玻璃37、颜色校正层38、和近红外线屏蔽层39,层压在其上面的铜箔层33、黑色屏幕层34、和粘合剂层35,层压在近红外线屏蔽层39下面和粘合剂层32上面的抗反射膜40制成。可在抗反射膜40下面层压另一个透明衬底31。
由于在本发明的电磁屏蔽滤波器用粘合剂组合物中使用了具有羟基而没有酸性基团的乙烯单体,即使在高温和高湿度条件下也能防止铜的氧化,这降低了电磁屏蔽滤波器的透射率并改善了等离子显示器的耐久性。
以下,通过实施例和比较例描述本发明。然而以下实施例和比较例只是用于理解本发明,本发明不受以下实施例的限制。
实施例1
(丙烯酸系共聚物的制备)
将包括98重量份的丙烯酸正丁酯(BA)和2重量份的(甲基)丙烯酸-2-羟乙酯(2-HEMA)的单体混合物加入到装备有氮气回流和冷却单元的1,000cc反应器中。然后,加入100重量份的乙酸乙酯(EAc)作为溶剂。在用氮气清洗反应器20分钟以除去氧气之后,设置温度为60℃。然后,加入0.03重量份的偶氮二异丁腈(AIBN)在乙酸乙酯中的溶液(稀释到50%)作为引发剂。反应进行8小时以制备分子量为1,500K(使用标准聚苯乙烯样品测量)的丙烯酸系共聚物(PA-1)。
(丙烯酸系粘合剂组合物的制备)
相对于100重量份的制备的丙烯酸系共聚物(PA-1)加入1.5重量份的三羟甲基丙烷的甲苯二异氰酸酯加合物(TDI-1)在乙酸乙酯中的溶液(稀释到10重量%)作为多官能基异氰酸酯交联剂。根据涂覆特征将得到的混合物稀释到适当的浓度,并将其均匀混合。然后,将其涂覆在38μm-厚的剥离膜(releasing film)上并干燥,以制备30μm厚的均匀的粘合剂层。
使用制备的粘合剂层进行电磁屏蔽膜的透明化。
实施例2
除了使用(甲基)丙烯酸-2-羟丙酯代替(甲基)丙烯酸-2-羟乙酯(2-HEMA)之外,进行实施例1的过程。
实施例3
(丙烯酸系共聚物的制备)
使用包括94重量份的丙烯酸正丁酯(BA)和6重量份的(甲基)丙烯酸-2-羟乙酯(2-HEMA)的单体混合物、以及0.04重量份的偶氮二异丁腈(AIBN)在乙酸乙酯中的溶液(稀释到50%)作为引发剂,以与实施例1相同的方法制备分子量为1,000K(使用标准聚苯乙烯样品测量)的丙烯酸系共聚物(PA-2)。
(丙烯酸系粘合剂组合物的制备)
除了使用PA-2作为丙烯酸系共聚物之外,进行实施例1的过程。
比较例1
(丙烯酸系共聚物的制备)
将包括94重量份的丙烯酸正丁酯(BA)和6重量份的丙烯酸酯(乙酸)的单体混合物加入到装备有氮气回流和冷却单元的1,000cc反应器中。然后,加入100重量份的乙酸乙酯(EAc)作为溶剂。在用氮气清洗反应器20分钟以除去氧气之后,设置温度为60℃。然后,加入0.04重量份的偶氮二异丁腈(AIBN)在乙酸乙酯中的溶液(稀释到50%)作为引发剂。反应进行8小时以制备分子量为1,000K(使用标准聚苯乙烯样品测量)的丙烯酸系共聚物(PA-3)。
(丙烯酸系粘合剂组合物的制备)
相对于100重量份的制备的丙烯酸系共聚物(PA-3)加入1.5重量份的三羟甲基丙烷(TDI-1)的甲苯二异氰酸酯加合物在乙酸乙酯中的溶液(稀释到10重量%)作为多官能基异氰酸酯交联剂。根据涂覆特征将得到的混合物稀释到适当的浓度,并将其均匀混合。然后,将其涂覆在38μm-厚的剥离膜上并干燥,以制备30μm厚的均匀的粘合剂层。
使用制备的粘合剂层进行电磁屏蔽膜的透明化。
(耐久性的评价)
将实施例1到3和比较例1中制备的各个粘合剂组合物在电磁屏蔽膜上处理。在透明化之后,在300nm到900nm的波长范围内测量透射率。在60℃和90%RH条件下曝光500小时之后,再次测量透射率。透射率测量结果如图4a到图4d中所示。透射率在680nm下的变化如以下表1中所示。
表1
曝光前的透射率 | 曝光后的透射率 | 透射率变化(%) | |
实施例1 | 76.5 | 76.5 | 0 |
实施例2 | 80.6 | 80.1 | 0.5 |
实施例3 | 79.4 | 79.0 | 0.4 |
比较例1 | 76.5 | 67.3 | 9.2 |
如图4a到4d和表1中所示,使用实施例1到3的没有酸性基团的丙烯酸系粘合剂组合物透明化的电磁屏蔽膜在曝光前后表现出很小的透射率变化。另一方面,使用比较例1的具有酸性团基团(-COOH)的粘合剂组合物透明化的电磁屏蔽膜有9.2%的透射率变化。
由此结果可以看出,如果使用本发明的没有酸性基团的丙烯酸系粘合剂组合物进行透明化,则防止了铜箔中铜的氧化,从而即使在高温和高湿度条件下,透射率也几乎没有变化,从而改善耐久性。
虽然已经参考优选实施方案详细描述了本发明,本领域的技术人员知道可以对其进行多种替换和修改,而不脱离附加的权利要求书所述的本发明的精神实质和范围。
权利要求书
(按照条约第19条的修改)
1.(修改)电磁屏蔽膜用丙烯酸系粘合剂组合物,其交联密度为1-95%,包括:
a)i)具有C1-C12烷基的(甲基)丙烯酸酯单体和ii)具有羟基的乙烯单体的丙烯酸系共聚物;和
b)多官能基异氰酸酯交联剂。
2.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其包括:
a)100重量份的丙烯酸系共聚物,其为以下i)和ii)的丙烯酸系共聚物:
i)90到99.9重量份的具有C1-C12烷基的(甲基)丙烯酸酯单体;和
ii)0.1到10重量份的具有羟基的乙烯单体;和
b)0.01到10重量份的多官能基异氰酸酯交联剂。
3.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有C1-C12烷基的(甲基)丙烯酸酯单体为选自由(甲基)丙烯酸丁酯、(甲基)丙烯酸-2-乙基己酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸甲酯、(甲基)丙烯酸正丙酯、(甲基)丙烯酸异丙酯、(甲基)丙烯酸叔丁酯、(甲基)丙烯酸戊酯、(甲基)丙烯酸正辛酯和(甲基)丙烯酸异壬酯组成的组中的一种或多种。
4.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有羟基的乙烯单体为选自由(甲基)丙烯酸-2-羟乙酯、(甲基)丙烯酸-2-羟丙酯、2-羟基乙二醇(甲基)丙烯酸酯和2-羟基丙二醇(甲基)丙烯酸酯组成的组中的一种或多种。
5.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有羟基的乙烯单体与所述多官能基异氰酸酯交联剂的异氰酸酯基团反应形成部分交联。
6.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述多官能基异氰酸酯交联剂为选自由甲苯二异氰酸酯、二苯甲烷二异氰酸酯、六亚甲基二异氰酸酯和甲苯二异氰酸酯的三羟甲基丙烷加合物组成的组中的一种或多种。
7.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其进一步包括选自由近红外线吸收剂、环氧树脂、固化剂、硅烷偶联剂、增塑剂、紫外稳定剂、抗氧化剂、染料、增强剂和填料组成的组中的一种或多种添加剂。
8.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述丙烯酸系共聚物通过溶液聚合、光聚合、本体聚合、悬浮聚合或乳液聚合制备。
9.(删除)
10.(修改)使用权利要求1-8中任一项的丙烯酸系粘合剂组合物透明化的等离子显示器用电磁屏蔽滤波器。
Claims (10)
1.电磁屏蔽膜用丙烯酸系粘合剂组合物,其包括:
a)i)具有C1-C12烷基的(甲基)丙烯酸酯单体和ii)具有羟基的乙烯单体的丙烯酸系共聚物;和
b)多官能基异氰酸酯交联剂。
2.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其包括:
a)100重量份的丙烯酸系共聚物,其为以下i)和ii)的丙烯酸系共聚物:
i)90到99.9重量份的具有C1-C12烷基的(甲基)丙烯酸酯单体;和
ii)0.1到10重量份的具有羟基的乙烯单体;和
b)0.01到10重量份的多官能基异氰酸酯交联剂。
3.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有C1-C12烷基的(甲基)丙烯酸酯单体为选自由(甲基)丙烯酸丁酯、(甲基)丙烯酸-2-乙基己酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸甲酯、(甲基)丙烯酸正丙酯、(甲基)丙烯酸异丙酯、(甲基)丙烯酸叔丁酯、(甲基)丙烯酸戊酯、(甲基)丙烯酸正辛酯和(甲基)丙烯酸异壬酯组成的组中的一种或多种。
4.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有羟基的乙烯单体为选自由(甲基)丙烯酸-2-羟乙酯、(甲基)丙烯酸-2-羟丙酯、2-羟基乙二醇(甲基)丙烯酸酯和2-羟基丙二醇(甲基)丙烯酸酯组成的组中的一种或多种。
5.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述具有羟基的乙烯单体与所述多官能基异氰酸酯交联剂的异氰酸酯基团反应形成部分交联。
6.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述多官能基异氰酸酯交联剂为选自由甲苯二异氰酸酯、二苯甲烷二异氰酸酯、六亚甲基二异氰酸酯和甲苯二异氰酸酯的三羟甲基丙烷加合物组成的组中的一种或多种。
7.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其进一步包括选自由近红外线吸收剂、环氧树脂、固化剂、硅烷偶联剂、增塑剂、紫外稳定剂、抗氧化剂、染料、增强剂和填料组成的组中的一种或多种添加剂。
8.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其中所述丙烯酸系共聚物通过溶液聚合、光聚合、本体聚合、悬浮聚合或乳液聚合制备。
9.权利要求1的电磁屏蔽膜用丙烯酸系粘合剂组合物,其交联密度为1-95%。
10.使用权利要求1-9中任一项的丙烯酸系粘合剂组合物透明化的等离子显示器用电磁屏蔽滤波器。