US20110123850A1 - Electrode Separator - Google Patents

Electrode Separator Download PDF

Info

Publication number
US20110123850A1
US20110123850A1 US12/933,977 US93397709A US2011123850A1 US 20110123850 A1 US20110123850 A1 US 20110123850A1 US 93397709 A US93397709 A US 93397709A US 2011123850 A1 US2011123850 A1 US 2011123850A1
Authority
US
United States
Prior art keywords
separator
pva
polymer
pss
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/933,977
Other languages
English (en)
Inventor
Hieu Duong
George Adamson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zpower LLC
Original Assignee
Zpower LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zpower LLC filed Critical Zpower LLC
Priority to US12/933,977 priority Critical patent/US20110123850A1/en
Assigned to ZPOWER, INC. reassignment ZPOWER, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DUONG, HIEU, ADAMSON, GEORGE
Assigned to ZPOWER, INC. reassignment ZPOWER, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DUONG, HIEU, ADAMSON, GEORGE
Publication of US20110123850A1 publication Critical patent/US20110123850A1/en
Assigned to ZPOWER, LLC reassignment ZPOWER, LLC CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: ZPOWER, INC.
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/022—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/16—Articles comprising two or more components, e.g. co-extruded layers
    • B29C48/18—Articles comprising two or more components, e.g. co-extruded layers the components being layers
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H01M50/417—Polyolefins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/446—Composite material consisting of a mixture of organic and inorganic materials
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
    • H01M50/457—Separators, membranes or diaphragms characterised by the material having a layered structure comprising three or more layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/04—Polymers of ethylene
    • B29K2023/06—PE, i.e. polyethylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2029/00—Use of polyvinylalcohols, polyvinylethers, polyvinylaldehydes, polyvinylketones or polyvinylketals or derivatives thereof as moulding material
    • B29K2029/04—PVOH, i.e. polyvinyl alcohol
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2081/00—Use of polymers having sulfur, with or without nitrogen, oxygen or carbon only, in the main chain, as moulding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/24—Condition, form or state of moulded material or of the material to be shaped crosslinked or vulcanised
    • B29K2105/243—Partially cured
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0003—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds having particular electrical or magnetic properties, e.g. piezoelectric
    • B29K2995/0007—Insulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0077—Yield strength; Tensile strength
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0094—Geometrical properties
    • B29K2995/0097—Thickness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2007/00—Flat articles, e.g. films or sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/34—Electrical apparatus, e.g. sparking plugs or parts thereof
    • B29L2031/3468—Batteries, accumulators or fuel cells
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/24—Alkaline accumulators
    • H01M10/32—Silver accumulators
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Definitions

  • This invention is concerned with electrical alkaline batteries, and in particular with separators for alkaline batteries and methods of making the same.
  • An electrical storage battery comprises one electrochemical cell or a plurality of electrochemical cells of the same type, the latter typically being connected in series to provide a higher voltage or in parallel to provide a higher charge capacity than provided by a single cell.
  • An electrochemical cell comprises an electrolyte interposed between and in contact with an anode and a cathode.
  • the anode comprises an active material that is readily oxidized
  • the cathode comprises an active material that is readily reduced.
  • the anode active material is oxidized and the cathode active material is reduced, so that electrons flow from the anode through an external load to the cathode, and ions flow through the electrolyte between the electrodes.
  • electrochemical cells used for electrical storage applications also include a separator between the anode and the cathode is required to prevent reactants and reaction products present at one electrode from reacting and/or interfering with reactions at the other electrode.
  • a battery separator must be electronically insulating, and remain so during the life of the battery, to avoid battery self-discharge via internal shorting between the electrodes.
  • a battery separator must be both an effective electrolyte transport barrier and a sufficiently good ionic conductor to avoid excessive separator resistance that substantially lowers the discharge voltage.
  • Primary batteries involve at least one irreversible electrode reaction and cannot be recharged with useful charge efficiency by applying a reverse voltage.
  • Secondary batteries involve relatively reversible electrode reactions and can be recharged with acceptable loss of charge capacity over numerous charge-discharge cycles. Separator requirements for secondary batteries tend to be more demanding since the separator must survive repeated charge-discharge cycles.
  • separator requirements are particularly stringent.
  • the separator must be chemically stable in strongly alkaline solution, resist oxidation in contact with the highly oxidizing cathode, and resist reduction in contact with the highly reducing anode. Since ions, especially metal oxide ions, from the cathode can be somewhat soluble in alkaline solutions and tend to be chemically reduced to metal on separator surfaces, the separator must also inhibit transport and/or chemical reduction of metal ions. Otherwise, a buildup of metal deposits within separator pores can increase the separator resistance in the short term and ultimately lead to shorting failure due to formation of a continuous metal path through the separator.
  • the separator must suppress dendritic growth and/or resist dendrite penetration to avoid failure due to formation of a dendritic short between the electrodes.
  • a related issue with anodes is shape change, in which the central part of the electrode tends to thicken during charge-discharge cycling. The causes of shape change are complicated and not well-understood but apparently involve differentials in the current distribution and solution mass transport along the electrode surface.
  • the separator preferably mitigates zinc electrode shape change by exhibiting uniform and stable ionic conductivity and ionic transport properties.
  • a separator stack comprised of a plurality of separators that perform specific functions is needed. Some of the required functions are resistance to electrochemical oxidation and silver ion transport from the cathode, and resistance to electrochemical reduction and dendrite penetration from the anode.
  • the invention provides a multi-functional battery separator comprising two or more active separator layers deposited from different polymer solutions to form a multilayered unitary structure comprising a free-standing film, a multiplex film on one side of a porous substrate, or separate films or multiplex films on opposite sides of a porous substrate.
  • the cascade coating method is used to simultaneously deposit the active separator layers wet so that the physical, electrical and morphological changes associated with the polymer drying out process are avoided or minimized.
  • the active separator layers of the multi-functional battery separator of the invention can also be deposited via conventional methods.
  • the invention also provides a process for fabricating the multi-functional battery separator.
  • the multilayered unitary structure of the separator of the invention provides better use of the separator active materials, which is believed to improve separator ionic conductivity and effectiveness as an ionic transport barrier.
  • the multilayered unitary structure also reduces battery production costs and eliminates gaps between individual layers in a separator stack that can contribute to battery failure.
  • the multi-functional battery separator is particularly useful for batteries with a zinc anode, for which dendrite formation is an issue, and a silver oxide cathode, which is highly oxidizing.
  • a multi-functional separator in this case can comprise a dendrite-resistant separator layer that faces the anode, and an oxidation-resistant separator layer that faces the cathode.
  • the invention relates to an electrochemical cell comprising
  • the alkaline electrolyte comprises an aqueous solution of a hydroxide of an alkali metal selected from the group consisting of potassium, sodium, lithium, rubidium, cesium, and mixtures thereof.
  • the cathode comprises an active material selected from the group consisting of silver oxide, nickel oxide, cobalt oxide, and manganese oxide.
  • the polyether polymer comprises polyethylene oxide or polypropylene oxide, or a copolymer or a mixture thereof.
  • the cross-linking agent is boric acid.
  • One or both of the PE solution and the PVA solution further comprise a powder of a metallic oxide selected from the group consisting of zirconium oxide, titanium oxide and aluminum oxide.
  • One or both of the PE solution and the PVA solution further comprise a titanate salt of an alkali metal selected from the group consisting of potassium, sodium, lithium, rubidium, cesium, and mixtures thereof.
  • One or both of the PE solution and the PVA solution further comprise a surfactant.
  • the PVA solution further comprises a plasticizer.
  • the PVA solution further comprises a conductivity enhancer consisting of a coploymer of polyvinyl alcohol and a hydroxyl-conducting polymer selected from the group consisting of polyacrylates, polylactones, polysulfonates, polycarboxylates, polysulfates, polysarconates, polyamides, and polyamidosulfonates.
  • the invention features a multi-functional separator comprising at least three active separator layers, wherein the multi-functional separator has an ionic resistance of ⁇ 10 ⁇ /cm2, electrical resistance of >10 k ⁇ /cm2, and a wet tensile strength of >0.1 lbf.
  • Embodiments of this aspect of may include one or more of the following features.
  • the ionic resistance of the separator is ⁇ 0.5 ⁇ /cm2.
  • At least two of the three active separator layers comprise a polymeric material each individually selected from PVA and PSA, or combinations thereof.
  • the PSA comprises PSS.
  • the multi-functional separator comprises the layers PVA/V6/PSS; PVA/V6/(PSS+PAA); V6/PVA/(PSS+PAA); PVA/(PSS+PAA(35%))/(PSS+PAA(35%)); (PSS+PAA(35%))/PVA/(PSS+PAA(35%)); or (PSS+PAA (35%))/(PVA(10%)+PSS (20% vs. PVA))/(PSS+PAA (35%)).
  • the multi-functional separator comprises the layers PVA/V6/(PSS+PAA); V6/PVA/(PSS+PAA); or (PSS+PAA(35%))/PVA/(PSS+PAA (35%)).
  • the separator thickness is ⁇ 100 ⁇ m.
  • the separator thickness is ⁇ 30 ⁇ m.
  • Each layer in the separator is ⁇ 10 ⁇ m.
  • the separator impedes dendrite formation relative to a separator made of the same thickness from PVA.
  • At least two layers of the separator comprise a polymeric material each individually selected from PVA, a quaternary ammonium polymer, or combinations thereof.
  • the invention provides a method of producing a separator comprising:
  • PSA polymer mixture and the PVA polymer mixture are provided to form a unitary separator comprising a PSA polymer layer and a PVA polymer layer, wherein the PSA polymer layer resists oxidation and the PVA polymer layer resists dendrite formation.
  • Embodiments of this aspect may include one or more of the following features.
  • the separator has a total thickness of less than 100 microns.
  • the method further comprises providing 1 to 10 additional polymer mixtures, wherein the polymer mixtures are provided to form a separator comprising a PSA polymer layer, a PVA polymer layer, and from 1 to 10 additional polymer layers.
  • the separator has an ionic resistance of ⁇ 10 ⁇ /cm2, electrical resistance of >10 k ⁇ /cm2, and a wet tensile strength of >0.1 lbf.
  • the ionic resistance of the separator is ⁇ 0.5 ⁇ /cm2.
  • FIG. 1 depicts a cross-sectional view of a bi-functional separator having two active separator layers deposited on opposite sides of an inert porous substrate film according to the invention
  • FIG. 2 depicts a cross-sectional view of a prior art cascade coating apparatus for producing a free-standing multi-layered film comprising wet layers;
  • FIG. 3 depicts a cross-sectional view of a cascade coating apparatus adapted to provide active separator layers on both sides of an optional substrate film;
  • FIG. 4 illustrates the electrode-separator configuration used for test cells incorporating a bi-functional separator according to the invention, or analogous individual separator layers;
  • FIG. 5 shows plots of charge capacity versus cycle number for two zinc-silver oxide cells (A and B), wherein the separator includes a ZrO 2 —PEO separator layer and two PVA separator layers (70 ⁇ m total thickness); and
  • FIG. 6 shows plots of charge capacity versus cycle number for two zinc-silver oxide cells (A and B) employing two bi-functional PVA/ZrO 2 —PEO separator layers (60 ⁇ m total thickness).
  • the invention provides a multi-functional battery separator comprising two or more active separator layers deposited from different polymer solutions to form a multilayered unitary structure comprising a free-standing film, a multiplex film on one side of a porous substrate, or separate films or multiplex films on opposite sides of a porous substrate.
  • the cascade coating method is used to simultaneously deposit the active separator layers wet so that the physical, electrical and morphological changes associated with the polymer drying out process are avoided or minimized.
  • the active separator layers of the multi-functional battery separator of the invention can also be deposited via conventional methods.
  • the invention also provides a process for fabricating the multi-functional battery separator.
  • battery encompasses electrical storage devices comprising one electrochemical cell or a plurality of electrochemical cells.
  • a “secondary battery” is rechargeable, whereas a “primary battery” is not rechargeable.
  • a battery anode is designated as the positive electrode during discharge, and as the negative electrode during charge.
  • alkaline battery refers to a primary battery or a secondary battery, wherein the primary or secondary battery comprises an alkaline electrolyte.
  • a “dopant” or “doping agent” refers to a chemical compound that is added to a substance in low concentrations in order to alter the optical/electrical properties of the semiconductor.
  • a dopant can be added to the powder active material of a cathode to improve its electronic properties (e.g., reduce its impedance and/or resistivity).
  • an “electrolyte” refers to a substance that behaves as an electrically conductive medium.
  • the electrolyte facilitates the mobilization of electrons and cations in the cell.
  • Electrolytes include mixtures of materials such as aqueous solutions of alkaline agents. Some electrolytes also comprise additives such as buffers.
  • an electrolyte comprises a buffer comprising a borate or a phosphate.
  • Exemplary electrolytes include, without limitation aqueous KOH, aqueous NaOH, or the liquid mixture of KOH in a polymer.
  • alkaline agent refers to a base or ionic salt of an alkali metal (e.g., an aqueous hydroxide of an alkali metal). Furthermore, an alkaline agent forms hydroxide ions when dissolved in water or other polar solvents. Exemplary alkaline electrolytes include without limitation LiOH, NaOH, KOH, CsOH, RbOH, or combinations thereof.
  • a “cycle” refers to a single charge and discharge of a battery.
  • polyvinylidene fluoride and its corresponding initials “PVDF” are used interchangeably as adjectives to distinguish polymers, solutions for preparing polymers, and polymer coatings. Use of these names and initials in no way implies the absence of other constituents. These adjectives also encompass substituted and co-polymerized polymers.
  • a substituted polymer denotes one for which a substituent group, a methyl group, for example, replaces a hydrogen on the polymer backbone.
  • polytetrafluoroethylene and its corresponding initials “PTFE” are used interchangeably as adjectives to distinguish polymers, solutions for preparing polymers, and polymer coatings. Use of these names and initials in no way implies the absence of other constituents. These adjectives also encompass substituted and co-polymerized polymers.
  • a substituted polymer denotes one for which a substituent group, a methyl group, for example, replaces a hydrogen on the polymer backbone.
  • Ah refers to Ampere (Amp) Hour and is a scientific unit for the capacity of a battery or electrochemical cell.
  • a derivative unit, “mAh” represents a milliamp hour and is 1/1000 of an Ah.
  • maximum voltage or “rated voltage” refers to the maximum voltage an electrochemical cell can be charged without interfering with the cell's intended utility.
  • the maximum voltage is less than about 3.0 V (e.g., less than about 2.8 V, less than about 2.5 V, about 2.3 V or less, or about 2.0 V).
  • the maximum voltage is less than about 15.0 V (e.g., less than about 13.0 V, or about 12.6 V or less).
  • the maximum voltage for a battery can vary depending on the number of charge cycles constituting the battery's useful life, the shelf-life of the battery, the power demands of the battery, the configuration of the electrodes in the battery, and the amount of active materials used in the battery.
  • an “anode” is an electrode through which (positive) electric current flows into a polarized electrical device.
  • the anode In a battery or galvanic cell, the anode is the negative electrode from which electrons flow during the discharging phase in the battery.
  • the anode is also the electrode that undergoes chemical oxidation during the discharging phase.
  • the anode in secondary, or rechargeable, cells, the anode is the electrode that undergoes chemical reduction during the cell's charging phase.
  • Anodes are formed from electrically conductive or semiconductive materials, e.g., metals, metal oxides, metal alloys, metal composites, semiconductors, or the like.
  • Common anode materials include Si, Sn, Al, Ti, Mg, Fe, Bi, Zn, Sb, Ni, Pb, Li, Zr, Hg, Cd, Cu, LiC 6 , mischmetals, alloys thereof, oxides thereof, or composites thereof.
  • Anodes can have many configurations.
  • an anode can be configured from a conductive mesh or grid that is coated with one or more anode materials.
  • an anode can be a solid sheet or bar of anode material.
  • a “cathode” is an electrode from which (positive) electric current flows out of a polarized electrical device.
  • the cathode In a battery or galvanic cell, the cathode is the positive electrode into which electrons flow during the discharging phase in the battery.
  • the cathode is also the electrode that undergoes chemical reduction during the discharging phase.
  • the cathode is the electrode that undergoes chemical oxidation during the cell's charging phase.
  • Cathodes are formed from electrically conductive or semiconductive materials, e.g., metals, metal oxides, metal alloys, metal composites, semiconductors, or the like.
  • Common cathode materials include AgO, Ag 2 O, HgO, Hg 2 O, CuO, CdO, NiOOH, Pb 2 O 4 , PbO 2 , LiFePO 4 , Li 3 V 2 (PO 4 ) 3 , V 6 O 13 , V 2 O 5 , Fe 3 O 4 , Fe 2 O 3 , MnO 2 , LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , or composites thereof.
  • Cathodes can also have many configurations.
  • a cathode can be configured from a conductive mesh that is coated with one or more cathode materials.
  • a cathode can be a solid sheet or bar of cathode material.
  • an “electronic device” is any device that is powered by electricity.
  • electronic device can include a portable computer, a portable music player, a cellular phone, a portable video player, or any device that combines the operational features thereof.
  • cycle life is the maximum number of times a secondary battery can be charged and discharged.
  • M denotes molar concentration
  • a zinc-silver oxide battery comprises an anode comprising zinc and a cathode comprising silver oxide. Nonetheless, more than one species is present at a battery electrode under most conditions.
  • a zinc electrode generally comprises zinc metal and zinc oxide (except when fully charged), and a silver oxide electrode usually comprises silver oxide (AgO and/or Ag 2 O) and silver metal (except when fully discharged).
  • oxide applied to alkaline batteries and alkaline battery electrodes encompasses corresponding “hydroxide” species, which are typically present, at least under some conditions.
  • substantially stable or “substantially inert” refers to a compound or component that remains substantially chemically unchanged in the presence of an alkaline electrolyte (e.g., potassium hydroxide) and/or in the presence of an oxidizing agent (e.g., silver ions present in the cathode or dissolved in the electrolyte).
  • an alkaline electrolyte e.g., potassium hydroxide
  • an oxidizing agent e.g., silver ions present in the cathode or dissolved in the electrolyte
  • charge profile refers to a graph of an electrochemical cell's voltage or capacity with time.
  • a charge profile can be superimposed on other graphs such as those including data points such as charge cycles or the like.
  • resistivity or “impedance” refers to the internal resistance of a cathode in an electrochemical cell. This property is typically expressed in units of Ohms or micro-Ohms.
  • first and/or “second” do not refer to order or denote relative positions in space or time, but these terms are used to distinguish between two different elements or components.
  • a first separator does not necessarily proceed a second separator in time or space; however, the first separator is not the second separator and vice versa.
  • a first separator it is possible for a first separator to proceed a second separator in space or time, it is equally possible that a second separator proceeds a first separator in space or time.
  • polyether polyethylene oxide
  • polypropylene oxide polypropylene oxide
  • polyvinyl alcohol polyvinyl alcohol
  • a substituted polymer denotes one for which a substituent group, a methyl group, for example, replaces a hydrogen on the polymer backbone.
  • oxidation-resistant refers to a separator that resists oxidation in an electrochemical cell of an alkaline battery and/or is substantially stable in the presence of an alkaline electrolyte and/or an oxidizing agent (e.g., silver ions).
  • an oxidizing agent e.g., silver ions
  • titanate salt refers to a chemical salt that includes in its chemical formula TiO 3 .
  • examples of titanate salts include potassium titanate, sodium titanate, lithium titanate, rubidium titanate, or cesium titanate, without limitation.
  • adjacent refers to the positions of at least two distinct elements (e.g., at least one separator and at least one electrode (e.g., an anode and/or a cathode)).
  • an element such as a separator is adjacent to another element such as an electrode or even a second separator
  • one element is positioned to contact or nearly contact another element.
  • the separator electrically contacts the electrode when the separator and electrode are in an electrolyte environment such as the environment inside an electrochemical cell.
  • the separator can be in physical contact or the separator can nearly contact the electrode such that any space between the separator and the electrode is void of any other separators or electrodes.
  • electrolyte can be present in any space between a separator that is adjacent to an electrode or another separator.
  • unitary structure refers to a structure that includes one or more elements that are concurrently or almost concurrently processed to form the structure.
  • an electrochemical cell separator that is a unitary structure is one in which all of the separator ingredients or starting materials concurrently undergo a process (other than mechanical combination) that combines them and forms a single separator.
  • a separator that includes a plurality of layers that are formed by coextruding the starting materials from a plurality of sources generates a unitary structure, wherein the interface between layers includes domains of each layer that terminates at the interface.
  • This unitary structure is not equivalent to a separator that includes a plurality of layers that are each individually formed and mechanically stacked to form a multi-layered separator.
  • the interface between layers in a unitary structure contains domains of each layer that joins at the interface, such that the interface comprises both layers simultaneously. This property is characteristic of unitary structures.
  • dendrite-resistant refers to a separator that reduces the formation of dendrites in an electrochemical cell of an alkaline battery under normal operating conditions, i.e., when the batteries are stored and used in temperatures from about ⁇ 20° C. to about 70° C., and are not overcharged or charged above their rated capacity and/or is substantially stable in the presence of an alkaline electrolyte, and/or is substantially stable in the presence of a reducing agent (e.g., an anode comprising zinc).
  • a dendrite-resistant separator inhibits transport and/or chemical reduction of metal ions.
  • Separators of the present invention comprise a unitary structure formed from at least two strata or layers.
  • the separator can include layers wherein each layer comprises the same material, or each layer comprises a different material; or, the strata are layered to provide layers of the same material and at least on layer of another material.
  • one stratum comprises an oxidation resistant material, and the remaining stratum comprises a dendrite resistant material.
  • at least one layer comprises an oxidation-resistant material, or at least one layer comprises a dendrite-resistant material.
  • the unitary structure is formed when the material comprising one layer (e.g., an oxidation-resistant material) is coextruded with the material comprising another layer (e.g., a dendrite resistant material or oxidation-resistant material).
  • the unitary separator is formed from the coextrusion of oxidation-resistant material with dendrite-resistant material.
  • the oxidation-resistant material comprises a polyether polymer mixture and the dendrite resistant material comprises a PVA polymer mixture.
  • the dendrite-resistant separator layer for use in a multi-functional separator for an alkaline zinc-silver oxide battery comprises a cross-linked polyvinyl alcohol (PVA) film deposited from a PVA solution comprising a cross-linking agent and a polyvinyl alcohol precursor polymer, which can be linear or branched and can be unsubstituted or substituted.
  • the PVA precursor polymer is at least 80% hydrolyzed and has an average molecular weight in the range from 150,000 to 190,000.
  • separators useful in electrochemical cells can be configured in any suitable way such that the separator is substantially inert in the presence of the anode, cathode and electrolyte of the electrochemical cell.
  • a separator for a rectangular battery electrode can be in the form of a sheet or film comparable in size or slightly larger than the electrode, and can simply be placed on the electrode or can be sealed around the edges. The edges of the separator can be sealed to the electrode, an electrode current collector, a battery case, or another separator sheet or film on the backside of the electrode via an adhesive sealant, a gasket, or fusion (heat sealing) of the separator or another material.
  • the separator can also be in the form of a sheet or film wrapped and folded around the electrode to form a single layer (front and back), an overlapping layer, or multiple layers.
  • the separator can be spirally wound with the electrodes in a jelly-roll configuration.
  • the separator is included in an electrode stack comprising a plurality of separators.
  • the oxidation-resistant separator of the invention can be incorporated in a battery in any suitable configuration.
  • separators of the present invention comprise active separator layers formulated from an ionic conducting polymer material (polyvinyl alcohol or polyethylene oxide, for example) and can include a metallic oxide filler material (zirconium oxide, titanium oxide or aluminum oxide, for example). Although not wishing to be limited by theory, it is theorized that the filler material impedes transport of detrimental ions (silver and zinc ions in zinc-silver oxide battery). Active separator layers can also include a conductivity enhancer (inorganic or organic), a surfactant, and/or a plasticizer.
  • an ionic conducting polymer material polyvinyl alcohol or polyethylene oxide, for example
  • a metallic oxide filler material zirconium oxide, titanium oxide or aluminum oxide, for example.
  • active separator layers can also include a conductivity enhancer (inorganic or organic), a surfactant, and/or a plasticizer.
  • the invention provides a multi-functional battery separator comprising a plurality of active separator layers that form a multilayered unitary structure.
  • Each of the active separator layers is deposited from a separate solution or mixture.
  • each solution or mixture has a different composition.
  • at least two of the separate mixtures or solutions have about the same composition.
  • At least two of the active separator layers are simultaneously deposited wet by the cascade coating method, either as a free-standing multi-functional separator or as multi-functional coatings on a porous substrate film. In this case, physical, electrical and morphological changes associated with the polymer drying out process are avoided or minimized.
  • at least one of the active separator layers is deposited as a free-standing film and at least one other active separator layer is deposited thereupon.
  • the multi-functional separator of the invention can further comprise a porous or nonporous substrate film, on which at least one of the active separator layers is deposited.
  • the multi-functional separator can comprise a multiplex film on one side of a porous substrate, or separate films or multiplex films on opposite sides of a porous substrate.
  • the invention also provides a process for fabricating the multi-functional battery separator.
  • FIG. 1 depicts a cross-sectional view of a bi-functional separator 100 comprising two active separator coatings 101 and 102 deposited on opposite sides of an inert porous substrate film 105 according to the invention.
  • Active materials 103 and 104 from coatings 101 and 102 respectively, have fully penetrated within the pores of substrate film 105 . At least some penetration of active materials 103 and 104 within the pores of substrate film 105 is preferred but can be less than full penetration.
  • Active separator layers for the multi-functional separator of the invention can be applied by any suitable method.
  • Methods for forming free-standing multi-functional separators or for applying separator layer coatings to a porous substrate include those selected from the group consisting of pouring, spreading, casting, pressing, backfilling, dipping, spraying, rolling, laminating, extruding, and combinations thereof.
  • the method of forming the multi-functional separator of the invention is the cascade coating method, which can be used to form free-standing multi-functional separators, or to apply multiple active separator layers to a porous substrate film.
  • the cascade coating method liquid or gelled solutions, each containing the constituents of a given layer, are co-extruded in sheets that flow together to simultaneously form the multi-layered structure.
  • FIG. 2 depicts a cross-sectional view of a one exemplary cascade coating apparatus 200 for producing a free-standing multi-layered film comprising two wet layers.
  • Solution 201 contained in reservoir 203 is flowed through slot 205 and forms film 207
  • solution 202 contained in reservoir 204 is flowed through slot 206 and forms film 208 disposed upon film 207 .
  • Solutions 201 and 202 can be caused to flow by any suitable means, including gravity (as shown), gas pressure, or a pump (not shown).
  • the extrusion rate (adjusted via solution viscosity and flow pressure) and solvent evaporation rate (adjusted via solution composition, temperature and humidity) are optimized to provide solid or semi-solid films of a desired consistency and wetness.
  • this apparatus can be readily expanded to form multi-functional separators having more than two layers.
  • Inter-diffusion and intermixing of the components of films 207 and 208 can be minimized by adjusting the solution viscosities, extrusion rates and solvent evaporation rates, and by applying heat to the extruded multi-layered film via radiant heating or forced convection heating.
  • Alternative solvents and surfactant additives for solutions 201 and 202 can also be used to render one adjacent separator layer hydrophobic and the other adjacent layer hydrophilic.
  • Polar surfactants having a hydrophobic head and a hydrophilic tail can be especially efficacious
  • FIG. 3 depicts a cross-sectional view of a cascade coating apparatus 300 adapted to provide active separator layers on both sides of a porous substrate film.
  • Solution 301 contained in reservoir 303 is flowed through slot 305 and forms active separator film 307
  • solution 302 contained in reservoir 304 is flowed through slot 306 and forms active separator film 308
  • both active separator film 307 and active separator film 308 are disposed on porous substrate film 309 as it passes between the openings in slots 305 and 306 .
  • Porous substrate film 309 can be conveyed via rollers 310 a - d of a conveyor. Active separator films 307 and 308 can penetrate into pores in porous substrate film partially (as shown) or fully.
  • One exemplary separator of the present invention includes 3 layers.
  • a first layer is a hydrophilic polymer dense film system.
  • This system can be prepared by co-extruding an aqueous polymer solution onto a second layer.
  • the aqueous polymer solution can be prepared by dissolving the polymer in water at 5-20 wt %.
  • Exemplary polymers include polyethylene oxide, polyethylene glycol, polyvinyl alcohol, or polyvinyl alcohol copolymers.
  • Polymer formulations can optionally include inert fillers, ion exchanging fillers, soluble fillers, plasticizers, extractable (immiscible) phase segregating liquids and copolymers with both hydrophobic and hydrophilic sub units, i.e., PEO-PMMA copolymers.
  • the second layer of this exemplary separator can be a hydrophilic composite film system.
  • This system can be prepared by co-extruding an aqueous composite mixture between the first layer and a third layer.
  • the aqueous composite mixture can be prepared by dispersing metal oxide particles in an aqueous polymer solution.
  • the metal oxide particles are zirconium dioxide, titanium dioxide, or combinations thereof.
  • Exemplary polymers useful for this second layer include polyethylene oxide, polyethylene glycol, polyvinyl alcohol, or polyvinyl alcohol copolymers.
  • the solid concentration of the aqueous composite mixture ranges from 10 to 40 wt %.
  • the metal oxide particles to polymer weight ratio ranges from 0.5 to 5.
  • the formulation can also have inert fillers, ion exchanging fillers, soluble fillers, plasticizers, extractable (immiscible) phase segregating liquids and copolymers with both hydrophobic and hydrophilic sub units, i.e., PEO-PMMA copolymers.
  • a third later can be a hydrophilic polymer dense film system.
  • One exemplary system is prepared by co-extruding an aqueous polymer solution between the second layer and an optional substrate.
  • the aqueous polymer solution can be prepared by dissolving the polymer in water at 5-20 weight percent.
  • the polymer can consist of polyethylene oxide, polyethylene glycol, polyvinyl alcohol or polyvinyl alcohol copolymers.
  • the formulation can also have inert fillers, ion exchanging fillers, soluble fillers, plasticizers, extractable (immiscible) phase segregating liquids and copolymers with both hydrophobic and hydrophilic sub units, i.e., PEO-PMMA copolymers.
  • the layers can have the same composition or different compositions.
  • two of the layers can include the same composition, or each of the three layers can comprise different compositions.
  • the only restrictions on the layer order are that they can not mix after co-extrusion but before they dry.
  • Exemplary processing conditions for the exemplary 3-layer separator system is prepared by simultaneously co-extruding 3 individual aqueous mixtures onto a carrier substrate using a triple-layer slot die.
  • the cast 3-layer film is dried at about 180 degrees Celsius in an 18-foot convection oven under about 1 foot per minute line speed.
  • the die gaps are set in various combinations to achieve a total dried film thickness of about 50 to 150 micrometers.
  • Exemplary materials for the substrate include polypropylene, hydrophilic non-woven polyolefins, polyesters, polyamides, perfluorinated polymers, or polysulfones.
  • the 3-layered separators described above are relatively environmentally friendly.
  • the use of other solvents is possible and some times preferred as when you want to prepare a layer by phase inversion.
  • An example would be PVDF:HFP in acetone when coextruded with an aqueous layer would cause the PVDF:HFP to exit the solution in a highly porous network.
  • the multi-functional separator of the invention can be used with any battery, comprising any electrolyte, any anode and any cathode.
  • the invention is especially suitable for use in an alkaline storage battery comprising a zinc anode and a silver oxide cathode, but can be used with other anodes and other cathodes.
  • the invention can be used with anodes comprising zinc, cadmium or mercury, or mixtures thereof, for example, and with cathodes comprising silver oxide, nickel oxide, cobalt oxide or manganese oxide, or mixtures thereof, for example.
  • the oxidation-resistant layer of the separator comprises a polyether polymer material that is coextruded with a dendrite-resistant material.
  • the polyether material can comprise polyethylene oxide (PEO) or polypropylene oxide (PPO), or a copolymer or a mixture thereof.
  • the polyether material can also be copolymerized or mixed with one or more other polymer materials, polyethylene, polypropylene and/or polytetrafluoroethylene (PTFE), for example.
  • the PE material is capable of forming a free-standing polyether film when extruded alone, or can form a free standing film when coextruded with a dendrite-resistant material.
  • the polyether material is substantially inert in the alkaline battery electrolyte and in the presence of silver ions.
  • the oxidation resistant material comprises a PE mixture that optionally includes zirconium oxide powder.
  • zirconium oxide powder inhibits silver ion transport by forming a surface complex with silver ions.
  • zirconium oxide encompasses any oxide of zirconium, including zirconium dioxide and yttria-stabilized zirconium oxide.
  • the zirconium oxide powder is dispersed throughout the PE material so as to provide a substantially uniform silver complexation and a uniform barrier to transport of silver ions.
  • the average particle size of the zirconium oxide powder is in the range from about 1 nm to about 5000 nm, e.g., from about 5 nm to about 100 nm.
  • the oxidation-resistant material further comprises an optional conductivity enhancer.
  • the conductivity enhancer can comprise an inorganic compound, potassium titanate, for example, or an organic material. Titanates of other alkali metals than potassium can be used. Suitable organic conductivity enhancing materials include organic sulfonates and carboxylates. Such organic compounds of sulfonic and carboxylic acids, which can be used singly or in combination, comprise a wide range of polymer materials that can include salts formed with a wide variety of electropositive cations, K + , Na + , Li + , Pb +2 , Ag + , NH4 + , Ba +2 , Sr +2 , Mg +2 , Ca +2 or anilinium, for example.
  • the conductivity enhancer can include a sulfonate or carboxylate copolymer, with polyvinyl alcohol, for example, or a polymer having a 2-acrylamido-2-methyl propanyl as a functional group.
  • a combination of one or more conductivity enhancing materials can be used.
  • Oxidation-resistant material that is coextruded to form a separator of the present invention can comprise from about 5 wt % to about 95 wt % (e.g., from about 20 wt % to about 60 wt %, or from about 30 wt % to about 50 wt %) of zirconium oxide and/or conductivity enhancer.
  • Oxidation-resistant materials can also comprise additives such as surfactants that improve dispersion of the zirconium oxide powder by preventing agglomeration of small particles.
  • Any suitable surfactant can be used, including one or more anionic, cationic, non-ionic, ampholytic, amphoteric and zwitterionic surfactants, and mixtures thereof.
  • the separator comprises an anionic surfactant.
  • the separator comprises an anionic surfactant, and the anionic surfactant comprises a salt of sulfate, a salt of sulfonate, a salt of carboxylate, or a salt of sarcosinate.
  • One useful surfactant comprises p-(1,1,3,3-tetramethylbutyl)-phenyl ether, which is commercially available under the trade name Triton X-100 from Rohm and Haas.
  • the oxidation-resistant material comprises from about 0.01 wt % to about 1 wt % of surfactant.
  • the oxidation-resistant separator layer comprises a polyether (PE) film deposited from a PE solution comprising a polyether polymer that can be linear or branched and can be unsubstituted or substituted.
  • the polyether polymer comprises a linear or branched polyethylene oxide (PEO) or polypropylene oxide (PPO), or a copolymer or a mixture thereof.
  • the polyether material can comprise a copolymer or a mixture of the polyether polymer with one or more polymer materials other than a polyether, for example, polyethylene, polypropylene, polyphenylene oxide, polysulfone, acrylonitrile butadiene styrene (ABS), or polytetrafluoroethylene.
  • Primary requirements are that the polyether film be substantially inert in the alkaline battery electrolyte and in the presence of silver ions.
  • Another exemplary polyether polymer is polyethylene oxide such as those having an average molecular weight in the range 0.5 to 5.0
  • the PE solution can also comprises a powder of a metallic oxide, zirconium oxide, titanium oxide or aluminum oxide, for example, as a filler to more effectively block transport of silver ions.
  • a metallic oxide filler is zirconium oxide, which is thought to inhibits silver ion transport by forming a surface complex with silver ions.
  • the powder of zirconium oxide (or other metallic oxide) is well dispersed throughout the PE film so as to provide a uniform barrier to transport of silver ions.
  • the average particle size of the zirconium oxide powder (or other metallic oxide powder) should be in the range from 1 to 5000 nm, preferably in the range from 5 to 200 nm. Zirconium oxide filler tends to increase the ionic conductivity of the oxidation-resistant separator layer.
  • the concentrations in weight percent of the components in a the PE solution are within the ranges: 87 to 95% water; 2 to 6% polyethylene oxide (PE polymer); 2 to 6% yttria-stabilized zirconium oxide (filler); 0.2 to 1.5% potassium titanate (conductivity enhancer); and 0.08 to 0.2% Triton X-100 (surfactant). These ranges can be adjusted for different PE polymers, fillers, conductivity enhancers, and surfactants.
  • the dendrite-resistant stratum of the separator comprises a polyvinyl polymer material that is coextruded with the oxidation-resistant material.
  • the PVA material comprises a cross-linked polyvinyl alcohol polymer and a cross-linking agent.
  • the cross-linked polyvinyl alcohol polymer is a copolymer.
  • the cross-linked PVA polymer is a copolymer comprising a first monomer, PVA, and a second monomer.
  • the PVA polymer is a copolymer comprising at least 60 mole percent of PVA and a second monomer.
  • the second monomer comprises vinyl acetate, ethylene, vinyl butyral, or any combination thereof.
  • the cross-linking agent used in the separators of the present invention comprises a monoaldehyde (e.g., formaldehyde or glyoxilic acid); aliphatic, furyl or aryl dialdehydes (e.g., glutaraldehyde, 2,6 furyldialdehyde or terephthaldehyde); dicarboxylic acids (e.g., oxalic acid or succinic acid); polyisocyanates; methylolmelamine; copolymers of styrene and maleic anhydride; germaic acid and its salts; boron compounds (e.g., boron oxide, boric acid or its salts; or metaboric acid or its salts); or salts of copper, zinc, aluminum or titanium.
  • the cross-linking agent comprises a monoaldehyde (e.g., formaldehyde or glyoxilic acid); aliphatic, furyl or aryl dialdehydes
  • the PVA material optionally comprises zirconium oxide powder.
  • the PVA material comprises from about 1 wt % to about 99 wt % (e.g., from about 2 wt % to about 98 wt %, from about 20 wt % to about 60 wt %, or from about 30 wt % to about 50 wt %).
  • the dendrite-resistant strata of the separator of the present invention comprises a reduced ionic conductivity.
  • the separator comprises an ionic resistance of less than about 20 m ⁇ /cm 2 , (e.g., less than about 10 m ⁇ /cm 2 , less than about 5 m ⁇ /cm 2 , or less than about 4 m ⁇ /cm 2 ).
  • the PVA material that forms the dendrite-resistant stratum of the separator of the present invention can optionally comprise any suitable additives such as a conductivity enhancer, a surfactant, a plasticizer, or the like.
  • the PVA material further comprises a conductivity enhancer.
  • the PVA material comprises a cross-linked polyvinyl alcohol polymer, a zirconium oxide powder, and a conductivity enhancer.
  • the conductivity enhancer comprises a copolymer of polyvinyl alcohol and a hydroxyl-conducting polymer. Suitable hydroxyl-conducting polymers have functional groups that facilitate migration of hydroxyl ions.
  • the hydroxyl-conducting polymer comprises polyacrylate, polylactone, polysulfonate, polycarboxylate, polysulfate, polysarconate, polyamide, polyamidosulfonate, or any combination thereof.
  • a solution containing a copolymer of a polyvinyl alcohol and a polylactone is sold commercially under the trade name Vytek® polymer by Celanese, Inc.
  • the separator comprises from about 1 wt % to about 10 wt % of conductivity enhancer.
  • the PVA material further comprises a surfactant.
  • the separator comprises a cross-linked polyvinyl alcohol polymer, a zirconium oxide powder, and a surfactant.
  • the surfactant comprises one or more surfactants selected from an anionic surfactant, a cationic surfactant, a nonionic surfactant, an ampholytic surfactant, an amphoteric surfactant, and a zwitterionic surfactant.
  • Such surfactants are commercially available.
  • the PVA material comprises from about 0.01 wt % to about 1 wt % of surfactant.
  • the dendrite-resistant stratum further comprises a plasticizer.
  • the dendrite-resistant stratum comprises a cross-linked polyvinyl alcohol polymer, a zirconium oxide powder, and a plasticizer.
  • the plasticizer comprises one or more plasticizers selected from glycerin, low-molecular-weight polyethylene glycols, aminoalcohols, polypropylene glycols, 1,3 pentanediol branched analogs, 1,3 pentanediol, and/or water.
  • the plasticizer comprises greater than about 1 wt % of glycerin, low-molecular-weight polyethylene glycols, aminoalcohols, polypropylene glycols, 1,3 pentanediol branched analogs, 1,3 pentanediol, or any combination thereof, and less than 99 wt % of water.
  • the plasticizer comprises from about 1 wt % to about 10 wt % of glycerin, low-molecular-weight polyethylene glycols, aminoalcohols, polypropylene glycols, 1,3 pentanediol branched analogs, 1,3 pentanediol, or any combination thereof, and from about 99 wt % to about 90 wt % of water.
  • the separator of the present invention further comprises a plasticizer.
  • the plasticizer comprises glycerin, a low-molecular-weight polyethylene glycol, an aminoalcohol, a polypropylene glycols, a 1,3 pentanediol branched analog, 1,3 pentanediol, or combinations thereof, and/or water.
  • the cross-linked polyvinyl alcohol polymer can be a copolymer comprising a copolymerized polymer and at least 60 mole percent polyvinyl alcohol.
  • the copolymer is formed by including the monomer of the copolymerized polymer in the PVA solution. Suitable monomers for forming a PVA copolymer include vinyl acetate, ethylene, vinyl butyral, and mixtures thereof.
  • Cross-linking is necessary to render the polyvinyl alcohol polymer insoluble in water.
  • Suitable cross-linking agents that can be added to the PVA solution to effect cross-linking of the polyvinyl alcohol precursor polymer include monoaldehydes (formaldehyde and glyoxilic acid, for example), aliphatic, furyl or aryl dialdehydes (glutaraldehyde, 2,6 furyldialdehyde and terephthaldehyde, for example), dicarboxylic acids (oxalic acid and succinic acid, for example), polyisocyanates, methylolmelamine, copolymers of styrene and maleic anhydride, germaic acid and its salts, boron, compounds (boron oxide, boric acid and its salts, and metaboric acid and its salts, for example), and salts of copper, zinc, aluminum and titanium.
  • a preferred cross-linking agent is boric acid.
  • the PVA solution further comprises a powder of an insoluble metallic oxide, zirconium oxide, titanium oxide or aluminum oxide, for example, as a filler material to more effectively block transport of silver and zinc ions and suppress growth of zinc dendrites.
  • a preferred filler material is zirconium oxide powder, as described in paragraph [0034] for the oxidation-resistant separator layer.
  • the concentrations in weight percent of the components in a PVA solution are 95% water, 3.1% polyvinyl alcohol (average molecular weight of 150,000), 1.9% zirconium oxide (ZrO 2 of 0.6 ⁇ m average particle size), and 0.06% boric acid.
  • the present invention provides a multilayered battery separator for use in an alkaline electrochemical cell.
  • the separator includes a PSA polymer material.
  • the layers can be stacked in any order.
  • the PSA polymer material comprises PSA, which can be present as a PSA homopolymer, a PSA copolymer (e.g., a block copolymer, a random copolymer, an alternating copolymer, or the like), or a mixture of PSA homopolymer or a PSA copolymer and another polymer or copolymer.
  • PSA can be present as a PSA homopolymer, a PSA copolymer (e.g., a block copolymer, a random copolymer, an alternating copolymer, or the like), or a mixture of PSA homopolymer or a PSA copolymer and another polymer or copolymer.
  • the PSA polymer material comprises a mixture of PSA (e.g., polystyrene sulfonic acid (PSS) or other polysulfonic acid of formula I) homopolymer or a PSA copolymer and another polymer or copolymer.
  • PSA polystyrene sulfonic acid
  • PSA copolymer e.g., polystyrene sulfonic acid (PSS) or other polysulfonic acid of formula I
  • the PSA polymer material comprises a mixture of PSA (e.g., polystyrene sulfonic acid or other polysulfonic acid of formula I) and polyacrylic acid (e.g., polymethylacrylic acid, acrylic acid grafted fluorinated polymer, or the like), acrylic acid copolymer, polyacrylamide, acrylamide copolymer, polyvinyl amine, vinyl amine copolymer, maleic acid copolymer, maleic anhydride copolymer, polyvinyl ether, vinyl ether copolymer, polyethylene glycol, ethylene glycol copolymer, polypropylene glycol, polypropylene glycol copolymer, sulfonated polysulfone, sulfonated polyethersulfone, sulfonated polyetheretherketone, polyallyl ether (e.g., polyvinyl ethet), polydivinylbenzene, or triallyltriazine.
  • PSA
  • the PSA polymer material comprises polystyrene sulfonic acid homopolymer.
  • PSA polymer material can also comprise one or more optional additives such as surfactants, plasticizers, fillers, combinations thereof, or the like, such as those described above.
  • optional additives such as surfactants, plasticizers, fillers, combinations thereof, or the like, such as those described above.
  • the multilayer separator may also include a quaternary ammonium polymer.
  • a quaternary ammonium polymer includes any polymer including a quaternary nitrogen. Examples of quaternary ammonium polymers include, but are not limited, poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)], a homopolymer of poly(2-dimethylamino)ethyl methacrylate) methyl chloride quaternary salt, poly(acrylamide-co-diallyldimethylammonium chloride), homopolymer of Polymer3: poly(diallyldimethylammonium chloride), poly(dimethylamine-co-epichlorohydrin-co-ethylenediamine) or mixtures thereof.
  • the separator of the present battery further comprises a substrate on which polymer materials (e.g., oxidation-resistant material and/or dendrite-resistant material) are coextruded.
  • polymer materials e.g., oxidation-resistant material and/or dendrite-resistant material
  • the separate polymer materials are coextruded onto a single surface of the substrate.
  • the polymer materials are coextruded onto opposing surfaces of the substrate such that at least two strata forming the separator are separated by the substrate.
  • Substrates useful in these novel separators can comprise any suitable material that is substantially inert in an alkaline electrochemical cell.
  • the substrate is a woven or non-woven sheet. In other embodiments, the substrate is a non-woven sheet.
  • the substrate film can comprise any suitable organic polymer or inorganic material that is electronically insulating, provides sufficient structural integrity, and is chemically and electrochemically stable in concentrated alkaline solutions.
  • suitable organic polymer materials comprise polyolefins (polyethylene or polypropylene, for example), polyethers (polyethylene oxide and polypropylene oxide, for example), polyfluorocarbons (polytetrafluoroethylene, for example), polyamides (nylon, for example), polysulfones (Udel® sold by Solvay, for example), polyethersulfones (Radel® sold by Solvay, for example), polyacrylates, polymethacrylates, polystyrenes, and mixtures, co-polymers and substituted polymers thereof.
  • Porous films of commercial blended polymers ABS (acrylonitrile butadiene styrene) or EPDM (ethylene-propylene-diene terpolymer), for example, can be used.
  • Suitable inorganic materials include metallic oxides, including aluminum oxide, titanium oxide, zirconium oxide, yttria-stabilized zirconium oxide, and mixtures thereof, and metallic nitrides, including titanium nitride, aluminum nitride, zirconium nitride, and mixtures thereof.
  • separators of the present invention can include any number of layers and can have any thickness; however, due to special considerations of electrochemical cell housings, it is desired to maximize the number of layers of the separator and minimize the overall thickness of the separator.
  • the separator comprises a total thickness of less than 200 microns (e.g., less than 150 microns or less than 100 microns). In other embodiments, the separator comprises from 2 to 20 layers (e.g., from 2 to 15 layers, from 2 to 10 layers, or from 2 to 5 layers. In other examples, the separator has a total thickness of less than 200 microns and comprises from about 2 to about 20 layers.
  • the invention provides a multi-functional battery separator comprising two or more active separator layers deposited from different polymer solutions to form a multilayered unitary structure comprising a free-standing film, a multiplex film on one side of a porous substrate, or separate films or multiplex films on opposite sides of a porous substrate.
  • the separator can be fashioned to resist both oxidation and dendrite formation.
  • a separator providing resistance to both oxidation and dendrite formation may posses three basic properties (three primary properties): ionic resistance acceptable for the application ( ⁇ 0.5 ⁇ /cm2 for high discharge rate applications or ⁇ 10 ⁇ /cm2 for low discharge rate applications), high electrical resistance (>10 k ⁇ /cm2), and wet tensile strength (>0.1 lbf).
  • additional properties of the separator such as chemical resistance, differential affinity for different ions present in the cell, sequestration of certain chemical species present in the electrolyte, or layers or surfaces that are more compliant or gel like, may be useful. However, many of the materials that impart these properties often diminish one or more of the three primary properties.
  • the current invention allows for materials with chemical resistance but high ionic resistance to be combined in a thin layer with a thicker layer that provides low ionic resistance but offers poorer chemical resistance thus producing a multilayer composite that meets both the three primary separator requirements and secondary chemical resistance requirements.
  • materials with very low ionic resistance but low tensile strength can be combined in a thick layer with a thin layer that provide good tensile strength but offer higher ionic resistance thus also producing a multilayer composite that meets both the three primary separator requirements and secondary chemical resistance requirements.
  • S is the total Newtons of force per length of film normal to the force (L) at break.
  • n is the number of layers which is greater than or equal to two
  • ⁇ i is the tensile strength (units of Newtons per cm 2 ) of the i th layer in the composite
  • t i is the thickness of the i th layer.
  • the multilayer separators of this invention also provide advantages for electrode shape change.
  • Many electrodes produce soluble species that can migrate and precipitate in parts of the cell that are not proximal to the electrode. This is one factor that drives shape change in zinc electrode for example.
  • Silver electrodes also have soluble intermediaries that if allowed to freely migrate away from the silver electrode the severely limit the cycle life of the cell.
  • Multilayer separators that satisfy the three primary separator requirements that also further satisfy specific transport properties can greatly reduce migration of soluble electrode species.
  • the relative transport properties of the individual layers of the multilayer separators are derived as a time dependent, transient, diffusion problem. For this problem, it is possible to set up a situation where the concentration diffusing ion at the boundary between two layers makes discontinues steps in concentration.
  • Fick's Second Law is a generalization where concentration is the main driving force for diffusion [A. N. Malakhov and A. L. Mladentsev, “Nonstationary Diffusion in a Multiphase Medium”, Radiophysics and Quantum Electronics, Vol. 35, p 38-46, 1995].
  • concentration is the main driving force for diffusion
  • a generalized form for this equation is
  • ⁇ c ⁇ ( x , t ) ⁇ t ⁇ ⁇ x ⁇ [ D ⁇ ( x ) ⁇ ⁇ ⁇ ⁇ ( x , t ) ⁇ x ]
  • C(x,t) is the concentration of the diffusing species at position x and at time t
  • D is the effective diffusion (or diffusion/migration) constant
  • ⁇ (x,t) is the electrochemical potential of the diffusing species.
  • ⁇ ° is the chemical potential at the reference conditions
  • R is the ideal gas constant and T the absolute temperature
  • a is the activity of the diffusing species
  • z is the charge on the ion
  • F is Faraday's constant
  • ⁇ is the electrostatic potential.
  • Multilayer separators can also provide advantages for dendrite penetration resistance.
  • Examples of materials that form metallic dendrites are zinc, silver, copper, lithium, and bismuth.
  • Dendrite penetration is a major cause of early cycle life failure for many chemistries of electrochemical cells.
  • Co-extruded multilayer separators of this invention help to decrease dendrite penetration.
  • the estimation of the maximum velocity of a growing dendrite is
  • F Faraday's constant
  • R is the ideal gas constant
  • t is the absolute temperature and is the overpotential
  • ⁇ is the surface energy of the dendrite material
  • D is the effective diffusion (or diffusion/migration) constant of the ion plating to form the dendrite
  • C ⁇ is the concentration of ion around the dendrite tip.
  • multilayer separator of this invention which resist dendrite growth possess the following property: the product of D C ⁇ in a first layer is at least 20% different from the product of D C ⁇ in an adjacent second layer. At lower overportentials and with materials with higher surface energies the step in the product DC ⁇ could be less than 20% between two layers to slow dendrite penetration.
  • electrochemical cell comprising a cathode, an anode, an electrolyte, and a separator, as described above.
  • electrochemical cells of the present invention any suitable cathode, anode, and electrolyte can be used.
  • Another aspect of the present invention provides electrochemical cells comprising an alkaline electrolyte, a cathode, and an anode; wherein the cathode comprises a first active material and a first binder material; the anode comprises a second active material and a second binder material.
  • the first binder material, the second binder material, or both comprises PVDF or PVDF copolymer.
  • the cathode comprises at least 90 wt % of the first active material.
  • the cathode comprises at least 90 wt % of an active material selected from AgO, Ag 2 O, HgO, Hg 2 O, CuO, CdO, NiOOH, Pb 2 O 4 , PbO 2 , LiFePO 4 , Li 3 V 2 (PO 4 ) 3 , V 6 O 13 , V 2 O 5 , Fe 3 O 4 , Fe 2 O 3 , MnO 2 , LiCoO 2 , LiNiO 2 , or LiMn 2 O 4 .
  • the active material of the cathode comprises AgO.
  • the AgO is doped with up to 10 wt % of Pb.
  • the AgO is doped with up to 5 wt % of Pb, or the AgO is doped with up to 5 wt % of Pb and is coated with up to 5 wt % Pb.
  • Other suitable silver oxide-type active materials include Ag 2 O or Ag 2 O 3 , which may be used in combination with AgO and/or in combination with each other.
  • a cathode comprises up to about 10 wt % (e.g., up to about 6 wt %) of a binder material.
  • the cathode comprises up to about 10 wt % of a binder that comprises PVDF or PVDF copolymer.
  • the binder material comprises a PVDF copolymer such as PVDF-co-HFP copolymer.
  • the PVDF-co-HFP copolymer has a mean molecular weight of less than about 600,000 amu (e.g., less than about 500,000 amu, or about 400,000 amu).
  • an anode useful in the present electrochemical cells comprises at least 90 wt % of the second active material.
  • an anode comprises at least about 90 wt % of an active material selected from Si, Sn, Al, Ti, Mg, Fe, Bi, Zn, Sb, Ni, Pb, Li, Zr, Hg, Cd, Cu, LiC 6 , mischmetals, or oxides thereof.
  • the anode comprises an active material comprising Zn or ZnO.
  • the anode comprises up to 10 wt % of a binder material.
  • the anode comprises up to 6 wt % of a binder material.
  • the anode comprises binder material comprises up to 10 wt % of a binder material comprising. PVDF or PVDF copolymer.
  • the binder material comprises a PVDF copolymer such as PVDF-co-HFP copolymer.
  • the PVDF-co-HFP copolymer has a mean molecular weight of less than about 600,000 amu (e.g., less than about 500,000 amu, or about 400,000 amu).
  • Electrochemical cells of the present invention comprise an alkaline electrolyte.
  • the electrolyte comprises NaOH or KOH.
  • the electrolyte can comprise aqueous NaOH or KOH, or NaOH or KOH mixtures with liquids substantially free of water, such as liquid polymers.
  • Exemplary alkaline polymer electrolytes include, without limitation, 90 wt % PEG-200 and 10 wt % KOH, 50 wt % PEG-200 and 50 wt % KOH; PEG-dimethyl ether that is saturated with KOH; PEG-dimethyl ether and 33 wt % KOH; PEG-dimethyl ether and 11 wt % KOH; and PEG-dimethyl ether (mean molecular weight of 500 amu) and 33 wt % KOH, that is further diluted to 11 wt % KOH with PEG-dimethyl ether having a mean molecular weight of 200 amu.
  • Exemplary electrolytes include aqueous metal-hydroxides such as NaOH and/or KOH.
  • Other exemplary electrolytes include mixtures of a metal hydroxide and a polymer that is liquid at a range of operating and/or storage temperatures for the electrochemical cell into which it employed.
  • the electrolyte is an aqueous mixture of NaOH or KOH having a concentration of at least 8 M.
  • Polymers useful for formulating an electrolyte of the present invention are also at least substantially miscible with an alkaline agent.
  • the polymer is at least substantially miscible with the alkaline agent over a range of temperatures that at least includes the operating and storage temperatures of the electrochemical device in which the mixture is used.
  • the polymer is at least substantially miscible, e.g., substantially miscible with the alkaline agent at a temperature of at least ⁇ 40° C.
  • the polymer is liquid at a temperature of at least ⁇ 30° C. (e.g., at least ⁇ 20° C., at least ⁇ 10° C., or from about ⁇ 40° C. to about 70° C.).
  • the polymer is at least substantially miscible with the alkaline agent at a temperature from about ⁇ 20° C. to about 60° C.
  • the polymer is at least substantially miscible with the alkaline agent at a temperature of from about ⁇ 10° C. to about 60° C.
  • the polymer can combine with the alkaline agent at a temperature in the range of temperatures of the operation of the electrochemical device in which is it stored to form a solution.
  • the electrolyte comprises a polymer of formula (I):
  • each of R 1 , R 2 , R 3 , and R 4 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , each of V 1 , V 2 , and V 3 , is independently a bond or —O—, each of Q 1 , Q 2 , and Q 3 , is independently a bond, hydrogen, or a C 1-4 linear unsubstituted alkyl, n is 1-5, and p is a positive integer of sufficient value such that the polymer of formula (I) has a total molecular weight of less than 10,000 amu (e.g., less than about 5000 amu, less than about 3000 amu, from about 50 amu to about 2000 amu, or from about 100 amu to about 1000 amu) and an alkaline agent.
  • 10,000 amu e.g., less than about 5000 amu, less than about 3000 amu, from about 50 amu to about 2000 amu, or from about 100 amu to about 1000
  • the polymer is straight or branched.
  • R 1 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is hydrogen.
  • R 4 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 , is a bond, and Q 3 is hydrogen.
  • both of R 1 and R 4 are (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , each n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and each Q 3 is hydrogen.
  • R 1 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —CH 3 , —CH 2 CH 3 , —CH 2 CH 2 CH 3 , or H.
  • R 1 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —CH 3 or H.
  • R 1 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, one of Q 1 or Q 2 is —CH 2 —, —CH 2 CH 2 —, or —CH 2 CH 2 CH 2 —; V 1 and V 2 are each a bond; V 3 is —O—, and Q 3 is H.
  • R 4 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , is a bond, and V 3 is —O— or a bond, and Q 3 is hydrogen, —CH 3 , —CH 2 CH 3 , or —CH 2 CH 2 CH 3 .
  • R 4 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —H, —CH 3 , —CH 2 CH 3 , or —CH 2 CH 2 CH 3 .
  • R 1 is (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —CH 3
  • R 4 is (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , is a bond, and V 3 is —O—, and Q 3 is —H.
  • R 2 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —CH 3 , —CH 2 CH 3 , —CH 2 CH 2 CH 3 , or H.
  • R 2 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, one of V 1 , Q 1 , V 2 , Q z , and V 3 is —O—, and Q 3 is —H.
  • R 3 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, each of V 1 , Q 1 , V 2 , Q 2 , and V 3 is a bond, and Q 3 is —CH 3 , —CH 2 CH 3 , —CH 2 CH 2 CH 3 , or H.
  • R 3 is independently (V 1 -Q 1 -V 2 -Q 2 -V 3 -Q 3 ) n , wherein n is 1, one of V 1 , Q 1 , V 2 , Q 2 , and V 3 is —O—, and Q 3 is —H.
  • the polymer comprises a polyethylene oxide. In other examples, the polymer comprises a polyethylene oxide selected from polyethylene glycol, polypropylene glycol, polybutylene glycol, alkyl-polyethylene glycol, alkyl-polypropylene glycol, alkyl-polybutylene glycol, and any combination thereof.
  • the polymer is a polyethylene oxide having a molecular weight or mean molecular weight of less than 10,000 amu (e.g., less than 5000 amu, or from about 100 amu to about 1000 amu). In other embodiments, the polymer comprises polyethylene glycol.
  • Alkaline agents useful in the electrolyte of the present invention are capable of producing hydroxyl ions when mixed with an aqueous or polar solvent such as water and/or a liquid polymer.
  • the alkaline agent comprises LiOH, NaOH, KOH, CsOH, RbOH, or combinations thereof.
  • the alkaline agent comprises LiOH, NaOH, KOH, or combinations thereof.
  • the alkaline agent comprises KOH.
  • the electrolyte of the present invention comprises a liquid polymer of formula (I) and an alkaline agent comprising LiOH, NaOH, KOH, CsOH, RbOH, or combinations thereof.
  • the electrolyte comprises a liquid polymer comprising a polyethylene oxide; and an alkaline agent comprising LiOH, NaOH, KOH, CsOH, RbOH, or combinations thereof.
  • the electrolyte comprises a polymer comprising a polyethylene oxide and an alkaline agent comprising KOH.
  • the electrolyte of the present invention comprises more than about 1 wt % of alkaline agent (e.g., more than about 5 wt % of alkaline agent, or from about 5 wt % to about 76 wt % of alkaline agent).
  • the electrolyte comprises a liquid polymer comprising a polyethylene oxide and 3 wt % or more (e.g., 4 wt % or more, from about 4 wt % to about 33 wt %, or from about 5 wt % to about 15 wt %) of an alkaline agent.
  • the electrolyte comprises polyethylene oxide and 5 wt % or more of KOH.
  • the electrolyte consists essentially of a polyethylene oxide having a molecular weight or mean molecular weight from about 100 amu to about 1000 amu and 5 wt % or more of KOH.
  • Electrolytes of the present invention can be substantially free of water.
  • the electrolyte comprises water in an amount of about 60% of the wt of the alkaline agent or less (e.g., about 50% of the wt of the alkaline agent or less, about 40% of the wt of the alkaline agent or less, about 30% of the wt of the alkaline agent or less, about 25% of the wt of the alkaline agent or less, about 20% of the wt of the alkaline agent or less, or about 10% of the wt of the alkaline agent or less).
  • Exemplary alkaline polymer electrolytes include, without limitation, 90 wt % PEG-200 and 10 wt % KOH, 50 wt % PEG-200 and 50 wt % KOH; PEG-dimethyl ether that is saturated with KOH; PEG-dimethyl ether and 33 wt % KOH; PEG-dimethyl ether and 11 wt % KOH; and PEG-dimethyl ether (mean molecular weight of 500 amu) and 33 wt % KOH, that is further diluted to 11 wt % KOH with PEG-dimethyl ether having a mean molecular weight of 200 amu.
  • the electrolyte is aq. KOH having a concentration of from about 10 M to about 18 M.
  • the alkaline electrolyte is an aqueous solution comprising a hydroxide of an alkali metal selected from the group consisting of potassium, sodium, lithium, rubidium, cesium, and mixtures thereof.
  • the hydroxide concentration is in the molar concentration range from 4 M to 16 M (e.g., from about 8 M to about 16 M, or from about 10 M to about 16 M).
  • the electrochemical cell is a zinc-silver oxide battery
  • a the electrolyte is 15 M potassium hydroxide.
  • the electrolyte can further comprise a gelling agent, polyethylene oxide, polyvinyl alcohol, carboxyalkyl cellulose, polyacylonitrile, polyacrylic acid, polymethacrylic acid, polyoxazoline, polyvinylpyrrolidine, polyacrylate or polymethacrylate, for example.
  • a gelling agent polyethylene oxide, polyvinyl alcohol, carboxyalkyl cellulose, polyacylonitrile, polyacrylic acid, polymethacrylic acid, polyoxazoline, polyvinylpyrrolidine, polyacrylate or polymethacrylate, for example.
  • the present invention also provides methods of producing a separator of the present invention comprising providing a PE polymer mixture, as described above, and providing a PVA polymer mixture as described above, wherein the PE polymer mixture and the PVA polymer mixture are provided to form a unitary separator comprising a PE polymer layer as described above and a PVA polymer layer as described above.
  • bi-functional separator comprising a polyvinyl alcohol (PVA) layer and a zirconium oxide-polyethylene oxide (ZrO 2 —PEO) layer.
  • PVA polyvinyl alcohol
  • ZrO 2 —PEO zirconium oxide-polyethylene oxide
  • zinc-silver oxide test cells incorporating the bi-functional separator (Cell B) and those incorporating individual separator layers of the same composition as the bi-functional separator layers (Cell A) were evaluated via charge-discharge cycle testing.
  • Solutions having substantially equivalent compositions were used to prepare the bi-functional separator and the individual separator layers.
  • Polyvinyl alcohol layers were deposited from a 10 wt % PVA solution.
  • the PEO solution comprised 87 to 97 wt % water, 2 to 6 wt % polyethylene oxide, 2 to 6 wt % yttria-stabilized zirconium oxide (filler), 0.2 to 1.5 wt % potassium titanate (conductivity enhancer), and 0.08 to 0.2 wt % Triton X-100 (surfactant).
  • Conventional dispersing techniques were used to provide a uniform dispersion of the filler.
  • the bi-functional separator was prepared by co-extrusion of the PVA and PEO solutions from a two-layer slot-die unit, and drying at 280° C.
  • the individual separator layers were prepared using conventional film casting techniques.
  • FIG. 4 illustrates the electrode-separator configuration used for the test cells, which comprised three cathodes ( 111 , 113 and 115 ) and two anodes ( 112 and 114 ).
  • Cathode 113 was two-sided, being sandwiched between anodes 112 and 114 , and had the same capacity as the two one-sided cathodes ( 111 and 115 ) combined.
  • the anodes comprised a total of 14 grams of zinc, and the cathodes comprised a total of 22 grams of silver.
  • Electrodes 111 , 112 , 113 , 114 and 115 were wrapped in individual Solupor separator films (DSM Solutech) 121 , 122 , 123 , 124 and 125 , respectively, and were charged with 40 wt % aqueous potassium hydroxide electrolyte under a reduced pressure chamber before being incorporated in cells.
  • the solution uptake ranged from 10 to 20 wt % for the anodes and 15 to 25% for the cathodes.
  • the Solupor films are passive separators in that they function primarily as electrolyte reservoirs.
  • an active separator stack 131 was serpentined back and forth between the electrodes.
  • Active separator stack comprised either two bi-functional PVA/ZrO 2 —PEO separator layers according to the invention, or a ZrO 2 —PEO layer and two PVA layers.
  • an oxidation-resistant ZrO 2 —PEO layer faced the cathode
  • a dendrite-resistant PVA layer faced the anode.
  • the two bi-functional layers had a total thickness of 60 ⁇ m, compared to 70 ⁇ m for the three individual layers.
  • each cell After being assembled, each cell was charged with an additional 0.25 mL of 40 wt % KOH solution, and was vacuum-sealed in a polyethylene bag for cycle testing. Cycle tests involved discharge at 950 mA and charge at 690 mA.
  • FIG. 5 shows plots of charge capacity versus cycle number for two zinc-silver oxide cells employing a ZrO 2 —PEO separator layer and two PVA separator layers. Both cells exhibited an appreciable loss in capacity after about 50 cycles and failed in less than 100 cycles.
  • FIG. 6 shows plots of charge capacity versus cycle number for two zinc-silver oxide cells (A and B) employing two bi-functional PVA/ZrO 2 —PEO separator layers. Capacity loss for both of these cells as practically negligible after more than 125 cycles.
  • separator materials are useful for constructing separators of this invention.
  • PVA is about 10 wt % PVA
  • V6 is about ⁇ 10 wt % PVA & ZrO 2 ( ⁇ 35 wt % vs. PVA)
  • Sample Code T5 is PSS+PAA (20%).
  • 6.5 wt % PSS prepared from resin (Mw 1M); to the PSS solution was added 20 wt % PAA (vs. PSS resin) in solution form (192058 Aldrich Poly(acrylic acid) partial sodium salt solution average Mw ⁇ 240,000 by GPC, 25 wt. % in H2O). film was cast and dried overnight at ambient condition
  • Sample Code T6 is PSS+PSS-co-MA(1:1) (20%).
  • MA is malaic anhydride/acid with PSS.
  • Sample Code T8 is PVA/T7/T7.
  • PVA is 10% PVA bottom layers with two T7 layers, where T7 is described above.
  • Sample Code P1 is PVA+PSS (10 wt % vs PVA).
  • PVA is a (10% stock) solution mixed with PSS solution (20% stock) to provide a 10 wt % PSS.
  • Sample Code P2 is PVA+PSS (20 wt % vs PVA).
  • PVA is a (10% stock) solution mixed with PSS solution (20% stock) to provide a 20 wt % PSS.
  • Sample Code P3 is PVA+PSS (20 wt % vs PVA).
  • PVA (9% stock) solution mixed with PSS solution (20% stock) to provide a 20 wt % PSS
  • Sample Code T9a is P2/T7/T7. P2 and T7 are described above.
  • Sample Code T9b is P3/T7/T7.
  • T7 is described above.
  • Sample Code T10 (1012-59) is T7/PVA/T7, in which a 10% PVA layer is sandwiched between two T7s.
  • Sample Code P4 is PVA(10%)+PSS (20% vs. PVA). PSS was obtained from a commercial 25 wt % solution.
  • Sample Code T11 is T7/P4/T7, in which T7 and P4 are described above.
  • Sample Code T10F3 is the same configuration as T10 in which each layer is 8 ⁇ m.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Composite Materials (AREA)
  • Inorganic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Cell Separators (AREA)
  • Secondary Cells (AREA)
US12/933,977 2008-03-27 2009-03-27 Electrode Separator Abandoned US20110123850A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/933,977 US20110123850A1 (en) 2008-03-27 2009-03-27 Electrode Separator

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US4002108P 2008-03-27 2008-03-27
PCT/US2009/001946 WO2009120382A1 (fr) 2008-03-27 2009-03-27 Séparateur d'électrode
US12/933,977 US20110123850A1 (en) 2008-03-27 2009-03-27 Electrode Separator

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2009/001946 A-371-Of-International WO2009120382A1 (fr) 2008-03-27 2009-03-27 Séparateur d'électrode

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/477,219 Division US9960399B2 (en) 2008-03-27 2014-09-04 Electrode separator

Publications (1)

Publication Number Publication Date
US20110123850A1 true US20110123850A1 (en) 2011-05-26

Family

ID=40801875

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/933,977 Abandoned US20110123850A1 (en) 2008-03-27 2009-03-27 Electrode Separator
US14/477,219 Active 2031-02-26 US9960399B2 (en) 2008-03-27 2014-09-04 Electrode separator

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/477,219 Active 2031-02-26 US9960399B2 (en) 2008-03-27 2014-09-04 Electrode separator

Country Status (8)

Country Link
US (2) US20110123850A1 (fr)
EP (2) EP2272119B1 (fr)
JP (2) JP5591220B2 (fr)
CN (1) CN102017232B (fr)
AU (1) AU2009229167B2 (fr)
CA (1) CA2719223C (fr)
DK (1) DK2272119T3 (fr)
WO (1) WO2009120382A1 (fr)

Cited By (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090029261A1 (en) * 2007-05-31 2009-01-29 A123 Systems, Inc. Separator including electroactive material for overcharge protection
US20110259505A1 (en) * 2009-09-29 2011-10-27 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured therefrom and method for manufacturing electrochemical device having the same
US20130034769A1 (en) * 2010-04-19 2013-02-07 Mitsubishi Plastics, Inc. Laminated porous film, separator for non-aqueous electrolyte battery, and non-aqueous electrolyte secondary battery
US20130224632A1 (en) * 2011-07-11 2013-08-29 California Institute Of Technology Novel separators for electrochemical systems
US20130266872A1 (en) * 2010-09-16 2013-10-10 Zpower, Llc Electrode separator
WO2014124107A2 (fr) 2013-02-06 2014-08-14 Encell Technology, Inc. Batterie comprenant une anode de fer enrobée et présentant des performances améliorées
WO2014124110A1 (fr) * 2013-02-06 2014-08-14 Encell Technology, Inc. Électrolyte amélioré pour batterie contenant une électrode en fer
EP2742552A4 (fr) * 2011-08-08 2015-05-06 Basf Se Cellules électrochimiques
US20150364790A1 (en) * 2013-02-01 2015-12-17 Nippon Shokubai Co., Ltd. Anion conducting material and cell
US9287592B2 (en) 2013-02-06 2016-03-15 Encell Technology, Inc. Process for forming a battery containing an iron electrode
US20160087271A1 (en) * 2014-09-24 2016-03-24 Schlumberger Technology Corporation Rechargeable Lithium Polymer Electrolyte Battery for Oilfield Use
US9450233B2 (en) 2013-02-06 2016-09-20 Encell Technology, Inc. Battery comprising a coated iron anode
US9559385B2 (en) 2013-02-06 2017-01-31 Encell Technology, Inc. Nickel iron battery employing an untreated polyolefin separator with a surfactant in the electrolyte
US9954210B2 (en) * 2011-10-20 2018-04-24 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured by the method and method for manufacturing electrochemical device including the separator
US9960399B2 (en) 2008-03-27 2018-05-01 Zpower, Llc Electrode separator
US9991492B2 (en) 2013-11-18 2018-06-05 California Institute Of Technology Separator enclosures for electrodes and electrochemical cells
US20180351161A1 (en) * 2016-02-01 2018-12-06 The Regents Of The University Of California Functional polymer binder for sulfur cathode fabrication
US10158110B2 (en) 2011-07-11 2018-12-18 California Institute Of Technology Separators for electrochemical systems
US10177361B2 (en) 2012-06-20 2019-01-08 Sumitomo Chemical Company, Limited Coating fluid, laminated porous film, and non-aqueous electrolyte secondary battery
US10448137B1 (en) 2018-06-21 2019-10-15 Bose Corporation Dual zone discharge of rechargeable batteries
US20200006763A1 (en) * 2017-03-15 2020-01-02 Kabushiki Kaisha Nihon Micronics Electricity storage device
US10587011B2 (en) 2013-02-06 2020-03-10 Encell Technology, Inc. Nickel-iron battery with high power
CN111341974A (zh) * 2020-03-13 2020-06-26 江苏厚生新能源科技有限公司 Pvdf涂胶隔膜及其制备方法、pvdf涂胶层、锂电池
US10707537B2 (en) 2013-02-06 2020-07-07 Encell Technology, Inc. Nickel-iron battery with high cycle life
US10714724B2 (en) 2013-11-18 2020-07-14 California Institute Of Technology Membranes for electrochemical cells
US10763004B2 (en) 2014-03-12 2020-09-01 3M Innovative Properties Company Conductive polymeric material
US10804573B2 (en) 2013-02-06 2020-10-13 Encell Technology, Inc. Electrolyte for battery containing an iron electrode
US10847843B2 (en) 2013-02-06 2020-11-24 Encell Technology, Inc. Electrolyte for a nickel-iron battery
US11161961B2 (en) * 2017-04-21 2021-11-02 Avomeen Analytical Services Shutdown and non-shutdown separators for electrochemical devices
US11271214B2 (en) 2015-12-02 2022-03-08 California Institute Of Technology Three-dimensional ion transport networks and current collectors for electrochemical cells
WO2023283309A1 (fr) * 2021-07-07 2023-01-12 Board Of Regents, The University Of Texas System Séparateurs destinés à être utilisés dans des dispositifs de stockage d'énergie
US20230198028A1 (en) * 2013-05-31 2023-06-22 Johan C. Fitter Metal accumulation inhibiting and performance enhancing supplement and a system for delivering the supplement

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012076950A1 (fr) * 2010-12-05 2012-06-14 Ramot At Tel-Aviv University Ltd. Dépôt électrophorétique de batteries en couches minces
JP2013203894A (ja) * 2012-03-28 2013-10-07 Asahi Kasei E-Materials Corp ポリオレフィン微多孔膜
KR101521178B1 (ko) * 2012-03-31 2015-05-19 한양대학교 산학협력단 리튬 이차 전지용 양극활물질 전구체의 제조 방법, 이에 의하여 제조된 리튬 이차 전지용 양극활물질 전구체, 및 이를 포함하는 리튬 이차 전지용 양극활물질
JP6324655B2 (ja) * 2012-06-20 2018-05-16 住友化学株式会社 セパレータの製造方法及び非水電解液二次電池
JP2014139880A (ja) * 2013-01-21 2014-07-31 National Institute Of Advanced Industrial & Technology アルカリ電解液二次電池用セパレータ、アルカリ電解液二次電池及びアルカリ電解液二次電池の製造方法
JP6296542B2 (ja) * 2014-03-28 2018-03-20 日産自動車株式会社 亜鉛二次電池用電解質及び亜鉛二次電池
JP6070664B2 (ja) * 2014-09-19 2017-02-01 トヨタ自動車株式会社 空気電池
CN104269506A (zh) * 2014-10-24 2015-01-07 深圳市星源材质科技股份有限公司 多层共挤涂覆制备锂电池复合隔膜的方法及装置
US20160233491A1 (en) * 2015-02-05 2016-08-11 Board Of Regents, The University Of Texas System Bismuth-antimony anodes for lithium or sodium ion batteries
WO2016140906A1 (fr) * 2015-03-02 2016-09-09 Graphene 3D Lab Inc. Composites thermoplastiques comprenant des polymères greffés à base de polyéthylène oxyde (peo) hydrosolubles utiles pour une fabrication additive tridimensionnelle
US10777795B2 (en) * 2015-03-05 2020-09-15 Nec Corporation Separator including resin member formed inside porous substrate, and secondary battery equipped therewith
JP6747793B2 (ja) * 2015-09-16 2020-08-26 マクセルホールディングス株式会社 アルカリ二次電池
WO2017130574A1 (fr) * 2016-01-25 2017-08-03 株式会社ダイセル Batterie secondaire
CN106848155B (zh) * 2017-02-23 2020-03-31 上海杰宁新能源科技发展有限公司 微孔聚烯烃表面涂层材料制备方法、涂层涂布方法和涂层
KR20200038299A (ko) * 2017-08-31 2020-04-10 리서치 파운데이션 오브 더 시티 유니버시티 오브 뉴욕 알칼리 배터리에서 선택성 이온 침투를 위한 이온 선택성 막
CN115350601A (zh) * 2017-09-12 2022-11-18 赛尔格有限责任公司 干法工艺聚合物膜及应用
CN108258172A (zh) * 2018-01-15 2018-07-06 湘潭大学 一种钛酸盐耐高温隔膜及其制备方法和用途
JP7310788B2 (ja) * 2020-12-21 2023-07-19 トヨタ自動車株式会社 亜鉛二次電池用セパレータ
WO2023127933A1 (fr) * 2021-12-28 2023-07-06 信越化学工業株式会社 Composition contenant un composé hybride inorganique/organique
CN117096435A (zh) * 2023-01-28 2023-11-21 北京中科海钠科技有限责任公司 一种钠离子电池电解液添加剂、电解液及钠离子电池

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5298348A (en) * 1993-04-16 1994-03-29 W. R. Grace & Co.-Conn. Battery separator for nickel/metal hydride batteries
US6048541A (en) * 1997-08-20 2000-04-11 Fuisz Technologies Ltd. Fast-dissolving comestible units formed under high-speed/high-pressure conditions
US7112389B1 (en) * 2005-09-30 2006-09-26 E. I. Du Pont De Nemours And Company Batteries including improved fine fiber separators
US20090148758A1 (en) * 2007-11-20 2009-06-11 Richard Vicari Oxidation resistant separator film for batteries

Family Cites Families (143)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2262061A (en) 1939-05-11 1941-11-11 Edison Inc Thomas A Electrical control
US2872498A (en) 1955-04-18 1959-02-03 Union Carbide Corp High density barrier film separators
US3216859A (en) 1961-11-17 1965-11-09 Electric Storage Battery Co Secondary battery separator and electrode assembly
US3498840A (en) * 1967-11-02 1970-03-03 Borden Inc Separator for alkaline batteries and method of making same
US3519484A (en) 1967-11-02 1970-07-07 Borden Inc Separator for alkaline electric cells and method of making
US3980497A (en) 1970-08-03 1976-09-14 The Gates Rubber Company Separators for alkaline batteries
US3754877A (en) 1972-02-04 1973-08-28 Hercules Inc Gelled fuel compositions
US3758343A (en) 1972-03-22 1973-09-11 S Magritz Silver zinc button cell
JPS5461B2 (fr) 1973-11-21 1979-01-05
US4067689A (en) 1974-02-27 1978-01-10 The United States Of America As Represented By The Secretary Of Agriculture Diquaternary ammonium cellulosic fabrics with wrinkle resistant properties
JPS56793B2 (fr) * 1974-10-24 1981-01-09
JPS5626108B2 (fr) 1975-01-20 1981-06-16
US4078125A (en) * 1976-05-27 1978-03-07 Westinghouse Electric Corporation Energy density iron-silver battery
US4064323A (en) 1976-10-26 1977-12-20 Esb Incorporated Battery having venting wrapper comprising gas previous plastic layer and fractured gas impervious layer
US4253927A (en) 1977-03-23 1981-03-03 Esb Inc. Material for an alkaline cell separator and a process of making
US4250029A (en) * 1977-04-25 1981-02-10 Rohm And Haas Company Coated membranes
JPS547537A (en) 1977-06-20 1979-01-20 Hitachi Maxell Silver oxide primary cell
US4158649A (en) 1977-10-17 1979-06-19 The United States Of America As Represented By The Secretary Of The Navy Polymeric membranes which contain polyphenylquinoxalines and which are useful as battery separators
IL53611A (en) 1977-12-14 1982-12-31 Scientific Res Foundation Separators for secondary cells
DE2757583C2 (de) 1977-12-23 1984-10-25 Varta Batterie Ag, 3000 Hannover Galvanische Zelle mit alkalischem Elektrolyten und Verfahren zu ihrer Herstellung
US4154912A (en) 1978-04-19 1979-05-15 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration In situ self cross-linking of polyvinyl alcohol battery separators
US4272470A (en) 1978-12-20 1981-06-09 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Cross-linked polyvinyl alcohol and method of making same
US4218280A (en) 1978-12-20 1980-08-19 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Method of cross-linking polyvinyl alcohol and other water soluble resins
JPS55105971A (en) 1979-02-05 1980-08-14 Japan Atom Energy Res Inst Improved cell separator and its manufacturing method
US4327164A (en) 1979-05-10 1982-04-27 W. R. Grace & Co. Battery separator
US4309494A (en) 1979-05-15 1982-01-05 Stockel Richard F Electrochemical cell having battery separator of ethylene-vinyl alcohol copolymer
US4192908A (en) 1979-06-15 1980-03-11 The United States Of America As Represented By The Secretary Of The Navy Mass-transport separator for alkaline nickel-zinc cells and cell
US4224394A (en) 1979-07-13 1980-09-23 Kimberly Clark Corporation Alkaline battery, separator therefore
US4298666A (en) 1980-02-27 1981-11-03 Celanese Corporation Coated open-celled microporous membranes
US4352770A (en) 1980-04-30 1982-10-05 International Telephone And Telegraph Corporation Process for forming shaped cellulosic product
US4298668A (en) * 1980-07-03 1981-11-03 Kimberly-Clark Corporation Alkaline battery, electrolyte absorber therefor
US4438185A (en) 1980-07-31 1984-03-20 Celanese Corporation Hydrophilic polymer coated microporous membranes capable of use as a battery separator
US4359510A (en) 1980-07-31 1982-11-16 Celanese Corporation Hydrophilic polymer coated microporous membranes capable of use as a battery separator
US4590107A (en) 1981-02-06 1986-05-20 Teepak, Inc. Thin-walled, low plasticized content regenerated cellulose sausage casing
US4371596A (en) 1981-02-27 1983-02-01 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Advanced inorganic separators for alkaline batteries and method of making the same
US4367191A (en) 1981-03-25 1983-01-04 Research Corporation Preparation of cellulose films or fibers from cellulose solutions
US4361632A (en) 1981-05-22 1982-11-30 Kimberly-Clark Corporation Alkaline battery, composite separator therefor
US4505998A (en) 1981-07-10 1985-03-19 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Alkaline battery containing a separator of a cross-linked copolymer of vinyl alcohol and unsaturated carboxylic acid
JPS5818870A (ja) 1981-07-27 1983-02-03 Furukawa Electric Co Ltd:The アルカリ電池用セパレ−タ
JPS5928588A (ja) 1982-08-09 1984-02-15 Meidensha Electric Mfg Co Ltd 亜鉛―臭素二次電池
US4434215A (en) 1982-09-02 1984-02-28 W. R. Grace & Co. Battery separator
US4592973A (en) 1983-10-05 1986-06-03 Castle Technology Corp. Supported liquid membrane electrochemical separators
US4972501A (en) 1984-03-01 1990-11-20 Canon Kabushiki Kaisha Image processing apparatus
US4756911A (en) 1986-04-16 1988-07-12 E. R. Squibb & Sons, Inc. Controlled release formulation
US4734344A (en) 1986-05-19 1988-03-29 W. R. Grace & Co. Battery separator
US6287432B1 (en) 1987-03-13 2001-09-11 The Standard Oil Company Solid multi-component membranes, electrochemical reactor components, electrochemical reactors and use of membranes, reactor components, and reactor for oxidation reactions
US4919865A (en) 1987-11-05 1990-04-24 Union Carbide Industrial Gases Technology Corporation Composite membranes of poly (methyl methacrylate) blends, their manufacture and their use
US5126219A (en) 1987-12-21 1992-06-30 Entek Manufacturing Inc. Microporous filaments and fibers, and articles made therefrom
US4767687A (en) 1987-12-22 1988-08-30 Lydall, Inc. Battery separator
US4965147A (en) 1988-07-25 1990-10-23 Societe Anonyme Dite: Cipel Separator for an electrochemical cell of the metal-air type and having an alkaline electrolyte
US5026617A (en) 1989-02-13 1991-06-25 Idemitsu Kosan Company Limited Separator for alkaline cell and alkaline cell prepared by using this separator
CA2002348A1 (fr) 1989-11-06 1991-05-06 Klaus Tomantschger Anodes de zinc pour piles electriques alcalines; les piles ainsi constituees
US5155144A (en) 1990-10-29 1992-10-13 Manganaro James L Polysaccharide-based porous sheets
EP0700104B1 (fr) 1991-06-11 1998-01-14 Fuji Electrochemical Co., Ltd Pile alcaline
US5188914A (en) 1991-10-09 1993-02-23 Eveready Battery Company, Inc. Low temperature molten compositions comprised of quaternary alkyl phosphonium salts
US5342659A (en) 1991-10-21 1994-08-30 Polymer Research Corp. Of America Method of grafting polymerizable monomers onto substrates
US5336384A (en) 1991-11-14 1994-08-09 The Dow Chemical Company Membrane-electrode structure for electrochemical cells
HUT67932A (en) 1991-12-19 1995-05-29 Environmental Batteries System Alkaline manganese dioxide cell of low mercury content or withot mercury
HU914046D0 (en) 1991-12-19 1992-04-28 Environmetal Batteries Systems Cylindrical alkaline manganese dioxide zinc cell with improved lower sealing
EP0563773B1 (fr) 1992-03-26 1996-06-12 Japan Vilene Company, Ltd. Séparateur pour batteries et batterie
DE69318766T2 (de) 1992-07-10 1998-10-08 Nippon Oil Co Ltd Zinkelektrode für alkalische Speicherbatterie
CA2110097C (fr) 1992-11-30 2002-07-09 Soichiro Kawakami Batterie secondaire
US5591539A (en) 1993-04-13 1997-01-07 Pall Corporation Electrolytically conductive battery separator polymeric film
US5389471A (en) 1993-04-16 1995-02-14 W. R. Grace & Co.-Conn. Wettable battery separator for alkaline batteries
US5336573A (en) 1993-07-20 1994-08-09 W. R. Grace & Co.-Conn. Battery separator
US5426004A (en) 1993-12-03 1995-06-20 Westinghouse Electric Corporation Separator systems for silver-iron batteries
DE69425236T2 (de) 1993-12-28 2000-11-30 Kao Corp Monatsbinde
US5821733A (en) 1994-02-22 1998-10-13 Packard Bell Nec Multiple cell and serially connected rechargeable batteries and charging system
US5604054A (en) 1994-07-13 1997-02-18 Rayovac Corporation Reduced environmental hazard LeClanche cell having improved performance ionically permeable separator
JP3359164B2 (ja) 1994-10-19 2002-12-24 キヤノン株式会社 二次電池
WO1997044511A1 (fr) 1995-04-25 1997-11-27 Kuraray Co., Ltd. Fibre aisement fibrillable
US5700599A (en) 1996-01-12 1997-12-23 Danko; Thomas High absorption rate battery separator
US5700600A (en) 1996-01-12 1997-12-23 Danko; Thomas Long life battery separator
US5626737A (en) 1996-03-05 1997-05-06 Motorola, Inc. Method of fabricating a high power density electrochemical charge storage device
US5830601A (en) 1996-03-11 1998-11-03 Motorola, Inc. Rechargeable electrochemical cell with modified electrolyte
GB9606914D0 (en) 1996-04-02 1996-06-05 Courtaulds Fibres Holdings Ltd Battery separators
US5780186A (en) 1996-05-09 1998-07-14 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration High performance zinc anode for battery applications
US6124058A (en) 1996-05-20 2000-09-26 Kuraray Co., Ltd. Separator for a battery comprising a fibrillatable fiber
US5763557A (en) 1996-09-24 1998-06-09 Polymer Research Corp. Of America Grafting of a polymer onto cellophane by ultrasonic induced free radical polymerization
US5948557A (en) 1996-10-18 1999-09-07 Ppg Industries, Inc. Very thin microporous material
US5962161A (en) 1997-01-14 1999-10-05 Daramic, Inc. Recombinant battery separator
US6033806A (en) 1997-03-05 2000-03-07 Nippon Oil Co., Ltd. Method of producing a cross-linked polyvinyl alcohol separator for an alkali-zinc secondary battery
US5928811A (en) 1997-04-11 1999-07-27 Amtek Research International Llc Gas recombinant battery separator
GB9722426D0 (en) 1997-10-23 1997-12-24 Univ London Pharmacy Controlled release formulations
US6057061A (en) 1997-11-13 2000-05-02 Celgard Inc. Ethylene-vinyl alcohol copolymer battery separator
US5942354A (en) 1997-12-02 1999-08-24 Viskase Corporation Reduced curl battery separator and method
US6153337A (en) 1997-12-19 2000-11-28 Moltech Corporation Separators for electrochemical cells
US6096450A (en) 1998-02-11 2000-08-01 Plug Power Inc. Fuel cell assembly fluid flow plate having conductive fibers and rigidizing material therein
US6159634A (en) 1998-04-15 2000-12-12 Duracell Inc. Battery separator
US6051335A (en) 1998-06-22 2000-04-18 Viskase Corporation Noncircular fiber battery separator and method
WO2000005774A1 (fr) 1998-07-23 2000-02-03 Massachusetts Institute Of Technology Electrolyte avec copolymere sequence
WO2000059052A2 (fr) 1999-03-29 2000-10-05 The Gillette Company Pile alcaline a separateur ameliore
EP1218952B1 (fr) * 1999-09-30 2005-04-13 Eveready Battery Company, Inc. Cellules electrochimiques comprenant des separateurs ultrafins, et procedes de fabrication associes
US6153328A (en) 1999-11-24 2000-11-28 Metallic Power, Inc. System and method for preventing the formation of dendrites in a metal/air fuel cell, battery or metal recovery apparatus
JP2001185116A (ja) * 1999-12-28 2001-07-06 Oji Paper Co Ltd 電池用セパレータ及びアルカリ二次電池
US6372379B1 (en) 2000-02-25 2002-04-16 Abbas M. Samii Microporous membrane battery separator for silver zinc batteries
US6495292B1 (en) 2000-04-26 2002-12-17 William W. Yen Wettable nonwoven battery separator
US6589612B1 (en) 2000-05-10 2003-07-08 The Gillette Company Battery and method of making the same
US6492062B1 (en) 2000-08-04 2002-12-10 The Gillette Company Primary alkaline battery including nickel oxyhydroxide
JP2002079363A (ja) 2000-09-04 2002-03-19 Ahresty Corp 低速高圧鋳造法
JPWO2002023663A1 (ja) 2000-09-11 2004-01-29 松下電器産業株式会社 アルカリ亜鉛二次電池およびその製造方法
US6670077B1 (en) 2000-09-29 2003-12-30 Eveready Battery Company, Inc. Impregnated separator for electrochemical cell and method of making same
US20030087157A1 (en) 2001-04-19 2003-05-08 Michael Cheiky Homogeneous separator
US6558849B2 (en) 2001-04-19 2003-05-06 Zinc Matrix Power, Inc. Battery separator with copper-containing inorganic salt
US7488558B2 (en) 2001-04-19 2009-02-10 Michael Cheiky Homogeneous separator
US6743548B2 (en) 2001-04-19 2004-06-01 Zinc Matrix Power, Inc. Silver-zinc alkaline rechargeable battery (stacking order)
US6682854B2 (en) 2001-04-19 2004-01-27 Zinc Matrix Power, Inc. Battery separator with fluoride-containing inorganic salt
US6929884B2 (en) 2001-04-19 2005-08-16 Zinc Matrix Power, Inc. Method for manufacture of films containing insoluble solids embedded in cellulose-based films
US6541160B2 (en) 2001-04-19 2003-04-01 Zinc Matrix Power, Inc. Battery separator with sulfide-containing inorganic salt
US6733920B2 (en) 2001-04-19 2004-05-11 Zinc Matrix Power, Inc. Recombinant separator
ATE509380T1 (de) 2001-05-24 2011-05-15 Ray O Vac Corp Ionenleitendes additiv für zinkanoden in alkalischen elektrochemischen zellen
JP3765396B2 (ja) 2001-08-20 2006-04-12 ソニー株式会社 電池
DE10154896C2 (de) * 2001-11-12 2003-10-16 Freudenberg Carl Kg Alkalische Zelle oder Batterie
CN100364160C (zh) 2003-03-06 2008-01-23 东丽株式会社 高分子电解质材料、高分子电解质部件、膜电极复合体和高分子电解质型燃料电池
CN100377405C (zh) 2003-04-09 2008-03-26 日本电气株式会社 燃料电池及制备该燃料电池的方法
US20060257728A1 (en) 2003-08-08 2006-11-16 Rovcal, Inc. Separators for use in alkaline cells having high capacity
TW200520292A (en) 2003-08-08 2005-06-16 Rovcal Inc High capacity alkaline cell
CN2649315Y (zh) * 2003-09-29 2004-10-20 轻工业塑料加工应用研究所 一种高阻隔性多层共挤吹塑膜
US7914920B2 (en) * 2003-10-09 2011-03-29 The Gillette Company Battery separator
CN100334752C (zh) 2004-02-20 2007-08-29 松下电器产业株式会社 锂离子二次电池的制备方法
US20070207693A1 (en) 2004-03-12 2007-09-06 Takahiro Tsukuda Heat-Resistant Nonwoven Fabric
JP4828096B2 (ja) 2004-03-30 2011-11-30 富士通株式会社 スルホン酸基含有プロトン伝導性ポリマー組成物、固体電解質膜および固体高分子型燃料電池
JP4354349B2 (ja) 2004-06-30 2009-10-28 パナソニック株式会社 アルカリ乾電池用セパレータの評価方法
JP2006054127A (ja) 2004-08-12 2006-02-23 Du Pont Teijin Advanced Paper Kk セパレーターおよびそれを用いた電気電子部品
WO2006025662A1 (fr) 2004-09-02 2006-03-09 Lg Chem, Ltd. Film poreux composite organique/mineral et dispositif electrochimique prepare au moyen de ce film
JP4689222B2 (ja) 2004-09-22 2011-05-25 信越ポリマー株式会社 導電性塗布膜およびその製造方法
US20060216584A1 (en) 2005-03-24 2006-09-28 Michael Cheiky Oxidation resistant electrolyte absorber
US20070020501A1 (en) 2005-07-21 2007-01-25 Ling-Feng Li Polyelectrolyte membranes as separator for battery and fuel cell applications
JP5148093B2 (ja) * 2005-09-28 2013-02-20 東レバッテリーセパレータフィルム株式会社 ポリエチレン多層微多孔膜及びその製造方法、並びに電池用セパレータ
US20070141456A1 (en) 2005-12-21 2007-06-21 General Electric Company Bipolar membrane
US8598052B2 (en) 2006-03-02 2013-12-03 Daio Paper Corporation Highly air-permeable and water-resistance sheet, a highly air-permeable and water-resistance sheet composite and an absorbent article, and a method for manufacturing a highly air-permeable and water-resistance sheet and a method for manufacturing a highly air-permeable and water-resistance sheet composite
JP2007294213A (ja) 2006-04-25 2007-11-08 Honda Motor Co Ltd 固体高分子型燃料電池用膜−電極構造体
US7807296B2 (en) 2006-08-23 2010-10-05 Roval, Inc. Copper-manganese mixed oxide cathode material for use in alkaline cells having high capacity
FR2906084B1 (fr) 2006-09-15 2008-11-14 Accumulateurs Fixes Composition pour electrode negative d'accumulateur a electrolyte alcalin.
WO2008039419A2 (fr) 2006-09-25 2008-04-03 Zpower Inc. Séparateur résistant à l'oxydation destiné à des accumulateurs à oxyde de zinc/argent
WO2008039417A1 (fr) * 2006-09-25 2008-04-03 Zpower Inc. Séparateur résistant à l'oxydation destiné à des accumulateurs alcalins
WO2008039416A1 (fr) 2006-09-25 2008-04-03 Zpower Inc. Séparateur résistant aux dendrites destiné à des accumulateurs alcalins
KR100971110B1 (ko) 2007-06-06 2010-07-20 데이진 가부시키가이샤 비수계 2 차 전지용 세퍼레이터 및 비수계 2 차 전지
KR101147604B1 (ko) 2007-10-12 2012-05-23 주식회사 엘지화학 젤리-롤형 전극조립체의 변형을 억제하기 위한 제조방법
DK2272119T3 (da) 2008-03-27 2014-07-07 Zpower Llc Elektrodeseparator
CN102334216B (zh) 2008-12-19 2017-06-16 株式会社Lg化学 高功率锂二次电池
AU2010229083A1 (en) 2009-03-27 2011-11-03 Zpower, Llc Electrode separator
US20130266872A1 (en) 2010-09-16 2013-10-10 Zpower, Llc Electrode separator

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5298348A (en) * 1993-04-16 1994-03-29 W. R. Grace & Co.-Conn. Battery separator for nickel/metal hydride batteries
US6048541A (en) * 1997-08-20 2000-04-11 Fuisz Technologies Ltd. Fast-dissolving comestible units formed under high-speed/high-pressure conditions
US7112389B1 (en) * 2005-09-30 2006-09-26 E. I. Du Pont De Nemours And Company Batteries including improved fine fiber separators
US20090148758A1 (en) * 2007-11-20 2009-06-11 Richard Vicari Oxidation resistant separator film for batteries

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
"unitary." Collings English Dictionary. London: Colins, 2000. *

Cited By (54)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9923180B2 (en) * 2007-05-31 2018-03-20 A123 Systems Llc Separator including electroactive material for overcharge protection
US20090029261A1 (en) * 2007-05-31 2009-01-29 A123 Systems, Inc. Separator including electroactive material for overcharge protection
US9960399B2 (en) 2008-03-27 2018-05-01 Zpower, Llc Electrode separator
US10756319B2 (en) * 2009-09-29 2020-08-25 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured therefrom and method for manufacturing electrochemical device having the same
US20110259505A1 (en) * 2009-09-29 2011-10-27 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured therefrom and method for manufacturing electrochemical device having the same
US8632652B2 (en) * 2009-09-29 2014-01-21 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured therefrom and method for manufacturing electrochemical device having the same
US20140101931A1 (en) * 2009-09-29 2014-04-17 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured therefrom and method for manufacturing electrochemical device having the same
US20130034769A1 (en) * 2010-04-19 2013-02-07 Mitsubishi Plastics, Inc. Laminated porous film, separator for non-aqueous electrolyte battery, and non-aqueous electrolyte secondary battery
US20130266872A1 (en) * 2010-09-16 2013-10-10 Zpower, Llc Electrode separator
US20160254514A1 (en) * 2011-07-11 2016-09-01 California Institute Of Technology Electrochemical systems with electronically conductive layers
US10693117B2 (en) * 2011-07-11 2020-06-23 California Institute Of Technology Electrochemical systems with ionically conductive and electronically insulating separator
US9379368B2 (en) * 2011-07-11 2016-06-28 California Institute Of Technology Electrochemical systems with electronically conductive layers
US11527802B2 (en) * 2011-07-11 2022-12-13 California Institute Of Technology Electrochemical systems with ionically conductive and electronically insulating separator
US10158110B2 (en) 2011-07-11 2018-12-18 California Institute Of Technology Separators for electrochemical systems
US20230291075A1 (en) * 2011-07-11 2023-09-14 California Institute Of Technology Electrochemical systems with ionically conductive and electronically insulating separator
US20130224632A1 (en) * 2011-07-11 2013-08-29 California Institute Of Technology Novel separators for electrochemical systems
US9954213B2 (en) * 2011-07-11 2018-04-24 California Institute Of Technology Electrochemical systems with at least one electronically and ionically conductive layer
EP2742552A4 (fr) * 2011-08-08 2015-05-06 Basf Se Cellules électrochimiques
US9954210B2 (en) * 2011-10-20 2018-04-24 Lg Chem, Ltd. Method for manufacturing separator, separator manufactured by the method and method for manufacturing electrochemical device including the separator
US10177361B2 (en) 2012-06-20 2019-01-08 Sumitomo Chemical Company, Limited Coating fluid, laminated porous film, and non-aqueous electrolyte secondary battery
US20150364790A1 (en) * 2013-02-01 2015-12-17 Nippon Shokubai Co., Ltd. Anion conducting material and cell
US10297861B2 (en) * 2013-02-01 2019-05-21 Nippon Shokubai Co., Ltd. Anion conducting material and cell
US10014558B2 (en) 2013-02-06 2018-07-03 Encell Technology, Inc. Nickel iron battery employing an untreated polyolefin separator with a surfactant in the electrolyte
US10868341B2 (en) 2013-02-06 2020-12-15 Encell Technology, Inc. Electrolyte for a nickel-iron battery
WO2014124107A2 (fr) 2013-02-06 2014-08-14 Encell Technology, Inc. Batterie comprenant une anode de fer enrobée et présentant des performances améliorées
US9559385B2 (en) 2013-02-06 2017-01-31 Encell Technology, Inc. Nickel iron battery employing an untreated polyolefin separator with a surfactant in the electrolyte
WO2014124107A3 (fr) * 2013-02-06 2015-03-05 Encell Technology, Inc. Batterie comprenant une anode de fer enrobée et présentant des performances améliorées
US9450233B2 (en) 2013-02-06 2016-09-20 Encell Technology, Inc. Battery comprising a coated iron anode
EP2954574A4 (fr) * 2013-02-06 2016-09-14 Encell Technology Inc Batterie comprenant une anode de fer enrobée et présentant des performances améliorées
WO2014124110A1 (fr) * 2013-02-06 2014-08-14 Encell Technology, Inc. Électrolyte amélioré pour batterie contenant une électrode en fer
US10868338B2 (en) 2013-02-06 2020-12-15 Encell Technology, Inc. Nickel-iron battery with high power
US10804573B2 (en) 2013-02-06 2020-10-13 Encell Technology, Inc. Electrolyte for battery containing an iron electrode
US10587011B2 (en) 2013-02-06 2020-03-10 Encell Technology, Inc. Nickel-iron battery with high power
US10854926B2 (en) 2013-02-06 2020-12-01 Encell Technology, Inc. Nickel-iron battery with high cycle life
US9287592B2 (en) 2013-02-06 2016-03-15 Encell Technology, Inc. Process for forming a battery containing an iron electrode
US10847843B2 (en) 2013-02-06 2020-11-24 Encell Technology, Inc. Electrolyte for a nickel-iron battery
US10707537B2 (en) 2013-02-06 2020-07-07 Encell Technology, Inc. Nickel-iron battery with high cycle life
AU2014214904B2 (en) * 2013-02-06 2018-05-10 Encell Technology, Inc. Battery comprising a coated iron anode and improved performance
US20230198028A1 (en) * 2013-05-31 2023-06-22 Johan C. Fitter Metal accumulation inhibiting and performance enhancing supplement and a system for delivering the supplement
US10714724B2 (en) 2013-11-18 2020-07-14 California Institute Of Technology Membranes for electrochemical cells
US9991492B2 (en) 2013-11-18 2018-06-05 California Institute Of Technology Separator enclosures for electrodes and electrochemical cells
US11177537B2 (en) 2013-11-18 2021-11-16 California Institute Of Technology Separator enclosures for electrodes and electrochemical cells
US10763004B2 (en) 2014-03-12 2020-09-01 3M Innovative Properties Company Conductive polymeric material
US20160087271A1 (en) * 2014-09-24 2016-03-24 Schlumberger Technology Corporation Rechargeable Lithium Polymer Electrolyte Battery for Oilfield Use
US11894562B2 (en) 2015-12-02 2024-02-06 California Institute Of Technology Three-dimensional ion transport networks and current collectors for electrochemical cells
US11271214B2 (en) 2015-12-02 2022-03-08 California Institute Of Technology Three-dimensional ion transport networks and current collectors for electrochemical cells
US10601030B2 (en) * 2016-02-01 2020-03-24 The Regents Of The University Of California Functional polymer binder for sulfur cathode fabrication
US20180351161A1 (en) * 2016-02-01 2018-12-06 The Regents Of The University Of California Functional polymer binder for sulfur cathode fabrication
US20200006763A1 (en) * 2017-03-15 2020-01-02 Kabushiki Kaisha Nihon Micronics Electricity storage device
US11161961B2 (en) * 2017-04-21 2021-11-02 Avomeen Analytical Services Shutdown and non-shutdown separators for electrochemical devices
US11553267B2 (en) 2018-06-21 2023-01-10 Bose Corporation Dual zone discharge of rechargeable batteries
US10448137B1 (en) 2018-06-21 2019-10-15 Bose Corporation Dual zone discharge of rechargeable batteries
CN111341974A (zh) * 2020-03-13 2020-06-26 江苏厚生新能源科技有限公司 Pvdf涂胶隔膜及其制备方法、pvdf涂胶层、锂电池
WO2023283309A1 (fr) * 2021-07-07 2023-01-12 Board Of Regents, The University Of Texas System Séparateurs destinés à être utilisés dans des dispositifs de stockage d'énergie

Also Published As

Publication number Publication date
JP2014099413A (ja) 2014-05-29
DK2272119T3 (da) 2014-07-07
AU2009229167A1 (en) 2009-10-01
CA2719223A1 (fr) 2009-10-01
EP2272119B1 (fr) 2014-04-23
JP5591220B2 (ja) 2014-09-17
US20150028516A1 (en) 2015-01-29
CN102017232B (zh) 2014-07-02
CN102017232A (zh) 2011-04-13
JP6215078B2 (ja) 2017-10-18
AU2009229167B2 (en) 2014-01-23
JP2011515821A (ja) 2011-05-19
US9960399B2 (en) 2018-05-01
EP2272119A1 (fr) 2011-01-12
CA2719223C (fr) 2017-07-04
WO2009120382A1 (fr) 2009-10-01
EP2639855A2 (fr) 2013-09-18
EP2639855A3 (fr) 2013-12-25

Similar Documents

Publication Publication Date Title
US9960399B2 (en) Electrode separator
JP2011515821A5 (fr)
US20160301077A1 (en) Electrodes and electrochemical cells employing the same
US20120189896A1 (en) Electrode separator
EP3413380B1 (fr) Anode comprenant de multiples couches de protection, et batterie secondaire au lithium la comprenant
US11990642B2 (en) Separator for electrochemical device and method for manufacturing the same
US9634359B2 (en) Electrolyte for zinc-based rechargeable batteries, method for producing the same and batteries including said electrolyte
CN101604746A (zh) 具有多孔保护膜的电极及其制造方法、非水电解质二次电池
KR20150071453A (ko) 고용량 특성을 갖는 리튬 이온 이차 전지용 음극
KR20190007740A (ko) 전극 보호층을 포함하는 음극 및 이를 적용한 리튬 이차전지
WO2008039419A2 (fr) Séparateur résistant à l'oxydation destiné à des accumulateurs à oxyde de zinc/argent
US20110123859A1 (en) Polymer Electrolytes
CN114270617A (zh) 具有耐热层的电化学装置用隔板和包括该隔板的二次电池
WO2008039417A1 (fr) Séparateur résistant à l'oxydation destiné à des accumulateurs alcalins
WO2008039416A1 (fr) Séparateur résistant aux dendrites destiné à des accumulateurs alcalins
US11380931B2 (en) Composite electrode plate and battery cell using the same
KR20200049649A (ko) 전기화학소자용 분리막 및 이를 제조하는 방법
KR20180107459A (ko) 다중 보호층을 포함하는 음극 및 이를 포함하는 나트륨 이차전지
KR20180107458A (ko) 나트륨 음극 및 이를 포함하는 나트륨 이차전지

Legal Events

Date Code Title Description
AS Assignment

Owner name: ZPOWER, INC., CALIFORNIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DUONG, HIEU;ADAMSON, GEORGE;SIGNING DATES FROM 20100722 TO 20100809;REEL/FRAME:024907/0253

AS Assignment

Owner name: ZPOWER, INC., CALIFORNIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DUONG, HIEU;ADAMSON, GEORGE;SIGNING DATES FROM 20100722 TO 20100809;REEL/FRAME:025888/0133

AS Assignment

Owner name: ZPOWER, LLC, CALIFORNIA

Free format text: CHANGE OF NAME;ASSIGNOR:ZPOWER, INC.;REEL/FRAME:026772/0492

Effective date: 20110401

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION