KR970704895A - 내식성 및 용접성이 우수한 강재 및 강관의 제조방법 - Google Patents
내식성 및 용접성이 우수한 강재 및 강관의 제조방법 Download PDFInfo
- Publication number
- KR970704895A KR970704895A KR1019970700279A KR19970700279A KR970704895A KR 970704895 A KR970704895 A KR 970704895A KR 1019970700279 A KR1019970700279 A KR 1019970700279A KR 19970700279 A KR19970700279 A KR 19970700279A KR 970704895 A KR970704895 A KR 970704895A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- steel
- temperature
- steel sheet
- manufacturing
- Prior art date
Abstract
습윤 탄산가스 또는 미량의 유화수소를 함유하는 환경속에서 우수한 내식성을 보이고, 용접성도 우수한 강재 및 강관을 저비용과 높은 생산성으로 제조한다. 중량% 로 Si 는 0.01 내지 0.6%, Mn 는 0.02 내지 1.8%, Cr는 7.5 내지 14.0%, Cu 는 1.5 내지 4.0%, Al 은 0.005 내지 0.1% 를 함유하고, C 가 0.02% 이하, N 이 0.02%이하, P 가 0.025% 이하, S 가 0.01% 이하로 저감되고, 잔부가 Fe 와 불가피적 불순물로 이루어지는 강편을 1100 내지 1300℃ 의 온도로 가열한 다음에, 1050℃ 이하의 온도에서의 누적 압하량이 65% 이상, 압연 종료 온도가 800℃ 이상에서 열간압연이 종료되고, 적어도 500℃ 까지 0.02℃/초 이하의 냉각속도로 냉각시켜서, 금속조직을 실질적으로 페라이트로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (13)
- 중량% 로Si: 0.01 내지 0.6%,Mn: 0.02 내지 1.8%,Cr: 7.5 내지 14.0%,Cu: 1.5 내지 4.0%,Al: 0.005 내지 0.10% 를 함유하고,C 를 0.02% 이하,N 을 0.02% 이하,P 를 0.025% 이하,S 를 0.01% 이하로 저감되고, 나머지가 Fe 및 불가피한 불순물로 이루어지는 강편을 1100 내지 1300℃ 의 온도로 가열한 다음에, 1050℃ 이하의 온도에서의 누적 압하량이 65% 이상, 압연 종료 온도가 800℃ 이상에서 열간압연을 종료하고, 적어도 500℃ 까지 0.02℃/초 이하의 냉각 속도로 냉각하여, 금속 조직이 실질적으로 페라이트로 이루어지는 것을 특징으로 하는 내식성 및 용접성이 우수한 강재의 제조방법.
- 제 1 항에 있어서, 열간압연 종료후의 강을 500℃ 이하로 냉각시킨 다음에, 650℃ 이상에서 다음의 식을 만족시키는 조건으로 재가열하는 내식성 및 용접성이 우수한 강재의 제조방법.상기식에서, T 는 재가열온도(K),t 는 재가열의 유지시간(min)
- 제 1 항 또는 제 2 항에 있어서, 강편이 부가 성분으로서 중량% 로,Ni: 1.5% 이하Co: 1.0% 이하Mo: 3.0% 이하W: 3.0% 이하의 1 또는 2 종을 함유하고, Ni + Co 의 합계 함유량이 1.5% 이하, Mo + W의 합계 함유량이 3.0% 이하인 내식성 및 용접성이 우수한 강재의 제조방법.
- 제 1항, 제 2 항 또는 제 3 항에 있어서, 강편이 부가 성분으로서, 중량%로,Nb, V, Ti, Zr, Ta 중 1 종 또는 2 종 이상을 합계 함유량으로 1.0 중량% 이하를 함유하고 있는 내식성 및 용접성이 우수한 강재의 제조방법.
- 제 1 항 내지 제 5 항 중 어느 한 항에 있어서, 강편의 C 와 N 의 함유량을 중량% 로,C 는 0.015% 이하,N 은 0.015% 이하로 저감되고, C 와 N 의 합계량이 0.02% 이하로 되는 내식성 및 용접성이 우수한 강재의 제조방법.
- 제 1 항 내지 제 5 항 중 어느 한 항에 있어서, 다음의 식에서 주어지는 강편 성분의 MC 값이 0 이상인 내식성 및 용접성이 우수한 강재의 제조방법.상기식에서, [% X]는 중량% 로 표시된 원소 X 의 함유량.
- 중량%로,Si: 0.01 내지 0.6%,Mn: 0.02 내지 1.8%,Cr: 7.5 내지 14.0%,Cu: 1.5 내지 4.0%,Al: 0.005 내지 0.10% 를 함유하고,C 를 0.02% 이하,N 을 0.02% 이하,P 를 0.025% 이하,S 를 0.01% 이하로 저감되고. 잔부가 Fe 와 불가피적 불순물로 이루어지는 강편을 다음의 공정 ①,②의 순서로 강관으로 하는 것을 특징으로 하는 내식성 및 용접성이 우수한 강관의 제조방법.① 강편을 1100 내지 1300℃의 온도로 가열한 후, 금속 조직을 실질적으로 오스테나이트 단상인 온도영역 및 1050℃ 이하의 온도에서의 누적 압하량이 65% 이상되도록 열간압연을 종료하고, 판 두께가 3.0㎜ 이상 25.4㎜ 이하의 핫 코일로 만드고, 금속 조직이 실질적으로 오스테나이트 단상인 온도 영역에서 핫 코일로서 감은후, 적어도 500℃ 까지 0.02℃/초 이하의 냉각 속도로 냉각시켜서, 금속 조직이 실질적으로 페라이트로 이루어지는 강판으로 만드는 공정.② 상기 핫 코일을 소정의 폭으로 절단한 다음에, 연속적으로 원통상으로 성형하면서, 강대 양단을 전기 저항 용접시켜 전봉 강관으로서 조관하는 공정.
- 제 7 항에 있어서, 핫 코일을 500℃ 이하로 냉각시킨 다음에, 650℃ 이상에서 다음의 식을 만족시키는 조건으로 재가열하는 내식성 및 용접성이 우수한 강관의 제조방법.상기식에서, T 는 재가열온도(K),t 는 재가열의 유지시간(min).
- 제 7 항 또는 제 8 항에 있어서, 강편이 부가성분으로서, 중량% 로Ni: 1.5% 이하,Co: 1.0% 이하,Mo: 3.0% 이하,W: 3.0% 이하의 1 종 또는 2 종 이상을 함유하고, Ni+Co 의 합계 함유량이 1.5% 이하, Mo+W 의 합계 함유량이 3.0% 이하인 내식성 및 용접성이 우수한 강관의 제조방법.
- 제 7항, 제 8 항 또는 제 9 항에 있어서, 강편이 부가 성분으로서, 중량%로,Nb, V, Ti, Zr, Ta 의 1 종 또는 2 종 이상의 합계 함유량으로 1.0 중량% 이하를 함유하고 있는 내식성 및 용접성이 우수한 강관의 제조방법.
- 제 7 항 내지 제 10 항 중 어느 한 항에 있어서, 강편의 C 와 N 의 함유량이 중량% 로,C 는 0.015% 이하,N 는 0.015% 이하로 저감되고, C 와 N 의 합계량이 0.02% 이하로 되는 내식성 및 용접성이 우수한 강관의 제조방법.
- 제 7 항 내지 제 11 항 중 어느 한 항에 있어서, 다음 식에서 주어지는 강편성분의 MC 값이 0 이상인 내식성 및 용접성이 우수한 강관의 제조방법.상기식에서, [% X]는 중량% 로 표시된 원소 X 의 함유량
- 제 7 항 내지 제 12 항 중 어느 한 항에 있어서, 전봉 용접에 의하여 조관하고, 전봉부의 온도를 Ms 점 이하까지 저하시킨 다음에, 적어도 전봉부와 그 양측 2 mm 이내를 포함하는 부분을 650℃ 이상 Acl변태점 이하의 온도로 재가열한 후 냉각시키는 내식성 및 용접성이 우수한 강관의 제조방법