WO2009099251A1 - 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 - Google Patents
加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 Download PDFInfo
- Publication number
- WO2009099251A1 WO2009099251A1 PCT/JP2009/052353 JP2009052353W WO2009099251A1 WO 2009099251 A1 WO2009099251 A1 WO 2009099251A1 JP 2009052353 W JP2009052353 W JP 2009052353W WO 2009099251 A1 WO2009099251 A1 WO 2009099251A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phase
- less
- steel sheet
- strength hot
- hot
- Prior art date
Abstract
Description
Claims