CN103319080B - 3-6mm钢化玻璃的钢化加工方法 - Google Patents
3-6mm钢化玻璃的钢化加工方法 Download PDFInfo
- Publication number
- CN103319080B CN103319080B CN201310197226.0A CN201310197226A CN103319080B CN 103319080 B CN103319080 B CN 103319080B CN 201310197226 A CN201310197226 A CN 201310197226A CN 103319080 B CN103319080 B CN 103319080B
- Authority
- CN
- China
- Prior art keywords
- glass
- interval
- roller
- way
- toughened glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了3-6mm钢化玻璃的钢化加工方法,包括以下步骤:将平板玻璃放入100℃沸腾的食盐水中煮1-2小时,食盐水浓度为15-18%;将玻璃水平放置到辊道上,通过辊道送到第一、二通道式钢化炉中,按区间依次进行热处理,本发明通过采用分区间加热、中间冷处理、二次热处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。
Description
技术领域
本发明属于玻璃制备领域,具体涉及钢化玻璃的制备工艺。
技术背景
钢化玻璃由于具有较高机械强度、优良耐温急变性、良好的安全性等优点,使得其被广泛应用。现有钢化玻璃生产过程大多采用以空气为冷却介质的钢化工艺,使被加热玻璃通过大量空气在短时间内进行激冷处理,从而完成钢化过程。现有钢化玻璃工艺导致自爆率较高。
发明内容
本发明的目的是提供一种3-6mm钢化玻璃的钢化加工方法,玻璃表面应力均匀、弯曲度、碎片、钢化度均符合要求。
本发明技术方案如下:
3-6mm钢化玻璃的钢化加工方法,其特征在于包括以下步骤:
(1)、将平板玻璃放入100℃沸腾的食盐水中煮1-2小时,食盐水浓度为15-18%;
(2)、将玻璃水平放置到辊道上,通过辊道送到第一通道式钢化炉中,按区间依次进行热处理:
第一区间:温度530-580℃,时间8-10分钟;第二区间:温度610-620℃,时间3-4分钟;
(3)、玻璃从第一通道式钢化炉出来后,进行空气缓冷至50℃以下,存放3-4小时;
(4)、将玻璃水平放置到辊道上,通过辊道送到第二通道式钢化炉中,按区间依次进行热处理:
第一区间:温度610-630℃,时间3-5分钟;第二区间:温度640-690℃,时间3-4分钟;
(5)、取出玻璃自然冷却。
本发明通过采用分区间加热、中间冷处理、二次热处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。
具体实施方式
3-6mm钢化玻璃的钢化加工方法,包括以下步骤:
(1)、将4mm平板玻璃放入100℃沸腾的食盐水中煮1小时,食盐水浓度为18%;
(2)、将玻璃水平放置到辊道上,通过辊道送到第一通道式钢化炉中,按区间依次进行热处理:
第一区间:温度530-540℃,时间8分钟;第二区间:温度610-620℃,时间3分钟;
(3)、玻璃从第一通道式钢化炉出来后,进行空气缓冷至50℃以下,存放3小时;
(4)、将玻璃水平放置到辊道上,通过辊道送到第二通道式钢化炉中,按区间依次进行热处理:
第一区间:温度610-620℃,时间3分钟;第二区间:温度640-650℃,时间4分钟;
(5)、取出玻璃自然冷却。
将加工好的钢化玻璃进行检测,其弯曲度达到0.9‰,50×50mm内碎片53粒,符合标准;钢化度=3.9N/cm,自爆率在1~2‰。
Claims (1)
1.3-6mm钢化玻璃的钢化加工方法,其特征在于包括以下步骤:
(1)、将平板玻璃放入100℃沸腾的食盐水中煮1-2小时,食盐水浓度为15-18%;
(2)、将玻璃水平放置到辊道上,通过辊道送到第一通道式钢化炉中,按区间依次进行热处理:
第一区间:温度530-580℃,时间8-10分钟;第二区间:温度610-620℃,时间3-4分钟;
(3)、玻璃从第一通道式钢化炉出来后,进行空气缓冷至50℃以下,存放3-4小时;
(4)、将玻璃水平放置到辊道上,通过辊道送到第二通道式钢化炉中,按区间依次进行热处理:
第一区间:温度610-630℃,时间3-5分钟;第二区间:温度640-690℃,时间3-4分钟;
(5)、取出玻璃自然冷却。