CN105886706A - 一种不锈钢制件热处理工艺 - Google Patents
一种不锈钢制件热处理工艺 Download PDFInfo
- Publication number
- CN105886706A CN105886706A CN201410431800.9A CN201410431800A CN105886706A CN 105886706 A CN105886706 A CN 105886706A CN 201410431800 A CN201410431800 A CN 201410431800A CN 105886706 A CN105886706 A CN 105886706A
- Authority
- CN
- China
- Prior art keywords
- rustless steel
- temperature
- stainless steel
- steel product
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种不锈钢制件热处理工艺,其包括以下步骤:淬火,将不锈钢制件加热至930℃~960℃,并在该温度下保温2.5~3.5小时,之后将所述不锈钢制件进行油冷,当所述不锈钢制件表面温度在≤110℃时取出;中温回火,将完成淬火的不锈钢制件放置在加热炉内加热至400℃~450℃,并在该温度下保温8~10小时,之后将不锈钢制件取出并空冷至室温。本发明不锈钢制件热处理工艺,经加热后进行油冷淬火,减少冷却中产生的应力,避免变形,同时提高了不锈钢制件的表面硬度;经过中温回火,得到回火屈氏体,使其具有较高的弹性和屈服点、及适当的韧性。
Description
技术领域
本发明涉及一种热处理工艺,特别涉及一种不锈钢制件热处理工艺。
背景技术
不锈钢是不锈耐酸钢的简称,耐空气、蒸汽、水等弱腐蚀介质或具有不锈性的钢种称为不锈钢;而将耐化学介质腐蚀(酸、碱、盐等化学浸蚀)的钢种称为耐酸钢。由于两者在化学成分上的差异而使他们的耐蚀性不同,普通不锈钢一般不耐化学介质腐蚀,而耐酸钢则一般均具有不锈性。由于具有以上特性,因此不锈钢的使用越来越广泛,但是,传统的不锈钢制件受生产工艺的影响,使其表面硬度低、弹性极限、屈服点和韧性不能满足设计需求。
发明内容
【1】要解决的技术问题
本发明要解决的技术问题是克服现有技术中的不足,提供一种能生产出表面硬度高、弹性极限、屈服点和韧性好的不锈钢制件热处理工艺。
【2】解决问题的技术方案
本发明提供一种不锈钢制件热处理工艺,其包括以下步骤:
A、淬火,将不锈钢制件加热至930℃~960℃,并在该温度下保温2.5~3.5小时,之后将所述不锈钢制件进行油冷,当所述不锈钢制件表面温度在≤110℃时取出;
B、中温回火,将完成淬火的不锈钢制件放置在加热炉内加热至400℃~450℃,并在该温度下保温8~10小时,之后将不锈钢制件取出并空冷至室温。
进一步的,在步骤A中,将不锈钢制件加热至950℃,并在该温度下保温3小时,之后将所述不锈钢制件进行油冷,当所述不锈钢制件表面温度在≤110℃时取出。
进一步的,在步骤B中,将完成淬火的不锈钢制件放置在加热炉内加热至430℃~440℃,并在该温度下保温9小时,之后将不锈钢制件取出并空冷至室温。
【3】有益效果
本发明不锈钢制件热处理工艺,经加热后进行油冷淬火,减少冷却中产生的应力,避免变形,同时提高了不锈钢制件的表面硬度;经过中温回火,得到回火屈氏体,使其具有较高的弹性和屈服点、及适当的韧性。
具体实施方式
本发明提供一种不锈钢制件热处理工艺,其包括以下步骤:
A、淬火,用加热炉将不锈钢制件加热至930℃~960℃,并在该温度下保温2.5~3.5小时,之后将该不锈钢制件进行油冷,当不锈钢制件表面温度在≤110℃时取出;
B、中温回火,将完成淬火的不锈钢制件放置在加热炉内加热至400℃~450℃,并在该温度下保温8~10小时,之后将不锈钢制件取出并空冷至室温。
为了达到更好的热处理效果,将不锈钢制件加热至950℃,并在该温度下保温3小时,之后将该不锈钢制件进行油冷,当不锈钢制件表面温度在≤110℃时取出;
将完成淬火的不锈钢制件放置在加热炉内加热至430℃~440℃,并在该温度下保温9小时,之后将不锈钢制件取出并空冷至室温。
本发明不锈钢制件热处理工艺,经加热后进行油冷淬火,减少冷却中产生的应力,避免变形,同时提高了不锈钢制件的表面硬度;经过中温回火,得到回火屈氏体,使其具有较高的弹性和屈服点、及适当的韧性。
Claims (3)
1.一种不锈钢制件热处理工艺,其特征在于,包括以下步骤:
A、淬火,将不锈钢制件加热至930℃~960℃,并在该温度下保温2.5~3.5小时,之后将所述不锈钢制件进行油冷,当所述不锈钢制件表面温度在≤110℃时取出;
B、中温回火,将完成淬火的不锈钢制件放置在加热炉内加热至400℃~450℃,并在该温度下保温8~10小时,之后将不锈钢制件取出并空冷至室温。
2.如权利要求1所述的锈钢制件热处理工艺,其特征在于:在步骤A中,将不锈钢制件加热至950℃,并在该温度下保温3小时,之后将所述不锈钢制件进行油冷,当所述不锈钢制件表面温度在≤110℃时取出。
3.如权利要求1所述的锈钢制件热处理工艺,其特征在于:在步骤B中,将完成淬火的不锈钢制件放置在加热炉内加热至430℃~440℃,并在该温度下保温9小时,之后将不锈钢制件取出并空冷至室温。