BR112017007973A2 - folha de aço galvanizada por imersão a quente - Google Patents
folha de aço galvanizada por imersão a quenteInfo
- Publication number
- BR112017007973A2 BR112017007973A2 BR112017007973A BR112017007973A BR112017007973A2 BR 112017007973 A2 BR112017007973 A2 BR 112017007973A2 BR 112017007973 A BR112017007973 A BR 112017007973A BR 112017007973 A BR112017007973 A BR 112017007973A BR 112017007973 A2 BR112017007973 A2 BR 112017007973A2
- Authority
- BR
- Brazil
- Prior art keywords
- layer
- steel sheet
- dip galvanized
- base steel
- hot dip
- Prior art date
Abstract
trata-se de uma folha de aço galvanizada por imersão a quente que compreende uma folha de aço de base e uma camada galvanizada por imersão a quente formada em pelo menos uma superfície da folha de aço de base, em que a camada galvanizada por imersão a quente inclui cristais colunares que compreende uma fase ¿ e que tem um teor de fe de mais do que 0% a 5% e um teor de al de mais do que 0% a 1,0% na superfície da folha de aço, sendo que 20% ou mais da interface inteira da camada galvanizada por imersão a quente e da folha de aço de base é adicionalmente revestida pela fase ¿, sendo que uma interface formada pela camada de aço de base e grânulos ¿ em que óxido grosso está presente entre os grânulos de cristal ¿ é 50% ou menos da interface inteira da fase ¿ e a folha de aço de base na camada galvanizada por imersão a quente, em que a camada de aço de base tem uma composição química específica e tem uma camada refinada diretamente adjacente à interface da folha de aço de base e da camada galvanizada por imersão a quente, sendo que a espessura média da camada refinada é 0,1 a 5,0 µm, sendo que o tamanho de grânulo médio de ferrita na camada refinada é 0,1 a 3,0 µm, em que a camada refinada contém um ou mais óxidos de si e mn e sendo que o diâmetro máximo dos óxidos é 0,01 a 0,4 µm.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014225398 | 2014-11-05 | ||
PCT/JP2015/081236 WO2016072478A1 (ja) | 2014-11-05 | 2015-11-05 | 溶融亜鉛めっき鋼板 |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112017007973A2 true BR112017007973A2 (pt) | 2017-12-19 |
Family
ID=55909199
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112017007973A BR112017007973A2 (pt) | 2014-11-05 | 2015-11-05 | folha de aço galvanizada por imersão a quente |
BR112017008043A BR112017008043A2 (pt) | 2014-11-05 | 2015-11-05 | chapa de aço galvanizada por imersão a quente |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112017008043A BR112017008043A2 (pt) | 2014-11-05 | 2015-11-05 | chapa de aço galvanizada por imersão a quente |
Country Status (11)
Country | Link |
---|---|
US (2) | US10822683B2 (pt) |
EP (2) | EP3216892B1 (pt) |
JP (2) | JP6519028B2 (pt) |
KR (2) | KR101913989B1 (pt) |
CN (2) | CN107148492B (pt) |
BR (2) | BR112017007973A2 (pt) |
ES (2) | ES2775480T3 (pt) |
MX (2) | MX2017005503A (pt) |
PL (2) | PL3216892T3 (pt) |
TW (2) | TWI558820B (pt) |
WO (2) | WO2016072475A1 (pt) |
Families Citing this family (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107109554B (zh) | 2014-11-05 | 2018-11-09 | 新日铁住金株式会社 | 热浸镀锌钢板 |
JP6519028B2 (ja) | 2014-11-05 | 2019-05-29 | 日本製鉄株式会社 | 溶融亜鉛めっき鋼板 |
JP6358406B2 (ja) * | 2016-08-05 | 2018-07-18 | 新日鐵住金株式会社 | 鋼板及びめっき鋼板 |
JP6892842B2 (ja) * | 2017-06-29 | 2021-06-23 | Jfeスチール株式会社 | 高強度冷延鋼板用の素材熱延鋼板およびその製造方法 |
JP6281671B1 (ja) * | 2017-07-31 | 2018-02-21 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼板 |
WO2019026113A1 (ja) * | 2017-07-31 | 2019-02-07 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼板 |
US11426975B2 (en) * | 2017-07-31 | 2022-08-30 | Nippon Steel Corporation | Hot-dip galvanized steel sheet |
TWI671410B (zh) * | 2018-03-30 | 2019-09-11 | 日商日本製鐵股份有限公司 | 鋼板及其製造方法 |
MX2020009987A (es) * | 2018-03-30 | 2020-10-14 | Nippon Steel Corp | Lamina de acero y metodo para fabricar la misma. |
KR102416183B1 (ko) * | 2018-04-13 | 2022-07-05 | 닛폰세이테츠 가부시키가이샤 | Ni 확산 도금 강판 및 Ni 확산 도금 강판의 제조 방법 |
US11878488B2 (en) * | 2020-03-23 | 2024-01-23 | Nippon Steel Corporation | Hot stamped component |
CN113355562B (zh) * | 2021-07-05 | 2022-11-25 | 华南理工大学 | 批量热浸锌铝镁合金镀层及其制备方法和应用 |
CN115558876B (zh) * | 2022-09-09 | 2024-05-10 | 首钢集团有限公司 | 一种热镀锌钢板及其制备方法 |
Family Cites Families (44)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5112575B1 (pt) * | 1970-12-30 | 1976-04-20 | ||
JPS533153B2 (pt) | 1974-07-19 | 1978-02-03 | ||
JP3198902B2 (ja) * | 1995-12-11 | 2001-08-13 | 日本鋼管株式会社 | 薄目付け溶融亜鉛めっき鋼板の製造方法 |
JP3139353B2 (ja) | 1995-12-11 | 2001-02-26 | 日本鋼管株式会社 | 薄目付け溶融亜鉛めっき鋼板の製造方法 |
JP3126911B2 (ja) | 1995-12-27 | 2001-01-22 | 川崎製鉄株式会社 | めっき密着性の良好な高強度溶融亜鉛めっき鋼板 |
JPH09241812A (ja) | 1996-03-01 | 1997-09-16 | Kobe Steel Ltd | 合金化溶融亜鉛めっき鋼板 |
JP3520741B2 (ja) | 1997-11-05 | 2004-04-19 | Jfeスチール株式会社 | めっき密着性に優れた合金化溶融亜鉛めっき鋼板 |
CA2310335C (en) | 1998-09-29 | 2009-05-19 | Kawasaki Steel Corporation | High strength thin steel sheet, high strength galvannealed steel sheet and manufacturing method thereof |
JP3752898B2 (ja) | 1999-07-15 | 2006-03-08 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法 |
JP4552310B2 (ja) | 1999-11-08 | 2010-09-29 | Jfeスチール株式会社 | 強度−延性バランスとめっき密着性に優れた溶融亜鉛めっき鋼板およびその製造方法 |
JP3661559B2 (ja) | 2000-04-25 | 2005-06-15 | 住友金属工業株式会社 | 加工性とめっき密着性に優れた合金化溶融亜鉛めっき高張力鋼板とその製造方法 |
JP3536814B2 (ja) * | 2000-11-29 | 2004-06-14 | 住友金属工業株式会社 | 美麗な溶融亜鉛めっき鋼板およびその製造方法 |
JP3898923B2 (ja) | 2001-06-06 | 2007-03-28 | 新日本製鐵株式会社 | 高加工時のめっき密着性および延性に優れた高強度溶融Znめっき鋼板及びその製造方法 |
JP5087813B2 (ja) | 2001-08-31 | 2012-12-05 | Jfeスチール株式会社 | めっき性に優れた高張力溶融亜鉛めっき鋼板およびその製造方法 |
JP4631241B2 (ja) | 2001-09-21 | 2011-02-16 | Jfeスチール株式会社 | 強度延性バランス、めっき密着性と耐食性に優れた高張力溶融亜鉛めっき鋼板および高張力合金化溶融亜鉛めっき鋼板 |
JP2004124187A (ja) | 2002-10-03 | 2004-04-22 | Sumitomo Metal Ind Ltd | 密着性・溶接性に優れた高強度溶融亜鉛めっき鋼板 |
JP4119804B2 (ja) | 2003-08-19 | 2008-07-16 | 新日本製鐵株式会社 | 密着性の優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法 |
JP4192051B2 (ja) | 2003-08-19 | 2008-12-03 | 新日本製鐵株式会社 | 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備 |
JP4457673B2 (ja) | 2004-01-19 | 2010-04-28 | Jfeスチール株式会社 | 耐二次加工脆性およびめっき密着性に優れた高成形性燃料タンク用めっき冷延鋼板およびその製造方法 |
JP4966485B2 (ja) | 2004-08-25 | 2012-07-04 | 住友金属工業株式会社 | 高張力溶融亜鉛めっき鋼板とその製造方法 |
JP4837464B2 (ja) | 2006-07-11 | 2011-12-14 | 新日本製鐵株式会社 | めっき密着性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法 |
PL1980638T3 (pl) | 2006-01-30 | 2014-03-31 | Nippon Steel & Sumitomo Metal Corp | Wysokowytrzymała blacha cynkowana ogniowo o doskonałej podatności na formowanie i nadająca się do platerowania, wysokowytrzymała stopowa blacha cynkowana ogniowo oraz procesy i urządzenie do ich wytwarzania |
JP4790525B2 (ja) | 2006-07-19 | 2011-10-12 | 新日本製鐵株式会社 | 耐チッピング性に優れた高強度合金化溶融めっき鋼板 |
BRPI1010678A2 (pt) | 2009-05-27 | 2016-03-15 | Nippon Steel Corp | chapade aço de alta resistência, chapa de aço banhada a quente e chapa de aço banhada a quente de liga que têm excelentes características de fadiga, alongamento e colisão, e método de fabricação para as ditas chapas de aço |
JP5703608B2 (ja) | 2009-07-30 | 2015-04-22 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
US10023947B2 (en) * | 2009-11-30 | 2018-07-17 | Nippon Steel & Sumitomo Metal Corporation | High strength steel plate with ultimate tensile strength of 900 MPa or more excellent in hydrogen embrittlement resistance and method of production of same |
JP5370104B2 (ja) * | 2009-11-30 | 2013-12-18 | 新日鐵住金株式会社 | 耐水素脆化特性に優れた引張最大強度900MPa以上の高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法 |
JP5434960B2 (ja) | 2010-05-31 | 2014-03-05 | Jfeスチール株式会社 | 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法 |
ES2698392T3 (es) * | 2010-07-09 | 2019-02-04 | Nippon Steel & Sumitomo Metal Corp | Chapa de acero galvanizado |
US20120100391A1 (en) * | 2010-10-21 | 2012-04-26 | Posco | Hot-dip galvanized steel sheet having excellent plating qualities, plating adhesion and spot weldability and manufacturing method thereof |
KR20120041544A (ko) * | 2010-10-21 | 2012-05-02 | 주식회사 포스코 | 도금성, 도금밀착성 및 스폿용접성이 우수한 용융아연도금강판 및 그 제조방법 |
JP5273324B1 (ja) | 2011-07-29 | 2013-08-28 | 新日鐵住金株式会社 | 曲げ性に優れた高強度亜鉛めっき鋼板およびその製造方法 |
EP2762589B8 (en) | 2011-09-30 | 2017-10-04 | Nippon Steel & Sumitomo Metal Corporation | High-strength hot-dip galvanized steel sheet excellent in impact resistance property and manufacturing method thereof, and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof |
ES2732799T3 (es) | 2011-09-30 | 2019-11-26 | Nippon Steel Corp | Chapa de acero galvanizada por inmersión en caliente y método de fabricación de la misma |
RU2576567C2 (ru) | 2011-09-30 | 2016-03-10 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Легированный, гальванизированный погружением стальной лист |
US9708679B2 (en) | 2011-09-30 | 2017-07-18 | Nippon Steel & Sumitomo Metal Corporation | High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet excellent in mechanical cutting property, and manufacturing method thereof |
EP2762582B1 (en) * | 2011-09-30 | 2019-03-06 | Nippon Steel & Sumitomo Metal Corporation | High-strength galvannealed steel sheet of high bake hardenability, high-strength alloyed galvannealed steel sheet, and method for manufacturing same |
RU2585889C2 (ru) * | 2011-09-30 | 2016-06-10 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Высокопрочный горячеоцинкованный стальной лист, имеющий превосходное сопротивление замедленному разрушению, и способ его изготовления |
EP2765212B1 (en) * | 2011-10-04 | 2017-05-17 | JFE Steel Corporation | High-strength steel sheet and method for manufacturing same |
TWI468534B (zh) * | 2012-02-08 | 2015-01-11 | Nippon Steel & Sumitomo Metal Corp | 高強度冷軋鋼板及其製造方法 |
CN102787271A (zh) * | 2012-07-17 | 2012-11-21 | 马钢(集团)控股有限公司 | 一种460MPa级高表面质量结构用热镀锌钢板的生产方法及其产品 |
KR101403076B1 (ko) | 2012-09-03 | 2014-06-02 | 주식회사 포스코 | 신장 플랜지성 및 도금밀착성이 우수한 고강도 합금화 용융아연도금강판 및 그 제조방법 |
CN107109554B (zh) | 2014-11-05 | 2018-11-09 | 新日铁住金株式会社 | 热浸镀锌钢板 |
JP6519028B2 (ja) | 2014-11-05 | 2019-05-29 | 日本製鉄株式会社 | 溶融亜鉛めっき鋼板 |
-
2015
- 2015-11-05 JP JP2016557817A patent/JP6519028B2/ja active Active
- 2015-11-05 US US15/521,535 patent/US10822683B2/en active Active
- 2015-11-05 KR KR1020177012050A patent/KR101913989B1/ko active IP Right Grant
- 2015-11-05 BR BR112017007973A patent/BR112017007973A2/pt not_active Application Discontinuation
- 2015-11-05 ES ES15857121T patent/ES2775480T3/es active Active
- 2015-11-05 WO PCT/JP2015/081231 patent/WO2016072475A1/ja active Application Filing
- 2015-11-05 CN CN201580058649.1A patent/CN107148492B/zh active Active
- 2015-11-05 EP EP15857863.3A patent/EP3216892B1/en active Active
- 2015-11-05 TW TW104136605A patent/TWI558820B/zh not_active IP Right Cessation
- 2015-11-05 EP EP15857121.6A patent/EP3216891B1/en active Active
- 2015-11-05 BR BR112017008043A patent/BR112017008043A2/pt active Search and Examination
- 2015-11-05 WO PCT/JP2015/081236 patent/WO2016072478A1/ja active Application Filing
- 2015-11-05 JP JP2016557814A patent/JP6365681B2/ja active Active
- 2015-11-05 PL PL15857863T patent/PL3216892T3/pl unknown
- 2015-11-05 KR KR1020177011181A patent/KR101918876B1/ko active IP Right Grant
- 2015-11-05 ES ES15857863T patent/ES2748019T3/es active Active
- 2015-11-05 TW TW104136604A patent/TWI601848B/zh not_active IP Right Cessation
- 2015-11-05 PL PL15857121T patent/PL3216891T3/pl unknown
- 2015-11-05 MX MX2017005503A patent/MX2017005503A/es unknown
- 2015-11-05 MX MX2017005505A patent/MX2017005505A/es unknown
- 2015-11-05 CN CN201580058632.6A patent/CN107148491B/zh active Active
- 2015-11-05 US US15/522,243 patent/US10822684B2/en active Active
Also Published As
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112017007973A2 (pt) | folha de aço galvanizada por imersão a quente | |
BR112017008311A2 (pt) | folha de aço galvanizada por mergulho a quente | |
BR112015001774A2 (pt) | chapa de aço galvanizada para conformação a quente | |
BR112017008460A2 (pt) | chapa de aço galvanizada por imersão a quente | |
BR112018010352A2 (pt) | método para marcar um substrato, substrato marcado, produto, e, uso de um substrato marcado. | |
BR112017017291A2 (pt) | chapa de aço laminada a quente | |
BR112019000965A2 (pt) | material de mancal de deslizamento de alumínio livre de chumbo com superfície funcional | |
BR112018010665A8 (pt) | ?método para fabricação de um material de acondicionamento laminado, material de acondicionamento laminado, e, recipiente de acondicionamento? | |
WO2014130582A3 (en) | Compounds useful as modulators of trpm8 | |
BR112014007483A2 (pt) | folha de aço galvanizado a quente de alta resistência que possui excelente resistência à fratura retardada e método de fabricação da mesma | |
BR112016021766A2 (pt) | Elemento chapa de aço conformado a quente de alta resistência | |
BR112017016840A2 (pt) | filme decorativo e artigo integrado no mesmo | |
BR112015016797A2 (pt) | reator dotado de um refrigerador | |
BR112017004711A2 (pt) | chapa de aço laminada a quente | |
TW201614284A (en) | Polarizing plate with pressure-sensitive adhesive layer | |
BR112016025251A2 (pt) | método para revestimento de uma tira de metal em movimento e tira de metal revestida pelo que produzida | |
BR112015026523A2 (pt) | aço limpo com baixo teor de oxigênio e produto de aço limpo com baixo teor de oxigênio | |
BR112015016722A2 (pt) | óleo de máquina de refrigeração e composição de fluido de trabalho para máquina de refrigeração | |
BR112016020313A2 (pt) | Método para incorporação de micronutrientes no invólucro externo de partículas baseadas em ureia | |
BR112015026344A2 (pt) | camada de proteção contra oxidação baseada em cromo | |
BR112015003894A2 (pt) | materiais revestidos com bioflavonoide | |
BR112019008329A2 (pt) | chapa de aço para carburação, e método de fabricação da chapa de aço para carburação | |
BR112015030003A2 (pt) | chapa de aço laminada a frio, chapa de aço laminada a frio galvanizada e método de produção da mesma | |
BR112012030807A2 (pt) | esferas flutuantes e sua utilização para formar barreiras de gás em superfícies líquidas | |
BR112018003267A2 (pt) | chapa de aço |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL CORPORATION (JP) |
|
B06U | Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette] | ||
B07A | Application suspended after technical examination (opinion) [chapter 7.1 patent gazette] | ||
B09B | Patent application refused [chapter 9.2 patent gazette] | ||
B09B | Patent application refused [chapter 9.2 patent gazette] |
Free format text: MANTIDO O INDEFERIMENTO UMA VEZ QUE NAO FOI APRESENTADO RECURSO DENTRO DO PRAZO LEGAL |