ZA200600314B - Process for preparing boehmitic aluminas having a high-a-conversion temperature - Google Patents
Process for preparing boehmitic aluminas having a high-a-conversion temperature Download PDFInfo
- Publication number
- ZA200600314B ZA200600314B ZA200600314A ZA200600314A ZA200600314B ZA 200600314 B ZA200600314 B ZA 200600314B ZA 200600314 A ZA200600314 A ZA 200600314A ZA 200600314 A ZA200600314 A ZA 200600314A ZA 200600314 B ZA200600314 B ZA 200600314B
- Authority
- ZA
- South Africa
- Prior art keywords
- aluminas
- hydrolysis
- acids
- aging
- alumina
- Prior art date
Links
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 8
- 238000006243 chemical reaction Methods 0.000 title description 25
- 230000007062 hydrolysis Effects 0.000 claims abstract description 28
- 238000006460 hydrolysis reaction Methods 0.000 claims abstract description 28
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims abstract description 16
- 238000000034 method Methods 0.000 claims abstract description 15
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims abstract description 11
- 229910052782 aluminium Inorganic materials 0.000 claims abstract description 11
- 239000012670 alkaline solution Substances 0.000 claims abstract description 5
- 230000032683 aging Effects 0.000 claims description 28
- 239000011148 porous material Substances 0.000 claims description 22
- 239000002253 acid Substances 0.000 claims description 18
- 150000007513 acids Chemical class 0.000 claims description 15
- 150000001735 carboxylic acids Chemical class 0.000 claims description 11
- 239000004411 aluminium Substances 0.000 claims description 9
- 238000001354 calcination Methods 0.000 claims description 9
- 239000013078 crystal Substances 0.000 claims description 8
- 239000000203 mixture Substances 0.000 claims description 8
- 150000003839 salts Chemical class 0.000 claims description 6
- 239000003054 catalyst Substances 0.000 claims description 5
- 150000001413 amino acids Chemical class 0.000 claims description 4
- 125000003277 amino group Chemical group 0.000 claims description 3
- -1 carboxy- Chemical class 0.000 claims description 3
- 239000000969 carrier Substances 0.000 claims description 3
- 239000007787 solid Substances 0.000 claims description 3
- BVKZGUZCCUSVTD-UHFFFAOYSA-N carbonic acid Chemical class OC(O)=O BVKZGUZCCUSVTD-UHFFFAOYSA-N 0.000 claims description 2
- 238000006555 catalytic reaction Methods 0.000 claims description 2
- 125000001424 substituent group Chemical group 0.000 claims description 2
- 150000003628 tricarboxylic acids Chemical class 0.000 claims description 2
- 239000007900 aqueous suspension Substances 0.000 claims 1
- 239000006185 dispersion Substances 0.000 claims 1
- 230000007935 neutral effect Effects 0.000 claims 1
- 239000002245 particle Substances 0.000 claims 1
- 150000004677 hydrates Chemical class 0.000 abstract description 2
- KRKNYBCHXYNGOX-UHFFFAOYSA-N citric acid Chemical compound OC(=O)CC(O)(C(O)=O)CC(O)=O KRKNYBCHXYNGOX-UHFFFAOYSA-N 0.000 description 14
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 13
- 239000000047 product Substances 0.000 description 11
- NLXLAEXVIDQMFP-UHFFFAOYSA-N Ammonium chloride Substances [NH4+].[Cl-] NLXLAEXVIDQMFP-UHFFFAOYSA-N 0.000 description 10
- VHUUQVKOLVNVRT-UHFFFAOYSA-N Ammonium hydroxide Chemical compound [NH4+].[OH-] VHUUQVKOLVNVRT-UHFFFAOYSA-N 0.000 description 10
- 235000011114 ammonium hydroxide Nutrition 0.000 description 10
- QFCVQKSWGFVMTB-UHFFFAOYSA-N trihexoxyalumane Chemical compound [Al+3].CCCCCC[O-].CCCCCC[O-].CCCCCC[O-] QFCVQKSWGFVMTB-UHFFFAOYSA-N 0.000 description 10
- MTCFGRXMJLQNBG-REOHCLBHSA-N (2S)-2-Amino-3-hydroxypropansäure Chemical compound OC[C@H](N)C(O)=O MTCFGRXMJLQNBG-REOHCLBHSA-N 0.000 description 8
- 150000001732 carboxylic acid derivatives Chemical class 0.000 description 8
- 239000002002 slurry Substances 0.000 description 7
- ROHFNLRQFUQHCH-YFKPBYRVSA-N L-leucine Chemical compound CC(C)C[C@H](N)C(O)=O ROHFNLRQFUQHCH-YFKPBYRVSA-N 0.000 description 6
- 235000015165 citric acid Nutrition 0.000 description 5
- CKLJMWTZIZZHCS-UHFFFAOYSA-N D-OH-Asp Natural products OC(=O)C(N)CC(O)=O CKLJMWTZIZZHCS-UHFFFAOYSA-N 0.000 description 4
- DHMQDGOQFOQNFH-UHFFFAOYSA-N Glycine Chemical compound NCC(O)=O DHMQDGOQFOQNFH-UHFFFAOYSA-N 0.000 description 4
- CKLJMWTZIZZHCS-UWTATZPHSA-N L-Aspartic acid Natural products OC(=O)[C@H](N)CC(O)=O CKLJMWTZIZZHCS-UWTATZPHSA-N 0.000 description 4
- CKLJMWTZIZZHCS-REOHCLBHSA-N L-aspartic acid Chemical compound OC(=O)[C@@H](N)CC(O)=O CKLJMWTZIZZHCS-REOHCLBHSA-N 0.000 description 4
- LCTONWCANYUPML-UHFFFAOYSA-N Pyruvic acid Chemical compound CC(=O)C(O)=O LCTONWCANYUPML-UHFFFAOYSA-N 0.000 description 4
- 229960005261 aspartic acid Drugs 0.000 description 4
- JVTAAEKCZFNVCJ-UHFFFAOYSA-N lactic acid Chemical compound CC(O)C(O)=O JVTAAEKCZFNVCJ-UHFFFAOYSA-N 0.000 description 4
- BJEPYKJPYRNKOW-UHFFFAOYSA-N malic acid Chemical compound OC(=O)C(O)CC(O)=O BJEPYKJPYRNKOW-UHFFFAOYSA-N 0.000 description 4
- 229960001153 serine Drugs 0.000 description 4
- 239000004395 L-leucine Substances 0.000 description 3
- 235000019454 L-leucine Nutrition 0.000 description 3
- 229940024606 amino acid Drugs 0.000 description 3
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 3
- 229960003136 leucine Drugs 0.000 description 3
- 235000011090 malic acid Nutrition 0.000 description 3
- 230000000704 physical effect Effects 0.000 description 3
- 238000003756 stirring Methods 0.000 description 3
- BJEPYKJPYRNKOW-REOHCLBHSA-N (S)-malic acid Chemical compound OC(=O)[C@@H](O)CC(O)=O BJEPYKJPYRNKOW-REOHCLBHSA-N 0.000 description 2
- UPVJICOVGRISCL-UHFFFAOYSA-N 2-hydroxy-2-(1-hydroxypropyl)propanedioic acid Chemical compound CCC(O)C(O)(C(O)=O)C(O)=O UPVJICOVGRISCL-UHFFFAOYSA-N 0.000 description 2
- QAOBWZAHOFFKKR-UHFFFAOYSA-N 2-hydroxy-2-propylpropanedioic acid Chemical compound CCCC(O)(C(O)=O)C(O)=O QAOBWZAHOFFKKR-UHFFFAOYSA-N 0.000 description 2
- FZIPCQLKPTZZIM-UHFFFAOYSA-N 2-oxidanylpropane-1,2,3-tricarboxylic acid Chemical compound OC(=O)CC(O)(C(O)=O)CC(O)=O.OC(=O)CC(O)(C(O)=O)CC(O)=O FZIPCQLKPTZZIM-UHFFFAOYSA-N 0.000 description 2
- QGZKDVFQNNGYKY-UHFFFAOYSA-N Ammonia Chemical compound N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 description 2
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 2
- 239000004471 Glycine Substances 0.000 description 2
- 230000004913 activation Effects 0.000 description 2
- 239000000654 additive Substances 0.000 description 2
- 150000003863 ammonium salts Chemical class 0.000 description 2
- KLOIYEQEVSIOOO-UHFFFAOYSA-N carbocromen Chemical compound CC1=C(CCN(CC)CC)C(=O)OC2=CC(OCC(=O)OCC)=CC=C21 KLOIYEQEVSIOOO-UHFFFAOYSA-N 0.000 description 2
- 238000011109 contamination Methods 0.000 description 2
- 229910052593 corundum Inorganic materials 0.000 description 2
- 229960002449 glycine Drugs 0.000 description 2
- 125000002887 hydroxy group Chemical group [H]O* 0.000 description 2
- 239000001630 malic acid Substances 0.000 description 2
- 229910052751 metal Inorganic materials 0.000 description 2
- 239000002184 metal Substances 0.000 description 2
- 150000002739 metals Chemical class 0.000 description 2
- 125000004043 oxo group Chemical group O=* 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 239000000725 suspension Substances 0.000 description 2
- 238000002076 thermal analysis method Methods 0.000 description 2
- HWKRAUXFMLQKLS-UHFFFAOYSA-N 2-oxidanylidenepropanoic acid Chemical compound CC(=O)C(O)=O.CC(=O)C(O)=O HWKRAUXFMLQKLS-UHFFFAOYSA-N 0.000 description 1
- KVZLHPXEUGJPAH-UHFFFAOYSA-N 2-oxidanylpropanoic acid Chemical compound CC(O)C(O)=O.CC(O)C(O)=O KVZLHPXEUGJPAH-UHFFFAOYSA-N 0.000 description 1
- ZZBAGJPKGRJIJH-UHFFFAOYSA-N 7h-purine-2-carbaldehyde Chemical compound O=CC1=NC=C2NC=NC2=N1 ZZBAGJPKGRJIJH-UHFFFAOYSA-N 0.000 description 1
- KRKNYBCHXYNGOX-UHFFFAOYSA-K Citrate Chemical compound [O-]C(=O)CC(O)(CC([O-])=O)C([O-])=O KRKNYBCHXYNGOX-UHFFFAOYSA-K 0.000 description 1
- FEWJPZIEWOKRBE-JCYAYHJZSA-N Dextrotartaric acid Chemical compound OC(=O)[C@H](O)[C@@H](O)C(O)=O FEWJPZIEWOKRBE-JCYAYHJZSA-N 0.000 description 1
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 1
- 239000001358 L(+)-tartaric acid Substances 0.000 description 1
- 235000011002 L(+)-tartaric acid Nutrition 0.000 description 1
- FEWJPZIEWOKRBE-LWMBPPNESA-N L-(+)-Tartaric acid Natural products OC(=O)[C@@H](O)[C@H](O)C(O)=O FEWJPZIEWOKRBE-LWMBPPNESA-N 0.000 description 1
- QIVBCDIJIAJPQS-VIFPVBQESA-N L-tryptophane Chemical compound C1=CC=C2C(C[C@H](N)C(O)=O)=CNC2=C1 QIVBCDIJIAJPQS-VIFPVBQESA-N 0.000 description 1
- SXFBQAMLJMDXOD-ZVGUSBNCSA-N OC(=O)C(O)C(O)C(O)=O.OC(=O)[C@H](O)[C@@H](O)C(O)=O Chemical compound OC(=O)C(O)C(O)C(O)=O.OC(=O)[C@H](O)[C@@H](O)C(O)=O SXFBQAMLJMDXOD-ZVGUSBNCSA-N 0.000 description 1
- QAOWNCQODCNURD-UHFFFAOYSA-L Sulfate Chemical compound [O-]S([O-])(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-L 0.000 description 1
- FEWJPZIEWOKRBE-UHFFFAOYSA-N Tartaric acid Natural products [H+].[H+].[O-]C(=O)C(O)C(O)C([O-])=O FEWJPZIEWOKRBE-UHFFFAOYSA-N 0.000 description 1
- XFBXDGLHUSUNMG-UHFFFAOYSA-N alumane;hydrate Chemical class O.[AlH3] XFBXDGLHUSUNMG-UHFFFAOYSA-N 0.000 description 1
- WNROFYMDJYEPJX-UHFFFAOYSA-K aluminium hydroxide Chemical class [OH-].[OH-].[OH-].[Al+3] WNROFYMDJYEPJX-UHFFFAOYSA-K 0.000 description 1
- 229910021502 aluminium hydroxide Inorganic materials 0.000 description 1
- 229910021529 ammonia Inorganic materials 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- 150000001450 anions Chemical class 0.000 description 1
- 125000004432 carbon atom Chemical group C* 0.000 description 1
- 230000015556 catabolic process Effects 0.000 description 1
- 230000000052 comparative effect Effects 0.000 description 1
- 238000012790 confirmation Methods 0.000 description 1
- 239000010431 corundum Substances 0.000 description 1
- 238000006731 degradation reaction Methods 0.000 description 1
- 230000018109 developmental process Effects 0.000 description 1
- 238000009826 distribution Methods 0.000 description 1
- 230000002349 favourable effect Effects 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 230000003301 hydrolyzing effect Effects 0.000 description 1
- 239000004310 lactic acid Substances 0.000 description 1
- 235000014655 lactic acid Nutrition 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 description 1
- 229910052753 mercury Inorganic materials 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 150000004682 monohydrates Chemical class 0.000 description 1
- 230000035515 penetration Effects 0.000 description 1
- 238000001556 precipitation Methods 0.000 description 1
- 238000010926 purge Methods 0.000 description 1
- 238000000746 purification Methods 0.000 description 1
- 229940107700 pyruvic acid Drugs 0.000 description 1
- 229910052708 sodium Inorganic materials 0.000 description 1
- 239000011734 sodium Substances 0.000 description 1
- 238000001179 sorption measurement Methods 0.000 description 1
- 238000001694 spray drying Methods 0.000 description 1
- 239000006228 supernatant Substances 0.000 description 1
- 238000003878 thermal aging Methods 0.000 description 1
- 238000002411 thermogravimetry Methods 0.000 description 1
- 229960004799 tryptophan Drugs 0.000 description 1
- 229960004441 tyrosine Drugs 0.000 description 1
- 229910001845 yogo sapphire Inorganic materials 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
- B01J21/04—Alumina
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/03—Precipitation; Co-precipitation
- B01J37/031—Precipitation
- B01J37/033—Using Hydrolysis
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F7/00—Compounds of aluminium
- C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F7/00—Compounds of aluminium
- C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
- C01F7/34—Preparation of aluminium hydroxide by precipitation from solutions containing aluminium salts
- C01F7/36—Preparation of aluminium hydroxide by precipitation from solutions containing aluminium salts from organic aluminium salts
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F7/00—Compounds of aluminium
- C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
- C01F7/44—Dehydration of aluminium oxide or hydroxide, i.e. all conversions of one form into another involving a loss of water
- C01F7/447—Dehydration of aluminium oxide or hydroxide, i.e. all conversions of one form into another involving a loss of water by wet processes
- C01F7/448—Dehydration of aluminium oxide or hydroxide, i.e. all conversions of one form into another involving a loss of water by wet processes using superatmospheric pressure, e.g. hydrothermal conversion of gibbsite into boehmite
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/10—Particle morphology extending in one dimension, e.g. needle-like
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/20—Particle morphology extending in two dimensions, e.g. plate-like
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/12—Surface area
- C01P2006/13—Surface area thermal stability thereof at high temperatures
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/14—Pore volume
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/16—Pore diameter
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/32—Thermal properties
- C01P2006/33—Phase transition temperatures
- C01P2006/36—Solid to solid transition temperatures
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Life Sciences & Earth Sciences (AREA)
- Materials Engineering (AREA)
- Inorganic Chemistry (AREA)
- Geology (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Nanotechnology (AREA)
- General Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- Composite Materials (AREA)
- Physics & Mathematics (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
- Catalysts (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Compositions Of Oxide Ceramics (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE10332775A DE10332775A1 (de) | 2003-07-17 | 2003-07-17 | Verfahren zur Herstellung böhmitischer Tonerden mit hoher a-Umwandlungstemperatur |
Publications (1)
Publication Number | Publication Date |
---|---|
ZA200600314B true ZA200600314B (en) | 2007-03-28 |
Family
ID=34071765
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ZA200600314A ZA200600314B (en) | 2003-07-17 | 2006-01-12 | Process for preparing boehmitic aluminas having a high-a-conversion temperature |
Country Status (9)
Country | Link |
---|---|
US (1) | US8147795B2 (ja) |
EP (1) | EP1646583B1 (ja) |
JP (1) | JP5132149B2 (ja) |
CN (1) | CN100404424C (ja) |
AT (1) | ATE554052T1 (ja) |
DE (1) | DE10332775A1 (ja) |
DK (1) | DK1646583T3 (ja) |
WO (1) | WO2005014482A2 (ja) |
ZA (1) | ZA200600314B (ja) |
Families Citing this family (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB0428557D0 (en) * | 2004-12-30 | 2005-02-09 | Magnesium Elektron Ltd | Thermally stable doped and undoped porous aluminium oxides and nanocomposite CeO -ZrO and A1 O containing mixed oxides |
MX2007014159A (es) * | 2005-05-12 | 2008-02-07 | Solvay | Catalizador y proceso de oxicloracion en el que se usa dicho catalizador. |
US8642001B2 (en) * | 2007-02-27 | 2014-02-04 | Albemarle Corporation | Aluminum hydroxide |
CN106517477A (zh) | 2009-09-18 | 2017-03-22 | 得克萨斯州A&M大学*** | 用于处理被污染流体的零价铁/氧化铁矿物/亚铁复合物 |
US10377648B2 (en) | 2009-09-18 | 2019-08-13 | The Texas A&M University System | Selenium removal using aluminum salt at conditioning and reaction stages to activate zero-valent iron (ZVI) in pironox process |
EP2686458A4 (en) | 2011-03-18 | 2015-04-15 | Orbite Aluminae Inc | METHODS FOR RECOVERING RARE EARTH ELEMENTS FROM ALUMINUM-CONTAINING MATERIALS |
CN103857810A (zh) | 2011-05-04 | 2014-06-11 | 奥贝特铝业有限公司 | 用于从各种矿石中回收稀土元素的方法 |
US9150428B2 (en) | 2011-06-03 | 2015-10-06 | Orbite Aluminae Inc. | Methods for separating iron ions from aluminum ions |
DE102011107702A1 (de) | 2011-07-14 | 2013-01-17 | Sasol Germany Gmbh | Verfahren zur Herstellung von Kompositen aus Aluminiumoxid und Cer-/Zirkonium-Mischoxiden |
WO2013007809A1 (en) | 2011-07-14 | 2013-01-17 | Treibacher Industrie Ag | Ceria zirconia alumina composition with enhanced thermal stability |
RU2014114938A (ru) | 2011-09-16 | 2015-10-27 | Орбит Элюминэ Инк. | Способы получения оксида алюминия и разнообразных других продуктов |
MX345108B (es) | 2011-12-15 | 2017-01-17 | Federal Mogul Sa | Dispositivo limpiaparabrisas. |
RU2579843C2 (ru) | 2012-01-10 | 2016-04-10 | Орбит Текнолоджис Инк. | Способы обработки красного шлама |
CA2903512C (en) | 2012-03-29 | 2017-12-05 | Orbite Technologies Inc. | Processes for treating fly ashes |
CN102730726B (zh) * | 2012-07-02 | 2014-08-27 | 泰山医学院 | 一种利用酯化反应水热法制备勃姆石粉体的方法 |
MY175471A (en) | 2012-07-12 | 2020-06-29 | Orbite Tech Inc | Processes for preparing titanium oxide and various other products |
AU2013298173B2 (en) | 2012-08-02 | 2016-11-24 | Sasol Technology (Proprietary) Limited | Catalysts |
JP2015535886A (ja) | 2012-09-26 | 2015-12-17 | オーバイト アルミナ インコーポレイテッドOrbite Aluminae Inc. | 種々の材料のHCl浸出によるアルミナおよび塩化マグネシウムを調製するためのプロセス |
AU2013344721A1 (en) | 2012-11-14 | 2015-07-02 | Orbite Aluminae Inc. | Methods for purifying aluminium ions |
RU2528979C1 (ru) * | 2013-05-13 | 2014-09-20 | Общество с ограниченной ответственностью "ПРИМА" | Способ получения альфа-фазы оксида алюминия |
CN104148096B (zh) * | 2013-05-15 | 2016-05-25 | 中国石油化工股份有限公司 | 一种双金属重整催化剂及其制备方法 |
CN104556176B (zh) * | 2013-10-22 | 2016-11-16 | 中国石油化工股份有限公司 | 一种氧化铝纳米颗粒的制备方法 |
CN106032286B (zh) * | 2015-03-13 | 2017-09-29 | 中国石油化工股份有限公司 | 一种氧化铝的生产方法 |
EP3504159A1 (en) * | 2016-08-29 | 2019-07-03 | Sasol (USA) Corporation | Method of producing an alumina dispersible at a ph greater than 8 |
WO2018110384A1 (ja) * | 2016-12-12 | 2018-06-21 | 多木化学株式会社 | アルミナ粉体 |
EP3599221A1 (en) * | 2018-07-27 | 2020-01-29 | SASOL Germany GmbH | Alpha alumina with high purity and high relative density, a method for its production and its use |
CN112678856B (zh) * | 2019-10-18 | 2022-10-21 | 中国石油化工股份有限公司 | 一种块状晶粒薄水铝石及其制备方法 |
CN112678852B (zh) * | 2019-10-18 | 2022-10-21 | 中国石油化工股份有限公司 | 一种片状晶粒薄水铝石及其制备方法 |
CN111099644A (zh) * | 2019-12-30 | 2020-05-05 | 南京禧通祥盛科技发展有限公司 | 活性超细氢氧化铝的制备方法 |
US20230256420A1 (en) | 2020-06-26 | 2023-08-17 | Basf Se | Shaped catalyst body for the production of ethylene oxide |
JP2023531736A (ja) | 2020-06-26 | 2023-07-25 | ビーエーエスエフ ソシエタス・ヨーロピア | 多孔質触媒支持体成形体 |
CN117545552A (zh) | 2021-06-25 | 2024-02-09 | 巴斯夫欧洲公司 | 高纯度压片阿尔法氧化铝催化剂载体 |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
NL273221A (ja) * | ||||
US2903418A (en) * | 1955-11-03 | 1959-09-08 | Exxon Research Engineering Co | Preparation of eta alumina by acid hydrolysis |
US3152865A (en) | 1961-01-06 | 1964-10-13 | Engelhard Ind Inc | Process for producing a stable alumina monohydrate |
JPS5115005B1 (ja) | 1967-08-29 | 1976-05-13 | ||
DE2446094A1 (de) * | 1974-01-07 | 1975-07-10 | Continental Oil Co | Verfahren zur herstellung von aluminiumoxyd |
US4202870A (en) * | 1979-04-23 | 1980-05-13 | Union Carbide Corporation | Process for producing alumina |
JPS6128335A (ja) | 1984-07-17 | 1986-02-08 | 鐘淵化学工業株式会社 | 保存安定性の改良された製菓・製パン用生地 |
JPH068171B2 (ja) * | 1985-04-30 | 1994-02-02 | 住友化学工業株式会社 | アルミナゾル組成物 |
JPH0664918A (ja) * | 1992-08-21 | 1994-03-08 | Asahi Glass Co Ltd | アルミナ水和物およびアルミナゾルの製造方法 |
US5455019A (en) | 1992-12-25 | 1995-10-03 | Chemical Company, Limited Sumitomo | Continuous process for preparing aluminum hydroxide |
JP3243912B2 (ja) * | 1992-12-25 | 2002-01-07 | 住友化学工業株式会社 | 水酸化アルミニウムの連続製造方法 |
JPH06263436A (ja) | 1993-03-10 | 1994-09-20 | Murata Mfg Co Ltd | 針状ベーマイト微粒子の製造方法 |
DE4337643C1 (de) * | 1993-11-04 | 1995-08-03 | Rwe Dea Ag | Verfahren zur Herstellung von in Wasser dispergierbaren Tonerdehydraten böhmitischer Struktur und Verwendung derselben |
JPH07267633A (ja) * | 1994-03-31 | 1995-10-17 | Kyocera Corp | ベーマイトゾルの作製法並びにそれを用いたアルミナ質多孔質体の作製法 |
DE19515820A1 (de) * | 1995-04-29 | 1996-10-31 | Inst Neue Mat Gemein Gmbh | Verfahren zur Herstellung schwach agglomerierter nanoskaliger Teilchen |
JP3610510B2 (ja) * | 1996-04-23 | 2005-01-12 | 三菱製紙株式会社 | アルミナ水和物分散液の製造方法 |
DE19836821A1 (de) * | 1998-08-14 | 2000-02-24 | Rwe Dea Ag | Böhmitische Tonerden und aus diesen erhältliche phasenreine, hochtemperaturstabile und hochporöse Aluminiumoxide |
DE10035679A1 (de) * | 2000-07-21 | 2002-01-31 | Inst Neue Mat Gemein Gmbh | Nanoskalige Korundpulver, daraus gefertigte Sinterkörper und Verfahren zu deren Herstellung |
JP4756782B2 (ja) * | 2001-07-12 | 2011-08-24 | 大明化学工業株式会社 | α−アルミナの製造方法 |
DE10332776B4 (de) * | 2003-07-17 | 2009-04-09 | Sasol Germany Gmbh | Verfahren zur Herstellung von Aluminiumtrihydraten mit hohem Porenvolumen |
-
2003
- 2003-07-17 DE DE10332775A patent/DE10332775A1/de not_active Withdrawn
-
2004
- 2004-07-16 JP JP2006519893A patent/JP5132149B2/ja not_active Expired - Fee Related
- 2004-07-16 EP EP04741108A patent/EP1646583B1/en not_active Expired - Lifetime
- 2004-07-16 AT AT04741108T patent/ATE554052T1/de active
- 2004-07-16 WO PCT/EP2004/007988 patent/WO2005014482A2/en active Application Filing
- 2004-07-16 DK DK04741108.7T patent/DK1646583T3/da active
- 2004-07-16 US US10/564,244 patent/US8147795B2/en not_active Expired - Fee Related
- 2004-07-16 CN CNB2004800206282A patent/CN100404424C/zh not_active Expired - Fee Related
-
2006
- 2006-01-12 ZA ZA200600314A patent/ZA200600314B/en unknown
Also Published As
Publication number | Publication date |
---|---|
DK1646583T3 (da) | 2012-07-23 |
CN1823009A (zh) | 2006-08-23 |
DE10332775A1 (de) | 2005-02-17 |
US20060246000A1 (en) | 2006-11-02 |
EP1646583B1 (en) | 2012-04-18 |
WO2005014482A3 (en) | 2005-08-25 |
CN100404424C (zh) | 2008-07-23 |
US8147795B2 (en) | 2012-04-03 |
EP1646583A2 (en) | 2006-04-19 |
ATE554052T1 (de) | 2012-05-15 |
JP2009513464A (ja) | 2009-04-02 |
WO2005014482A2 (en) | 2005-02-17 |
JP5132149B2 (ja) | 2013-01-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ZA200600314B (en) | Process for preparing boehmitic aluminas having a high-a-conversion temperature | |
US5002747A (en) | Process for obtaining ceric oxide | |
US4344928A (en) | Process for preparing alumina particulates, at least a fraction of which being ultrafine boehmite | |
CA2841803C (en) | Method for producing composites of aluminum oxide and cerium/zirconium mixed oxides | |
JP5326001B2 (ja) | アルミナまたはオキシ水酸化アルミニウム基材上にランタンペロブスカイトを含む組成物、調製方法および触媒における使用 | |
Osman et al. | Effect of precursor on the performance of alumina for the dehydration of methanol to dimethyl ether | |
EP1200349B2 (en) | Process for the preparation of quasi-crystalline boehmites from inexpensive precursors | |
CA2381301C (en) | Process for the preparation of quasi-crystalline boehmites | |
KR102638941B1 (ko) | 자동차 촉매 컨버터를 위한 세륨, 지르코늄, 알루미늄 및 란타넘으로부터 제조된 내노화성 혼합 산화물 | |
US20080305333A1 (en) | Boehmitic Aluminas and High-Temperature Stable, High-Porosity, Pure-Phase Aluminium Oxides Obtained Therefrom | |
US6555496B1 (en) | Micro-crystalline boehmites containing additives | |
US20060120952A1 (en) | Mesostructured transition aluminas | |
KR20130000419A (ko) | 지르코늄, 세륨 및 1종 이상의 다른 희토류의 산화물을 함유하며 특정 다공도를 갖는 조성물, 그의 제조 방법 및 촉매작용에서의 그의 용도 | |
EP2240273A1 (en) | Low temperature water gas shift catalyst | |
WO2008043060A2 (en) | Highly dispersed nickel hydrogenation catalysts and methods for making the same | |
JP2007524564A (ja) | ジルコニウム、プラセオジム、ランタンまたはネオジムの酸化物を主体とした組成物、その調製方法および触媒系における使用 | |
Amini et al. | Synthesis and Characterization of Amorphous Nano‐Alumina Powders with High Surface Area for Biodiesel Production | |
Byun et al. | Influence of calcination temperature on the structure and properties of Al 2 O 3 as support for Pd catalyst | |
KR20200101417A (ko) | 다공성 알루미늄 하이드레이트 | |
EP2392548B1 (en) | Process for preparing an amorphous silica-alumina composition and relative amorphous silica-alumina composition | |
Bakardjieva et al. | Characteristic of hydrous iron (III) oxides prepared by homogeneous precipitation of iron (III) sulphate with urea | |
JPH08268716A (ja) | 擬ベ−マイト粉の粒径制御方法 | |
US10569255B2 (en) | Hydrocarbon synthesis catalyst, its preparation process and its use | |
CN109569557B (zh) | 一种有序洞结构的氧化钛材料及其制备方法和应用 | |
US20070152181A1 (en) | Mesostructured hydrated alumina - surfactant composite compositions and mesostructured transition alumina compositions derived therefrom |