JPH097230A - 光ディスク及びその製造方法 - Google Patents
光ディスク及びその製造方法Info
- Publication number
- JPH097230A JPH097230A JP7174093A JP17409395A JPH097230A JP H097230 A JPH097230 A JP H097230A JP 7174093 A JP7174093 A JP 7174093A JP 17409395 A JP17409395 A JP 17409395A JP H097230 A JPH097230 A JP H097230A
- Authority
- JP
- Japan
- Prior art keywords
- pair
- radiation
- adhesive layer
- transparent substrates
- outer peripheral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 耐熱性に優れ接着強度を十分に得ることがで
きる貼り合わせ型光ディスクを提供することを目的とす
る。 【構成】 一対の透明基板に各々、外周部を除いて、放
射線硬化型粘着剤層を形成すると共に、外周部に紫外線
硬化型樹脂を塗布した後、一対の透明基板を放射線硬化
型粘着剤層により貼り合わせると共に紫外線硬化型樹脂
に紫外線を照射して外周部を強固に固着させる。
きる貼り合わせ型光ディスクを提供することを目的とす
る。 【構成】 一対の透明基板に各々、外周部を除いて、放
射線硬化型粘着剤層を形成すると共に、外周部に紫外線
硬化型樹脂を塗布した後、一対の透明基板を放射線硬化
型粘着剤層により貼り合わせると共に紫外線硬化型樹脂
に紫外線を照射して外周部を強固に固着させる。
Description
【0002】
【0001】
【0003】
【産業上の利用分野】本発明は、一対のディスクを貼り
合わせてなる光ディスク及びその製造方法に関する。
合わせてなる光ディスク及びその製造方法に関する。
【0004】
【0002】
【0005】
【従来の技術】従来、ビデオディスク等の光学式ディス
クとして、図2で示すように透光性の樹脂基板21の一
面に情報を担持するピット列又はグルーブを同心円状又
は螺旋状に形成し、その上方に反射膜22及び保護膜2
3を順次形成した一対のディスクを、保護膜23を相対
向させて接着剤層24により貼り合わせた両面記録ディ
スクが知られており、ディスクの中心に設けられたセン
ターホールを照準にして、ディスクをクランプし回転さ
せて、ディスクの各面の記録領域へ読取りビームを照射
し、光学的に情報を再生する構成となっている。
クとして、図2で示すように透光性の樹脂基板21の一
面に情報を担持するピット列又はグルーブを同心円状又
は螺旋状に形成し、その上方に反射膜22及び保護膜2
3を順次形成した一対のディスクを、保護膜23を相対
向させて接着剤層24により貼り合わせた両面記録ディ
スクが知られており、ディスクの中心に設けられたセン
ターホールを照準にして、ディスクをクランプし回転さ
せて、ディスクの各面の記録領域へ読取りビームを照射
し、光学的に情報を再生する構成となっている。
【0006】このような貼り合わせ型光学式ディスクで
は、その接着剤層として一般にホットメルト型粘着剤が
用いられている。
は、その接着剤層として一般にホットメルト型粘着剤が
用いられている。
【0007】
【0003】
【0008】
【発明が解決しようとする課題】しかしながらホットメ
ルト型粘着剤は、熱可塑性で有る為、耐熱性で劣り、熱
によりディスクの変形、又は剥がれが生じ易いという問
題があった。そこで耐熱性が良好である放射線硬化型粘
着剤をディスクの貼り合わせ用として用いることが考え
られる。放射線硬化型粘着剤は、紫外線、電子線等の放
射線の照射により硬化して粘着性を発現するが、放射線
の照射により分子構造が3重結合となり、流動性が無く
なるため、放射線の照射前の塗布された表面が粗いと十
分な接着面積が得られなくなる。よって、接着強度が不
足し、貼り合わせたディスクの端面より剥がれが生じ易
いという問題が生じる。本発明は、かかる事情に基づい
てなされたものであり、貼り合わせ端面から剥がれの生
じないような光ディスク及びその製造方法を得ることを
目的とする。
ルト型粘着剤は、熱可塑性で有る為、耐熱性で劣り、熱
によりディスクの変形、又は剥がれが生じ易いという問
題があった。そこで耐熱性が良好である放射線硬化型粘
着剤をディスクの貼り合わせ用として用いることが考え
られる。放射線硬化型粘着剤は、紫外線、電子線等の放
射線の照射により硬化して粘着性を発現するが、放射線
の照射により分子構造が3重結合となり、流動性が無く
なるため、放射線の照射前の塗布された表面が粗いと十
分な接着面積が得られなくなる。よって、接着強度が不
足し、貼り合わせたディスクの端面より剥がれが生じ易
いという問題が生じる。本発明は、かかる事情に基づい
てなされたものであり、貼り合わせ端面から剥がれの生
じないような光ディスク及びその製造方法を得ることを
目的とする。
【0009】
【0004】
【0010】
【課題を解決するための手段】請求項1記載の本発明に
かかる光ディスクでは、主面に外周部及び内周部を残し
て記録領域を有し、対向する一対の透明基板と、一対の
透明基板の対向する記録領域の間に設けられ一対の透明
基板を接着する放射線硬化型粘着剤層と、一対の透明基
板の対向する外周部間に設けられ一対の透明基板の外周
部を固着する紫外線硬化型樹脂層とを有する。
かかる光ディスクでは、主面に外周部及び内周部を残し
て記録領域を有し、対向する一対の透明基板と、一対の
透明基板の対向する記録領域の間に設けられ一対の透明
基板を接着する放射線硬化型粘着剤層と、一対の透明基
板の対向する外周部間に設けられ一対の透明基板の外周
部を固着する紫外線硬化型樹脂層とを有する。
【0011】
【0005】請求項2記載の本発明にかかる光ディスク
の製造方法では、主面に外周部及び内周部を残して記録
領域を有する一対の透明基板を作成する工程と、一対の
透明基板の記録領域上に放射線硬化型粘着剤層を形成
し、放射線硬化型粘着剤層に放射線を照射し、粘着性を
付与する工程と、一方の透明基板の外周部に紫外線硬化
型樹脂を環状に滴下する工程と、一対の透明基板を放射
線硬化型粘着剤層により貼り合わせる工程と、紫外線硬
化型樹脂に紫外線を照射し、硬化させ、一対の透明基板
の外周部を固着する工程とを有する。
の製造方法では、主面に外周部及び内周部を残して記録
領域を有する一対の透明基板を作成する工程と、一対の
透明基板の記録領域上に放射線硬化型粘着剤層を形成
し、放射線硬化型粘着剤層に放射線を照射し、粘着性を
付与する工程と、一方の透明基板の外周部に紫外線硬化
型樹脂を環状に滴下する工程と、一対の透明基板を放射
線硬化型粘着剤層により貼り合わせる工程と、紫外線硬
化型樹脂に紫外線を照射し、硬化させ、一対の透明基板
の外周部を固着する工程とを有する。
【0012】
【0006】
【0013】
【作用】一対の透明基板の対向する記録領域間の放射線
硬化型粘着剤層は、粘着性を保持し、及び外周部間の紫
外線硬化型樹脂層は硬化して一対の透明基板を接着して
いるので、ディスク変形の応力を吸収すると共に貼り合
わせ端部で強固に固着される。
硬化型粘着剤層は、粘着性を保持し、及び外周部間の紫
外線硬化型樹脂層は硬化して一対の透明基板を接着して
いるので、ディスク変形の応力を吸収すると共に貼り合
わせ端部で強固に固着される。
【0014】
【0007】
【0015】
【実施例】以下に本発明の一実施例を図1に基づいて詳
細に説明する。本実施例の光ディスクは、一対のディス
クを貼り合わせた構成となっている。まず、主面に外周
部及び内周部を除いて微細な凹凸による情報を表すピッ
ト又はグルーブが形成された記録領域を有する一対の透
明基板1を射出成形等によって作製し、その後外周部及
び内周部を除いた記録領域上にアルミニウム等からなる
反射膜2を形成し、さらに透明基板の内周部、外周部及
び記録領域上を覆うように紫外線硬化型樹脂等からなる
保護膜3を形成して一対のディスクを得る。尚、透明基
板1は、ポリメチルメタクリレート(PMMA)、ポリ
カーボネート(PC)等の合成樹脂板又はガラス板から
なり、厚さ0.2〜0.8mm、例えば0.6mm厚の
円形基板である。
細に説明する。本実施例の光ディスクは、一対のディス
クを貼り合わせた構成となっている。まず、主面に外周
部及び内周部を除いて微細な凹凸による情報を表すピッ
ト又はグルーブが形成された記録領域を有する一対の透
明基板1を射出成形等によって作製し、その後外周部及
び内周部を除いた記録領域上にアルミニウム等からなる
反射膜2を形成し、さらに透明基板の内周部、外周部及
び記録領域上を覆うように紫外線硬化型樹脂等からなる
保護膜3を形成して一対のディスクを得る。尚、透明基
板1は、ポリメチルメタクリレート(PMMA)、ポリ
カーボネート(PC)等の合成樹脂板又はガラス板から
なり、厚さ0.2〜0.8mm、例えば0.6mm厚の
円形基板である。
【0016】
【0008】次に図1(a)に示すように、内周部及び
外周部を除いて保護膜3上に数十ミクロン厚の放射線硬
化型粘着剤層4を、スクリーン印刷法により形成する。
放射線硬化型粘着剤はアクリルオリゴマーを主成分と
し、ゴム状ポリマー、粘着付与剤を必須成分として含
み、揮発性溶剤を含有しないもので室温(20℃)未硬
化状態で50,000cps以下、例えば21,500
cpsの粘度を有するもの、例えばセメダイン社製「C
T−110K10」等が適している。次に図1(b)に
示すように放射線硬化型粘着剤層4に所定量の放射線を
照射し、液体状態から硬化させ粘着性を発現させる。
外周部を除いて保護膜3上に数十ミクロン厚の放射線硬
化型粘着剤層4を、スクリーン印刷法により形成する。
放射線硬化型粘着剤はアクリルオリゴマーを主成分と
し、ゴム状ポリマー、粘着付与剤を必須成分として含
み、揮発性溶剤を含有しないもので室温(20℃)未硬
化状態で50,000cps以下、例えば21,500
cpsの粘度を有するもの、例えばセメダイン社製「C
T−110K10」等が適している。次に図1(b)に
示すように放射線硬化型粘着剤層4に所定量の放射線を
照射し、液体状態から硬化させ粘着性を発現させる。
【0017】
【0009】次いで図1(c)に示すように一方のディ
スクの放射線硬化型粘着剤層4が形成されていない保護
膜3上の内周部及び外周部に液状の紫外線硬化型樹脂5
を環状に滴下する。紫外線硬化型樹脂5は、多官能アク
リレートモノマーを主成分とし、室温(20℃)未硬化
状態で530cpsの粘度を有するもの、例えば大日本
インキ化学工業(株)社製「ダイキュアクリア SD−
301」等が適している。
スクの放射線硬化型粘着剤層4が形成されていない保護
膜3上の内周部及び外周部に液状の紫外線硬化型樹脂5
を環状に滴下する。紫外線硬化型樹脂5は、多官能アク
リレートモノマーを主成分とし、室温(20℃)未硬化
状態で530cpsの粘度を有するもの、例えば大日本
インキ化学工業(株)社製「ダイキュアクリア SD−
301」等が適している。
【0018】
【0010】次に図1(d)に示すように一対のディス
クを対向させて加圧し、放射線硬化型粘着剤層4により
貼り合わせた後、内周部、外周部及び外周部からあふれ
でて貼り合わせ端面を覆う部分の紫外線硬化型樹脂に紫
外線を照射し、硬化させることにより、一対のディスク
は内周部、外周部で強固に固着されることになる。
クを対向させて加圧し、放射線硬化型粘着剤層4により
貼り合わせた後、内周部、外周部及び外周部からあふれ
でて貼り合わせ端面を覆う部分の紫外線硬化型樹脂に紫
外線を照射し、硬化させることにより、一対のディスク
は内周部、外周部で強固に固着されることになる。
【0019】
【0011】上記実施例では再生専用型の貼り合わせデ
ィスクについて説明したが、記録領域上にシアニン系有
機色素、磁気光学材料、相変化型材料からなる記録層を
形成した書き込み可能なタイプの貼り合わせディスクに
対しても適用できる。
ィスクについて説明したが、記録領域上にシアニン系有
機色素、磁気光学材料、相変化型材料からなる記録層を
形成した書き込み可能なタイプの貼り合わせディスクに
対しても適用できる。
【0020】また、貼り合わせディスクの一方を再生専
用型、他方を書き込み可能タイプとしても良い。さら
に、紫外線硬化型樹脂による固着は外周部及び貼り合わ
せ外周端面のみとしても良い。
用型、他方を書き込み可能タイプとしても良い。さら
に、紫外線硬化型樹脂による固着は外周部及び貼り合わ
せ外周端面のみとしても良い。
【0021】
【0012】
【0022】
【発明の効果】以上のように本発明では、少なくとも外
周部を除いて放射線硬化型粘着剤層により、一対のディ
スクを貼り合わせると共に、外周部を紫外線硬化型樹脂
により強固に固着することにより、ディスク変形の応力
を吸収すると共に貼り合わせ外周端での剥がれを防止す
ることができる。
周部を除いて放射線硬化型粘着剤層により、一対のディ
スクを貼り合わせると共に、外周部を紫外線硬化型樹脂
により強固に固着することにより、ディスク変形の応力
を吸収すると共に貼り合わせ外周端での剥がれを防止す
ることができる。
【図1】本発明における光ディスクの製造方法を示す工
程図である。
程図である。
【図2】従来の光ディスクの構成を示す概略側面断面図
である。
である。
1 ・・・・・ 基板 2 ・・・・・ 反射膜 3 ・・・・・ 保護膜 4 ・・・・・ 放射線硬化型粘着剤層 5 ・・・・・ 紫外線硬化型樹脂
───────────────────────────────────────────────────── フロントページの続き (72)発明者 笹野 光彦 山梨県中巨摩郡田富町西花輪2680番地 パ イオニアビデオ株式会社内 (72)発明者 本川 昌明 山梨県中巨摩郡田富町西花輪2680番地 パ イオニアビデオ株式会社内 (72)発明者 平井 良和 山梨県中巨摩郡田富町西花輪2680番地 パ イオニアビデオ株式会社内 (72)発明者 丸山 治久 山梨県中巨摩郡田富町西花輪2680番地 パ イオニアビデオ株式会社内
Claims (2)
- 【請求項1】 主面に外周部及び内周部を残して記録領
域を有し、対向する一対の透明基板と、前記一対の透明
基板の対向する記録領域の間に設けられ一対の透明基板
を接着する放射線硬化型粘着剤層と、前記一対の透明基
板の対向する外周部間に設けられ前記一対の透明基板の
外周部を固着する紫外線硬化型樹脂層とを有する光ディ
スク。 - 【請求項2】 主面に外周部及び内周部を残して記録領
域を有する一対の透明基板を作成する工程と、前記一対
の透明基板の記録領域上に放射線硬化型粘着剤層を形成
し、該放射線硬化型粘着剤層に放射線を照射し、粘着性
を付与する工程と、前記一方の透明基板の外周部に紫外
線硬化型樹脂を環状に滴下する工程と、前記一対の透明
基板を前記放射線硬化型粘着剤層により貼り合わせる工
程と、前記紫外線硬化型樹脂に紫外線を照射し、硬化さ
せ一対の透明基板の外周部を固着する工程とを有する光
ディスクの製造方法。 【0001】