JP5294137B2 - 硬質ポリウレタンフォームの製造方法 - Google Patents
硬質ポリウレタンフォームの製造方法 Download PDFInfo
- Publication number
- JP5294137B2 JP5294137B2 JP2007328557A JP2007328557A JP5294137B2 JP 5294137 B2 JP5294137 B2 JP 5294137B2 JP 2007328557 A JP2007328557 A JP 2007328557A JP 2007328557 A JP2007328557 A JP 2007328557A JP 5294137 B2 JP5294137 B2 JP 5294137B2
- Authority
- JP
- Japan
- Prior art keywords
- isocyanate
- rigid polyurethane
- polyurethane foam
- catalyst
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
実施例1〜5、比較例1〜2
表1に示す原料を用いて、硬質ポリウレタンフォームを製造した。
ラボミキサーにより攪拌混合されて得られた発泡性の混合物を、幅=500mm、厚さ=60mm、深さ=500mmの内部寸法を有する天面開放型のモールドに上方から注入して、発泡・硬化させた。注型を開始してから10分間経過後に脱型し、500mm(幅方向)×60mm(厚み方向)×500mm(組成物の流れ方向=発泡方向)の寸法を有する成形品を得た。
MR−200 :ミリオネート(登録商標)MR−200
ポリメリックMDI
日本ポリウレタン工業(株)製
イソシアネート含量=31.0%
二核体含有量=41%
二核体中の4,4′−MDI含有量=99%
TCPP :トリス(β−クロロプロピル)ホスフェート
CR530 :含ハロゲン縮合リン酸エステル
CR733S :非ハロゲン縮合リン酸エステル
※難燃剤は全て大八化学工業(株)製
B−8462 :シリコン整泡剤
ゴールドシュミット製
P15 :商品名DABCO(登録商標)P15
三級アミン触媒
エアープロダクツ製
TR20 :商品名TOYOCAT(登録商標)−TR20
三級アミン触媒
東ソー(株)製
DT :TOYOCAT−DT
ペンタメチルジエチレントリアミン
三級アミン触媒
東ソー(株)製
NMM :N−メチルモルフォリン
ポリオール−1:ジエチレングリコール/フタル酸系ポリエステルポリオール
水酸基価=210mgKOH/g
ポリオール−2:ポリ(オキシプロピレン)ポリオール
開始剤=シュークローズとグリセリン混合物
水酸基価=375mgKOH/g
発泡状態:
目視観察にて評価
○:外観に異常が確認されない
×:陥没や収縮が確認される
酸素指数:
JIS K7201に準拠
コーンカロリー試験:
ISO5660に準拠
コーンカロリメーター(アトラス社製「CONE2A」)
寸法安定性:
試料〔100mm(幅方向)×60mm(厚み方向)×100mm(発泡方向)〕を、温度25℃×湿度50RH%の雰囲気下に48時間放置し、放置前後の寸法(発泡方向・幅方向・厚み方向)からその変化率を測定した。
○ :変化率1%未満
○〜△:変化率1%以上〜2%未満
△ :変化率2%以上〜5%未満
△〜×:変化率5%以上〜10%未満
× :10%以上
圧縮強度:
試料〔100mm(幅方向)×60mm(厚み方向)×100mm(発泡方向)〕について、JIS K 7220に準拠して、厚み方向における10%圧縮時の圧縮応力を測定した。
○:外観に異常が確認されない
×:陥没や収縮が確認される
Claims (2)
- 有機ポリイソシアネート(A)と水(B)とを、全配合物に対して10〜70質量%の難燃剤(C)、整泡剤(D)、イソシアヌレート化反応触媒を含む触媒(E)の存在下、かつ、全イソシアネート反応性基の5モル%以下のポリオールの存在下又は不存在下で、
水のイソシアネート反応性当量を9として計算したときのイソシアネートインデックス(全イソシアネート基/全イソシアネート反応性基のモル比の100倍)が150以上の条件下で、ウレア化反応及びイソシアヌレート化反応により発泡・硬化させることを特徴とする硬質ポリウレタンフォームの製造方法。 - 有機ポリイソシアネート(A)が、ポリメリックMDIであることを特徴とする、請求項1記載の硬質ポリウレタンフォームの製造方法。