WO2019188262A1 - 表面処理銅箔及び銅張積層板 - Google Patents

表面処理銅箔及び銅張積層板 Download PDF

Info

Publication number
WO2019188262A1
WO2019188262A1 PCT/JP2019/010096 JP2019010096W WO2019188262A1 WO 2019188262 A1 WO2019188262 A1 WO 2019188262A1 JP 2019010096 W JP2019010096 W JP 2019010096W WO 2019188262 A1 WO2019188262 A1 WO 2019188262A1
Authority
WO
WIPO (PCT)
Prior art keywords
copper foil
silane compound
treated copper
treated
treatment layer
Prior art date
Application number
PCT/JP2019/010096
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
友希 大理
Original Assignee
Ｊｘ金属株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｘ金属株式会社 filed Critical Ｊｘ金属株式会社
Priority to MYPI2020004832A priority Critical patent/MY194720A/en
Priority to CN201980010640.1A priority patent/CN111655900B/zh
Priority to KR1020207020817A priority patent/KR102502018B1/ko
Publication of WO2019188262A1 publication Critical patent/WO2019188262A1/ja
Priority to PH12020551281A priority patent/PH12020551281A1/en

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/48—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 not containing phosphates, hexavalent chromium compounds, fluorides or complex fluorides, molybdates, tungstates, vanadates or oxalates
    • C23C22/52—Treatment of copper or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C26/00—Coating not provided for in groups C23C2/00 - C23C24/00
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K1/00—Printed circuits
    • H05K1/02—Details
    • H05K1/03—Use of materials for the substrate
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2222/00—Aspects relating to chemical surface treatment of metallic material by reaction of the surface with a reactive medium
    • C23C2222/20—Use of solutions containing silanes

Definitions

  • the present invention relates to a surface-treated copper foil and a copper clad laminate.
  • Copper clad laminates are widely used in various applications such as flexible printed wiring boards.
  • This flexible printed wiring board is formed by etching a copper foil of a copper-clad laminate to form a conductor pattern (also referred to as a “wiring pattern”), and connecting and mounting electronic components on the conductor pattern with solder. Manufactured.
  • the loss of signal power in electronic circuits can be roughly divided into two.
  • One is conductor loss, that is, loss due to copper foil
  • the other is dielectric loss, that is, loss due to resin base material.
  • the conductor loss has a skin effect in a high frequency region and has a characteristic that the current flows on the surface of the conductor. Therefore, if the copper foil surface is rough, the current flows along a complicated path. Therefore, in order to reduce the conductor loss, it is desirable to reduce the surface roughness of the copper foil.
  • the dielectric loss depends on the type of the resin base material, it is desirable to use a resin base material formed from a low dielectric material (for example, a liquid crystal polymer or a low dielectric polyimide). Moreover, since dielectric loss is also influenced by the adhesive agent which adhere
  • a silane compound between copper foil and a resin base material
  • the roughened particles electrodeposited on the surface of the copper foil increase the conductor loss due to the skin effect, and cause the phenomenon that the roughened particles, which are called powder fall off, are peeled off. It is desirable to reduce the amount of roughened particles.
  • the number of roughened particles to be electrodeposited on the surface of the copper foil is reduced, the anchor effect by the roughened particles is lowered, and sufficient adhesion between the copper foil and the resin base material cannot be obtained.
  • resin base materials formed from low dielectric materials such as liquid crystal polymers and low dielectric polyimides are less likely to adhere to copper foils than conventional resin base materials.
  • the surface treatment layer of a silane compound has the effect which improves the adhesiveness between copper foil and a resin base material, it cannot be said that the adhesive improvement effect is sufficient depending on the kind.
  • An embodiment of the present invention has been made to solve the above-described problems, and is a surface-treated copper foil capable of improving the adhesion with a resin base material, particularly a resin base material suitable for high-frequency applications.
  • the purpose is to provide.
  • Another object of the present invention is to provide a copper-clad laminate having excellent adhesion between a resin substrate, particularly a resin substrate suitable for high frequency applications, and a surface-treated copper foil.
  • the present inventors have found that the position (mass number: m / z) at which the peak is detected when the surface treatment layer of the silane compound is measured by TOF-SIMS.
  • the present inventors have found that it is related to the adhesion between the surface treatment layer of the silane compound and the resin substrate, and have completed the surface-treated copper foil and the copper clad laminate according to the embodiment of the present invention.
  • the surface-treated copper foil according to the embodiment of the present invention has a surface-treated layer of a silane compound on the surface of the copper foil, and when the surface-treated layer of the silane compound is measured by TOF-SIMS, 240.9 To 241.1, 241.9 to 242.1, 242.9 to 243.1, 243.9 to 244.1, 244.9 to 245.1, 260.9 to 261.1, 261.9 to 262 .1 and 262.9 to 263.1, a peak is detected at the position of at least one mass number (m / z) selected from the group consisting of.
  • the copper clad laminated board which concerns on embodiment of this invention contains the resin base material joined on the surface treatment layer of the said silane compound of the said surface treatment copper foil and the said surface treatment copper foil.
  • the embodiment of the present invention it is possible to provide a surface-treated copper foil capable of enhancing the adhesion with a resin base material, particularly a resin base material suitable for high frequency applications. Moreover, according to embodiment of this invention, the copper clad laminated board excellent in the adhesiveness between a resin base material, especially the resin base material suitable for a high frequency use, and surface-treated copper foil can be provided.
  • FIG. 2 is a TOF-SIMS spectrum (mass number (m / z) is in the range of 240 to 260) in the surface treatment layer of the silane compound of the surface-treated copper foil obtained in Example 1 and Comparative Examples 1 and 2.
  • FIG. 3 is a TOF-SIMS spectrum (mass number (m / z) is in the range of 260 to 263.5) in the surface treatment layer of the silane compound of the surface-treated copper foil obtained in Example 1 and Comparative Examples 1 and 2.
  • FIG. 3 is a TOF-SIMS spectrum (mass number (m / z) is in the range of 260 to 263.5) in the surface treatment layer of the silane compound of the surface-treated copper foil obtained in Example 1 and Comparative Examples 1 and 2.
  • the surface-treated copper foil which concerns on embodiment of this invention has the surface treatment layer of a silane compound on the copper foil surface.
  • the “surface treatment layer of a silane compound” means a film formed from a silane compound.
  • the “copper foil” includes not only copper foil but also copper alloy foil.
  • the surface-treated copper foil according to the embodiment of the present invention is 240.9 to 241.1, 241. 9 to 242.1, 242.9 to 243.1, 243.9 to 244.1, 244.9 to 245.1, 260.9 to 261.1, 261.9 to 262.1, and 262.9 to A peak is detected at the position of at least one mass number (m / z) selected from the group consisting of 263.1.
  • mass number m / z
  • the mass number of 240.9 to 241.1 is preferably 241.03, and the mass number of 241.9 to 242.1 is preferably 242.03, and 242.9 to 243.1.
  • the mass number is preferably 243.03, the mass number of 243.9 to 244.1 is preferably 244.05, and the mass number of 244.9 to 245.1 is preferably 245.05.
  • the mass number of 260.9 to 261.1 is preferably 261.01, the mass number of 261.9 to 262.1 is preferably 262.01, and 262.9 to 263.1.
  • the mass number is preferably 263.03.
  • the silane compound is not particularly limited as long as a peak is detected at the position of the above mass number when the surface treatment layer of the silane compound is measured by TOF-SIMS.
  • the silane compound has a reactive functional group and a hydrolyzable group.
  • the “reactive functional group” refers to a chemical interaction with a resin substrate (for example, an interaction by van der Waals force, an interaction by Coulomb force, but is not limited thereto). )
  • the “hydrolyzable group” means a reactive group that can be hydrolyzed by moisture and chemically bonded to the copper foil.
  • a reactive functional group of a silane compound From an adhesive viewpoint with respect to a resin base material, at least 1 sort (s) selected from an amino group, a (meth) acryl group, a thiol group (mercapto group), and an epoxy group.
  • the “(meth) acryl group” means both an acryl group and a methacryl group.
  • Alkoxy groups such as a methoxy group, an ethoxy group, a propoxy group; An acyloxy group etc. are mentioned. Among these, alkoxy groups such as a methoxy group, an ethoxy group, and a propoxy group are preferable because they have a high effect of improving the adhesion between the resin base material and the surface-treated copper foil.
  • silane compound can be manufactured by a well-known method, you may use a commercial item.
  • examples of commercially available products that can be used as the silane compound include KBM series and KBE series manufactured by Shin-Etsu Chemical Co., Ltd.
  • a commercially available silane compound is used alone, when the surface treatment layer of the silane compound is measured by TOF-SIMS, a peak is hardly detected at the position of the above mass number. Therefore, when using a commercially available silane compound, it is preferable to use a mixture of two or more silane compounds.
  • a preferable mixture of silane compounds is a mixture of KBM603 (N-2- (aminoethyl) -3-aminopropyltrimethoxysilane) and KBM503 (3-methacryloxypropyltrimethoxysilane), KBM602 (N-2- A mixture of (aminoethyl) -3-aminopropyldimethoxysilane) and KBM503 (3-methacryloxypropyltrimethoxysilane), KBM603 (N-2- (aminoethyl) -3-aminopropyltrimethoxysilane) and KBE503 ( A mixture of 3-methacryloxypropyltriethoxysilane), KBM602 (N-2- (aminoethyl) -3-aminopropyldimethoxysilane) and KBE503 (3-methacryloxypropyltriethoxysilane), KBM903 (3 -
  • the surface roughness of the surface treatment layer of the silane compound is not particularly limited, but the ten-point average roughness Rz is preferably 0.1 to 2.0 ⁇ m, more preferably 0.50 to 1.0 ⁇ m.
  • the arithmetic average roughness Ra is preferably 0.01 to 0.30, more preferably 0.05 to 0.16.
  • a rolled copper foil or an electrolytic copper foil can be used.
  • the rolled copper foil is preferable because the surface roughness is small and the conductor loss can be reduced.
  • middle layer may be sufficient as copper foil.
  • the carrier and the intermediate layer are not particularly limited, and known ones can be used.
  • a roughening treatment layer may be formed on the surface of the copper foil by subjecting it to a roughening treatment from the viewpoint of enhancing the adhesion to the resin base material.
  • the “roughening treatment layer” in this specification means a layer of roughening particles electrodeposited on a copper foil.
  • the roughened particles are not particularly limited, and are formed from copper, nickel, phosphorus, tungsten, arsenic, molybdenum, chromium, cobalt, zinc, or an alloy containing one or more of them, which is generally used for the roughening treatment. Fine particles.
  • the roughened particles electrodeposited on the surface of the copper foil increase the conductor loss due to the skin effect, and can cause the phenomenon that the roughened particles called powder fall off, so the copper foil can be used as necessary. It is good also as an aspect which makes the roughening particle
  • one or more layers selected from the group consisting of a heat resistant treatment layer, a rust prevention treatment layer and a chromate treatment layer are provided from the viewpoint of improving various properties. Also good. These layers may be a single layer or a plurality of layers.
  • a surface-treated copper foil having a surface-treated layer of a silane compound having the above characteristics on the surface of the copper foil is manufactured by preparing a solution containing the silane compound and then surface-treating the copper foil using this solution. Can do.
  • the solution containing a silane compound can contain a solvent such as water in addition to the silane compound.
  • the concentration of the silane compound in the solution is not particularly limited, but it is preferable that the silane concentration of the silane compound in the solution is 0.5 volume% to 10 volume%. From the viewpoint of solubility in a solvent in the solution, the silane concentration of the entire silane compound in the solution is preferably 0.1% to 5.0% by volume.
  • the solution containing the silane compound can be prepared, for example, by adding the silane compound to a solvent and mixing.
  • the surface treatment conditions may be appropriately adjusted according to the type of silane compound used. Specifically, the temperature of the solution is 10 to 30 ° C., the pH of the solution is 1 to 12, the treatment time is 1 to 5 seconds, the drying temperature is 100 to 150 ° C., and the drying time is 10 to 300 seconds. A surface treatment may be performed.
  • the pH of the solution is particularly preferably around neutral, that is, 3 to 10. When the silane compound contains an amino group, the pH of the solution is preferably 6-12.
  • the surface treatment method is not particularly limited, and a known method such as a coating method or a dipping method can be used.
  • the adhesion amount of the silane compound can be controlled by changing the coating means such as showering and spraying or adjusting the number of coatings. It is also possible to control the adhesion amount of the silane compound by adjusting the concentration of the silane compound in the solution containing the silane compound.
  • an electroplating method can be used.
  • the amount of electrodeposition of the roughened particles on the copper foil surface can be controlled mainly by adjusting the current density and the electrodeposition time.
  • the amount of electrodeposition of the roughened particles mainly affects the surface roughness of the surface-treated copper foil.
  • the roughening treatment for example, the following roughening treatment method (1) or roughening treatment method (2) can be used.
  • the heat treatment, anti-rust treatment or chromate treatment should be applied before the surface treatment of the silane compound. What is necessary is just to go to the foil surface.
  • These treatment methods are not particularly limited, and can be performed according to known methods.
  • the surface-treated copper foil produced as described above has a surface treatment layer of a silane compound in which a peak is detected at a specific position (mass number: m / z) when measured by TOF-SIMS. Therefore, the adhesiveness between the surface treatment layer of the silane compound and the resin base material is high.
  • this surface-treated copper foil can improve the adhesion to the resin substrate even when there are few roughened particles electrodeposited on the copper foil surface by the roughening treatment or when the roughening treatment is not performed. it can.
  • this surface-treated copper foil is suitable not only for conventional resin base materials but also for resin base materials suitable for high frequency applications that are harder to adhere to copper foil than conventional resin base materials (liquid crystal polymers, low dielectric materials such as low dielectric polyimides). It can also be used for bonding to a resin base material formed from a material.
  • a copper clad laminate according to an embodiment of the present invention includes the above-described surface-treated copper foil and a resin base material bonded onto the surface-treated layer of the silane compound of the surface-treated copper foil.
  • the resin base material is preferably a resin base material formed from a low dielectric material.
  • low dielectric in this specification means that the dielectric loss tangent (1 GHz) is 0.01 or less.
  • the low dielectric material include, but are not limited to, liquid crystal polymer (LCP), low dielectric polyimide, low dielectric epoxy resin, fluorine resin, polyphenylene ether resin, and the like.
  • liquid crystal polymer means an aromatic polyester that exhibits optical anisotropy in the liquid phase.
  • the liquid crystal polymer is generally commercially available, and for example, Vecstar (registered trademark) series manufactured by Kuraray Co., Ltd. can be used.
  • “low dielectric polyimide” means, for example, a polyimide having a relative dielectric constant (1 GHz) of 3.3 or less and a dielectric loss tangent (1 GHz) of 0.005 or less.
  • the low dielectric polyimide is generally commercially available, and for example, U varnish, Upilex (registered trademark) manufactured by Ube Industries, Ltd. can be used.
  • the fluororesin include PTFE.
  • Polyphenylene ether resins also include compounds with other resins such as polystyrene.
  • the copper clad laminate having the above-described configuration is formed by placing a resin base material on the surface treatment layer of the silane compound of the surface-treated copper foil, and then applying pressure between the surface-treated copper foil and the resin base material. Can be manufactured.
  • the applied pressure is not particularly limited, and may be appropriately set according to the type of the surface-treated copper foil and the resin base material to be used.
  • the copper clad laminate produced as described above is a surface-treated copper having a surface-treated layer of a silane compound in which a peak is detected at a specific position (mass number: m / z) when measured by TOF-SIMS. Since the foil is provided, the adhesiveness between the surface-treated copper foil and the resin base material is excellent. Therefore, this copper-clad laminate is suitable for use in applications such as flexible wiring boards, rigid wiring boards, shield materials, RF-IDs, planar heating elements, and radiators.
  • silane compounds used in each example and comparative example are as follows. ⁇ KBM603 (Shin-Etsu Chemical Co., Ltd., N-2- (aminoethyl) -3-aminopropyltrimethoxysilane) ⁇ KBM503 (Shin-Etsu Chemical Co., Ltd., 3-methacryloxypropyltrimethoxysilane)
  • Example 1 In accordance with the roughening method (2) described above, a roughened layer is obtained by subjecting a rolled copper foil of 12 ⁇ m thickness (BHZ-Z-HA-V2 manufactured by JX Metals Co., Ltd.) to the following conditions. Formed.
  • a surface treatment layer is formed using a solution containing a silane compound under the following conditions to form a surface treatment layer of the silane compound.
  • a treated copper foil was obtained.
  • Silane compound A mixture of KBM603 and KBM503 (volume ratio of KBM603 to KBM503 is 75:25)
  • Concentration of silane compound in solution 1% by volume Solution temperature: 20 ° C Solution pH: 4.5 Processing time: 3 seconds
  • Application frequency 1 time Drying temperature: 110 ° C Drying time: 30 seconds
  • a resin substrate made of a liquid crystal polymer (Vecstar (registered trademark) CT-Z manufactured by Kuraray Co., Ltd.) having a thickness of 50 ⁇ m was disposed on the surface-treated layer of the silane compound of the surface-treated copper foil obtained above.
  • a resin substrate made of a liquid crystal polymer (Vecstar (registered trademark) CT-Z manufactured by Kuraray Co., Ltd.) having a thickness of 50 ⁇ m was disposed.
  • the copper clad laminated board was obtained by pressurizing and joining. At this time, the applied pressure was set to 4 MPa.
  • Example 1 A surface-treated copper foil and a copper clad laminate were prepared in the same manner as in Example 1 except that KBM603 was used as the silane compound, the concentration of the silane compound in the solution was changed to 4% by volume, and the pH of the solution was changed to 11.
  • Comparative Example 2 A surface-treated copper foil and a copper clad laminate were prepared in the same manner as in Example 1 except that KBM503 was used as the silane compound.
  • the surface-treated copper foils obtained in the above examples and comparative examples were subjected to TOF-SIMS analysis of the silane compound surface treatment layer.
  • the analysis conditions are shown below.
  • FIGS. 1 and 2 show a spectrum of TOF-SIMS in the range of mass number (m / z) from 240 to 260.
  • FIG. 2 shows a spectrum of TOF-SIMS in the range of mass number (m / z) from 260 to 263.5. It is a spectrum.
  • the mass number (m / z) is position A at 240.9 to 241.1, position B at 241.9 to 242.1, 242.9 to 243. 1 position C, 243.9 to 244.1 position D, 244.9 to 245.1 position E, 260.9 to 261.1 position F, 261.9 to 262.1 positions G and 262
  • a peak was detected at position H between .9 and 263.1.
  • Example 1 the mass numbers (m / z) are 241.03, 242.03, 243.03, 244.05, 245.05, 261.01, 262.01, and 263.03. A peak was detected at the position of. In contrast, in Comparative Examples 1 and 2, no peak was detected at any of the positions A to H.
  • the 10-point average roughness Rz and arithmetic average roughness Ra of the surface treatment layer of the silane compound were measured for the surface-treated copper foils obtained in the above Examples and Comparative Examples.
  • the results are shown in Table 1.
  • the ten-point average roughness Rz and arithmetic average roughness Ra of the surface treatment layer of the silane compound were measured according to JIS B0601: 1982 using a contact roughness meter Surfcoder SE-600 manufactured by Kosaka Laboratory. In this measurement, the measurement reference length is 0.8 mm, the evaluation length is 4 mm, the cutoff value is 0.25 mm, the feeding speed is 0.1 mm / second, and the measurement position is changed in the width direction of the surface-treated copper foil. 10 times, and the average of the 10 measurements was taken as the evaluation result.
  • 90 degree peel strength was measured about the copper clad laminated board obtained by said Example and comparative example.
  • the results are shown in Table 1.
  • the 90 degree peel strength was measured in accordance with JIS C6471: 1995. Specifically, the strength when the conductor (surface-treated copper foil) width was 3 mm and the resin substrate and the surface-treated copper foil were peeled at a speed of 50 mm / min at an angle of 90 degrees was measured. The measurement was performed twice, and the average value was taken as the result of 90 degree peel strength.
  • Example 1 has a 90 degree peel strength higher than that of Comparative Examples 1 and 2, and has high adhesion between the surface treatment layer of the silane compound and the resin substrate. It was.
  • the embodiment of the present invention it is possible to provide a surface-treated copper foil capable of improving the adhesion with a resin substrate, particularly a resin substrate suitable for high frequency applications. Moreover, according to embodiment of this invention, the copper clad laminated board excellent in the adhesiveness between a resin base material, especially the resin base material suitable for a high frequency use, and surface-treated copper foil can be provided.
  • the surface-treated copper foil according to the embodiment of the present invention has a surface-treated layer of a silane compound that has high adhesion to the resin substrate, it can be used for the production of a copper-clad laminate.
  • the copper-clad laminate according to the embodiment of the present invention is excellent in adhesion between the resin base material and the surface-treated copper foil. Therefore, the flexible wiring board, the rigid wiring board, the shield material, the RF-ID, It can be used for applications such as planar heating elements and radiators.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • General Chemical & Material Sciences (AREA)
  • Laminated Bodies (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Chemical Treatment Of Metals (AREA)
PCT/JP2019/010096 2018-03-29 2019-03-12 表面処理銅箔及び銅張積層板 WO2019188262A1 (ja)

Priority Applications (4)

Application Number Priority Date Filing Date Title
MYPI2020004832A MY194720A (en) 2018-03-29 2019-03-12 Surface treated copper foil and copper clad laminate
CN201980010640.1A CN111655900B (zh) 2018-03-29 2019-03-12 表面处理铜箔及覆铜积层板
KR1020207020817A KR102502018B1 (ko) 2018-03-29 2019-03-12 표면 처리 구리박 및 동장 적층판
PH12020551281A PH12020551281A1 (en) 2018-03-29 2020-08-19 Surface treated copper foil and copper clad laminate

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018065668A JP6413039B1 (ja) 2018-03-29 2018-03-29 表面処理銅箔及び銅張積層板
JP2018-065668 2018-03-29

Publications (1)

Publication Number Publication Date
WO2019188262A1 true WO2019188262A1 (ja) 2019-10-03

Family

ID=63920543

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/010096 WO2019188262A1 (ja) 2018-03-29 2019-03-12 表面処理銅箔及び銅張積層板

Country Status (7)

Country Link
JP (1) JP6413039B1 (zh)
KR (1) KR102502018B1 (zh)
CN (1) CN111655900B (zh)
MY (1) MY194720A (zh)
PH (1) PH12020551281A1 (zh)
TW (1) TWI687527B (zh)
WO (1) WO2019188262A1 (zh)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI715424B (zh) * 2020-01-22 2021-01-01 長春石油化學股份有限公司 電解銅箔、電極及包含其之鋰離子電池

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009263790A (ja) * 2008-04-04 2009-11-12 Nippon Paint Co Ltd 銅の表面調整組成物および表面処理方法
JP2016006227A (ja) * 2014-05-28 2016-01-14 Jx日鉱日石金属株式会社 表面処理銅箔、キャリア付銅箔、積層体、プリント配線板、電子機器、表面処理銅箔の製造方法及びプリント配線板の製造方法
JP2017088971A (ja) * 2015-11-12 2017-05-25 Ｊｘ金属株式会社 キャリア付銅箔、キャリア付銅箔の製造方法、積層体、プリント配線板の製造方法及び電子機器の製造方法
JP2017122274A (ja) * 2016-01-04 2017-07-13 Ｊｘ金属株式会社 表面処理銅箔
JP6334034B1 (ja) * 2017-06-09 2018-05-30 Ｊｘ金属株式会社 表面処理銅箔及びその製造方法、並びに銅張積層板

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102498600A (zh) * 2009-09-11 2012-06-13 Jx日矿日石金属株式会社 锂离子电池集电体用铜箔
JP5885054B2 (ja) * 2010-04-06 2016-03-15 福田金属箔粉工業株式会社 銅張積層板用処理銅箔及び該処理銅箔を絶縁性樹脂基材に接着してなる銅張積層板並びに該銅張積層板を用いたプリント配線板。
JP2012112009A (ja) 2010-11-26 2012-06-14 Hitachi Cable Ltd 銅箔、及び銅箔の製造方法
WO2012132577A1 (ja) * 2011-03-30 2012-10-04 Jx日鉱日石金属株式会社 印刷回路用銅箔
MY169065A (en) * 2012-03-29 2019-02-12 Jx Nippon Mining & Metals Corp Surface-treated copper foil
CN104769165B (zh) * 2012-11-09 2017-08-25 Jx日矿日石金属株式会社 表面处理铜箔及使用其的积层板、覆铜积层板、印刷配线板以及电子机器
KR101852671B1 (ko) * 2015-01-21 2018-06-04 제이엑스금속주식회사 캐리어 부착 동박, 적층체, 프린트 배선판, 및, 프린트 배선판의 제조 방법
JP6294862B2 (ja) * 2015-12-09 2018-03-14 古河電気工業株式会社 プリント配線板用表面処理銅箔、プリント配線板用銅張積層板及びプリント配線板
JP6811240B2 (ja) * 2016-07-22 2021-01-13 京セラ株式会社 有機絶縁体、金属張積層板および配線基板

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009263790A (ja) * 2008-04-04 2009-11-12 Nippon Paint Co Ltd 銅の表面調整組成物および表面処理方法
JP2016006227A (ja) * 2014-05-28 2016-01-14 Jx日鉱日石金属株式会社 表面処理銅箔、キャリア付銅箔、積層体、プリント配線板、電子機器、表面処理銅箔の製造方法及びプリント配線板の製造方法
JP2017088971A (ja) * 2015-11-12 2017-05-25 Ｊｘ金属株式会社 キャリア付銅箔、キャリア付銅箔の製造方法、積層体、プリント配線板の製造方法及び電子機器の製造方法
JP2017122274A (ja) * 2016-01-04 2017-07-13 Ｊｘ金属株式会社 表面処理銅箔
JP6334034B1 (ja) * 2017-06-09 2018-05-30 Ｊｘ金属株式会社 表面処理銅箔及びその製造方法、並びに銅張積層板

Also Published As

Publication number Publication date
CN111655900B (zh) 2022-05-13
JP6413039B1 (ja) 2018-10-24
MY194720A (en) 2022-12-15
TW201942369A (zh) 2019-11-01
KR20200100138A (ko) 2020-08-25
TWI687527B (zh) 2020-03-11
CN111655900A (zh) 2020-09-11
PH12020551281A1 (en) 2021-05-31
JP2019173139A (ja) 2019-10-10
KR102502018B1 (ko) 2023-02-21

Similar Documents

Publication Publication Date Title
JP6149066B2 (ja) 表面処理銅箔
JP6190846B2 (ja) 表面処理銅箔
TWI645759B (zh) 印刷配線板用表面處理銅箔、印刷配線板用覆銅積層板及印刷配線板
JP5871426B2 (ja) 高周波伝送用表面処理銅箔、高周波伝送用積層板及び高周波伝送用プリント配線板
JP7177956B2 (ja) 粗化処理銅箔、キャリア付銅箔、銅張積層板及びプリント配線板
WO2019188262A1 (ja) 表面処理銅箔及び銅張積層板
JP6854114B2 (ja) 表面処理銅箔
TWI668337B (zh) Surface treated copper foil and its manufacturing method, and copper clad laminate
JP2019019414A (ja) 表面処理銅箔、積層体及びプリント配線板
CN115024029A (zh) 电磁波屏蔽膜
JP2019049017A (ja) 表面処理銅箔及び銅張積層板
JP2005064110A (ja) 電子部品用部材並びにこれを用いた電子部品
TW202403111A (zh) 粗化處理銅箔、附載體銅箔、銅箔積層板及印刷配線板
TW202403110A (zh) 粗化處理銅箔、附載體銅箔、銅箔積層板及印刷配線板

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19774989

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20207020817

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19774989

Country of ref document: EP

Kind code of ref document: A1