CN103571025A - 持久型防雾滴聚烯烃薄膜母料 - Google Patents
持久型防雾滴聚烯烃薄膜母料 Download PDFInfo
- Publication number
- CN103571025A CN103571025A CN201210250678.6A CN201210250678A CN103571025A CN 103571025 A CN103571025 A CN 103571025A CN 201210250678 A CN201210250678 A CN 201210250678A CN 103571025 A CN103571025 A CN 103571025A
- Authority
- CN
- China
- Prior art keywords
- mlldpe
- masterbatch
- vam
- grafts
- droplet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种防雾滴聚乙烯薄膜母料及其制备方法，以mLLDPE的重量为百分之百计，包括：（1）100％的mLLDPE，（2）6%～12%的防雾滴剂，（3）5%～10%的mLLDPE-g-VAM接枝物；该母料明显改善防雾滴剂与PE树脂相容性，阻碍了小分子防雾滴剂在PE树脂内部的快速迁移和析出，解决了聚乙烯棚膜使用的中后期雾滴害问题。该母料从一般内添加型吹塑农用聚乙烯棚膜防雾滴持效期3～10个月左右可延长至35个月以上，显著提高了农用聚乙烯棚膜的防雾滴性能，具有较好的市场应用前景。
Description
技术领域
本发明涉及一种聚乙烯树脂组合物，具体涉及在聚乙烯棚膜中显著提高防雾滴效果和持久性的聚乙烯薄膜母料。
背景技术
目前，我国的塑料大棚膜主要是聚乙烯棚膜，聚乙烯具有优良的耐寒、防尘、易加工等特性，但它是一种疏水性树脂，其薄膜的表面张力与水的表面张力相差较大。早春或晚秋季节时，塑料大棚内外的温度和湿度差异较大，采用普通薄膜覆盖棚室后，当塑料薄膜表面温度达到露点以下时，空气中的水汽达到饱和或过饱和时就会在棚膜内壁凝结成大量雾滴。雾滴的存在会导致光散射或反射，降低作为农用或园艺用大棚膜的透光性，影响作物的光合作用。同时雾滴滴落在棚内植物上，还会造成植物的叶、茎、芽的枯萎或腐烂，直接降低作物的产量和质量。我国于20世纪80年代末期进行聚乙烯防雾滴膜的研制，利用表面活性剂提高聚乙烯的临界表面张力，从而使凝聚在聚乙烯膜内壁的微小水珠铺展成一层透明水膜，并顺膜壁向下流入地面，达到防雾滴的效果。
现有技术中，提高塑料表面的润湿性并赋予其无滴性的方法主要有两种：外涂覆无滴剂型和内添加无滴剂型。一是外涂覆法采用高压喷枪在大棚内进行表面喷涂处理。该方法的相关报道较多，如：JP2001211760、JP03-244907、JP2003013038(A)、EP0732387、ZL200510025184.8、ZL200610064906.5等。由于这种方法不仅需要喷涂设备，操作繁琐，成本较高，而且存在溶剂挥发污染环境的问题，所以国内多采用内添加法。二是内添加法就是在塑料棚膜的生产过程中，将无滴剂添加到原料树脂中一同进行混炼、塑化，而后吹塑成膜。如：ZL03119742.6提供了一种由马来酸酐醇醚酯混合物和高碳醇醚混合物共同组成的无滴聚乙烯棚膜组合物。CN1225929A公开了一种以含氟、含硅表面活性剂的消雾剂与以多元醇酯和烷基酚聚氧乙烯醚的无滴剂按比例配制成消雾型高效无滴剂，用其生产出具有优良的消雾功能和无滴效率的农用大棚膜。JP 11310648采用乙烯和己烯共聚物与LDPE和适量的硬脂酸酯类防雾滴剂、含氟表面活性剂共同吹制成薄膜，其防雾滴有效期达10个月。JP 11322965提供了一种由含氟表面活性剂和失水山梨醇单硬脂酸酯、二甘油二硬脂酸酯、亚甲基二硬脂酰胺、水解石共同组成的防雾滴剂，添加到LLDPE棚膜中可以表现出良好的长期防雾滴性能。
上述专利基本都是直接添加防雾滴剂，虽然在提高聚乙烯薄膜防雾滴性方面已取得明显的效果，但在薄膜防雾滴的持效性方面不是十分理想。由于防雾滴剂与PE树脂相容性差，亲水性的小分子防雾滴剂在PE树脂内部存在迁移和析出的问题，在水的不断作用下,常会出现防雾滴剂逐渐流失而丧失其功能，其防雾滴持效期只能维持3～10个月左右，这样在聚乙烯棚膜使用的中后期雾滴害问题比较突出。
发明内容
本发明目的在于提供一种防雾滴持效期在35个月以上且初期防雾滴效果优良的mLLDPE防雾滴薄膜母料。本发明进一步提出母料的制备方法。
本发明防雾滴聚乙烯薄膜母料，以茂金属线性低密度聚乙烯（mLLDPE）的重量为百分之百计，主要包括以下组份：
1）100%的mLLDPE
2）6%～12%的防雾滴剂
3）5%～10%的mLLDPE-g-VAM接枝物
所述的mLLDPE-g-VAM接枝物是在引发剂的作用下将接枝单体接枝到mLLDPE主链上的接枝共聚物。引发剂选自叔丁基过氧化氢、2,5-二甲基-2,5-二叔丁基过氧化己烷（BPDH）、二叔丁基过氧化物（DTBP）、过氧化二异丙苯（DCP）、过氧化苯甲酰（BPO）中的一种，优选BPO。接枝单体为醋酸乙烯酯（VAM），纯度≥99%。聚合物mLLDPE以采用单活性中心催化剂——茂金属催化体系制备的聚乙烯，可以是乙烯和丁烯-1、己烯-1、辛烯-1共聚而得，也可以由乙烯均聚而得。其中密度（ρ）：0.865～0.941g/cm3；熔体流动速率（MFR）：0.5～10g/10min。
所述的熔体流动速率（MFR）是在190℃，2.16Kg负荷下的测定值。
所述的mLLDPE-g-VAM接枝物的制备方法为：按mLLDPE的重量百分比计，将5～10份的醋酸乙烯酯（VAM）与100份的mLLDPE高速混合5～10min，将混合好的物料在密闭容器中放置10～20h；然后取0.05～0.2份的引发剂和丙酮按重量比为1∶2～1∶4配制成混合溶液，再将混合溶液和放置好的混合物料高速混合5～10min，最后通过双螺杆挤出机中进行熔融接枝反应，反应温度160～210℃，反应时间5～10min，挤出、冷却、造粒，得到VAM接枝率为2％～4％的mLLDPE-g-VAM接枝物。
所述的引发剂为有机过氧化物均为市售产品，其半衰期温度因生产商的不同而略有差别，一般BPO的半衰期T=131～134℃/1min；BPDH的半衰期T=179～186℃/1min。
所述的mLLDPE可以是粉状或粒状树脂，但为达到更好的混合效果以粉状树脂最佳。
本发明所述的防雾滴剂为多元醇脂肪酸酯类化合物(含10-22个C的脂肪酸)，可以选自失水山梨醇单月桂酸酯(S-20)、失水山梨醇单棕榈酸酯(S-40)、失水山梨醇单硬脂酸酯(S-60)、失水山梨醇三硬脂酸酯(S-65)、失水山梨醇单油酸酯(S-80)、失水山梨醇三油酸酯(S-85)等中的一种或多种混合物，其用量为6%～12%（按mLLDPE的重量百分比计）。
本发明所述母料的制备可以在密炼机、捏合机、双螺杆挤出机中进行，但以双螺杆挤出机为最佳。选用双螺杆挤出机制备时，可以采用原料预先混合、再进行挤出的制备工艺。
具体地，本发明提供的mLLDPE防雾滴母料的制备方法如下：按mLLDPE的重量百分比计，将100份的mLLDPE和5～10份的mLLDPE-g-VAM接枝物一起放入到高速混合器中，高速混合3～5min；然后再加入6～12份的防雾滴剂、0.1～0.2份的稳定剂、0.1～0.2份的抗氧剂高速混合3～5min；最后将混合好的物料加入双螺杆挤出机，反应温度170～220℃，反应时间3～5min，挤出、冷却、造粒，制得mLLDPE防雾滴薄膜母料。
本发明在mLLDPE防雾滴母料的制备过程中还可加入一定量的热稳定剂和抗氧剂等助剂，助剂的加入只为满足稳定加工的要求，不会对母料的性能产生影响。
所述的抗氧剂可以是酚类、受阻胺类、亚磷酸酯类抗氧剂中的一种或数种复配物，如1010、1076、168、2246、1010与168复配等。稳定剂为硬脂酸盐类，如硬脂酸锌、硬脂酸钙、硬脂酸镁等。
本发明的mLLDPE防雾滴母料在聚乙烯棚膜中的添加量为10%～15%（按聚乙烯棚膜树脂的重量份计），即可制得初期防雾滴效果优良，防雾滴持效期在35个月以上的聚乙烯棚膜。
本发明所述的母料中，首先，mLLDPE防雾滴母料中mLLDPE-g-VAM接枝物的极性作用可以明显改善防雾滴剂和载体树脂mLLDPE的相容性，且mLLDPE与聚乙烯棚膜的基础树脂有着相似的分子结构，使得防雾滴剂以母粒的形式就能够均匀地分散在聚乙烯棚膜中，进而赋予聚乙烯棚膜良好的防流滴性能。
同时，这种低接枝率的mLLDPE-g-VAM接枝物对防雾滴剂小分子有一定的吸附，但这种吸附在不影响雾滴剂在棚膜基础树脂中分散的情况下，又能够阻碍防雾滴剂小分子在聚乙烯棚膜中的快速迁移和析出，起到一定的缓释作用，使得防雾滴剂慢慢地向膜表面迁移，达到长期防雾滴的效果。
其次，mLLDPE-g-VAM接枝物的分子主链结构与聚乙烯分子结构相同，使其具有亲水性的乙酯侧基能够均匀地分散到聚乙烯棚膜表面，又因其具有多羟基强氢键特点，可以有效地提高膜面的表面张力，极大地降低水与膜面之间的接触角，在薄膜表面上很容易吸附周围环境中的微量水分，从而使凝结薄膜表面上的细小雾滴迅速扩散形成连续的水膜，这样就极大地提高了聚乙烯棚膜的初期防雾滴性。
具体实施方式
⑴原料
1）树脂
2）有机过氧化物
BPO 半衰期T=133℃/1min，兰州助剂厂
BPDH 半衰期T=186℃/1min，兰州助剂厂
3）其它助剂
⑵性能测试
薄膜接触角θ的测定：取8cm×2cm的防雾滴膜固定在载玻片上,于接触角测定仪上进行测定。
初期防雾滴性:将烧杯置于60℃的恒温水槽中，环境温度为室温，观察15min内薄膜表面的水迹情况。A:膜面无变化；B:膜面产生水迹，但在3min内消失；C:膜面产生水迹，但在15min内消失；D:15min后膜面仍有水迹，但透明。
高温防雾滴性：取一块长15cm，宽15cm，厚度约为0.08mm的正方形棚膜，罩于500mL的烧杯上，杯口扎紧，烧杯内装有300mL水。然后将烧杯置于60℃的恒温水槽中，呈15°倾角，环境温度为室温。60℃时膜上雾滴面积超过膜面的1/3视为失效。棚膜从开始使用到失效所经历的时间定义为棚膜的无滴持效期。
低温防雾滴性:取一块长15cm，宽15cm，厚度约为0.08mm的正方形棚膜，罩于500mL的烧杯上，杯口扎紧，烧杯内装有300mL水。然后将烧杯置于18℃的恒温水槽中，环境温度为-5℃。膜上雾滴面积超过1/4视为失效。
棚膜防滴持久性评价：农田大棚覆盖进行实际观测，棚膜内表面鳞片状水滴的分布面积达到50%的天数。●：棚膜内表面鳞片状水滴的分布面积达到50%以下，膜透明性好。○：棚膜内表面鳞片状水滴的分布面积达到50%以上，膜透明性差。
接枝率:化学滴定法。
⑶设备及仪器
Ф67双螺杆挤出机 长/径=34/1 德国Lestreiz公司
10升高速混合机 阜新塑料机械厂
Ф120三层复合吹膜机 大连橡塑机械厂
接触角测定仪J2150 承德实验机公司
实施例及对比例
列举以下实施例来说明本发明的发明效果，但是本发明的保护范围并不仅限于这些实施例，组合物中各组分以基础树脂mLLDPE的重量份数计。
实施例1
（一）mLLDPE-g-VAM接枝物的制备：将6份的醋酸乙烯酯（VAM）与100份的mLLDPE高速混合5min，将混合好的物料在密闭容器中放置12h；然后取0.08份的BPO和0.2份丙酮配制成混合溶液，再将混合溶液和放置好的混合物一起放入10L高速混合机中，高速混合5min；最后将混合好的物料加入到Ф67双螺杆挤出机中，螺杆各段反应温度（℃）依次为：160，165，170，180，195，210，190，180，170；进行熔融接枝反应，反应6min后，挤出、冷却、造粒，得到mLLDPE-g-VAM接枝物（接枝率：2.3%）。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（HPR18H10AX）和5.5份接枝率为2.3%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入7份失水山梨醇单月桂酸酯(S-20)、0.1份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例2
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（HPR18H10AX）和7份接枝率为2.3%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入9份失水山梨醇单月桂酸酯(S-20)、0.15份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例3
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（HPR18H10AX）和8份接枝率为2.3%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入10份失水山梨醇单月桂酸酯(S-20)、0.15份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例4
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（HPR18H10AX）和9份接枝率为2.3%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入11份失水山梨醇单月桂酸酯(S-20)、0.15份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例5
（一）mLLDPE-g-VAM接枝物的制备：将9份的醋酸乙烯酯（VAM）与100份的mLLDPE高速混合5min，将混合好的物料在密闭容器中放置12h；然后取0.12份的BPO和0.4份丙酮配制成混合溶液，再将混合溶液和放置好的混合物一起放入10L高速混合机中，高速混合5min；最后将混合好的物料加入到Ф67双螺杆挤出机中，螺杆各段反应温度（℃）依次为：160，165，170，180，195，210，190，180，170；进行熔融接枝反应，反应6min后，挤出、冷却、造粒，得到mLLDPE-g-VAM接枝物（接枝率：3.4%）。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（ECD350）和5.5份接枝率为3.4%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入7份失水山梨醇单棕榈酸酯(S-40)、0.1份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例6
（一）mLLDPE-g-VAM接枝物的制备：同实施例5。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（ECD350）和7份接枝率为3.4%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入9份失水山梨醇单棕榈酸酯(S-40)、0.15份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例7
（一）mLLDPE-g-VAM接枝物的制备：同实施例5。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（ECD350）和8份接枝率为3.4%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入10份失水山梨醇单棕榈酸酯(S-40)、0.15份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
实施例8
（一）mLLDPE-g-VAM接枝物的制备：将8份的醋酸乙烯酯（VAM）与100份的mLLDPE高速混合5min，将混合好的物料在密闭容器中放置12h；然后取0.15份的BPDH和0.5份丙酮配制成混合溶液，再将混合溶液和放置好的混合物一起放入10L高速混合机中，高速混合5min；最后将混合好的物料加入到Ф67双螺杆挤出机中，螺杆各段反应温度（℃）依次为：160，165，170，180，195，210，190，180，170；进行熔融接枝反应，反应6min后，挤出、冷却、造粒，得到mLLDPE-g-VAM接枝物（接枝率：3.1%）。
（二）mLLDPE防雾滴母料的制备：将100份mLLDPE（ECD350）和9份接枝率为3.1%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入6份失水山梨醇单月桂酸酯(S-20)、5份失水山梨醇单棕榈酸酯(S-40)、0.15份抗氧剂168、0.2份硬脂酸锌，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
对比例1
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：其它条件与实施例1相同，不同之处在于母料的制备过程中mLLDPE-g-VAM接枝物（接枝率：2.3%）的加入量为4份，即：将100份mLLDPE（HPR18H10AX）和4份接枝率为2.3%的mLLDPE-g-VAM接枝物一起放入到10升高速混合机中，高速混合3min；然后再加入7份失水山梨醇单月桂酸酯(S-20)、0.1份抗氧剂1010、0.15份硬脂酸钙，高速混合5min；将混合后的物料加入到Ф67双螺杆挤出机，螺杆各段反应温度（℃）依次为：170，180，190，200，210，220，200，190，180；反应4min后，挤出、冷却、造粒，得到mLLDPE防雾滴母料。
对比例2
mLLDPE防雾滴母料的制备：其它条件与实施例2相同，不同之处在于母料的制备过程中不加mLLDPE-g-VAM接枝物（接枝率：2.3%）。
对比例3
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：其它条件与实施例3相同，不同之处在于母料的制备过程中不加入失水山梨醇单月桂酸酯(S-20)。
对比例4
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）mLLDPE防雾滴母料的制备：其它条件与实施例4相同，不同之处在于母料的制备过程中不加失水山梨醇单月桂酸酯(S-20)。
对比例5
（一）mLLDPE-g-VAM接枝物的制备：同实施例5。
（二）mLLDPE防雾滴母料的制备：其它条件与实施例5相同，不同之处在于母料的制备过程中不加mLLDPE-g-VAM接枝物（接枝率：3.4%）。
对比例6
（一）mLLDPE-g-VAM接枝物的制备：同实施例5。
（二）mLLDPE防雾滴母料的制备：其它条件与实施例6相同，不同之处在于母料的制备过程中不加入失水山梨醇单棕榈酸酯(S-40)。
对比例7
mLLDPE防雾滴母料的制备：其它条件与实施例7相同，不同之处在于母料的制备过程中不加mLLDPE-g-VAM接枝物（接枝率：3.4%）。
对比例8
（一）mLLDPE-g-VAM接枝物的制备：同实施例8。
（二）mLLDPE防雾滴薄膜母料的制备：其它条件与实施例8相同，不同之处在于母料的制备过程中不加入失水山梨醇单棕榈酸酯(S-40)和失水山梨醇单月桂酸酯(S-20)。
实施例1～8和对比例1～8所制得的防雾滴母料在棚膜中的应用对比：将线性低密度聚乙烯棚膜专用树脂LLDPE（LL106AA）分别与实施例1～8和对比例1～8所制得的防雾滴母料以10%的添加量（按LLDPE重量份计）进行混合均匀，其中对比例3制备的母料还需与1.0份失水山梨醇单月桂酸酯(S-20)进行预先混合；对比例6制得的母料还需与0.9份失水山梨醇单棕榈酸酯(S-40)预先混合；对比例8制备的母料还需与0.6份失水山梨醇单月桂酸酯(S-20)和0.5份失水山梨醇单棕榈酸酯(S-40)进行预先混合，然后在Ф120三层复合吹膜机组上吹制宽幅棚膜（幅宽8m，厚度为0.08mm），分别标记为：实施膜1～8和对比膜1～8，其棚膜防雾滴性能的测试结果见表1。
对比膜9
（一）mLLDPE-g-VAM接枝物的制备：同实施例1。
（二）聚乙烯棚膜的制备：在棚膜的制备过程中mLLDPE-g-VAM接枝物（接枝率：2.3%）和失水山梨醇单月桂酸酯(S-20)不是以母料的形式加入，而是直接加入到聚乙烯棚膜专用树脂LLDPE（LL106AA）中，且加入量同实施例1用量的10%相同，即：按LLDPE重量份计，将100份线性低密度聚乙烯棚膜专用树脂LLDPE（LL106AA）与0.55份接枝率为2.3%的mLLDPE-g-VAM、0.7份失水山梨醇单月桂酸酯(S-20)直接进行混合，然后在Ф120三层复合吹膜机组上吹制宽幅棚膜（幅宽8m，厚度为0.08mm），其棚膜防雾滴性能的测试结果见表1。
表1 含10%实施例和对比例母料的棚膜防雾滴性能
Claims (7)
1.一种防雾滴聚乙烯薄膜母料，以mLLDPE的重量为百分之百计，其特征在于包括以下组份：
1）100%的mLLDPE
2）6%～12%的防雾滴剂
3）5%～10%的mLLDPE-g-VAM接枝物
所述的mLLDPE-g-VAM接枝物是在引发剂的作用下将醋酸乙烯酯单体接枝到mLLDPE主链上的接枝共聚物。
2.如权利要求1所述的聚乙烯薄膜母料，其特征在于所述的引发剂选自叔丁基过氧化氢、2,5-二甲基-2,5-二叔丁基过氧化己烷、二叔丁基过氧化物、过氧化二异丙苯、过氧化苯甲酰中的一种。
3.如权利要求1所述的聚乙烯薄膜母料，其特征在于所述的mLLDPE-g-VAM接枝物的制备方法为：按mLLDPE的重量百分比计，将5～10份的醋酸乙烯酯与100份的mLLDPE高速混合5～10min，将混合好的物料在密闭容器中放置10～20h；然后取0.05～0.2份的引发剂和丙酮按重量比为1∶2～1∶4配制成混合溶液，再将混合溶液和放置好的混合物料高速混合5～10min，最后通过双螺杆挤出机中进行熔融接枝反应，反应温度160～210℃，反应时间5～10min，挤出、冷却、造粒，得到mLLDPE-g-VAM接枝物。
4.如权利要求1所述的聚乙烯薄膜母料，其特征在于所述的防雾滴剂选自失水山梨醇单月桂酸酯、失水山梨醇单棕榈酸酯、失水山梨醇单硬脂酸酯、失水山梨醇三硬脂酸酯、失水山梨醇单油酸酯、失水山梨醇三油酸酯等中的一种或多种混合物，按mLLDPE的重量百分比计，其用量为6%～12%。
5.如权利要求1所述的聚乙烯薄膜母料，其特征在于薄膜母料制备过程中加入抗氧剂和热稳定剂。
6.如权利要求1所述的聚乙烯薄膜母料，其特征在于按聚乙烯棚膜树脂的重量份计，所述的mLLDPE防雾滴母料在聚乙烯棚膜中的添加量为10%～15%。
7.一种如权利要求1-5之一所述的聚乙烯薄膜母料的制备方法，其特征在于包括：按mLLDPE的重量百分比计，将100份的mLLDPE和5～10份的mLLDPE-g-VAM接枝物一起放入到高速混合器中，高速混合3～5min；然后再加入6～12份的防雾滴剂高速混合3～5min；最后将混合好的物料加入双螺杆挤出机，反应温度170～220℃，反应时间3～5min，挤出、冷却、造粒，制得防雾滴聚乙烯薄膜母料。