JP6890370B2 - ゴム補強用アラミド短繊維集束体 - Google Patents
ゴム補強用アラミド短繊維集束体 Download PDFInfo
- Publication number
- JP6890370B2 JP6890370B2 JP2017003796A JP2017003796A JP6890370B2 JP 6890370 B2 JP6890370 B2 JP 6890370B2 JP 2017003796 A JP2017003796 A JP 2017003796A JP 2017003796 A JP2017003796 A JP 2017003796A JP 6890370 B2 JP6890370 B2 JP 6890370B2
- Authority
- JP
- Japan
- Prior art keywords
- aramid
- fiber
- wax
- rubber
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(2)ワックスを水分散させたエマルジョン状態にして、ラテックスを含有する集束剤と混合したものを、集束体を構成するアラミド短繊維の表面に付着させた、上記(1)記載のゴム補強用アラミド短繊維集束体。
(3)アラミド短繊維が、あらかじめエポキシ基含有化合物を繊維骨格内に浸透させたアラミド繊維である、上記(1)または(2)記載のゴム補強用アラミド短繊維集束体。
(4)アラミド繊維の表面に、ラテックスを含有する集束剤と、オレフィン系ワックス及び脂肪酸アミド系ワックスから選ばれる少なくとも1種のワックスと、を水に分散させてエマルジョン状態としたものを付着させた後、
前記集束剤及びワックスを付着させたアラミド繊維集束体をカットする
ことを特徴とするアラミド短繊維集束体の製造方法。
集束剤の付着量が1質量%以上であれば、短繊維束を構成する単糸に付与することでゴムとの接着性を向上させることができ、20質量%以下であれば、繊維表面に形成する被膜が厚くなりすぎることなく繊維束の内部まで集束剤を付与することができる。集束剤のより好ましい付着量は2〜15質量%であり、特に3〜10質量%が好ましい。
試料約5gの質量を測定し、300℃×20分の熱処理を行い、25℃65%RHで5分間放置した後、再度質量を測定する。ここで使う水分率は、[乾燥前質量−乾燥後質量]/[乾燥後質量]で得られるドライベース水分率である。
JIS L 1017の接着力−A法に準じて、PPTA繊維複合体(カット前)を未加硫ゴムに埋め込み、加圧下で150℃、30分プレス加硫を行ない、放冷後、コードをゴムブロックから30cm/minの速度で引き抜き、その引き抜き荷重をN/cmで表示した。接着評価におけるゴムコンパウンドとしては、クロロプレン未加硫ゴムを使用した。
カットした短繊維50gを2mm×2mmのふるいにかけ、ふるい上に残留した短繊維量を測定した。 ファイバーボール発生率(%)=ふるい残留量/ふるい投入量
(ゴム練り方法)短繊維集束体を、クロロプレンゴムを主成分とする未加硫ゴム中に短繊維集束体を20%となるように配合し、ニーダーで5分間混練した。その後、短繊維が配向するようにロール通しを行い、プレス加硫により厚さ2mmのゴムシートを作り、短繊維の配向方向及び非配向方向にサンプルを切り出し、それぞれJIS K6251引張試験に従い性能評価を行った。
公知の方法で得られたポリパラフェニレンテレフタルアミド(PPTA)(分子量約20,000)1kgを4kgの濃硫酸に溶解し、直径0.1mmのホールを1,000個有する口金からせん断速度30,000sec−1となるよう吐出し、4℃の水中に紡糸した後、10質量%の水酸化ナトリウム水溶液で、10℃×15秒の条件で中和処理した。その後、脱水処理をして、110℃で低温乾燥を行い、水分率を35%に調整した。
このPPTA繊維に、エポキシ基含有化合物として、ソルビトールポリグリシジルエーテルを50質量%含有する油剤(ジイソステアリルアジペート/ジオレイルアジペート/硬化ヒマシ油エチレンオキサイド/鉱物油の混合物)を、水分率0%に換算したときの繊維質量に対し1.0%含浸させた後、巻き取り工程でボビンに巻き取った。
実施例1において、ワックスを付着させなかった以外は、実施例1と同様の方法により得られたPPTA繊維複合体を、3.5mmにカットし短繊維集束体を得た。
実施例1において、RFL水溶液からなる集束剤に含浸させる直前のPPTA繊維複合体の水分率を10%とし、かつワックスを付着させなかった以外は、実施例1と同様の方法により得られたPPTA繊維複合体を、3.5mmにカットし短繊維集束体を得た。
実施例3において、ワックスを付着させなかった以外は、実施例3と同様の方法により得られたPPTA繊維複合体を、3.5mmにカットし短繊維集束体を得た。
Claims (4)
- 集束体を構成するアラミド短繊維の表面に、ラテックスを含有する集束剤と、オレフィン系ワックス及び脂肪酸アミド系ワックスから選ばれる少なくとも1種のワックスが付着していることを特徴とするゴム補強用アラミド短繊維集束体。
- ワックスを水分散させたエマルジョン状態にして、ラテックスを含有する集束剤と混合したものを、集束体を構成するアラミド短繊維の表面に付着させた、請求項1記載のゴム補強用アラミド短繊維集束体。
- アラミド短繊維が、あらかじめエポキシ基含有化合物を繊維骨格内に浸透させたアラミド繊維である、請求項1または2記載のゴム補強用アラミド短繊維集束体。
- アラミド繊維の表面に、ラテックスを含有する集束剤と、オレフィン系ワックス及び脂肪酸アミド系ワックスから選ばれる少なくとも1種のワックスと、を水に分散させてエマルジョン状態としたものを付着させた後、
前記集束剤及びワックスを付着させたアラミド繊維集束体をカットする
ことを特徴とするアラミド短繊維集束体の製造方法。