CN1306129C - 一种多孔混凝土砌块 - Google Patents
一种多孔混凝土砌块 Download PDFInfo
- Publication number
- CN1306129C CN1306129C CNB2004100773326A CN200410077332A CN1306129C CN 1306129 C CN1306129 C CN 1306129C CN B2004100773326 A CNB2004100773326 A CN B2004100773326A CN 200410077332 A CN200410077332 A CN 200410077332A CN 1306129 C CN1306129 C CN 1306129C
- Authority
- CN
- China
- Prior art keywords
- present
- porous concrete
- building blocks
- raw material
- block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种多孔混凝土砌块,其是由水泥、煤灰、发泡剂、添加剂等原料制成;本发明的多孔混凝土砌块的比重较采用沙石作为原料的砌块小;本发明的砌块在生产过程中可产生大量的细小气泡,使砌块内形成有一些细小的气孔,从而使本发明具有良好的隔音、隔热、防火性能;同时由于主要原料采用的是废弃的粉煤灰,可解决粉煤灰的处置问题,变废为宝,从而有利于保护环境。
Description
技术领域
本发明涉及一种水泥混凝土砌块,特别是一种作为建筑墙体材料的水泥混凝土砌块。
背景技术
由于水泥混凝土砌块既可保护土地资源及生态环境,又无须进行烧制,因此其作为一种建筑墙体材料正逐步取代红砖,并且其已得到广泛的应用。现在作为水泥混凝土砌块的主要原料是水泥和沙石,由于沙石的比重比较大,并且由沙石制的水泥混凝土砌块内比较密实,从而使由沙石为原料的水泥混凝土砌块的比重比较大,并且这种水泥混凝土砌块在隔音、隔热、防火等性能上都存在一定的局限性。
发明内容
为了克服现有技术的不足,本发明提供一种比重轻、并且具有良好的隔音、隔热、防火性能的多孔混凝土砌块。
本发明解决其技术问题所采用的技术方案是:
一种多孔混凝土砌块,其特征在于它是由下述重量百分比的原料制成:水泥55~65%、煤灰34~45%、发泡剂0.2~0.6%、添加剂0.2~0.5%。
本发明的多孔混凝土砌块,其最佳的各原料组分的重量百分配比为:水泥60%、煤灰39.3%、发泡剂0.4%、添加剂0.3%。
本发明的发泡剂优选采用由60~70%H2O2和30~40%Ca(ClO)2组成的混合物。
本发明的添加剂优选采用甲醛树脂、环氧树脂或乙烯树脂中的一种或一种以上的混合物。
本发明的多孔混凝土砌块可采用如下方法制得:按上述配比备齐原料,然后将配制好的原料加入搅拌机内,并加入一定比例的水后搅拌均匀,将搅拌均匀的混凝土浆料浇灌成砌块,待砌块自然风干即可。
本发明的有益效果是:本发明的多孔混凝土砌块由水泥和煤灰作为主要原料,由于粉煤灰的比重比沙石轻,因此本发明的多孔混凝土砌块的比重较采用沙石作为原料的砌块小;由于在原料中加入了发泡剂,在生产砌块过程中发泡剂可产生大量的细小气泡,使砌块内形成有一些细小的气孔,从而使本发明具有良好的隔音、隔热、防火性能;同时由于主要原料采用的是废弃的粉煤灰,可解决粉煤灰的处置问题,变废为宝,从而有利于保护环境。
下面结合附图和实施例对本发明进一步说明。
具体实施方式
实施例1
将水泥500千克、煤灰300千克、H2O22500毫克、Ca(ClO)21500毫克、甲醛树脂2500毫克加入到搅拌机内,搅拌均匀,并加入一定量的水制成浆料,将搅拌均匀的混凝土浆料浇灌成砌块,待砌块自然风干即制得本发明的多孔混凝土砌块。
实施例2
将水泥550千克、煤灰450千克、H2O23000毫克、Ca(ClO)22000毫克、甲醛树脂3000毫克加入到搅拌机内,搅拌均匀,并加入一定量的水制成浆料,将搅拌均匀的混凝土浆料浇灌成砌块,待砌块自然风干即制得本发明的多孔混凝土砌块。
实施例3
将水泥650千克、煤灰350千克、H2O24000毫克、Ca(ClO)23000毫克、甲醛树脂5000毫克加入到搅拌机内,搅拌均匀,并加入一定量的水制成浆料,将搅拌均匀的混凝土浆料浇灌成砌块,待砌块自然风干即制得本发明的多孔混凝土砌块。
实践证明,本发明的多孔混凝土砌块的密度在500kg/M3~1200kg/M3之间,导热率在0.092~0.132kgcal/m/hr/m2/℃之间,抗压强度在32~78kg/cm2之间,满足建筑材料的要求,并且本发明的多孔混凝土砌块重量轻,并具有良好的隔音、隔热、防火性能。
Claims (4)
1.一种多孔混凝土砌块,其特征在于它是由下述重量百分比的原料制成:水泥55~65%、煤灰34~45%、发泡剂0.2~0.6%、添加剂0.2~0.5%。
2.一种多孔混凝土砌块,其特征在于它是由下述重量百分比的原料制成:水泥60%、煤灰39.3%、发泡剂0.4%、添加剂0.3%。
3.根据权利要求1或2所述的一种多孔混凝土砌块,其特征在于所述发泡剂由60~70%H2O2和30~40%Ca(ClO)2组成。
4.根据权利要求1或2所述的一种多孔混凝土砌块,其特征在于所述添加剂为甲醛树脂、环氧树脂或乙烯树脂中的一种或一种以上的混合物。