CN115142197A - 一种驱蚊亲肤无纺布及其制备方法 - Google Patents
一种驱蚊亲肤无纺布及其制备方法 Download PDFInfo
- Publication number
- CN115142197A CN115142197A CN202210846083.0A CN202210846083A CN115142197A CN 115142197 A CN115142197 A CN 115142197A CN 202210846083 A CN202210846083 A CN 202210846083A CN 115142197 A CN115142197 A CN 115142197A
- Authority
- CN
- China
- Prior art keywords
- parts
- mosquito
- woven fabric
- skin
- friendly non
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种驱蚊亲肤无纺布及其制备方法,所述驱蚊亲肤无纺布包括以下重量份的原料:聚对苯二甲酸乙二醇酯50~62份、聚乙二醇改性聚对苯二甲酸乙二醇酯25~30份、丙烯酰胺接枝改性天然橡胶12~16份、聚羟基脂肪酸酯6~9份、泡沸石粉2~3份、沉淀白炭黑3~4.5份、艾叶提取物1.5~2份、天竺葵提取物1~1.4份、银离子抗菌母粒5~7份、棕榈酸异辛酯3~5份。本发明的驱蚊亲肤无纺布透气率高,透气性能良好;吸湿常数大,吸湿速率高,容易吸水吸汗,吸水率较高,吸水吸汗量较大,具有良好的亲肤性能;此外,具有较好的力学性能和良好的驱蚊效果和抗菌抑菌效果。
Description
技术领域
本发明涉及无纺布技术领域,具体涉及一种驱蚊亲肤无纺布及其制备方法。
背景技术
无纺布又称不织布、针刺棉、针刺无纺布等,采用聚酯纤维,涤纶纤维(简称:PET)材质生产,经过针刺工艺制作而成,可做出不同的厚度、手感、硬度等。无纺布具有防潮、透气、柔韧、轻薄、阻燃、无毒无味、价格低廉、可循环再用等特点。
无纺布是一种非织造布,它是直接利用高聚物切片、短纤维或长丝将纤维通过气流或机械成网,然后经过水刺,针刺,或热轧加固,最后经过后整理形成的无编织的布料。具有柔软、透气和平面结构的新型纤维制品,优点是不产生纤维屑,强韧、耐用、丝般柔软,也是增强材料的一种,而且还有棉质的感觉,和棉织品相比,无纺布的袋子容易成形,而且造价便宜。
但是,目前所使用的亲肤无纺布还存在以下问题:
1、不具备驱蚊效果,或者驱蚊效果差;
2、需要跟粘胶纤维、棉纤维等混合生产,纯化纤的聚酯无纺布吸湿(吸汗)性能差,透气性能差,不亲肤,舒适性差;
3、改性添加剂添加过多等原因,导致力学性能变差,容易损坏不耐用。
发明内容
基于上述情况,本发明的目的在于提供一种驱蚊亲肤无纺布及其制备方法,可有效解决以上问题。本发明的驱蚊亲肤无纺布通过精选原料组成,并优化各原料含量,既充分发挥各原料的优点,又相互补充,相互促进,制得的驱蚊亲肤无纺布的透气率高,透气性能良好;吸湿常数大,吸湿速率高,容易吸水吸汗,吸水率较高,吸水吸汗量较大,具有良好的亲肤性能;此外,本发明的驱蚊亲肤无纺布的顶破强力大,具有较好的力学性能。此外,本发明的驱蚊亲肤无纺布具有良好的驱蚊效果和抗菌抑菌效果。
为解决以上技术问题,本发明提供的技术方案是:
一种驱蚊亲肤无纺布,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯50~62份、
聚乙二醇改性聚对苯二甲酸乙二醇酯25~30份、
丙烯酰胺接枝改性天然橡胶12~16份、
聚羟基脂肪酸酯6~9份、
泡沸石粉2~3份、
沉淀白炭黑3~4.5份、
艾叶提取物1.5~2份、
天竺葵提取物1~1.4份、
银离子抗菌母粒5~7份、
棕榈酸异辛酯3~5份。
本发明的驱蚊亲肤无纺布通过精选原料组成,并优化各原料含量,既充分发挥各原料的优点,又相互补充,相互促进,制得的驱蚊亲肤无纺布的透气率高,透气性能良好;吸湿常数大,吸湿速率高,容易吸水吸汗,吸水率较高,吸水吸汗量较大,具有良好的亲肤性能;此外,本发明的驱蚊亲肤无纺布的顶破强力大,具有较好的力学性能。此外,本发明的驱蚊亲肤无纺布具有良好的驱蚊效果和抗菌抑菌效果。
优选的,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯56份、
聚乙二醇改性聚对苯二甲酸乙二醇酯27.5份、
丙烯酰胺接枝改性天然橡胶14份、
聚羟基脂肪酸酯7.5份、
泡沸石粉2.5份、
沉淀白炭黑3.7份、
艾叶提取物1.8份、
天竺葵提取物1.2份、
银离子抗菌母粒6份、
棕榈酸异辛酯4份。
优选的,所述驱蚊亲肤无纺布还包括以下重量份的原料:热稳定剂3~4.5份。
优选的,所述热稳定剂为硬脂酸锌和硬脂酸的混合物;所述硬脂酸锌和硬脂酸的混合物中硬脂酸锌和硬脂酸的质量之比为1:0.35~0.45。
优选的,所述驱蚊亲肤无纺布还包括以下重量份的原料:抗紫外线剂2~4份。
优选的,所述抗紫外线剂为2-苯基苯咪唑-5-磺酸。
优选的,所述泡沸石粉的粒径为5000~6000目。
优选的,所述沉淀白炭黑的孔容为1.5~1.8cm3/g。
优选的,所述银离子抗菌母粒中银系抗菌粉的含量为20~25wt%,载体树脂为聚对苯二甲酸乙二醇酯,含量为58~66wt%。
本发明还提供一种所述的驱蚊亲肤无纺布的制备方法,包括下列步骤:
A、按重量份分别称取所述的驱蚊亲肤无纺布的各原料,将泡沸石粉和沉淀白炭黑分别烘干后,与艾叶提取物和天竺葵提取物混合均匀,再与剩余原料混合均匀,得到混合料;
B、将所述混合料送入双螺杆挤出机熔融成混合熔体;
C、所述混合熔体经挤出、拉丝、铺网、热轧后,得到所述驱蚊亲肤无纺布。
本发明与现有技术相比,具有以下优点及有益效果:
本发明的驱蚊亲肤无纺布通过精选原料组成,并优化各原料含量,选择了适当比例的聚对苯二甲酸乙二醇酯、聚乙二醇改性聚对苯二甲酸乙二醇酯(提升亲水亲肤性)、丙烯酰胺接枝改性天然橡胶(具有增强作用,还能提升亲水亲肤性)、聚羟基脂肪酸酯(提升亲水亲肤性)、泡沸石粉、沉淀白炭黑、艾叶提取物、天竺葵提取物(艾叶提取物和天竺葵提取物先被吸附到泡沸石粉和沉淀白炭黑的微孔结构中,制成成品后缓慢释放出来,起到良好的驱蚊效果,且艾叶提取物和天竺葵提取物相互配合驱蚊效果更佳;此外,泡沸石粉和沉淀白炭黑均匀良好的吸附性能,可吸水吸汗,且沉淀白炭黑还能起到良好的增强作用)、银离子抗菌母粒(赋予抗菌抑菌性能)、棕榈酸异辛酯(提升亲肤性),既充分发挥各原料的优点,又相互补充,相互促进,制得的驱蚊亲肤无纺布的透气率高,透气性能良好;吸湿常数大,吸湿速率高,容易吸水吸汗,吸水率较高,吸水吸汗量较大,具有良好的亲肤性能;此外,本发明的驱蚊亲肤无纺布的顶破强力大,具有较好的力学性能。此外,本发明的驱蚊亲肤无纺布具有良好的驱蚊效果和抗菌抑菌效果。
具体实施方式
为了使本领域的技术人员更好地理解本发明的技术方案,下面结合具体实施例对本发明的优选实施方案进行描述,但是不能理解为对本专利的限制。
下述实施例中所述试验方法或测试方法,如无特殊说明,均为常规方法;所述试剂和材料,如无特殊说明,均从常规商业途径获得,或以常规方法制备。
实施例1:
一种驱蚊亲肤无纺布,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯50份、
聚乙二醇改性聚对苯二甲酸乙二醇酯25份、
丙烯酰胺接枝改性天然橡胶12份、
聚羟基脂肪酸酯6份、
泡沸石粉2份、
沉淀白炭黑3份、
艾叶提取物1.5份、
天竺葵提取物1份、
银离子抗菌母粒5份、
棕榈酸异辛酯3份。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:热稳定剂3份。
在本实施例中,所述热稳定剂为硬脂酸锌和硬脂酸的混合物;所述硬脂酸锌和硬脂酸的混合物中硬脂酸锌和硬脂酸的质量之比为1:0.35。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:抗紫外线剂2份。
在本实施例中,所述抗紫外线剂为2-苯基苯咪唑-5-磺酸。
在本实施例中,所述泡沸石粉的粒径为5000目。
在本实施例中,所述沉淀白炭黑的孔容为1.5~1.8cm3/g。
在本实施例中,所述银离子抗菌母粒中银系抗菌粉的含量为20wt%,载体树脂为聚对苯二甲酸乙二醇酯,含量为66wt%。
一种所述的驱蚊亲肤无纺布的制备方法,包括下列步骤:
A、按重量份分别称取所述的驱蚊亲肤无纺布的各原料,将泡沸石粉和沉淀白炭黑分别烘干后,与艾叶提取物和天竺葵提取物混合均匀,再与剩余原料混合均匀,得到混合料;
B、将所述混合料送入双螺杆挤出机熔融成混合熔体;
C、所述混合熔体经挤出、拉丝、铺网、热轧后,得到所述驱蚊亲肤无纺布。
实施例2:
一种驱蚊亲肤无纺布,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯62份、
聚乙二醇改性聚对苯二甲酸乙二醇酯30份、
丙烯酰胺接枝改性天然橡胶16份、
聚羟基脂肪酸酯9份、
泡沸石粉3份、
沉淀白炭黑4.5份、
艾叶提取物2份、
天竺葵提取物1.4份、
银离子抗菌母粒7份、
棕榈酸异辛酯5份。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:热稳定剂4.5份。
在本实施例中,所述热稳定剂为硬脂酸锌和硬脂酸的混合物;所述硬脂酸锌和硬脂酸的混合物中硬脂酸锌和硬脂酸的质量之比为1:0.45。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:抗紫外线剂4份。
在本实施例中,所述抗紫外线剂为2-苯基苯咪唑-5-磺酸。
在本实施例中,所述泡沸石粉的粒径为6000目。
在本实施例中,所述沉淀白炭黑的孔容为1.5~1.8cm3/g。
在本实施例中,所述银离子抗菌母粒中银系抗菌粉的含量为25wt%,载体树脂为聚对苯二甲酸乙二醇酯,含量为58wt%。
一种所述的驱蚊亲肤无纺布的制备方法,包括下列步骤:
A、按重量份分别称取所述的驱蚊亲肤无纺布的各原料,将泡沸石粉和沉淀白炭黑分别烘干后,与艾叶提取物和天竺葵提取物混合均匀,再与剩余原料混合均匀,得到混合料;
B、将所述混合料送入双螺杆挤出机熔融成混合熔体;
C、所述混合熔体经挤出、拉丝、铺网、热轧后,得到所述驱蚊亲肤无纺布。
实施例3:
一种驱蚊亲肤无纺布,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯56份、
聚乙二醇改性聚对苯二甲酸乙二醇酯27.5份、
丙烯酰胺接枝改性天然橡胶14份、
聚羟基脂肪酸酯7.5份、
泡沸石粉2.5份、
沉淀白炭黑3.7份、
艾叶提取物1.8份、
天竺葵提取物1.2份、
银离子抗菌母粒6份、
棕榈酸异辛酯4份。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:热稳定剂3.8份。
在本实施例中,所述热稳定剂为硬脂酸锌和硬脂酸的混合物;所述硬脂酸锌和硬脂酸的混合物中硬脂酸锌和硬脂酸的质量之比为1:0.4。
在本实施例中,所述驱蚊亲肤无纺布还包括以下重量份的原料:抗紫外线剂3份。
在本实施例中,所述抗紫外线剂为2-苯基苯咪唑-5-磺酸。
在本实施例中,所述泡沸石粉的粒径为5500目。
在本实施例中,所述沉淀白炭黑的孔容为1.5~1.8cm3/g。
在本实施例中,所述银离子抗菌母粒中银系抗菌粉的含量为22.5wt%,载体树脂为聚对苯二甲酸乙二醇酯,含量为62wt%。
一种所述的驱蚊亲肤无纺布的制备方法,包括下列步骤:
A、按重量份分别称取所述的驱蚊亲肤无纺布的各原料,将泡沸石粉和沉淀白炭黑分别烘干后,与艾叶提取物和天竺葵提取物混合均匀,再与剩余原料混合均匀,得到混合料;
B、将所述混合料送入双螺杆挤出机熔融成混合熔体;
C、所述混合熔体经挤出、拉丝、铺网、热轧后,得到所述驱蚊亲肤无纺布。
对比例1:
与实施例3的区别在于,没有聚乙二醇改性聚对苯二甲酸乙二醇酯,其他与实施例3相同。
对比例2:
与实施例3的区别在于,没有丙烯酰胺接枝改性天然橡胶,其他与实施例3相同。
对比例3:
与实施例3的区别在于,没有聚羟基脂肪酸酯,其他与实施例3相同。
对比例4:
与实施例3的区别在于,没有泡沸石粉,其他与实施例3相同。
对比例5:
与实施例3的区别在于,没有沉淀白炭黑,其他与实施例3相同。
对比例6:
与实施例3的区别在于,没有棕榈酸异辛酯,其他与实施例3相同。
下面对本发明实施例1至实施例3得到的驱蚊亲肤无纺布以及对比例1-6得到的无纺布分别进行性能测试,测试结果如表1所示:
表1
从上表可以看出,本发明的驱蚊亲肤无纺布的透气率高,透气性能良好;吸湿常数大,吸湿速率高,容易吸水吸汗,吸水率较高,吸水吸汗量较大,具有良好的亲肤性能;此外,本发明的驱蚊亲肤无纺布的顶破强力大,具有较好的力学性能。
此外,经测试本发明的驱蚊亲肤无纺布具有良好的驱蚊效果和抗菌抑菌效果。
以上仅是本发明的优选实施方式,应当指出的是,上述优选实施方式不应视为对本发明的限制,本发明的保护范围应当以权利要求所限定的范围为准。对于本技术领域的普通技术人员来说,在不脱离本发明的精神和范围内,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种驱蚊亲肤无纺布,其特征在于,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯50~62份、
聚乙二醇改性聚对苯二甲酸乙二醇酯25~30份、
丙烯酰胺接枝改性天然橡胶12~16份、
聚羟基脂肪酸酯6~9份、
泡沸石粉2~3份、
沉淀白炭黑3~4.5份、
艾叶提取物1.5~2份、
天竺葵提取物1~1.4份、
银离子抗菌母粒5~7份、
棕榈酸异辛酯3~5份。
2.根据权利要求1所述的驱蚊亲肤无纺布,其特征在于,所述驱蚊亲肤无纺布包括以下重量份的原料:
聚对苯二甲酸乙二醇酯56份、
聚乙二醇改性聚对苯二甲酸乙二醇酯27.5份、
丙烯酰胺接枝改性天然橡胶14份、
聚羟基脂肪酸酯7.5份、
泡沸石粉2.5份、
沉淀白炭黑3.7份、
艾叶提取物1.8份、
天竺葵提取物1.2份、
银离子抗菌母粒6份、
棕榈酸异辛酯4份。
3.根据权利要求1或2任一项所述的驱蚊亲肤无纺布,其特征在于,所述驱蚊亲肤无纺布还包括以下重量份的原料:热稳定剂3~4.5份。
4.根据权利要求3所述的驱蚊亲肤无纺布,其特征在于,所述热稳定剂为硬脂酸锌和硬脂酸的混合物;所述硬脂酸锌和硬脂酸的混合物中硬脂酸锌和硬脂酸的质量之比为1:0.35~0.45。
5.根据权利要求1或2任一项所述的驱蚊亲肤无纺布,其特征在于,所述驱蚊亲肤无纺布还包括以下重量份的原料:抗紫外线剂2~4份。
6.根据权利要求5所述的驱蚊亲肤无纺布,其特征在于,所述抗紫外线剂为2-苯基苯咪唑-5-磺酸。
7.根据权利要求4或6任一项所述的驱蚊亲肤无纺布,其特征在于,所述泡沸石粉的粒径为5000~6000目。
8.根据权利要求4或6任一项所述的驱蚊亲肤无纺布,其特征在于,所述沉淀白炭黑的孔容为1.5~1.8cm3/g。
9.根据权利要求4或6任一项所述的驱蚊亲肤无纺布,其特征在于,所述银离子抗菌母粒中银系抗菌粉的含量为20~25wt%,载体树脂为聚对苯二甲酸乙二醇酯,含量为58~66wt%。
10.一种如权利要求1所述的驱蚊亲肤无纺布的制备方法,其特征在于,包括下列步骤:
A、按重量份分别称取所述的驱蚊亲肤无纺布的各原料,将泡沸石粉和沉淀白炭黑分别烘干后,与艾叶提取物和天竺葵提取物混合均匀,再与剩余原料混合均匀,得到混合料;
B、将所述混合料送入双螺杆挤出机熔融成混合熔体;
C、所述混合熔体经挤出、拉丝、铺网、热轧后,得到所述驱蚊亲肤无纺布。