JP2016132846A - 壁紙裏打ち用不織布 - Google Patents
壁紙裏打ち用不織布 Download PDFInfo
- Publication number
- JP2016132846A JP2016132846A JP2015009989A JP2015009989A JP2016132846A JP 2016132846 A JP2016132846 A JP 2016132846A JP 2015009989 A JP2015009989 A JP 2015009989A JP 2015009989 A JP2015009989 A JP 2015009989A JP 2016132846 A JP2016132846 A JP 2016132846A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- wallpaper
- fibers
- fiber
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】壁紙裏打ち用不織布において、パルプ繊維とコットンリンターと繊維状バインダーとを含むことを特徴とする壁紙裏打ち用不織布であり、繊維状バインダーの一部または全てがポリビニルアルコール繊維であること、表面に顔料が付与されていることが好ましい。
【選択図】なし
Description
パルパー分散タンク中の水に、下記配合で繊維を投入して10分間混合分散した後、貯蔵タンクに送り、一定量ずつ抄紙機に送り抄造し、ヤンキードライヤー面に当てて乾燥し、坪量100g/m2の壁紙裏打ち用不織布を得た。
未叩解コットンリンター 5部
芯鞘繊維状バインダー
(商品名:メルティー(登録商標)4080、ユニチカ社製、2.2dtex×5mm)
20部
繊維の部数を表1記載のように変えた以外は、実施例1と同様にして壁紙裏打ち用不織布を得た。
繊維の配合を下記のように変えた以外は、実施例1と同様にして壁紙裏打ち用不織布を得た。
未叩解コットンリンター 10部
PVA繊維状バインダー
(商品名:VPB107、クラレ社製、1.1dtex×3mm、PVA繊維)
10部
繊維の配合を下記のように変えた以外は、実施例1と同様にして壁紙裏打ち用不織布を得た。
未叩解コットンリンター 20部
芯鞘繊維状バインダー
(商品名:メルティー(登録商標)4080、ユニチカ社製、2.2dtex×5mm)
10部
繊維状バインダー
(商品名:VPB107、クラレ社製、1.1dtex×3mm、PVA繊維)
5部
繊維の配合を下記のように変えた以外は、実施例1と同様にして壁紙裏打ち用紙を得た。
未叩解コットンリンター 40部
繊維の配合を下記のように変えた以外は、実施例1と同様にして壁紙裏打ち用不織布を得た。
芯鞘繊維状バインダー
(商品名:メルティー(登録商標)4080、ユニチカ社製、2.2dtex×5mm)
5部
パルパー分散タンク中の水に未叩解コットンリンター、芯鞘繊維状バインダー(商品名:メルティー4080、ユニチカ社製、2.2デシテックス×5mm)を95:5の比率で投入して10分間混合分散した後、第一貯蔵タンクに送り、第1層用として一定量ずつ第一抄紙ヘッドに送り、坪量60g/m2となるように第1層を先に抄造した。
パルパー分散タンク中の水に未叩解コットンリンター、芯鞘繊維状バインダー(商品名:メルティー4080、ユニチカ社製、2.2デシテックス×5mm)を95:5の比率で投入して10分間混合分散した後、第一貯蔵タンクに送り、第1層用として一定量ずつ第一抄紙ヘッドに送り、坪量40g/m2となるように第1層を先に抄造した。
顔料として酸化チタン(商品名:W−10、石原産業社製)、バインダーとしてアクリルエマルジョン(商品名:ボンコート(登録商標)MAT−200−E、DIC社製)及びポリビニルアルコール(商品名:PVA−110、クラレ社製)をそれぞれ100:20:5の比率で水に分散、混合し、顔料塗工液を作製した。本塗工液をエアナイフ塗工装置にて実施例6の不織布の表面に乾燥質量で25g/m2塗工後乾燥させ、壁紙裏打ち用不織布を得た。
顔料をカオリン(商品名:ニュークレイ、エンゲルハード社製)に変えた以外は、実施例7と同様にして壁紙裏打ち用不織布を得た。
壁紙裏打ち用不織布を温度20℃、湿度65%RHの環境下で24時間以上調湿し、サンプルの横方向の長さ(原寸)を正確に測定する。このサンプルを温度23℃の水中へ5分間浸した後、速やかにサンプルの長さを測定し、原寸に対する伸び率を求めた。0に近いほど寸法安定性が良い。従来の経験則より、伸び率は0.6%以内が望ましく、最低でも1.0%以内が必要である。結果を表1及び2に示した。
壁紙裏打ち用不織布を温度23℃、湿度50%RH環境下で24時間調湿した後、MD方向32cm×CD方向15cmとなるように裁断した。なお、サンプリングの際は紙面を擦らないよう十分注意をして行った。ガラス板上に坪量150g/m2の上質紙2枚を敷き、クリップにて固定した。次に幅250mm×長さ130mm×厚さ15mmの金属立方体(重さ400g)にガーゼを4重に巻きつけ、上質紙面を2回擦り、ガーゼ面をならした。上質紙上に壁紙裏打ち用不織布を、ポリ塩化ビニル塗工・印刷面となる表面を上にして乗せ、その表面を用意したガーゼを巻きつけた金属立方体にて、自重によりMD方向で上から下に向かって1回擦った。壁紙裏打ち用不織布の上下方向の向きを変え、同様に上から下に向かって1回擦った。この壁紙裏打ち用不織布の擦った場所に、塗工厚200μmのアプリケーターを用い、塩化ビニルペーストを塗工し、145℃の乾燥機中に1分間入れ、塩化ビニルペーストをゲル化させた。ゲル化したポリ塩化ビニル層面の中央部に5cm×10cmの切り抜いた型紙を乗せ、その中に発生した毛羽立ち由来の突起物の数を計測した。結果は、同様にして作製したサンプル4枚の計測値の合計(200cm2あたりの個数)を計測した。計測した突起物の数が25個以下を「◎」、26〜50個を「○」、51〜150個を「△」、151個以上を「×」と評価した。結果を表1及び2に示した。
グラビア印刷機を用いて水性インキ(黒)で印刷し、印刷状態を観察し、◎〜×の評価を行った。結果を表1及び2に示した。
◎:印刷状態が非常に良好
○:印刷状態が良好
△:僅かに印刷抜けが見られる
×:印刷抜けが多く使用できない
実施例6〜8の壁紙裏打ち用不織布の不透明度をJIS P 8149:2000に準じて測定し、隠蔽性の評価を行った。壁紙裏打ち用不織布の不透明度は84%以上が好ましい。より好ましくは86%以上であり、隠蔽性が良好となる。不透明度が84%以上の場合、壁紙メーカーにて改めて壁紙裏打ち用不織布に隠蔽性を付与する工程を省略することが可能となる。結果を表2に示した。
Claims (3)
- 壁紙裏打ち用不織布において、パルプ繊維とコットンリンターと繊維状バインダーとを含むことを特徴とする壁紙裏打ち用不織布。
- 繊維状バインダーの一部または全てがポリビニルアルコール繊維である請求項1記載の壁紙裏打ち用不織布。
- 表面に顔料が付与されている請求項1または2記載の壁紙裏打ち用不織布。