WO2011102115A1 - 耐候性塩化ビニル系樹脂組成物 - Google Patents
耐候性塩化ビニル系樹脂組成物 Download PDFInfo
- Publication number
- WO2011102115A1 WO2011102115A1 PCT/JP2011/000830 JP2011000830W WO2011102115A1 WO 2011102115 A1 WO2011102115 A1 WO 2011102115A1 JP 2011000830 W JP2011000830 W JP 2011000830W WO 2011102115 A1 WO2011102115 A1 WO 2011102115A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- vinyl chloride
- chloride resin
- mass
- resin composition
- Prior art date
Abstract
Description
また、カルシウム-亜鉛系やマグネシウム-亜鉛系、カルシウム-マグネシウム-亜鉛系の安定剤を配合した塩化ビニル系樹脂は、耐候性を必要とする製品に使用する場合、耐着色性が問題となることが多い。
従って、塩化ビニル系樹脂に、高い透明性を付与しつつ、良好な耐着色性も付与できる安定剤が求められている。
本発明の第2の目的は、透明性が高いだけでなく、耐候性、熱安定性、耐着色性にも優れた塩化ビニル製の透明成型品を提供することにある。
(A)少なくとも一種の有機酸亜鉛塩を0.001~10質量部、
(B)少なくとも一種の亜鉛変性ハイドロタルサイト系化合物を0.001~10質量部、
(C)下記一般式(I)で表されるシュウ酸アニリド系紫外線吸収剤を0.01~20質量部含有してなることを特徴とする透明製品用塩化ビニル系樹脂組成物、及び該透明製品用塩化ビニル系樹脂組成物を成形してなることを特徴とする透明成形品である。
但し、式中のR1は水素原子又は炭素原子数1~12の直鎖型又は分岐型のアルキル基、R2は炭素原子数1~12の直鎖型又は分岐型のアルキル基であり、R3及びR4は、各々独立に水素原子又は炭素原子数1~18の直鎖型又は分岐型のアルキル基である。
また、前記(B)亜鉛変性ハイドロタルサイト系化合物は、下記一般式(II)で表される亜鉛変性ハイドロタルサイト系化合物であることが好ましい。
My1Zny2Alx(OH)2(CO3)x/2・mH2O (II)
但し、式中のMは、マグネシウム、又は、マグネシウム及びカルシウムであり、x、y1及びy2は各々下記の式で表される条件を満足する数であり、mは0又は任意の正数である;0<x≦0.5、y1+y2=1-x、y1≧y2、0.3≦y1<1、0<y2<0.5。
また、本発明の透明製品用塩化ビニル系樹脂組成物は、有機スズ系化合物を含有しないことが好ましい。
前記フェノール類としては、フェノール、クレゾール、エチルフェノール、シクロヘキシルフェノール、ノニルフェノール、ドデシルフェノール等が挙げられる。
また、(A)成分として使用する上記有機酸亜鉛塩の含有量は、塩化ビニル系樹脂100質量部に対して、0.001~10質量部であることが必要であり、0.01~5質量部であることが好ましい。有機酸亜鉛塩の含有量が0.001質量部未満では、耐着色性及び耐候性が不十分であり、10質量部を超えると熱安定性が低下する。
My1Zny2Alx(OH)2(CO3)x/2・mH2O (II)
但し、(II)式中のMは、マグネシウム、又は、マグネシウム及びカルシウムを表すが、透明性の観点から、特にマグネシウムが好ましい。x、y1及びy2は、各々下記の関係式で表される条件を満足する数、mは0又は任意の正数を表す。
0<x≦0.5、y1+y2=1-x、y1≧y2、0.3≦y1<1、0<y2<0.5
Mg0.38Zn0.3Al0.32(OH)2(CO3)0.16・0.2H2O
Mg0.45Zn0.23Al0.32(OH)2(CO3)0.16
Mg0.48Zn0.18Al0.34(OH)2(CO3)0.17
Mg0.48Zn0.2Al0.32(OH)2(CO3)0.16
Mg0.5Zn0.17Al0.33(OH)2(CO3)0.165・0.45H2O
Mg0.5Zn0.18Al0.32(OH)2(CO3)0.16
Mg0.5Zn0.2Al0.3(OH)2(CO3)0.16
Mg0.5Zn0.2Al0.3(OH)2(CO3)0.15・0.52H2O
Mg0.5Zn0.25Al0.25(OH)2(CO3)0.125
Mg0.51Zn0.17Al0.32(OH)2(CO3)0.16
Mg0.52Zn0.16Al0.32(OH)2(CO3)0.16・0.5H2O
Mg0.55Zn0.15Al0.32(OH)2(CO3)0.15
Mg0.6Zn0.14Al0.26(OH)2(CO3)0.13
Mg0.6Zn0.16Al0.24(OH)2(CO3)0.12
Mg0.6Zn0.2Al0.2(OH)2(CO3)0.1
Mg0.4Ca0.1Zn0.18Al0.32(OH)2(CO3)0.16
Mg0.3Ca0.2Zn0.2Al0.3(OH)2(CO3)0.15
Mg0.5Zn0.17Al0.33(OH)2(CO3)0.17・0.5H2O
Mg0.5Zn0.17Al0.33(OH)2(CO3)0.17・0.42H2O
Mg0.6Zn0.16Al0.24(OH)2(CO3)0.12・0.45H2O
Mg0.5Zn0.25Al0.25(OH)2(CO3)0.13・0.39H2O
Mg0.5Zn0.17Al0.33(OH)2(CO3)0.17
Mg0.5Zn0.25Al0.25(OH)2(CO3)0.13
また、(B)成分として用いられる亜鉛変性ハイドロタルサイト系化合物の屈折率は、透明性の点から1.52~1.56であることが好ましい。
本発明においては、上記亜鉛変性ハイドロタルサイト系化合物の表面を、ステアリン酸等の高級脂肪酸類、オレイン酸アルカリ金属塩等の高級脂肪酸金属塩類、ドデシルベンゼンスルホン酸アルカリ金属塩等の有機スルホン酸金属塩類、高級脂肪酸アミド類、高級脂肪酸エステル類又はワックス等で被覆したものも使用することができる。
本発明における(B)成分の亜鉛変性ハイドロタルサイト系化合物の使用量は、ポリ塩化ビニル系樹脂100質量部に対して0.001~10質量部、好ましくは0.05~5質量部である。使用量が0.001質量部未満では樹脂組成物の熱安定性が不十分であり、10質量部を超えると、樹脂組成物の耐着色性を低下させる等の性能低下が生じる。
但し、式(I)中のR1は、水素原子又は炭素原子数1~12の直鎖又は分岐のアルキル基、R2は炭素原子数1~12の直鎖又は分岐のアルキル基であり、R3及びR4は、各々独立に水素原子又は炭素原子数1~18の直鎖又は分岐のアルキル基である。
上記糖アルコールの例としては、マンニトール、マルチトール、ラクチトール、ソルビトール、エリスリトール、グリセリン、キシリトール、イノシトール等が挙げられ、耐候性、熱安定性、耐着色性、透明性等の点から、特にマンニトール、マルチトール及びラクチトールが好ましい。
前記糖アルコールを使用する場合、使用量は、塩化ビニル系樹脂100質量部に対して0.001~1質量部であり、耐候性、熱安定性、耐着色性の点から、0.005~0.5質量部であることが好ましく、0.01~0.3質量部であることが特に好ましい。
上記滑剤は、例えば、低分子ワックス、パラフィンワックス、ポリエチレンワックス、塩素化炭化水素、フルオロカーボン等の炭化水素系滑剤;カルナバワックス、キャンデリラワックス等の天然ワックス系滑剤;ラウリン酸、ステアリン酸、ベヘニン酸等の高級脂肪酸、又はヒドロキシステアリン酸のようなオキシ脂肪酸等の脂肪酸系滑剤;ステアリルアミド、ラウリルアミド、オレイルアミド等の脂肪族アミド化合物又はメチレンビスステアリルアミド、エチレンビスステアリルアミドのようなアルキレンビス脂肪族アミド等の脂肪族アミド系滑剤;ステアリルステアレート、ブチルステアレート等の脂肪酸1価アルコールエステル化合物又は、グリセリントリステアレート、ソルビタントリステアレート、ペンタエリスリトールテトラステアレート、ジペンタエリスリトールヘキサステアレート、ポリグリセリンポリリシノレート、硬化ヒマシ油等の脂肪酸多価アルコールエステル化合物、又は、ジペンタエリスリトールのアジピン酸・ステアリン酸エステルのような1価脂肪酸及び多塩基性有機酸と、多価アルコールの複合エステル化合物等の脂肪酸アルコールエステル系滑剤;ステアリルアルコール、ラウリルアルコール、パルミチルアルコール等の脂肪族アルコール系滑剤;金属石鹸類;部分ケン化モンタン酸エステル等のモンタン酸系滑剤;アクリル系滑剤;シリコーンオイル等の、公知の滑剤の中から適宜選択することができる。
これらの滑剤は、1種類のみ使用してもよいし、2種以上を併用してもよい。
本発明においては、特に透明性の観点から、1価脂肪酸及び多塩基性有機酸と多価アルコールとの複合エステル化合物等の、脂肪酸アルコールエステル系滑剤を使用することが好ましい。
また、前記フェノール類としては、フェノール、クレゾール、エチルフェノール、シクロヘキシルフェノール、ノニルフェノール、ドデシルフェノール等が挙げられる。
Mg1-XAlX(OH)2(Aq-)X/q・aH2O
但し、式中のqは1又は2であり、Aq-はq価のアニオン、即ち(CO3)2-又は(ClO4)-であり、Xは0<X≦0.5、aは0又は正数を表す。
Mg0.750Al0.250(OH)2(CO3)0.125・0.5H2O
Mg0.692Al0.308(OH)2(CO3)0.154・0.1H2O
Mg0.683Al0.317(OH)2(CO3)0.159・0.5H2O
Mg0.667Al0.333(OH)2(CO3)0.167・0.1H2O
Mg0.750Al0.250(OH)2(ClO4)0.250・0.5H2O
Mg0.692Al0.308(OH)2(ClO4)0.308・0.1H2O
Mg0.667Al0.333(OH)2(ClO4)0.333・0.1H2O
市販品としては、DHT-4A(協和化学工業(株)製)、マグセラ-1(協和化学工
業(株)製)等が挙げられる。
前記β-ジケトン化合物としては、例えば、アセチルアセトン、トリアセチルメタン、2,4,6-ヘプタトリオン、ブタノイルアセチルメタン、ラウロイルアセチルメタン、パルミトイルアセチルメタン、ステアロイルアセチルメタン、フェニルアセチルアセチルメタン、ジシクロヘキシルカルボニルメタン、ベンゾイルホルミルメタン、ベンゾイルアセチルメタン、ジベンゾイルメタン、オクチルベンゾイルメタン、ステアロイルベンゾイルメタン、ビス(4-オクチルベンゾイル)メタン、ベンゾイルジアセチルメタン、4-メトキシベンゾイルベンゾイルメタン、ビス(4-カルボキシメチルベンゾイル)メタン、2-カルボキシメチルベンゾイルアセチルオクチルメタン、デヒドロ酢酸、シクロヘキサン-1,3-ジオン、3,6-ジメチル-2,4-ジオキシシクロヘキサン-1カルボン酸メチル、2-アセチルシクロヘキサノン、ジメドン、2-ベンゾイルシクロヘキサン等が挙げられる。
また、これらβ-ジケトン化合物の金属塩も使用することができ、該β-ジケトン金属塩を提供し得る金属種としては、例えば、リチウム、ナトリウム及びカリウム等のアルカリ金属;マグネシウム、カルシウム、ストロンチウム、亜鉛、アルミニウム等が挙げられる。
前記リン酸エステル系難燃剤の例としては、例えば、トリメチルホスフェート、トリエチルホスフェート、トリブチルホスフェート、トリブトキシエチルホスフェート、トリスクロロエチルホスフェート、トリスジクロロプロピルホスフェート、トリフェニルホスフェート、トリクレジルホスフェート、クレジルジフェニルホスフェート、トリキシレニルホスフェート、オクチルジフェニルホスフェート、キシレニルジフェニルホスフェート、トリスイソプロピルフェニルホスフェート、2-エチルヘキシルジフェニルホスフェート、t-ブチルフェニルジフェニルホスフェート、ビス-(t-ブチルフェニル)フェニルホスフェート、トリス-(t-ブチルフェニル)ホスフェート、イソプロピルフェニルジフェニルホスフェート、ビス-(イソプロピルフェニル)ジフェニルホスフェート、トリス-(イソプロピルフェニル)ホスフェート等が挙げられる。
また、前記その他の有機系難燃助剤としては、例えば、ペンタエリスリトールが挙げられる。
その他、本発明の透明製品用塩化ビニル系樹脂組成物には、必要に応じて通常塩化ビニル系樹脂に使用される添加剤、例えば、架橋剤、帯電防止剤、防曇剤、プレートアウト防止剤、表面処理剤、防曇剤、蛍光剤、防黴剤、殺菌剤、発泡剤、金属不活性剤、離型剤、顔料、加工助剤、酸化防止剤、光安定剤等を、本発明の効果を損なわない範囲で配合することができる。
以下、実施例及び比較例をもって本発明を更に詳細に説明する。しかし、本発明はこれらによって何ら制限を受けるものではない。
下記表1に記載された成分をヘンシェルミキサーでブレンドした後、2本ロール成形機(大竹機械工業(株)製)を用いて、加工温度170℃、ロール回転数30rpm、混練時間3分の条件でロール混練し、縦600mm×横300mm×厚さ0.6mmのシートを作製した。
また、上記で得られた0.6mm厚のシートを2枚張り合わせ、プレス成形機(東邦マシナリー(株)製:30トン)を用いて、190℃で5分間又は30分間プレス加工を行って、1mm厚のシートをそれぞれ作製した。これらのシートを用いて、以下の方法により、耐着色性試験、透明性試験、耐候性試験を行った。
<耐着色性試験>
190℃で5分及び30分プレス加工した1mm厚のシートについて、色差計TC-8600A((有)東京電色製の商品名)を使用してそれぞれ黄色度(Y.I.)を、測定した。結果を表1に示す。
<透明性試験>
上記190℃で5分プレス加工した1mm厚のシートについて、ヘイズガードII((株)東洋精機製作所製の商品名)を使用してHaze値を測定した。
<耐候性試験>
上記、190℃で5分プレス加工した1mm厚のシートについて、サンシャインウェザーメーター(早坂理工(株)製:120分中18分雨有り)による300時間及び600時間紫外線照射後のΔY.I.を測定した。実施例1と4については900時間紫外線照射後のΔY.I.も測定した。
また、長時間の紫外線照射による変色の度合いも、シュウ酸アニリド系紫外線吸収剤を添加した本発明の透明製品用塩化ビニル系樹脂組成物の方が、他の紫外線吸収剤を添加したものよりも少なく、耐候性にも優れることが確認された。
Claims (5)
- 更に、(D)成分として少なくとも一種の糖アルコールを0.001~1.0質量部含有する、請求項1に記載された透明製品用塩化ビニル系樹脂組成物。
- 前記(B)亜鉛変性ハイドロタルサイト系化合物が、下記一般式(II)で表される亜鉛変性ハイドロタルサイト系化合物である、請求項1又は2に記載された透明製品用塩化ビニル系樹脂組成物;
My1Zny2Alx(OH)2(CO3)x/2・mH2O (II)
但し、式中のMは、マグネシウム、又は、マグネシウム及びカルシウムであり、x、y1及びy2は各々下記の式で表される条件を満足する数であり、mは0又は任意の正数である;
0<x≦0.5、y1+y2=1-x、y1≧y2、0.3≦y1<1、0<y2<0.5。 - 前記組成物が、有機スズ系化合物を含有しない、請求項1~3の何れかに記載された透明製品用塩化ビニル系樹脂組成物。
- 請求項1~4の何れかに記載された透明製品用塩化ビニル系樹脂組成物を成形してなることを特徴とする透明成形品。