CN102191689A - 一种合成革用雾面丝滑蜡感处理剂及其制备方法 - Google Patents

一种合成革用雾面丝滑蜡感处理剂及其制备方法 Download PDF

Info

Publication number
CN102191689A
CN102191689A CN2010105693997A CN201010569399A CN102191689A CN 102191689 A CN102191689 A CN 102191689A CN 2010105693997 A CN2010105693997 A CN 2010105693997A CN 201010569399 A CN201010569399 A CN 201010569399A CN 102191689 A CN102191689 A CN 102191689A
Authority
CN
China
Prior art keywords
weight portions
finishing agent
synthetic leather
weight
weight portion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105693997A
Other languages
English (en)
Inventor
齐春红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Baoze Polymer Materials Co Ltd
Original Assignee
Jiangsu Baoze Polymer Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Baoze Polymer Materials Co Ltd filed Critical Jiangsu Baoze Polymer Materials Co Ltd
Priority to CN2010105693997A priority Critical patent/CN102191689A/zh
Publication of CN102191689A publication Critical patent/CN102191689A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种合成革用雾面丝滑蜡感处理剂及其制备方法。所述合成革用雾面丝滑蜡感处理剂由以下组分组成：改性聚氨酯树脂、DMF、醋酸丁酯、二氧化硅消光粉、改性氨基硅氧烷、二甲基硅油、芥酸酰胺、聚氨酯色珠和有机硅流平剂。本发明所公开的合成革用雾面丝滑蜡感处理剂雾面消光效果佳，独特的丝滑蜡感，革面真皮效果强，应用该丝滑蜡感处理剂的合成革，其丝滑手感，综合效果佳。

Description

一种合成革用雾面丝滑蜡感处理剂及其制备方法
技术领域
本发明涉及一种合成革用雾面丝滑蜡感处理剂，特别涉及应用于合成革后段工艺的合成革用丝滑蜡感处理剂，属于创新型后段材料。本发明还涉及一种合成革用雾面丝滑蜡感处理剂的制备方法。
背景技术
合成革通常分为PU革(聚氨酯革)和PVC革(聚氯乙烯革)。对于PVC革来说，为了得到针对不同产品、不同要求的柔软度、光亮度，在制造过程中需要对PVC进行表面处理。在实践中，PVC经表面处理后很难在光泽自然、手感柔软的基础上得到很好的真皮效果。
发明内容
本发明的目的是提供一种合成革用雾面丝滑蜡感处理剂。
本发明的合成革用雾面丝滑蜡感处理剂通过以下技术方案实现：
本发明所公开的合成革用雾面丝滑蜡感处理剂，由以下组分组成：改性聚氨酯树脂、DMF、醋酸丁酯、二氧化硅消光粉、改性氨基硅氧烷、二甲基硅油、芥酸酰胺、聚氨酯色珠和有机硅流平剂。
本发明提供的合成革用雾面丝滑蜡感处理剂的各组分的配比可以为：改性聚氨酯树脂30～40重量份，DMF 20～30重量份，醋酸丁酯20～30重量份，二氧化硅消光粉4～5重量份，改性氨基硅氧烷1～4重量份，二甲基硅油1～3重量份，芥酸酰胺1～3重量份，聚氨酯色珠3～5重量份，有机硅流平剂1～2重量份。
在本发明的一个实施例中，合成革用雾面丝滑蜡感处理剂的各组分的配比如下：改性聚氨酯树脂40重量份，DMF 20重量份，醋酸丁酯20重量份，二氧化硅消光粉4重量份，改性氨基硅氧烷2重量份，二甲基硅油2重量份，芥酸酰胺3重量份，聚氨酯色珠3重量份，有机硅流平剂1重量份。
在本发明的另一实施例中，合成革用雾面丝滑蜡感处理剂的各组分的配比如下：改性聚氨酯树脂30重量份，DMF 30重量份，醋酸丁酯30重量份，二氧化硅消光粉5重量份，改性氨基硅氧烷1重量份，二甲基硅油3重量份，芥酸酰胺1重量份，聚氨酯色珠5重量份，有机硅流平剂2重量份。
在本发明的另一实施例中，合成革用雾面丝滑蜡感处理剂的各组分的配比如下：改性聚氨酯树脂35重量份，DMF 25重量份，醋酸丁酯25重量份，二氧化硅消光粉4.5重量份，改性氨基硅氧烷4重量份，二甲基硅油1重量份，芥酸酰胺2重量份，聚氨酯色珠4重量份，有机硅流平剂1.5重量份。
本发明还提供一种合成革用雾面丝滑蜡感处理剂的制备方法，包含以下步骤：
1)将部分改性聚氨酯树脂以及DMF、醋酸丁酯、二氧化硅消光粉搅拌后研磨过滤，弃去滤渣；
2)在步骤1)得到的混合物中加入改性氨基硅氧烷、二甲基硅油、芥酸酰胺、聚氨酯色珠均匀搅拌；
3)在步骤2)得到的混合物中加入剩余的聚氨酯树脂以及有机硅流平剂，搅拌均匀后过滤，弃去滤渣，即得所述合成革用雾面丝滑蜡感处理剂。
本发明提供的合成革用雾面丝滑蜡感处理剂的制备方法中的各组分的配比可以如下：改性聚氨酯树脂30～40重量份，DMF 20～30重量份，醋酸丁酯20～30重量份，二氧化硅消光粉4～5重量份，改性氨基硅氧烷1～4重量份，二甲基硅油1～3重量份，芥酸酰胺1～3重量份，聚氨酯色珠3～5重量份，有机硅流平剂1～2重量份。
在本发明的一个实施例中，合成革用雾面丝滑蜡感处理剂的制备方法中的步骤1)、2)、3)均在常温常压下进行。
由于采用以上技术方案，本发明与现有技术相比具有如下优点：
1、雾面丝滑蜡感处理剂是环保型材料，符合欧盟的环保标准；
2、组成丝滑蜡感处理剂的各组分相互协调、共同作用，雾面消光效果佳，独特的丝滑蜡感，革面真皮效果强，应用该丝滑蜡感处理剂的合成革，其丝滑手感，综合效果佳；
3、将该雾面丝滑蜡感处理剂在现有合成革生产线上应用，工艺简单，是后段印刷的一种新型材料，无需改变生产设备增加成本。
具体实施方式
下面通过实施例，对本发明技术方案进行详细说明，但是本发明的保护范围不局限于所述实施例。
实施例1
合成革用雾面丝滑蜡感处理剂由改性聚氨酯树脂40重量份，DMF 20重量份，醋酸丁酯20重量份，二氧化硅消光粉4重量份，改性氨基硅氧烷2重量份，二甲基硅油2重量份，芥酸酰胺3重量份，聚氨酯色珠3重量份，有机硅流平剂1重量份组成。
上述合成革用雾面丝滑蜡感处理剂的制备方法是：在常温常压下，将10重量份改性聚氨酯树脂、20重量份DMF、20重量份醋酸丁酯以及4重量份二氧化硅消光粉充分混合，搅拌至少30分钟后进行研磨过滤，弃去滤渣。在得到的混合物中加入2重量份改性氨基硅氧烷、2重量份二甲基硅油、3重量份芥酸酰胺、3重量份聚氨酯色珠，搅拌至少30分钟。待搅拌均匀后加入30重量份改性聚氨酯树脂和1重量份有机硅流平剂，搅拌至少30分钟后过滤，弃去滤渣，即得本发明的合成革用雾面丝滑蜡感处理剂。所得到的合成革用雾面丝滑蜡感处理剂的性能指标见表1。
上述制备过程中所采用的搅拌、过滤等方法均为本领域内惯用的方法。
实施例2
合成革用雾面丝滑蜡感处理剂由改性聚氨酯树脂30重量份，DMF 30重量份，醋酸丁酯30重量份，二氧化硅消光粉5重量份，改性氨基硅氧烷1重量份，二甲基硅油3重量份，芥酸酰胺1重量份，聚氨酯色珠5重量份，有机硅流平剂2重量份组成。
上述合成革用雾面丝滑蜡感处理剂的制备方法是：在常温常压下，将12重量份改性聚氨酯树脂、30重量份DMF、30重量份醋酸丁酯以及5重量份二氧化硅消光粉充分混合，搅拌至少30分钟后进行研磨过滤，弃去滤渣。在得到的混合物中加入1重量份改性氨基硅氧烷、3重量份二甲基硅油、1重量份芥酸酰胺、5重量份聚氨酯色珠，搅拌至少30分钟。待搅拌均匀后加入18重量份改性聚氨酯树脂和2重量份有机硅流平剂，搅拌至少30分钟后过滤，弃去滤渣，即得本发明的合成革用雾面丝滑蜡感处理剂。所得到的合成革用雾面丝滑蜡感处理剂的性能指标见表1。
上述制备过程中所采用的搅拌、过滤等方法均为本领域内惯用的方法。
实施例3
合成革用雾面丝滑蜡感处理剂由改性聚氨酯树脂35重量份，DMF 25重量份，醋酸丁酯25重量份，二氧化硅消光粉4.5重量份，改性氨基硅氧烷4重量份，二甲基硅油1重量份，芥酸酰胺2重量份，聚氨酯色珠4重量份，有机硅流平剂1.5重量份组成。
上述合成革用雾面丝滑蜡感处理剂的制备方法是：在常温常压下，将20重量份改性聚氨酯树脂、25重量份DMF、25重量份醋酸丁酯以及4.5重量份二氧化硅消光粉充分混合，搅拌至少30分钟后进行研磨过滤，弃去滤渣。在得到的混合物中加入4重量份改性氨基硅氧烷、1重量份二甲基硅油、2重量份芥酸酰胺、4重量份聚氨酯色珠，搅拌至少30分钟。待搅拌均匀后加入15重量份改性聚氨酯树脂和1.5重量份有机硅流平剂，搅拌至少30分钟后过滤，弃去滤渣，即得本发明的合成革用雾面丝滑蜡感处理剂。所得到的合成革用雾面丝滑蜡感处理剂的性能指标见表1。
上述制备过程中所采用的搅拌、过滤等方法均为本领域内惯用的方法。
表1
Figure BDA0000035600100000051
以上所述仅为本发明的较佳实施例，并非用来限定本发明的实施范围；如果不脱离本发明的精神和范围，对本发明进行修改或者等同替换，均应涵盖在本发明权利要求的保护范围当中。

Claims (8)

1.一种合成革用雾面丝滑蜡感处理剂，其特征在于，由以下组分组成：改性聚氨酯树脂、DMF、醋酸丁酯、二氧化硅消光粉、改性氨基硅氧烷、二甲基硅油、芥酸酰胺、聚氨酯色珠和有机硅流平剂。
2.根据权利要求1所述的合成革用雾面丝滑蜡感处理剂，其特征在于，所述各组分的配比如下：改性聚氨酯树脂30～40重量份，DMF 20～30重量份，醋酸丁酯20～30重量份，二氧化硅消光粉4～5重量份，改性氨基硅氧烷1～4重量份，二甲基硅油1～3重量份，芥酸酰胺1～3重量份，聚氨酯色珠3～5重量份，有机硅流平剂1～2重量份。
3.根据权利要求2所述的合成革用雾面丝滑蜡感处理剂，其特征在于，所述各组分的配比如下：改性聚氨酯树脂40重量份，DMF 20重量份，醋酸丁酯20重量份，二氧化硅消光粉4重量份，改性氨基硅氧烷2重量份，二甲基硅油2重量份，芥酸酰胺3重量份，聚氨酯色珠3重量份，有机硅流平剂1重量份。
4.根据权利要求2所述的合成革用雾面丝滑蜡感处理剂，其特征在于，所述各组分的配比如下：改性聚氨酯树脂30重量份，DMF 30重量份，醋酸丁酯30重量份，二氧化硅消光粉5重量份，改性氨基硅氧烷1重量份，二甲基硅油3重量份，芥酸酰胺1重量份，聚氨酯色珠5重量份，有机硅流平剂2重量份。
5.根据权利要求2所述的合成革用雾面丝滑蜡感处理剂，其特征在于，所述各组分的配比如下：改性聚氨酯树脂35重量份，DMF 25重量份，醋酸丁酯25重量份，二氧化硅消光粉4.5重量份，改性氨基硅氧烷4重量份，二甲基硅油1重量份，芥酸酰胺2重量份，聚氨酯色珠4重量份，有机硅流平剂1.5重量份。
6.权利要求1-5任一项所述的合成革用雾面丝滑蜡感处理剂的制备方法，其特征在于，包含以下步骤：
1)将部分改性聚氨酯树脂以及DMF、醋酸丁酯、二氧化硅消光粉搅拌后研磨过滤，弃去滤渣；
2)在步骤1)得到的混合物中加入改性氨基硅氧烷、二甲基硅油、芥酸酰胺、聚氨酯色珠均匀搅拌；
3)在步骤2)得到的混合物中加入剩余的聚氨酯树脂以及有机硅流平剂，搅拌均匀后过滤，弃去滤渣，即得所述合成革用雾面丝滑蜡感处理剂。
7.根据权利要求6所述的合成革用雾面丝滑蜡感处理剂的制备方法，其特征在于，各组分的配比如下：改性聚氨酯树脂30～40重量份，DMF20～30重量份，醋酸丁酯20～30重量份，二氧化硅消光粉4～5重量份，改性氨基硅氧烷1～4重量份，二甲基硅油1～3重量份，芥酸酰胺1～3重量份，聚氨酯色珠3～5重量份，有机硅流平剂1～2重量份。
8.根据权利要求6所述的合成革用雾面丝滑蜡感处理剂的制备方法，其特征在于，所有步骤均在常温常压下进行。
CN2010105693997A 2010-12-01 2010-12-01 一种合成革用雾面丝滑蜡感处理剂及其制备方法 Pending CN102191689A (zh)