JP7457052B2 - ポリエステル/ウール混紡生地のリサイクル方法 - Google Patents
ポリエステル/ウール混紡生地のリサイクル方法 Download PDFInfo
- Publication number
- JP7457052B2 JP7457052B2 JP2022062276A JP2022062276A JP7457052B2 JP 7457052 B2 JP7457052 B2 JP 7457052B2 JP 2022062276 A JP2022062276 A JP 2022062276A JP 2022062276 A JP2022062276 A JP 2022062276A JP 7457052 B2 JP7457052 B2 JP 7457052B2
- Authority
- JP
- Japan
- Prior art keywords
- acid
- polyester
- fabric
- wool
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ケラチンに分解したとしても、ポリエステル繊維に染料が残る場合があり、脱色がさらに必要である。
本開示において提供されるポリエステル/ウール混紡生地のリサイクル方法が分離手順及び脱色手順の両方を含むこと、及び同じ製造工程においてポリエステルとウールとが分離され、脱色されたポリエステル繊維を得ることができることを実証するために、以下の実施例が説明される。
1L耐圧反応槽内に、20gのPETポリエステル(ポリエチレンテレフタレート)-ウール混紡生地(L=19%、PETポリエステル92重量%、ウール8重量パーセント)が配置され、500mlの水、10gのマレイン酸、2.0gの次亜塩素酸ナトリウムが投入され、混合物は、165℃において2時間攪拌された。その後、ウールがウールケラチンに分解された。
実施例1と同様であるが、マレイン酸の代わりにシュウ酸のみが使用され、得られたPET生地は、重量比で99.8%の純度を有し、L=79%、a=1.2、b=5.4であった。
実施例1と同様であるが、次亜塩素酸ナトリウムの代わりに次亜塩素酸カルシウムのみが使用され、得られたPET生地は、重量比で99.4%の純度を有し、L=84%、a=-0.4、b=4.6であった。
1L耐圧反応槽内に、20gのPETポリエステル-ウール混紡生地(L=18%、PETポリエステル73重量%、ウール27重量%)が配置され、500mlの水、12gの酢酸、1.5gの次亜塩素酸ナトリウムが投入され、混合物は、165℃において2時間攪拌された。その後、ウールがウールケラチンに分解された。
実施例4と同様であるが、酢酸の代わりにシュウ酸のみが使用され、得られたPET生地は、重量比で99.9%の純度を有し、L=85%、a=1.8、b=5.9であった。
実施例4と同様であるが、1.5gの代わりに2.5gの次亜塩素酸ナトリウムのみが使用され、得られたPET生地は、重量比で99.9%の純度を有し、L=88%、a=-0.1、b=4.3であった。
1L耐圧反応槽内に、20gのPETポリエステル-ウール混紡生地(L=19%、PETポリエステル92重量%、ウール8重量%)が配置され、500mlの水、10gのマレイン酸が投入され、混合物は、165℃において2時間攪拌された。その後、ウールがウールケラチンに分解された。
1L耐圧反応槽内に、20gのPETポリエステル-ウール混紡生地(L=20%、PETポリエステル76重量%、ウール24重量%)が配置され、500mlの水、10gのギ酸が投入され、混合物は、170℃において2時間攪拌された。その後、ウールがウールケラチンに分解された。
Claims (11)
- 染料を含有するポリエステル/ウール混紡生地を、酸化剤を含有する酸性水溶液中に配置し、加熱及び浸漬し、前記ポリエステル/ウール混紡生地のウールの分解と、脱色による前記染料の除去とを同時に行い、
ろ過によりポリエステル生地が得られ、
前記浸漬は、130~200℃において前記酸性水溶液中で行われる、
ポリエステル/ウール混紡生地のリサイクル方法。 - 前記染料は、物理染料又は化学染料を含む、請求項1に記載のリサイクル方法。
- 前記浸漬は、ポリエステルのガラス転移点より高い温度で行われる、請求項1又は2に記載のリサイクル方法。
- 前記酸性水溶液は、有機酸を含み、
前記有機酸は、一塩基酸、二塩基酸、1~18個の炭素を備えるカルボン酸無水物であり、ギ酸、酢酸、無水酢酸、シュウ酸、プロピオン酸、マロン酸、酪酸、コハク酸、吉草酸、グルタル酸、カプロン酸、アジピン酸、イソオクタン酸、クエン酸、マレイン酸、無水マレイン酸、安息香酸、又はシクロヘキサン酸を含む、
請求項1又は2に記載のリサイクル方法。 - 前記酸性水溶液中の前記有機酸は、0.1~3.0wt%の濃度を有する、請求項4に記載のリサイクル方法。
- 前記酸性水溶液中の前記酸化剤は、0.06~1.2wt%の濃度を有する、請求項1又は2に記載のリサイクル方法。
- 前記ポリエステル/ウール混紡生地の前記酸性水溶液に対する重量比は、1:8から1:30である、請求項1又は2に記載のリサイクル方法。
- 前記浸漬は、0.5~3時間行われる、請求項1又は2に記載のリサイクル方法。
- 前記酸化剤は、過酸化水素、過マンガン酸カリウム、次亜塩素酸カルシウム、オゾン、硝酸、硝酸塩、塩素酸ナトリウム、塩素酸カルシウム、塩素酸塩、過塩素酸塩、次亜塩素酸ナトリウム、次亜塩素酸塩、過ホウ酸ナトリウム、二クロム酸ナトリウム、二クロム酸塩、又はそれらの組み合わせを含む、請求項1又は2に記載のリサイクル方法。
- 前記ろ過は、1~30mmのフィルタスクリーンを使用する、請求項1又は2に記載のリサイクル方法。
- 得られた前記ポリエステル生地は、75%以上のL値、±4のa値、及び±8のb値を有する、請求項1又は2に記載のリサイクル方法。