JPS5882723A - ３−ヒドロキシ酪酸重合体からの成形品の製造方法 - Google Patents

３−ヒドロキシ酪酸重合体からの成形品の製造方法

Info

Publication number
JPS5882723A
JPS5882723A JP57190702A JP19070282A JPS5882723A JP S5882723 A JPS5882723 A JP S5882723A JP 57190702 A JP57190702 A JP 57190702A JP 19070282 A JP19070282 A JP 19070282A JP S5882723 A JPS5882723 A JP S5882723A
Authority
JP
Japan
Prior art keywords
polymer
preform
thickness
stretching
nip
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP57190702A
Other languages
English (en)
Other versions
JPH0263054B2 (ja
Inventor
ピ−タ−・ジヨン・バ−ハム
ポ−ル・ア−サ−・ホルメス
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Imperial Chemical Industries Ltd
Original Assignee
Imperial Chemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Imperial Chemical Industries Ltd filed Critical Imperial Chemical Industries Ltd
Publication of JPS5882723A publication Critical patent/JPS5882723A/ja
Publication of JPH0263054B2 publication Critical patent/JPH0263054B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は８−ヒドロキシ酪酸重合体に関する。
ポリ（８−ヒドロキシＷｉｔ＠）は式 ％式％ の−り返し単位から成る熱可履性のポリエステルで、エ
ネルギー保存物質としての多くの微生物、以上１、アゾ
トバクタ−属、バチルスＩ１４、／１ｙｓ−スピリリウ
ム属の細菌によって蓄積される。゛この重合体はエネル
ギーおよび栄養源としての適当な基質、例えば炭化水素
またはメタノール上、水性培養基中で微生物を培養する
ことによって好適に製造される。基質はもちろん微生物
が吸収できるものでなければならない。重合体の蓄積を
促進するには、培養の少なくとも一部は、栄養について
微生物の生長には必須であるが、重合体の蓄積には必要
とされないという制限のある条件下で行うのが好ましい
。適当な方法の例はヨーロッパ特許第１５６６９号およ
び同第４６８４４号明細書に記載されている、 ８−ヒドロキシ酪酸単位と他のヒドロキシカルボン酸単
位、例えば８−ヒドロキシ吉草酸単位の両単位を含有す
る重合体も微生物学的に製造することができる。かくし
て、微生物学的に製造され九８−ヒドロキシ酪酸残基と
８−ヒドロキシ吉草識残基を含有するヘテロポリマーに
ついてワーレン（Ｗａｌｌｏｗ）等が［エンピロンメン
タルサイエンスアンドテクノロジー（Ｅｎｖｉｒｏｎｍ
ｅｎｔａｌ　Ｓｃイー％６＃　ａｎｄ　ＴｅｃｈｓｏＬ
ｏｇｙ月８（１９７４）、５７６−９に記載している。
また、ヨーロッパ特許第５２４５９号明細書に記載され
るように、共重合体中に８−ヒドロキシ吉草酸単位をも
たらすプロピオン酸のようなある種の基質上で微生物を
培養することによっているいろな共重合体を製造するこ
とができる。
この重合体を含有するセルは、例えばアメリカ特許第８
，１０７，１７２号明細書に記載されるように成形材料
としてそのま＼使用することができるが、一般的にはそ
の重合体をセル材料の残りから分離するのが望ましい。
この分離を行うために提案された方法としてアセトンに
よる処理のような方法によってセルを破壊し、次いで重
合体が可溶である溶剤で処理することによって破壊され
たセルから重合体を抽出する方法がわる。アメリカ特許
第８，０８６，９５９号および同第８．０４４．９４２
号明細書にこのような方法の例が記載されている。これ
らの方法において、使用溶剤はピリジン、またはメチレ
ンとエタノールの混合物である。セルの形態で製造され
る重合体に対する他の抽出溶剤として１．２−プロピレ
ンカルボネートのような環状カルボネート類（アメリカ
特許第４．１０１，５３８号明細書を参照）、クロロホ
ルム（アメリカ特許第＆２７５，６１０号明細書を参照
）および１，２−ジクロロエタン（ヨーロッパ特許第１
５１２８号明細書く開示される）がある。
アメリカ特許第ｆ３，２７５，６１０号明細書は他のセ
ル破壊方法、すなわち超音波振動法、粉砕法、フレンチ
プレス法、凍結／融解法およびリゾチーム処理法を開示
しているが、一方前記ヨーロッパ特許第１５１２８号明
細書に記載されるように１微生物を培養することによっ
て製造されるセル懸濁物の噴霧またはフラッシュ乾燥も
十分にセルを破壊し、重合体をセルから抽出できるよう
にする。
他のヒドロキシカルボン酸類の単位および／またはジオ
ール、例えばエチレングリコールおよび／マタはジカル
ボン酸、例えばイソフタル酸から誘導される単位を含有
する共重合体も微生物学的に製造された重合体または共
重合体をそのようなヒドロキシカルボン酸、そのラクト
ン、例えばビバロラクトン、ジオール、ジカルボン酸お
よび／またはそれから製造されるポリエステルとともに
溶融することに起るエステル交換によって製造すること
ができる。
従って、以下の配達において、ＨＢ重合体とは３−ヒド
ロキシ酪酸の単独重合体ばか勺でなく、上記のような共
重合体も、８−ヒドロキシ酪酸残基が重合体鎖の少なく
とも４０モルチ、好ましくは少なくとも５０モルチ、最
も好ましくは少なくとも８０モル慢を占めるという条件
において意味する。
繊維、リボン、フィルムおよびびんのようなある種の成
形品の製造において、その製品にある程度の配向を銹発
するのがしばしば望まれる。
常用の配向法としては次のものがある。
（６）　　非晶質の予備成形物を形成し１次いでその予
備成形物を通常はガラス転移＠度Ｔ２以上であるが、そ
れに近い温度で、例えば−軸方向または二軸方向におい
て引張応力に付して塑性変形（ｙｉ＃ｉｄ）させ、かつ
延伸する方法。
（６）　　結晶性の予備成形物を結晶の融点Ｔｔｙｃ以
下であるが、それに近い温度で延伸する方法。
方法（ａ）はしばしばポリエステル、例えばポリエチレ
ンテレフタレート、およびポリアミド、例えばポリヘキ
サメチレンアジパミド（ナイロン６６）およびカプロラ
クタム（ナイロン６）に適合するが、これに対して方法
（６）はしげしげオレフィン系重合体、例えばポリプロ
ピレンおよびポリエチレンに適合する。
本発明者はＨＢ重合体の配向はこれらの方法によっては
困難であること、すなわち適当な予備成形物の製造条件
と延伸条件が臨界的であるが、−貫して再現困難である
ことを見い出した。一般Ｋ。
その予備成形物は昇温下でも脆く、従ってそれらが塑性
変形および配向する前に破壊する傾向がある。
ＨＢ重合体の１つの特定の配向法がヨーロッパ特許第２
４８１０号明細書に開示されている。この特許明細書に
記載される方法においては、配向はＨＢ単独重合体の貧
溶媒溶液から形成されたゲルから溶媒を絞液することに
よって造った「パーチメント（ｐａｒｅｈｍａＫｔ　）
Ｊをロール掛け、すなわち延伸することくよって誘発さ
せている。必要とされる温度は「パーチメント」の残留
溶媒含量に依存し、［パーチメントが乾燥されて残留溶
媒が除去されているときは「パーチメントの融点のオー
ダーの比較的高い温度が必要とされる。これらのパーチ
メントは通常の重合体よシ低い融点（約１５０℃）を示
し、溶融処理によって重合体から形成した製品が示す粒
状球晶結晶化の徴候を示さないある特別の形の重合体で
ある。
本発明者は、例えば溶融成形または溶液流延成形によっ
て製造したＨＢ重合体の溶剤を含まない予備成形物を例
えば、結晶の融点よシ低い温度においてロール掛けする
ことＫよって圧縮力に付すならば予備成形物は一層展延
性になシ、かくして常用の配向法の適用がさらに可能に
なることをここに見い出した。
従って、本発明者はＨＢ重合体の溶剤を含まない予備成
形物を重合体のガラス転移ＩＬ度Ｃｒｔ）と結晶融点（
７’ｙｙｃ）との間の温度において圧縮力に付し、その
厚さを少なくとも５−下げ、次いで圧縮予備成形物を一
軸また二軸延伸することから成るＨＢ重合体から成形品
を製造する方法を提供する。
圧縮力は多くの方法で適用することができる。
かくして、重合体のシートまたはブラックは所望の温度
に保持されたプレスの定盤間で圧力ＫＩ＃に供してもよ
い。
もう１つの方法は、例えば予備成形物を所望の温度に保
持された一対のニップローラのニップを通過させること
によってロール掛は操作に付すことである。ニップは所
望の断面形状のロール掛は製品な造るように適当に型彫
シされていてもよい。
別法として個体状の予備成形物を所望の温［Ｋ保持され
ているダイを通して押し出す方法である。
このような方法はニー・サイフェリー（Ｊ、Ｃ４ｆｇｒ
ｒｉ）およびアイ・エム・ワード（１、Ｍ、Ｗａデｄ）
編「ウルトラハイモジュラスホリマースＣＵＬｔｒａ　
Ｈ４ｇｈＭｏｄｔｔｌｕａ　Ｐｏ１ｙｔｌＬｅデｊ）」
（アプライドサイエンスノくブリシャーズ（Ａｐｐｌｉ
ｅｄ　Ｓｃｔｔｔｓｃｇ　Ｐｘｂｌｔｓｈｇｒｓ〕、ロ
ンドン（Ｌｏｘｄｏ罰、１９７９年）Ｋ記載されている
。予備成形物は通常テーパーがついているダイから、例
えば静水圧によって押し出すことができる。さらに５そ
して％にこのような「冷間」押出の開始後、その押出は
ダイから出てくる押出物を引っ張ることによって助長す
ることができる。
予備成形物がダイを通過する際に所望の圧縮力が加わる
。
初めに１予備成形物は厚さｔ、％幅す。および長さ１０
　　を持つ。圧縮操作後、厚さｔｌ、幅ｂ１　　および
長さ１．　　になる。
予備成形物は複数回の圧縮操作に付すことができ、各操
作で予備成形物の厚さは次第に減少する。
かくして予備成形物は一連の２対またはそれ以上のニッ
プローラを通過することができる。各圧縮操作は少なく
とも５チ、すなわち １１− ｔニー、＜０．９５ （式中、ｔ７はｎ回目の圧縮操作後の厚さであり、そし
てｔ％−１はｎ回目の圧縮工程の前の厚さである。） 予備成形物の厚さを減するのが好ましい。
圧縮がこれらの段階において予備成形物を複数対のニッ
プローラ間に通し、ロール掛けすることによって影響さ
れる場合、幾つかのケースにおいては予備成形物を第一
の方向でロール掛けし、次いでロール掛けされた予備成
形物を第一の方向に対して直角の方向においてさらにロ
ール掛ける工程に供するのが望ましいだろう。
全厚さの減少は少なくともｚ〇−５すなわちｈく０．８
　（ただし、ｉは全圧縮操作終了後のｔ。
最終厚さである）であるのが好ましい。
予備成形物をダイを通して押し出す場合、厚さｔ５は対
応するダイの寸法であると考えられるが、押出物の実際
の厚さは、押出物に引張力を加えて、例えば予備成形物
がダイを通過するのを助けるならげ、１ｆＬよりかなシ
小さくなることがわかるだろう。
ここで断面積Ａは幅すと厚さｔで定まると考えられる。
厚さの減少Δｔで与えられる断面積の減少△Ａはもちろ
ん予備成形物の幾何学的形状Ｋ、および予備成形物の幅
すが圧縮操作中に変わるかどうかに依存する。
すなわち、　△Ａ！＝　Ａ　ｔ　　Ａ　。
＝ｆＣｂ＋　、　ｔ＋　）−ｆｃ　ｂｏ　、　ｔｏ　）
ただし、面積Ａ＝ｆＣｂ、ｔ＞ 直径ｄｏ（すなわち、ｂｏ＝　！ｏ−ｄｏ　）および厚
さｔｏの円形ジスクをその直径が均一に増加することが
できるようにプレスの定盤間でプレスするときは、容積
変化が無視できると仮定すると、ｄ♂１．＝ｄ、２ｔ、
であるから比例断面積の減少碧はで与えられる。
断面長方形のテープ、リボンまたはシートが非型彫ニッ
プを通してロール掛けることによる圧縮に供されるとき
は、一般に＃１Ｋ１９とんど、または全く変化がない、
すなわち６．−６．であることが見い出され喪。
面積の減少は比例厚さの減少に等しい。長さの増加がΔ
ｌｌであるとき、長さの比例増加、すなわちｔｌ、１−
Ｘ で与えられる。
直径４の円形断面の予備成形物（す表わち、ｂｏ＝　ｔ
ｏ＝　ｄｏ　）を、例えば型彫ニップを通してロール掛
けすることＫよって、またはダイを通して冷間押出する
ことＫよって圧縮に供して直径ｄ、の円形断面の製品を
得るときは、その比例断面積の減少は で与えられ、また伸張率は容積変化が無視できるとして で与えられる。
圧縮操作に続いて、予備成形物は重合体のＴ。
と融点の間の温度における一軸または二軸延伸操作に付
される。
８−ヒドロキシ酪酸単独重合体は融点的１８０℃、Ｔ、
約０℃を持つ。ＨＢ共重合体、例えば８−ヒドロキシ吉
草酸単位を含有するＨＢ共重合体はＨＢ単独重合体より
低い融点を持ち、かつしげしげより低いＴ、を持つ。Ｈ
Ｂ共重合体の融点は共単竜体単位の割合に依存し、例え
ば約２５モルチの８−ヒドロキシ吉草酸単位を含有する
共重合体は１８０℃のオーダーの融点を持つ。
圧縮操作が行われる温度はＨＢ重合体の融点より５０〜
１５０℃低い温度が好ましい。すなわち、ＨＢ単独重合
体についての圧縮操作温度は８０〜１８０℃、％［５０
〜１００℃の範囲が好ましい。
延伸操作は重合体の結晶融点よＪ４０〜９０℃低い＠度
で行うのが好ましい。すなわち、ＨＢ単独重合体の延伸
操作温度は９０〜１４０℃の範囲ある。
予備成形物は、例えば溶液キャスティングによって製造
することができるが、溶融加工によって製造するのが好
ましい。例えばビレットは、例えば圧縮成形または射出
成形によって製造することができ、また連続長尺物は、
例えば押出法によって製造することができる。後者の場
合、その工程は連続法で運転することができる。例えば
フィルムはＨＥ重合体のスリットダイを通しての溶融押
出によって予備成形物を形成し、それを水浴を通過させ
ることによって固化および結晶化させ、少なくとも１対
のニップロールを通過させることＫよってロール掛けし
、次いで例えばテンターの使用によって一軸または二軸
延伸することによって製造することができる。
四軸延伸フイルムはある場合にはこれをフィブリル化し
て縫合糸の製造に用いられる繊維にすることができる。
繊維はまた一般に円形断面の予備成形物を押し出し、続
いて圧縮操作をする１例えば所望断面のロール掛は予備
成形物に相当する型彫表面を有する一対のニップローラ
を通過させることＫよって製造することもできる。ロー
ル掛は予備成形物は次にこれを一軸延伸することができ
る。一方、圧縮操作は前記固体状態の押出法で行うこと
ができるＯ 延伸工程において、少なくとも１つの寸法（厚さ以外の
）Ｋおける延伸比、すなわち延伸予備成形物の寸法：ｌ
Ｅ縮予備成形物の寸法は少なくとも１．５：１．特に少
なくとも２：ｌであるのが好ましい。達成できる蛾大延
伸度はある程度は圧縮操作中に適用される厚さの減少度
に依存することが見い出された。配向させるには少なく
とも５−の厚さの減少が必要であるが、大き過ぎる厚さ
の減少は達成可能の蛾大全延伸比（例えば、最終長さ：
圧縮工程前の長さ）を制限するだろう。好ましくは、全
延伸比は少なくとも１つの方向において少なくとも８：
１である。
予備成形物を一軸延伸する場合、圧縮操作および延伸は
全延伸比が少なくとも４　：　１．　％に５＝１となる
ように行なうのが好ましい。
本発明を次の実施例によって説明する。実施例１〜６に
おいて、ＨＢ重合体はグルコース上でアＣ５ＣＮＣＩＢ
　１１５９９）の好気培養によって製造した８−ヒドロ
キシ酪酸単独重合体で、以下においてはＰＨＢと称する
。ＰＨＥは室温において水性セル懸濁液から１，２−ジ
クロロエタンによシ抽出し、続いて溶解ＰＨＢを含有し
ている溶剤層を水性層からデカンテーションによって分
離することＫよって単離した。すなわち、その溶液を濾
過し、次いで溶液をメタノール／水溶液に加えることに
よってＰＨＢを沈殿させた。沈殿したＰＨＢを濾過によ
って分離し、メタノールで洗浄し、乾燥した。乾燥した
重合体を約１０重量−のクロロホルムによりペーストに
形成し、これを室温で家庭用ミンサーを通過させること
Ｋよって粒状化した。この粒体を次にオープン中で乾燥
してクロロホルムを除去し、１９０℃で溶融押出成形し
、そして再粒状化した。
実施例１ 粒体を１９０℃で８分間圧縮成形することによってほぼ
１００Ｘ８０Ｘ１．８ｍの寸法を持つ重合体のブラック
を作った。これらのブラックを次に６０℃の水浴中で１
０分間アニーリングした。次に、幅１５１、直径７．６
　ａｍの約１０〜１５ｒｐｓで回転している一対の未加
熱ロールのニップに通すことによって室温でそれらの長
さに沿ってロール械けした。これらのブラックは第１表
に記すような回数そのニップに通した。試料の厚さおよ
び長さをロール掛けの前後において測定し、達成された
厚さの減少および伸びを求めた。それらの試料から試験
片を切）取シ、引張緩衝強度（ＡＳＴＭＤ１９２Ｂ−６
８による）および引張特性を２８℃において測定した。
引張特性はゲージ長２０鴎、幅Ｚｔｍｌの試料を用い、
歪速度０．５分−亀でインストロン（Ｉｎ５ｔｒｏｎ）
型万能引張試験機で測定した。
引張特性の測定に加えてこの引張試験でロール掛は試料
をさらに室温で模擬−軸延伸した。
ロール掛は試料は全て有意の配向度を示した。
展延性および引張衝撃強度の改良は第１表にはつき〕示
されている。
実施例２ 型の寸法を１００Ｘ１００Ｘ１．８ｍに大きくした点を
除いて実施例１に記載したようにしてブラックを作製、
アニーリングした。ブラックは幅８０ａ１直径１５ｃＩ
Ｒの１００℃に加熱された１５ｒμで回転している一対
のローラのニップを、その厚さが６０−まで減少し、ロ
ール掛は方向の伸びが１５０％になるまで同一方向に繰
〕返し通した。横断方向の伸びは無視した。
機械的性質はロール掛は方向に対して平行に切断した試
験片（ＭＺ））および直角に切断した試験片（ＴＤ）を
用いて実施例１のように測定した。結果を第２表に示す
。
第２表 実施例８ 各試料が互いに゛直角の方向に遂次的にロール掛けされ
るように試料をニップに通した後９０°廻した点を除い
【実施例２を繰ル返した。ロール掛けは全厚さの減少が
５８憾に表るまで続けた。機械的性質を実施例１に記載
したように最初のロール掛は方向に対して平行な方向（
ＭＤ）と直角の方向（ＴＤ）について測定した。結果を
第８表に示す。
ＭＤとＴＤの両方向における伸びは約５０チであった。
第８表 実施例４ 溶融押出粒状物を５０ｍＸ１゜５■のスロットダイを通
して１９０℃で再押出成形してリボンを得た。これを６
０℃の水浴に通して重合体を結晶化させ、次いで実施例
１で使用した約１０〜１５ｒｐｍで回転している約５０
℃に加熱され九ローラのニップに通した。
水浴から取り出した結晶性のリボンは不透明で脆かった
。ニップを１回通過させると、リボンは透明で展延性に
なった。ニップを通すと、その長さは１２０−まで増加
し、その厚さは１．１諺から０．４５．まで減少した。
すなわち厚さの減少率は５９−でありへ。リボンの引張
特性を実施例１に記載したように押出方向（ＭＤ）とそ
れに対して直角の方向（ＴＤ）で測定した。結果を第４
表に示す。
第４表 辛　試料はこの荷重で塑性変形およびネッキングを起こ
し、そして破断するまで一定荷重で８００−の伸張率ま
で延伸された。
実施例５ 溶融押出重合体の粒状物を直径４１ｍ＋のダイを通Ｌ−
Ｃ’１９０℃で再押出成形してモノフィラメントを得た
。これを６０℃の水浴に通してその重合体を結晶化させ
た。引取速度はがなりの引落率の押出物を与えるように
調整した。巻き取られた繊維の直径は約ＩＮであった。
この結晶性製品を続いて８Ｏ−４０ｒ声で回転し、約５
０’ＣＩＣ加熱されている１組の宝石側工人用ロールの
型彫ニップに通した。ニップは押出モノフィラメントよ
シわずかい小さい直径の円形型彫を有していた。
ロール掛は後、繊維をインストロン型万能試験機（モデ
ル１１２２）の温度キャビネット中で１６７分−１およ
び１６７分−ｌの伸張速度を用いて１２５℃において破
断するまで延伸した。結果を！５表表示示。
第５表 実施例６ 重合体粒状物の４種の試料を押出成形し、次いで実施例
５に記載の方法を用いて程度を変えてロール掛けした。
それらを次に１４５℃および１６．７分゛１の歪速度で
延伸したが、延伸は繊維が破断する前に止めた。伸張繊
維を１２５℃で５分間「ヒートセット」した後、それら
繊維をオープンから取シ出し、２８℃において１分−１
の伸張速度で引張特性を測定した。結果を第６表に示す
が、これらの結果はモノフィラメントの引張強度が冷間
ロール掛は一熱間延伸法の結果として５倍まで増加した
ことを示している。
実施例？ グルコースとプロピオン酸の混合炭素源上でアルカリゲ
ネス・オイトロファス突然変移株５８０１／Ｃ５の好気
培養によって製造した９ｚ−のヒドロキシ酪酸単位と８
％のヒドロキシ吉草酸単位から成る共重合体を用いて実
施例５に記載した実験を繰シ返した。重合体は前記のよ
うに抽出および粒状化した。結果を第７表に示す。
第７表 実施例８ に記載した室温における引張試験用のロール掛けおよび
延伸された繊維を製造した。結果を第８表に示す。
実施例９ 実施例７に記載の方法によるが、炭素源としてグルコー
スを、続いてプロピオン酸を用いて製造した９６チのヒ
ドロキシ酪酸単位と４係のヒドロキシ吉草酸炭素から成
る共重合体を用いて実施例５を繰り返した。結果を第９
表に示す。
実施例１０ 実施例９の共重合体を用いて実施例８に記載の実験を繰
シ返した。
実施例１１ 実施例１で使用した重合体の試料をクロロホルムに溶解
し、得られた溶液をワットマンＧＦ／Ｂガラス繊維Ｐ紙
でＦ遇して微粒不純物を除去した。
この溶液を回転蒸発器上で重合体濃度として１０％’／
ｖまで濃縮した後、トルエンで注意深く洗ってグリース
を除去し、そして水平な表面の上に置いた１１００Ｘ１
００のガラスシートの上に注いだ。溶液の使用量は溶剤
蒸発後の重合体の最終厚さが１ｍ＋［なるように計算し
た。溶剤をゆつくり蒸発させ、そしてポリテンシートを
そのガラスシートの上にかけて空中に浮遊するごみで溶
液が汚されないようＫした。
手でされって乾燥していたら、得られた不透明の重合体
シートの端を切り取シ、プレス機で２０、０００　ｐ、
　ａ、　ｉの力で２８℃においてプレスした。このプレ
スで厚さは約２〇−減少した。このプレス工程で実際上
透明になったフィルムを次にティー・エム・ロング伸張
機（Ｔ、Ｍ、Ｌｏｎｇｓｔｒｅｔｃｈｅｒ）を用いて１
０分−１の延伸速度で１５０１つの方向で４．０　：　
１であシ、それに垂直な方向で４．６　：　１であり、
得られたフィルムは厚さが約２５μ惰であった。
このフィルムの機械的性質を温度制御されたキャビネッ
トを持つインストロン型万能試験機と０．４分−１の歪
速度を用いて測定した。結果を第１１表に示す。
実施例１２ 冷間プレス段階を除いて実施例１１を繰ジ返した。この
場合、温度と延伸速度のいがなる組み合せでもロング伸
張機でこのフィルムを配向することは不可能であること
が実証された。すなわち、グリップのところであらゆる
時点で試料の破壊が起こった。
実施例１８ 前記実施例で用いた単独重合体および共重合体に関して
常用の配向法、すなわち冷間ロール掛は工程または固体
状態の圧縮工程を持たない配向法を試みたが、全く成功
しなかった。
これらの結晶性重合体は融点までのあらゆる温度で延伸
実験中に脆くも破壊されやすいことが見い出された。
射出または圧縮成形、それに続いて溶融物を一５℃以下
に急冷することＫよって製造した単独重合体の非晶質の
試料を延伸する試みも同じく不成功に終った。約−５℃
以下の温度で試料は脆い破片に破壊された。−２℃と＋
７℃の間で試料は塑性変形し、非常に小さい応力（１〜
２ＭＰａ）において１０００−以上まで延びたが、解放
すると実質的に１００ＩＩＩ弾性回復した。伸長した重
合体をヒートセットする試みも全て不成功で、試料を破
壊させた。７℃以上で非晶質重合体のモジュラスは急速
に落ち（１０℃において０．０４８　ＧＰａ）、約１０
０〜２００−の伸長後ネッキング破壊によって破壊する
傾向が出た。
典形的な結果を第１８表に示す。

Claims (1)

    【特許請求の範囲】
  1. ８−ヒドロキシ酪酸残基が重合体鎖の少なくとも４０モ
    ル％を形成している重合体材料の溶剤を含まない予備成
    形物をその重合体のガラス転移温度と結晶融点の間の温
    度で圧縮力に付してその厚さを少なくとも５％減少させ
    、次いで圧縮され九予備成形物を一軸ま九は二輪延伸す
    ることを特徴とする８−ヒドロキシ酪酸重合体から成形
    品を製造する方法。
JP57190702A 1980-04-30 1982-10-29 ３−ヒドロキシ酪酸重合体からの成形品の製造方法 Granted JPS5882723A (ja)