CN103484634A - 一种c级钢热处理方法 - Google Patents

一种c级钢热处理方法 Download PDF

Info

Publication number
CN103484634A
CN103484634A CN201310434555.2A CN201310434555A CN103484634A CN 103484634 A CN103484634 A CN 103484634A CN 201310434555 A CN201310434555 A CN 201310434555A CN 103484634 A CN103484634 A CN 103484634A
Authority
CN
China
Prior art keywords
hours
temperature
normalizing
warming
tempering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310434555.2A
Other languages
English (en)
Inventor
杨龙兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Yanggong Machinery Manufacturing Co Ltd
Original Assignee
Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Yanggong Machinery Manufacturing Co Ltd filed Critical Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority to CN201310434555.2A priority Critical patent/CN103484634A/zh
Publication of CN103484634A publication Critical patent/CN103484634A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种C级钢热处理方法，步骤如下：（1）将钢随炉升温至500-550℃，保温1.5-2小时；（2）升温至700-750℃，保温1.5-2小时；（3）正火温度为900-920℃，正火时间为5-6小时；空冷；（4）回火温度为630-650℃，回火时间5-6小时。应用本发明的方法C级钢的试棒机械性能指标一次达标率在95%以上。

Description

一种C级钢热处理方法
技术领域
本发明属于热处理技术领域，具体涉及一种C级钢热处理方法。
背景技术
现有方法生产的C级钢铸件试棒机械性能一次达标率仅有50-60%，已经严重影响车间的生产进度及订单及时兑现，提高C级钢铸件试棒性能一次达标率成为亟待解决的问题。C级钢铸件除了成分要控制在工艺范围之内外，要达到所要求的性能指标，热处理是至关重要的一道工序。
发明内容
本发明提供了一种C级钢热处理方法，应用该方法C级钢的试棒机械性能指标一次达标率在95%以上。
    本发明提供一种C级钢热处理方法，步骤如下： （1）、将钢随炉升温至500-550℃，保温1.5-2小时；
（2）、升温至700-750℃，保温1.5-2小时；
（3）、正火温度为900-920℃，正火时间为5-6小时；空冷；
（4）、回火温度为630-650℃，回火时间5-6小时。
    进一步地，步骤（1）中，将钢随炉升温至520℃，保温1.5小时。
    进一步地，步骤（2）中，升温至720℃，保温2小时。
    进一步地，步骤（3）中，正火温度为910℃，正火时间为6小时。
    进一步地，步骤（4）中，回火温度为640℃，回火时间5小时。
应用本发明的方法C级钢的试棒机械性能指标一次达标率在95%以上。
具体实施方式
实施例1
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至520℃，保温1.5小时；
（2）、升温至720℃，保温2小时；
（3）、正火温度为910℃，正火时间为6小时；空冷；
（4）、回火温度为640℃，回火时间5小时。
实施例2
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至500℃，保温1.5小时；
（2）、升温至750℃，保温2小时；
（3）、正火温度为910℃，正火时间为5小时；空冷；
（4）、回火温度为630℃，回火时间5小时。
实施例3
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至550℃，保温1.5小时；
（2）、升温至750℃，保温2小时；
（3）、正火温度为910℃，正火时间为6小时；空冷；
（4）、回火温度为630℃，回火时间6小时。
实施例4
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至500℃，保温2小时；
（2）、升温至750℃，保温2小时；
（3）、正火温度为900℃，正火时间为6小时；空冷；
（4）、回火温度为640℃，回火时间6小时。
实施例5
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至550℃，保温1.5小时；
（2）、升温至740℃，保温1.5小时；
（3）、正火温度为900℃，正火时间为6小时；空冷；
（4）、回火温度为650℃，回火时间5.5小时。
实施例6
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至550℃，保温1.5小时；
（2）、升温至740℃，保温2小时；
（3）、正火温度为920℃，正火时间为6小时；空冷；
（4）、回火温度为640℃，回火时间6小时。
实施例7
本发明的一种C级钢热处理方法步骤如下： （1）、将钢随炉升温至500℃，保温1.5小时；
（2）、升温至700℃，保温2小时；
（3）、正火温度为920℃，正火时间为6小时；空冷；
（4）、回火温度为640℃，回火时间5小时。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (5)

1.一种C级钢热处理方法，步骤如下： （1）、将钢随炉升温至500-550℃，保温1.5-2小时；
（1）、升温至700-750℃，保温1.5-2小时；
（2）、正火温度为900-920℃，正火时间为5-6小时；空冷；
（3）、回火温度为630-650℃，回火时间5-6小时。
2.根据权利要求1所述的热处理方法，其特征在于：步骤（1）中，将钢随炉升温至520℃，保温1.5小时。
3.根据权利要求1所述的热处理方法，其特征在于：步骤（2）中，升温至720℃，保温2小时。
4.根据权利要求1所述的热处理方法，其特征在于：步骤（3）中，正火温度为910℃，正火时间为6小时。
5.根据权利要求1所述的热处理方法，其特征在于：步骤（4）中，回火温度为640℃，回火时间5小时。
CN201310434555.2A 2013-09-23 2013-09-23 一种c级钢热处理方法 Pending CN103484634A (zh)